CN107129622A - Snow defence show and colour - Google Patents

Snow defence show and colour Download PDF

Info

Publication number
CN107129622A
CN107129622A CN201710532843.XA CN201710532843A CN107129622A CN 107129622 A CN107129622 A CN 107129622A CN 201710532843 A CN201710532843 A CN 201710532843A CN 107129622 A CN107129622 A CN 107129622A
Authority
CN
China
Prior art keywords
weight
parts
colour
snow defence
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710532843.XA
Other languages
Chinese (zh)
Inventor
梅霖陶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Mark Vision Network Technology Co Ltd
Original Assignee
Sichuan Mark Vision Network Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan Mark Vision Network Technology Co Ltd filed Critical Sichuan Mark Vision Network Technology Co Ltd
Priority to CN201710532843.XA priority Critical patent/CN107129622A/en
Publication of CN107129622A publication Critical patent/CN107129622A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of snow defence show and colour, belong to technical field of advertisement.The snow defence show and colour of the present invention includes：The parts by weight of polyethylene 80~86；The parts by weight of calcium carbonate 5~10, the parts by weight of polyacrylamide 3~5, the parts by weight of ethyl cellulose 3~5, the parts by weight of antifreeze 1~5, the parts by weight of foaming agent 0.5~1.8, the parts by weight of paraffin 5~10, the parts by weight of acetic acid 5~8, the parts by weight of attapulgite 2~4, the parts by weight of graphite 2~4, the parts by weight of potassium nitrate 2~4, the parts by weight of ice crystal sand 5~10, the parts by weight of calcium chloride 3~6.The snow defence show and colour of the present invention is shined upon, and the heat storage phase-changing material in snow defence show and colour absorbs heat energy and stored, and under conditions of no daylight, heat storage phase-changing material releases energy.So as to play the anti-freeze effect of snow defence.The snow defence show and colour of the present invention is easy to make, and technique is simple, is conducive to popularization and application.

Description

Snow defence show and colour
Technical field
The present invention relates to a kind of snow defence show and colour, belong to technical field of advertisement.
Background technology
Show and colour is the carrier of advertisement, and existing advertisement form is various, there is image, word, video, audio etc., wherein The advertisement of picture and text form is most common.The advertisement of many picture and text forms, road sign are disposed in the outdoor, or even field, can usually face snow, The extreme weather conditions such as ice.Not only block vision, and fragile show and colour, so as to reduce its service life.
Polyethylene odorless, nontoxic, with excellent resistance to low temperature, chemical stability is good, is resistant to invading for most of soda acids Erosion.Common solvent is not dissolved under normal temperature, water imbibition is small, and electrical insulating property is excellent.
The content of the invention
The invention solves the problems that first technical problem be to provide a kind of snow defence show and colour.
In order to solve the above technical problems, the snow defence show and colour of the present invention includes：The parts by weight of polyethylene 80~86；Calcium carbonate 5~10 parts by weight, the parts by weight of polyacrylamide 3~5, the parts by weight of ethyl cellulose 3~5, the parts by weight of antifreeze 1~5, foaming agent 0.5~1.8 parts by weight, the parts by weight of paraffin 5~10, the parts by weight of acetic acid 5~8, the parts by weight of attapulgite 2~4, the weight of graphite 2~4 Part, the parts by weight of potassium nitrate 2~4, the parts by weight of ice crystal sand 5~10, the parts by weight of calcium chloride 3~6.
Further, the one kind of the foaming agent in Arcton 11, dicholorodifluoromethane, pentamethylene and isopentane Or several mixing.
Further, the antifreeze be 2,2,2- nitroso three, 0.15~0.17wt% of ethanol, sodium nitrate 0.09~ 0.12wt%, BTA 0.05~0.08wt% of amine salt, remaining is the mixture of ethylene glycol.
Further, the snow defence show and colour is prepared by following methods：
A. material is weighed, polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C storage Can material；
D. mixed material and antifreeze in a steps and b step are mixed at 100~110 DEG C and knead 5~8 points Clock, adds mixture C and foaming agent, is kneaded 8~12 minutes at 120~140 DEG C, is cooled to 80~85 DEG C, keeps 80~85 DEG C, 0.5~0.6Mpa obtains snow defence show and colour in 15~20 minutes.
The invention solves the problems that second technical problem be to provide a kind of preparation method of above-mentioned snow defence show and colour.
To solve second technical problem of the present invention, the technique of the preparation method of snow defence show and colour of the invention is such as Under：
A. material is weighed, polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C；
D. mixed material and antifreeze in a steps and b step are mixed at 100~110 DEG C and knead 5~8 points Clock, adds mixture C and foaming agent, is kneaded 8~12 minutes at 120~140 DEG C, is cooled to 80~85 DEG C, keeps 80~85 DEG C, 0.5~0.6Mpa obtains snow defence show and colour in 15~20 minutes.
Beneficial effect：The snow defence show and colour of the present invention is shined upon, the heat accumulation phase transformation material in snow defence show and colour Material absorbs heat energy and stored, and under conditions of no daylight, heat storage phase-changing material releases energy.So as to play snow defence anti-caking The effect of ice.
The snow defence show and colour of the present invention is easy to make, and technique is simple, is conducive to popularization and application.
Embodiment
The snow defence show and colour of the present invention includes：The parts by weight of polyethylene 80~86；The parts by weight of calcium carbonate 5~10, polypropylene The parts by weight of acid amides 3~5, the parts by weight of ethyl cellulose 3~5, the parts by weight of antifreeze 1~5, the parts by weight of foaming agent 0.5~1.8, stone The parts by weight of wax 5~10, the parts by weight of acetic acid 5~8, the parts by weight of attapulgite 2~4, the parts by weight of graphite 2~4, the weight of potassium nitrate 2~4 Part, the parts by weight of ice crystal sand 5~10, the parts by weight of calcium chloride 3~6.
Further, the one kind of the foaming agent in Arcton 11, dicholorodifluoromethane, pentamethylene and isopentane Or several mixing.
Further, the antifreeze be 2,2,2- nitroso three, 0.15~0.17wt% of ethanol, sodium nitrate 0.09~ 0.12wt%, BTA 0.05~0.08wt% of amine salt, remaining is the mixture of ethylene glycol.
Further, the snow defence show and colour is prepared by following methods：
A. material is weighed, polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C storage Can material；
D. mixed material and antifreeze in a steps and b step are mixed at 100~110 DEG C and knead 5~8 points Clock, adds mixture C and foaming agent, is kneaded 8~12 minutes at 120~140 DEG C, is cooled to 80~85 DEG C, keeps 80~85 DEG C, 0.5~0.6Mpa obtains snow defence show and colour in 15~20 minutes.
The technique of the preparation method of the snow defence show and colour of the present invention is as follows：
A. material is weighed, polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C；
D. mixed material and antifreeze in a steps and b step are mixed at 100~110 DEG C and knead 5~8 points Clock, adds mixture C and foaming agent, is kneaded 8~12 minutes at 120~140 DEG C, is cooled to 80~85 DEG C, keeps 80~85 DEG C, 0.5~0.6Mpa obtains snow defence show and colour in 15~20 minutes.
Embodiment 1
Take the ethanol 0.2g of 2,2,2- nitroso three, sodium nitrate 0.12g, BTA amine salt 0.08g, ethylene glycol 120g mixing Obtain antifreeze.
Weigh the parts by weight of polyethylene 80, the parts by weight of calcium carbonate 8, the parts by weight of polyacrylamide 4, the parts by weight of ethyl cellulose 4, The parts by weight of antifreeze 5, the parts by weight of pentamethylene 1, the parts by weight of paraffin 6, the parts by weight of acetic acid 6, the parts by weight of attapulgite 3, the weight of graphite 3 Part, the parts by weight of potassium nitrate 3, the parts by weight of ice crystal sand 7, the parts by weight of calcium chloride 4.
A. polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C storage Can material；
D. mixed material and antifreeze in a steps and b step are mixed at 100 DEG C and kneaded 7 minutes, added Mixture C and pentamethylene, are kneaded 10 minutes at 130 DEG C, are cooled to 80 DEG C, are kept for 80 DEG C, 0.5Mpa is prevented for 20 minutes Avenge show and colour.
Embodiment 2
Take the ethanol 0.2g of 2,2,2- nitroso three, sodium nitrate 0.12g, BTA amine salt 0.08g, ethylene glycol 120g mixing Obtain antifreeze.
Weigh the parts by weight of polyethylene 85, the parts by weight of calcium carbonate 5, the parts by weight of polyacrylamide 3, the parts by weight of ethyl cellulose 4, The parts by weight of antifreeze 5, the parts by weight of isopentane 1, the parts by weight of paraffin 8, the parts by weight of acetic acid 8, the parts by weight of attapulgite 4, the weight of graphite 3 Part, the parts by weight of potassium nitrate 4, the parts by weight of ice crystal sand 8, the parts by weight of calcium chloride 5.
A. polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C storage Can material；
D. mixed material and antifreeze in a steps and b step are mixed at 110 DEG C and kneaded 5 minutes, added Mixture C and isopentane, are kneaded 10 minutes at 120 DEG C, are cooled to 80 DEG C, are kept for 80 DEG C, 0.6Mpa is prevented for 15 minutes Avenge show and colour.

Claims (5)

1. snow defence show and colour, it is characterised in that the snow defence show and colour includes：The parts by weight of polyethylene 80~86；Calcium carbonate 5 ~10 parts by weight, the parts by weight of polyacrylamide 3~5, the parts by weight of ethyl cellulose 3~5, the parts by weight of antifreeze 1~5, foaming agent 0.5~1.8 parts by weight, the parts by weight of paraffin 5~10, the parts by weight of acetic acid 5~8, the parts by weight of attapulgite 2~4, the weight of graphite 2~4 Part, the parts by weight of potassium nitrate 2~4, the parts by weight of ice crystal sand 5~10, the parts by weight of calcium chloride 3~6.
2. snow defence show and colour according to claim 1, it is characterised in that the foaming agent is selected from Arcton 11, two One or more of mixing in dichlorodifluoromethane, pentamethylene and isopentane.
3. snow defence show and colour according to claim 1 or 2, it is characterised in that the antifreeze is 2,2,2- nitrosos Three 0.15~0.17wt% of ethanol, 0.09~0.12wt% of sodium nitrate, BTA 0.05~0.08wt% of amine salt, remaining is second The mixture of glycol.
4. the snow defence show and colour according to any one of claim 1-3, it is characterised in that the snow defence show and colour by Following methods are prepared：
A. material is weighed, polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C energy storage material Material；
D. mixed material and antifreeze in a steps and b step are mixed at 100~110 DEG C and kneaded 5~8 minutes, Mixture C and foaming agent are added, is kneaded 8~12 minutes at 120~140 DEG C, 80~85 DEG C are cooled to, is kept for 80~85 DEG C, 0.5~0.6Mpa obtains snow defence show and colour in 15~20 minutes.
5. the preparation method of the snow defence show and colour according to any one of claim 1-4, it is characterised in that methods described Technique it is as follows：
A. material is weighed, polyethylene and polyacrylamide are mixed；
B. calcium carbonate and ethyl cellulose are mixed；
C. by paraffin, acetic acid, attapulgite, graphite, potassium nitrate, ice crystal sand, calcium chloride is well mixed, and obtains mixture C；
D. mixed material and antifreeze in a steps and b step are mixed at 100~110 DEG C and kneaded 5~8 minutes, Mixture C and foaming agent are added, is kneaded 8~12 minutes at 120~140 DEG C, 80~85 DEG C are cooled to, is kept for 80~85 DEG C, 0.5~0.6Mpa obtains snow defence show and colour in 15~20 minutes.
CN201710532843.XA 2017-07-03 2017-07-03 Snow defence show and colour Pending CN107129622A (en)