CN107090253A - A kind of antiultraviolet insulation film and its manufacture method - Google Patents
A kind of antiultraviolet insulation film and its manufacture method Download PDFInfo
- Publication number
- CN107090253A CN107090253A CN201710294005.3A CN201710294005A CN107090253A CN 107090253 A CN107090253 A CN 107090253A CN 201710294005 A CN201710294005 A CN 201710294005A CN 107090253 A CN107090253 A CN 107090253A
- Authority
- CN
- China
- Prior art keywords
- glue
- line
- uvioresistant
- film
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antiultraviolet insulation film and its manufacture method, to reduce the freezing time of the indoor ultraviolet of extremely frigid zones and window.The present invention includes cuticular layer, stripping film, uses layer, it is made up of using layer heat absorption glue-line, base film, uvioresistant glue-line, in base film heat absorption glue-line incorporated above, cuticular layer is set on heat absorption glue-line, uvioresistant glue-line is introduced below base film, stripping film is provided below in uvioresistant glue-line.The present invention is film of the Pasting on window, with good UVResistant effect and good endothermic effect.
Description
Technical field
The invention belongs to adhesive foil field of material technology, specifically, a kind of antiultraviolet insulation film is particularly to.
Background technology
In some extremely frigid zones, ultraviolet is stronger;Day and night temperature is big simultaneously, and evening window easily freezes.Existing folder
Layer glass be to be made up of a sheet glass together with one or more pieces glass or plastics, although laminated glass have shock resistance, every
The performances such as sound, safety, but ultraviolet can not be prevented so that ultraviolet is directly through glassy layer.
The content of the invention
The invention aims to overcome a kind of film of the deficiencies in the prior art there is provided Pasting on window, with
Reduce the freezing time of the indoor ultraviolet of extremely frigid zones and window.
To reach above-mentioned purpose, the present invention uses following scheme:
A kind of antiultraviolet insulation film, comprising cuticular layer, stripping film is thin by heat absorption glue-line, base material using layer using layer
Film, uvioresistant glue-line composition, in base film heat absorption glue-line incorporated above, set cuticular layer, in base on heat absorption glue-line
Uvioresistant glue-line is introduced below material film, stripping film is provided below in uvioresistant glue-line;
Cuticular layer thickness is 25~100 μm, and light transmittance is more than 90%;
Base film thickness is 25~100 μm;
The bondline thickness that absorbs heat is 2~8 μm;
The material component of heat absorption glue of glue-line of absorbing heat is with weight proportion:
Resin is:Silica gel, acrylic glue, pressure sensitive adhesive, one kind of OCA glue;
Heat absorption material be:One kind in FeMnC μm of Ox, Fe3C μm of O5, PbS and combinations thereof;
Auxiliary agent is:Polyoxyethylated alkyl phenol, polyoxyethylene aliphatic alcohol ether, the fatty acid ester compounded thing of higher alcohols, polyoxy second
One kind and mixture in alkene polyoxy propyl alcohol amidogen ether;
Solvent is:One kind and mixture in ethyl acetate, toluene, propylene glycol methyl ether acetate;
Vapored away after solvent, preparation are added in preparation;
The material component of uvioresistant glue-line is with weight proportion:
Glue is:Silica gel, acrylic glue, pressure sensitive adhesive, one kind of OCA glue;
Uvioresistant material is:Salicylic acid esters, benzophenone class, benzotriazole, group-substituted acrylonitrile, triazines are with being obstructed
One kind or its combination in amine;
Auxiliary agent is:Polyoxyethylated alkyl phenol, polyoxyethylene aliphatic alcohol ether, the fatty acid ester compounded thing of higher alcohols, polyoxy second
One kind and mixture in alkene polyoxy propyl alcohol amidogen ether;
Solvent is:One kind and mixture in ethyl acetate, toluene, propylene glycol methyl ether acetate;
Vapored away after solvent, preparation are added in preparation.
Further, in certain embodiments, cuticular layer can be any one in PET, PVC, PC, OPP, PE, wherein
Based on PET;
Base film can be any one in PET, PVC, PC, OPP, PE, wherein based on PET;
Stripping film can be any one in PET, PVC, PC, OPP, PE;
Uvioresistant bondline thickness is 15~75 μm.
A kind of preparation method of antiultraviolet insulation film, method is as follows:
With micro- one layer of glue (group added with heat absorption material of gravure roller coating on the base film (PET base material) of 50 μ m-thicks
Point:42 parts of resin, absorb heat 15 parts of material, 8 parts of auxiliary agent, 35 parts of solvent), obtained after 150 DEG C of baking oven heat cures after one layer 5 μm
Absorbed heat glue-line, and the cuticular layer (PET film) of the μ m-thick of last layer 50 is then covered on heat absorption glue-line;
One layer of silica gel glue (component for being added with uvioresistant auxiliary agent is coated with below base film (PET base material):Tree
45 parts of fat, 3 parts of ultraviolet light material, 10 parts of auxiliary agent, 42 parts of solvent), obtained after 180 DEG C of baking oven heat cures after one layer 30 μm
Uvioresistant glue-line, the stripping film (PET) of the μ m-thick of last layer 40 is then cladded with uvioresistant glue-line, insulation film is obtained.
The present invention is film of the Pasting on window, to reduce the knot of the indoor ultraviolet of extremely frigid zones and winter window
The ice time, with good UVResistant effect and good endothermic effect.
Brief description of the drawings
Fig. 1 is the structural representation of the embodiment of the present invention.
Description of reference numerals:
Cuticular layer 11, stripping film 13, using layer 20, absorb heat glue-line 21, base film 22, uvioresistant glue-line 24.
Embodiment
For the feature, technological means and the specific purposes reached, function of the present invention can be further appreciated that, this hair is parsed
Bright advantage and spirit, by the present invention is further elaborated by the following examples.
Cuticular layer can be any one in PET, PVC, PC, OPP, PE, wherein based on PET, thickness is 25~100
μm, light transmittance is more than 90%;
Base film 22 can be any one in PET, PVC, PC, OPP, PE, wherein based on PET, thickness is 25
~100 μm μm.
The coated thereon one of base film 22 heat absorption glue-line 21, plays heat absorption insulation effect.
Main glue silica gel, acrylic glue, pressure sensitive adhesive, the OCA glue of heat absorption glue-line 21 can.Can be photocuring,
Can be heat cure, wherein based on heat cure, thickness is 2~8 μm.
Glue-line 21 absorb heat containing heat absorption material, heat absorption material be mainly one kind in FeMnC μm of Ox, Fe3C μm O5, PbS or
It is combined.
Below base film 22 one layer of uvioresistant glue-line 24 is scribbled (relative to scribbling above heat absorption glue).Uvioresistant
The main glue silica gel of line glue-line 24, acrylic glue, pressure sensitive adhesive, OCA glue can, based on heat cure mode, thickness is 15-75
μm。
Uvioresistant glue-line 24 contains uvioresistant material, mainly salicylic acid esters, benzophenone class, benzotriazole, take
For vinyl cyanide, triazines and one kind in hindered amines or its combine.
The lower section of uvioresistant glue-line 24 is covered with one layer of stripping film 13, during stripping film 13 can be PET, PVC, PC, OPP, PE
Any one.
During preparation, step is as follows:
With micro- one layer of glue added with heat absorption material of gravure roller coating on the base film 22 (PET base material) of 65 μ m-thicks
(component:46 parts of resin, absorb heat 9 parts of material, 10 parts of auxiliary agent, 40 parts of solvent), one layer 3 μm are obtained after 150 DEG C of baking oven heat cures
Heat absorption glue-line 21 afterwards, then covers the PET film (cuticular layer 11) of the μ m-thick of last layer 40 on heat absorption glue-line 21;
Solvent is mainly one kind and mixture in ethyl acetate, toluene, propylene glycol methyl ether acetate;
Vapored away after solvent, preparation are added in preparation;
Auxiliary agent is mainly polyoxyethylated alkyl phenol, polyoxyethylene aliphatic alcohol ether, the fatty acid ester compounded thing of higher alcohols, polyoxy
One kind and mixture in ethene polyoxy propyl alcohol amidogen ether.
One layer of silica gel glue (component for being added with uvioresistant auxiliary agent is coated with below base film 22 (PET base material):
60 parts of resin, 1 part of ultraviolet light material, 9 parts of auxiliary agent, 50 parts of solvent), obtained after 180 DEG C of baking oven heat cures after one layer 45 μm
Uvioresistant glue-line 24, the stripping film 13 (PET mould release membrances) of the μ m-thick of last layer 50 is then cladded with uvioresistant glue-line 24.It is molten
Agent is mainly one kind and mixture in ethyl acetate, toluene, propylene glycol methyl ether acetate;Solvent is added in preparation, after preparation
Vapor away.
Auxiliary agent is mainly polyoxyethylated alkyl phenol, polyoxyethylene aliphatic alcohol ether, the fatty acid ester compounded thing of higher alcohols, polyoxy
One kind and mixture in ethene polyoxy propyl alcohol amidogen ether.
The ultraviolet protective test of antiultraviolet insulation film of the present invention:
One hundred yuan of banknote is placed in " standard sources is to color case ", Μ MV light sources is opened, treats to show clearly on banknote
After watermark, antiultraviolet insulation film (sample thin film) is covered in above banknote, antiultraviolet insulation film (sample is as a result shown
Product film) banknote watermark can be shielded completely, show that sample thin film has good UVResistant effect.
The heat absorption experiment test of antiultraviolet insulation film of the present invention:
6 150ml Clear glass bottles and jars are taken, load 100ml pure water, is placed in refrigerator after freezing completely and takes out, immediately
Cover rubber stopper, and antiultraviolet insulation film (sample thin film) is sticked outside 3 vials wherein, then in other 3
The individual vial for not pasting sample thin film is together positioned under the same position of sunlight, the same terms, the thawing of ice in observation bottle
Time (environment temperature is measured as 23 DEG C);
As a result it is as shown in the table:
1. 2. 3. it is the vial for having pasted antiultraviolet insulation film, is 4. 5. 6. the vial for not pasting sample thin film;
As a result show after glass bottle sticker antiultraviolet insulation film (sample thin film), the thawing speed of ice substantially adds in bottle
It hurry up, it is shown that the good endothermic effect of film.
Embodiment described above only expresses some embodiments of the present invention, and it describes more specific and detailed, but simultaneously
Therefore limitation of the scope of the invention can not be interpreted as.It should be pointed out that for the person of ordinary skill of the art,
Without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection model of the present invention
Enclose.Therefore, protection scope of the present invention should be determined by the appended claims.
Claims (3)
1. a kind of antiultraviolet insulation film, comprising:Cuticular layer, stripping film uses layer, it is characterised in that using layer by absorbing heat
Glue-line, base film, uvioresistant glue-line composition, in base film heat absorption glue-line incorporated above, are set on heat absorption glue-line
Cuticular layer, uvioresistant glue-line is introduced below base film, stripping film is provided below in uvioresistant glue-line;
Cuticular layer thickness is 25~100 μm, and light transmittance is more than 90%;
Base film thickness is 25~100 μm;
The bondline thickness that absorbs heat is 2~8 μm;
The material component of heat absorption glue of glue-line of absorbing heat is with weight proportion:
Resin is:Silica gel, acrylic glue, pressure sensitive adhesive, one kind of OCA glue;
Heat absorption material be:One kind in FeMnC μm of Ox, Fe3C μm of O5, PbS and combinations thereof;
Auxiliary agent is:Polyoxyethylated alkyl phenol, polyoxyethylene aliphatic alcohol ether, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene gather
One kind and mixture in oxygen propyl alcohol amidogen ether;
Solvent is:One kind and mixture in ethyl acetate, toluene, propylene glycol methyl ether acetate;
Vapored away after solvent, preparation are added in preparation;
The material component of uvioresistant glue-line is with weight proportion:
Glue is:Silica gel, acrylic glue, pressure sensitive adhesive, one kind of OCA glue;
Uvioresistant material is:Salicylic acid esters, benzophenone class, benzotriazole, group-substituted acrylonitrile, triazines and hindered amines
In one kind or its combination;
Auxiliary agent is:Polyoxyethylated alkyl phenol, polyoxyethylene aliphatic alcohol ether, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene gather
One kind and mixture in oxygen propyl alcohol amidogen ether;
Solvent is:One kind and mixture in ethyl acetate, toluene, propylene glycol methyl ether acetate;
Vapored away after solvent, preparation are added in preparation.
2. a kind of antiultraviolet insulation film according to claim 1, it is characterised in that the cuticular layer is:PET、
Any one in PVC, PC, OPP, PE;
Base film is:Any one in PET, PVC, PC, OPP, PE;
Stripping film is:Any one in PET, PVC, PC, OPP, PE;
Uvioresistant bondline thickness is 15~75 μm.
3. a kind of preparation method of the antiultraviolet insulation film as described in any one of claim 1~2, it is characterised in that method
It is as follows:
With micro- one layer of glue added with heat absorption material of gravure roller coating on the base film of 50 μ m-thicks, through 150 DEG C of baking oven thermosettings
The glue-line that absorbs heat is obtained after change, then cuticular layer is covered with heat absorption glue-line;
One layer of silica gel glue for being added with uvioresistant auxiliary agent is coated with below base film, after 180 DEG C of baking oven heat cures
Uvioresistant glue-line is obtained, then stripping film is covered with outside uvioresistant glue-line, obtains insulation film.