CN107097323A - A kind of solid wooden compound floor toning edge sealing process - Google Patents

A kind of solid wooden compound floor toning edge sealing process Download PDF

Info

Publication number
CN107097323A
CN107097323A CN201710398509.XA CN201710398509A CN107097323A CN 107097323 A CN107097323 A CN 107097323A CN 201710398509 A CN201710398509 A CN 201710398509A CN 107097323 A CN107097323 A CN 107097323A
Authority
CN
China
Prior art keywords
blank
paint
toning
edge sealing
lamp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710398509.XA
Other languages
Chinese (zh)
Inventor
赵坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUBEI YANJIALONG WOOD PRODUCTS CO Ltd
Original Assignee
HUBEI YANJIALONG WOOD PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUBEI YANJIALONG WOOD PRODUCTS CO Ltd filed Critical HUBEI YANJIALONG WOOD PRODUCTS CO Ltd
Priority to CN201710398509.XA priority Critical patent/CN107097323A/en
Publication of CN107097323A publication Critical patent/CN107097323A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of solid wooden compound floor toning edge sealing process, comprise the following steps：(1) fixed length, fixed width, fixed thick cutting are carried out to blank and just sand is handled, washed ore polishing, is then primed in blank upper roller；(2) side of blank four fluting tenon, chamfering, toning alcohol edge sealing is smeared on the side of blank four, and toning alcohol is dissolved in industrial alcohol by color essence and is made；(3) sanding and polishing is carried out to blank surface, then in blank surface roller coat sanding paint, 320 mesh belt sandings is used after solidifying through UV lamp；(4) finish paint is applied；(5) examination and test of products is carried out, if white edge occurs in the side of floor four, toning alcohol is smeared to supplement at white edge so that with floor surface solid colour at white edge, obtain solid wooden floor board finished product；The present invention carries out toning edge sealing using the price alcohol lower than paraffin, and improves production technology, and the solid wooden compound floor yields of production can reduce production cost 10% up to more than 99% compared to paraffin edge sealing.

Description

A kind of solid wooden compound floor toning edge sealing process
Technical field
The present invention relates to a kind of solid wooden compound floor toning edge sealing process, belong to woodwork technology field.
Background technology
General production solid wooden compound floor process be tenon of first slotting, then finish coatings, four banding waxes, into product examine Test, pack.Because floor is difficult to accomplish no difference of height when slotting tenon, and there be chamfering on the side of surface four, is sprayed with sealing wax machine The wax (through color accurate adjustment color) shot out is difficult that the edges of boards of non-japanning are completely covered, therefore floor is after mating formation, it appears that had " white edge ", product qualification rate is less than 30%.Meanwhile, it is easy to produce wax stain on surface with side of sealing with wax, in subsequent survey process such as It was found that defective in quality, sanding again-paint is needed, paint film adhesion is influenceed because plate face has wax, causes that conjunction can not be done over again into The product of lattice.
The content of the invention
It is an object of the invention to overcome the shortcomings of existing solid wooden compound floor production technology there is provided one kind without using wax liquor Solid wooden compound floor toning edge sealing process, solve after composite floor board japanning that edge sealing is also easy to produce " white edge " and with side of sealing with wax again The problem of cost is high.
Realize that technical scheme that the object of the invention used is mixed colours edge sealing process for a kind of, solid wooden compound floor, including such as Lower step：
(1) fixed length, fixed width, fixed thick cutting and sand at the beginning of 180 mesh abrasive bands is carried out to blank to handle, then using 180 mesh or 240 mesh abrasive band washed ore polishings, then prime in blank upper roller；
(2) side of blank four fluting tenon, chamfering, in the side of blank four spraying toning alcohol edge sealing, the toning alcohol is by color essence It is dissolved in industrial alcohol and is made；
(3) sanding and polishing is carried out to blank surface using 240 mesh abrasive bands, then in blank surface with 15~25g/m3Cover with paint, lacquer, colour wash, etc. The road sanding paint of roller coat 2~3 is measured, 320 mesh belt sandings are used after solidifying through UV lamp；
(4) the blank surface coating finish paint after sanding；
(5) examination and test of products is carried out, if white edge occurs in the side of floor four, toning alcohol is smeared to supplement at white edge so that white With floor surface solid colour at side, solid wooden floor board finished product is obtained.
The particular content that step (1) central roll is primed is：
(1-1) roller coat aqueous priming paint on blank, aqueous priming paint is air-dried using infrared ray air-dry machine；
(1-2) is on blank with 25~35g/m3The reflowable putty of covering with paint amount roller coat UV, solidifies through UV lamp and by 240 mesh sand Band sanding, fills and leads up blank pore；
(1-3) is on blank with 15~25g/m3One of anticracking paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
(1-4) is on blank with 25~35g/m3One of wear resistant paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
(1-5) is on blank with 15~25g/m3The road sanding paint of covering with paint amount roller coat 2~5, uses 240 mesh after solidifying through UV lamp Belt sanding.
In step (1-2), if blank timber is crude fibre timber, first with 40~50g/m3It is heavy that covering with paint amount smears UV Putty, then the reflowable putty of roller coat UV, solidify through UV lamp and by 240 mesh abrasive band sandings.
Chamfering is the wide 0.3~0.5mm in inclined-plane at 45 ° of chamferings, chamfering in step (2).
The particular content of coating finish paint is in step (3), applies 1~2 layer of tinter and through UV lamp in blank surface first Solidification, then applies glossiness regulation and paints and solidify through UV lamp.
The glossiness regulation paint is lusterless paint, flat enamel, dumb light paint or high lac varnish.
As shown from the above technical solution, the solid wooden compound floor toning edge sealing process that the present invention is provided, uses toning alcohol Substitution toning paraffin, alcohol has good volatility, volatilized after edge sealing, will not produce " pollution of wax stain " on surface, and And paint film adhesion is not influenceed, when there are " white edge " quality problems need not sanding-japanning again, only need to be at white edge Supplement smears toning alcohol, you can do over again into qualified products.
The present invention changes production process, and upper surface is painted again after four bandings toning alcohol, even if edge banding machine is ejected The toning alcohol come is difficult to the edges of boards of non-japanning being completely covered, because unlapped region is located at edges of boards, in upper surface paint Shi Liyong roller coat finish paint can allow edge sealing close to edges of boards coloring of the plate face without colouring simultaneously, make up edge sealing process and leave not Foot, efficiently solves floor and has looked " white edge " problem after mating formation.
Apply priming paint in the present invention on blank includes five steps altogether, and first layer aqueous priming paint can increase paint film attachment It can also on a small quantity be mixed colours in power, aqueous priming paint, be blank coloring grounding；Second layer putty layer, fills and leads up blank pore, equals blank surface It is whole；Third layer anticracking paint can prevent timber crack；4th layer of wear resistant paint is used to increasing paint wearability, lacquer painting hardness up to 2H very To 3H；Layer 5 sanding paint is used to improve plate face flatness, smoothness, while making slab thickness uniformity.
The present invention carries out just sand first after to slab fixed length, fixed width, fixed thick cutting, carries out essence again on the basis of first sand Sand, improves plate face flatness, smoothness, and first carrying out just sand can avoid because the wooden harder direct washed ore of slab does not reach polishing effect Really；After mortice opening first using 240 mesh belt sandings polish, eliminate because mortice opening cause paint film tilt, cracking and caused by blank Smoothness declines, and also to the road sanding paint of blank surface roller coat 2~3 and is polished before doing finish paint, eliminates because film curing corrugation is made Into blank smoothness decline.
Compared with prior art, the present invention carries out toning edge sealing using the price alcohol lower than paraffin, and improves life Production. art, use the solid wooden compound floor yields of solid wooden compound floor of the present invention toning edge sealing process production up to 99% with On, it can reduce production cost 10% compared to paraffin edge sealing.
Embodiment
The present invention is illustrated in detail with reference to embodiment, present disclosure is not limited to following implementation Example.
Embodiment 1：
A kind of solid wooden compound floor toning edge sealing process, blank selects the crude fibre timber such as Europe rubber, toothed oak wood, heavy bamboo, including Following steps：
(1) fixed length, fixed width, fixed thick cutting and sand at the beginning of 180 mesh abrasive bands are carried out to blank to handle, and then use 240 mesh sand Band washed ore polishing, then primes, the particular content of roller coat priming paint is in blank upper roller：
(1-1) roller coat aqueous priming paint on blank, aqueous priming paint is air-dried using infrared ray air-dry machine；
(1-2) is on blank with 42g/m3Covering with paint amount smears the heavy putty of UV, then with 30g/m3Covering with paint amount roller coat UV can be returned Putty is flowed, solidifies through UV lamp and by 240 mesh abrasive band sandings, fills and leads up blank pore；
(1-3) is on blank with 20g/m3One of anticracking paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
(1-4) is on blank with 25g/m3One of wear resistant paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
(1-5) is on blank with 20g/m3The road sanding paint of covering with paint amount roller coat 3, is beaten after solidifying through UV lamp using 240 mesh abrasive bands Mill；
(2) side of blank four fluting tenon, chamfering, chamfering is the wide 0.5mm in inclined-plane at 45 ° of chamferings, chamfering, is smeared on the side of blank four Toning alcohol edge sealing, the toning alcohol is dissolved in industrial alcohol by color essence and is made, the requirement of toning alcohol color and finish paint Tinter solid colour；
(3) sanding and polishing is carried out to blank surface using 240 mesh abrasive bands, then in blank surface with 20g/m3Covering with paint amount roller 2~3 road sanding paints are applied, 320 mesh belt sandings are used after solidifying through UV lamp；
(4) the blank surface coating finish paint after sanding, particular content is to apply 1 layer of tinter simultaneously in blank surface first Solidify through UV lamp, then apply dumb light paint and solidify through UV lamp；
(5) examination and test of products is carried out, if white edge occurs in the side of floor four, toning alcohol is smeared to supplement at white edge so that white With floor surface solid colour at side, solid wooden floor board finished product is obtained.
Through examining, the solid wooden compound floor qualification rate prepared is up to 99.5%, and supplement smears qualification rate after toning alcohol Up to 100%, hardness of paint film is 2H.
Embodiment 2：
A kind of solid wooden compound floor is mixed colours edge sealing process, blank from face cream pigeonpea, birch, husky Billy etc. it is wooden it is fine and close, The timber of fiber finer, comprises the following steps：
(1) fixed length, fixed width, fixed thick cutting and sand at the beginning of 180 mesh abrasive bands are carried out to blank to handle, and then use 180 mesh sand Band washed ore polishing, then primes, the particular content of roller coat priming paint is in blank upper roller：
(1-1) roller coat aqueous priming paint on blank, aqueous priming paint is air-dried using infrared ray air-dry machine；
(1-2) is on blank with 30g/m3The reflowable putty of covering with paint amount roller coat UV, solidifies through UV lamp and by 240 mesh abrasive band sand Light, fills and leads up blank pore；
(1-3) is on blank with 25g/m3One of anticracking paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
(1-4) is on blank with 35g/m3One of wear resistant paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
(1-5) is on blank with 25g/m3The road sanding paint of covering with paint amount roller coat 2, is beaten after solidifying through UV lamp using 240 mesh abrasive bands Mill；
(2) side of blank four fluting tenon, chamfering, chamfering is the wide 0.3mm in inclined-plane at 45 ° of chamferings, chamfering, is smeared on the side of blank four Toning alcohol edge sealing, the toning alcohol is dissolved in industrial alcohol by color essence and is made, the requirement of toning alcohol color and finish paint Tinter solid colour；
(3) sanding and polishing is carried out to blank surface using 240 mesh abrasive bands, then in blank surface with 20g/m3Covering with paint amount roller 2~3 road sanding paints are applied, 320 mesh belt sandings are used after solidifying through UV lamp；
(4) the blank surface coating finish paint after sanding, particular content is to apply 1 layer of tinter simultaneously in blank surface first Solidify through UV lamp, then apply dumb light paint and solidify through UV lamp；
(5) examination and test of products is carried out, if white edge occurs in the side of floor four, toning alcohol is smeared to supplement at white edge so that white With floor surface solid colour at side, solid wooden floor board finished product is obtained.
Through examining, the solid wooden compound floor qualification rate prepared is up to 99.8%, and supplement smears qualification rate after toning alcohol Up to 100%, hardness of paint film is 3H.

Claims (6)

  1. The edge sealing process 1. a kind of solid wooden compound floor is mixed colours, it is characterised in that comprise the following steps：
    (1) fixed length, fixed width, fixed thick cutting and sand at the beginning of 180 mesh abrasive bands are carried out to blank to handle, and then use 180 mesh or 240 mesh Abrasive band washed ore polishing, then primes in blank upper roller；
    (2) side of blank four fluting tenon, chamfering, in the side of blank four spraying toning alcohol edge sealing, the toning alcohol is dissolved by color essence It is made in industrial alcohol；
    (3) sanding and polishing is carried out to blank surface using 240 mesh abrasive bands, then in blank surface with 15~25g/m3Covering with paint amount roller 2~3 road sanding paints are applied, 320 mesh belt sandings are used after solidifying through UV lamp；
    (4) the blank surface coating finish paint after sanding；
    (5) examination and test of products is carried out, if white edge occurs in the side of floor four, toning alcohol is smeared to supplement at white edge so that at white edge With floor surface solid colour, solid wooden floor board finished product is obtained.
  2. The edge sealing process 2. solid wooden compound floor according to claim 1 is mixed colours, it is characterised in that：Step (1) central roll linging The particular content of paint is：
    (1-1) roller coat aqueous priming paint on blank, aqueous priming paint is air-dried using infrared ray air-dry machine；
    (1-2) is on blank with 25~35g/m3The reflowable putty of covering with paint amount roller coat UV, solidifies through UV lamp and by 240 mesh abrasive band sand Light, fills and leads up blank pore；
    (1-3) is on blank with 15~25g/m3One of anticracking paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
    (1-4) is on blank with 25~35g/m3One of wear resistant paint of covering with paint amount roller coat simultaneously solidifies through UV lamp；
    (1-5) is on blank with 15~25g/m3The road sanding paint of covering with paint amount roller coat 2~5, uses 240 mesh abrasive bands after solidifying through UV lamp Polishing.
  3. The edge sealing process 3. solid wooden compound floor according to claim 2 is mixed colours, it is characterised in that：In step (1-2), if base Material timber is crude fibre timber, then first with 40~50g/m3Covering with paint amount smears the heavy putty of UV, then the reflowable putty of roller coat UV, Solidify through UV lamp and by 240 mesh abrasive band sandings.
  4. The edge sealing process 4. solid wooden compound floor according to claim 1 is mixed colours, it is characterised in that：Chamfering is in step (2) Wide 0.3~the 0.5mm in inclined-plane at 45 ° of chamferings, chamfering.
  5. The edge sealing process 5. solid wooden compound floor according to claim 1 is mixed colours, it is characterised in that：Applicator surface in step (3) The particular content of paint is to apply 1~2 layer of tinter in blank surface first and solidify through UV lamp, then applies glossiness regulation Paint and solidify through UV lamp.
  6. The edge sealing process 6. solid wooden compound floor according to claim 5 is mixed colours, it is characterised in that：The glossiness regulation paint For lusterless paint, flat enamel, dumb light paint or high lac varnish.
CN201710398509.XA 2017-05-31 2017-05-31 A kind of solid wooden compound floor toning edge sealing process Pending CN107097323A (en)