CN107129606A - A kind of heat resistant rubber product sizing material - Google Patents
A kind of heat resistant rubber product sizing material Download PDFInfo
- Publication number
- CN107129606A CN107129606A CN201710321703.8A CN201710321703A CN107129606A CN 107129606 A CN107129606 A CN 107129606A CN 201710321703 A CN201710321703 A CN 201710321703A CN 107129606 A CN107129606 A CN 107129606A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- rubber
- sizing material
- butadiene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to rubber processing technique field, and in particular to a kind of electro-insulating rubber product and its preparation technology.A kind of heat resistant rubber product sizing material, it is characterised in that its formula components is as follows：The parts by weight of butadiene-styrene rubber 80 120, the parts by weight of zinc oxide 10 15, the parts by weight of stearic acid 13, the parts by weight of age resistor 26, the parts by weight of accelerator 25, the parts by weight of high abrasion charcoal 40 55, the parts by weight of Petropols 48 and the parts by weight of calcium carbonate 36.The formula of the rubber sizing material of the present invention is obtained by test of many times, and obtained rubbery heat resistance is good；Butadiene-styrene rubber additive carries out rational proportion and obtains rubber, good, durable with effect, can be widely used in conveyer belt rubber cover, and method is simple, and cost is low.
Description
Technical field
The present invention relates to rubber processing technique field, and in particular to a kind of heat resistant rubber product sizing material and its application.
Background technology
Natural rubber or synthetic rubber are in sulfur cross-linking system, peroxide vulcanizing system, resin curative systems or metal
Under the effect such as oxide curative systems, formed in vulcanization crosslinking under high temperature, condition of high voltage.Under high temperature, condition of high voltage, above-mentioned sulphur
Change system easily produces pollution human body, the exudate of medicament, volatile matter.For many years, although people are in basic robber materialses, glue
A large amount of improvements have been done in terms of material formula, production technology and post processing, but still have been difficult to preparation and have met medicine first water
The rubber of standard.
In ageing of rubber factors, oxidation is most common, and heat, oxygen collective effect are extremely common.In a constant temperature
In the range of degree, heat is only capable of encouraging the effect of oxygen, and heating up to the influence that rubber performance is reduced has exponential relationship.
The information for being disclosed in the background section is merely intended to understanding of the increase to the general background of the present invention, without answering
When the prior art for being considered as recognizing or implying the information structure in any form well known to persons skilled in the art.
The content of the invention
The present invention provides a kind of with heat-resisting, oxygen rubber sizing compound formula and application thereof.
A kind of heat resistant rubber product sizing material, the formula components are as follows：Butadiene-styrene rubber 80-120 parts by weight, zinc oxide 10-
15 parts by weight, stearic acid 1-3 parts by weight, age resistor 2-6 parts by weight, accelerator 2-5 parts by weight, high abrasion charcoal 40-55 parts by weight,
Petropols 4-8 parts by weight and calcium carbonate 3-6 parts by weight.
It is preferred that, the heat resistant rubber product sizing material, its formula components are as follows：Butadiene-styrene rubber 90-100 parts by weight, oxidation
Zinc 12-14 parts by weight, stearic acid 2-3 parts by weight, age resistor 3-5 parts by weight, accelerator 4-5 parts by weight, high abrasion charcoal 45-50 weights
Measure part, Petropols 5-7 parts by weight and calcium carbonate 5-6 parts by weight.
Further preferably, described heat resistant rubber product sizing material, its formula components are as follows：The parts by weight of butadiene-styrene rubber 100, oxygen
Change the parts by weight of zinc 13, the parts by weight of stearic acid 2, the parts by weight of age resistor 4, the parts by weight of accelerator 4, the parts by weight of high abrasion charcoal 47, oil
The parts by weight of resin 5 and the parts by weight of calcium carbonate 5.
Application of the rubber sizing material of the present invention in hot material conveyor belt rubber cover is prepared.
Compared with prior art, the present invention has the advantages that：
(1) formula of rubber sizing material of the invention is obtained by test of many times, and obtained rubbery heat resistance is good.
(2) butadiene-styrene rubber additive carries out rational proportion and obtains rubber, good, durable with effect, can be covered in conveyer belt
Widely used in lid glue, method is simple, and cost is low.
Embodiment
The embodiment of the present invention is described in detail with reference to embodiment, it is to be understood that the guarantor of the present invention
Shield scope is not limited by embodiment.
Explicitly indicated that unless otherwise other, otherwise in entire disclosure and claims, term " comprising " or its change
Change such as "comprising" or " including " etc. and will be understood to comprise stated element or part, and do not exclude other members
Part or other parts.
Embodiment 1：
A kind of heat resistant rubber product sizing compound formula, the formula components are as follows：The parts by weight of butadiene-styrene rubber 80, the weight of zinc oxide 12
Measure part, the parts by weight of stearic acid 1, the parts by weight of age resistor 2, the parts by weight of accelerator 3, the parts by weight of high abrasion charcoal 50, the weight of Petropols 6
Part, the parts by weight of calcium carbonate 4.
Embodiment 2：
A kind of heat resistant rubber product sizing compound formula, the formula components are as follows：The parts by weight of butadiene-styrene rubber 100, zinc oxide 10
Parts by weight, the parts by weight of stearic acid 3, the parts by weight of age resistor 6, the parts by weight of accelerator 4, the parts by weight of high abrasion charcoal 45, the weight of Petropols 7
Measure part, the parts by weight of calcium carbonate 5.
Embodiment 3：
A kind of heat resistant rubber product sizing compound formula, the formula components are as follows：The parts by weight of butadiene-styrene rubber 110, zinc oxide 11
Parts by weight, the parts by weight of stearic acid 2.5, the parts by weight of age resistor 3.5, the parts by weight of accelerator 4, the parts by weight of high abrasion charcoal 55, oil tree
The parts by weight of fat 5, the parts by weight of calcium carbonate 4.
Embodiment 4：
A kind of heat resistant rubber product sizing compound formula, the formula components are as follows：The parts by weight of butadiene-styrene rubber 120, zinc oxide 13
Parts by weight, the parts by weight of stearic acid 3, the parts by weight of age resistor 3, the parts by weight of accelerator 6, the parts by weight of high abrasion charcoal 52, Petropols 5.5
Parts by weight, the parts by weight of calcium carbonate 4.5.
Heat resistant rubber product in embodiment 1-4 is prepared using preparation technology known in the art, and tests its performance
Constant is as shown in table 1.
The performance parameters of table 1 are determined
As it can be seen from table 1 the indices of heat resistant rubber product are also superior to country obtained by 1-3 of the embodiment of the present invention
Standard.
It is foregoing to the present invention specific illustrative embodiment description be in order to illustrate and illustration purpose.These descriptions
It is not wishing to limit the invention to disclosed precise forms, and it will be apparent that according to above-mentioned teaching, can be much changed
And change.The purpose of selecting and describing the exemplary embodiment is that explaining that the certain principles and its reality of the present invention should
With so that those skilled in the art can realize and using the present invention a variety of exemplaries and
A variety of selections and change.The scope of the present invention is intended to be limited by claims and its equivalents.
Claims (4)
1. a kind of heat resistant rubber product sizing material, it is characterised in that its formula components is as follows：Butadiene-styrene rubber 80-120 parts by weight, oxygen
Change zinc 10-15 parts by weight, stearic acid 1-3 parts by weight, age resistor 2-6 parts by weight, accelerator 2-5 parts by weight, high abrasion charcoal 40-55
Parts by weight, Petropols 4-8 parts by weight and calcium carbonate 3-6 parts by weight.
2. rubber sizing material according to claim 1, it is characterised in that its formula components is as follows：Butadiene-styrene rubber 90-
100 parts by weight, zinc oxide 12-14 parts by weight, stearic acid 2-3 parts by weight, age resistor 3-5 parts by weight, accelerator 4-5 parts by weight,
High abrasion charcoal 45-50 parts by weight, Petropols 5-7 parts by weight and calcium carbonate 5-6 parts by weight.
3. rubber sizing material according to claim 1, it is characterised in that its formula components is as follows：The weight of butadiene-styrene rubber 100
Measure part, the parts by weight of zinc oxide 13, the parts by weight of stearic acid 2, the parts by weight of age resistor 4, the parts by weight of accelerator 4, the weight of high abrasion charcoal 47
Part, the parts by weight of Petropols 5 and the parts by weight of calcium carbonate 5.
4. application of the rubber sizing material in hot material conveyor belt rubber cover is prepared according to claim 1-3.