CN107090214A - A kind of metallic stamping pieces protective coating and preparation method thereof - Google Patents

A kind of metallic stamping pieces protective coating and preparation method thereof Download PDF

Info

Publication number
CN107090214A
CN107090214A CN201710314059.1A CN201710314059A CN107090214A CN 107090214 A CN107090214 A CN 107090214A CN 201710314059 A CN201710314059 A CN 201710314059A CN 107090214 A CN107090214 A CN 107090214A
Authority
CN
China
Prior art keywords
parts
agent
protective coating
metallic stamping
styrene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710314059.1A
Other languages
Chinese (zh)
Inventor
闻继尧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongzhi County Anhui Province Dong Xin Stamping Parts Co Ltd
Original Assignee
Dongzhi County Anhui Province Dong Xin Stamping Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongzhi County Anhui Province Dong Xin Stamping Parts Co Ltd filed Critical Dongzhi County Anhui Province Dong Xin Stamping Parts Co Ltd
Priority to CN201710314059.1A priority Critical patent/CN107090214A/en
Publication of CN107090214A publication Critical patent/CN107090214A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of metallic stamping pieces protective coating, it is made up of the raw material of following parts by weight：5 25 parts of the nitrile rubber, 6 16 parts of erucyl amide, 8 16 parts of Lauryl Alcohol ester, 2 18 parts of chrome green, 3 13 parts of dodecanedioic acid, modified 5 15 parts of kieselguhr, 5 25 parts of epoxy resin latex, 3 17 parts of acrylic acid, 4 16 parts of aluminium chloride, 1 11 parts of styrene-acrylic emulsion, 3 15 parts of polyvinyl alcohol, 28 parts of mica powder, 4 16 parts of levelling agent, 3 17 parts of bonding agent, 5 15 parts of alloyed powder, 4 16 parts of fluxing agent.The present invention has the advantages that anticorrosion effect is good and easy to use.

Description

A kind of metallic stamping pieces protective coating and preparation method thereof
Technical field
The present invention relates to metal protection field, more particularly to a kind of metallic stamping pieces protective coating and preparation method thereof.
Background technology
At present, with the development of science and technology, the field such as industry is also all in rapid advances, because its people is to metal quality It is required that also more and more higher, people generally require to coat one layer of protective coating in metal surface, so that the effect of protection metal is reached, The effective service life for extending metal, but existing metal protection coating selects unreasonable or processing technology because of its material The problems such as, effectively metal can not be protected in use, the processing for being unfavorable for enterprise is used.
The content of the invention
In order to overcome the defect of above-mentioned prior art, it is an object of the invention to provide a kind of metallic stamping pieces protective coating and Its preparation method.
The present invention takes following technical scheme to realize：A kind of metallic stamping pieces protective coating, by following parts by weight Several raw material compositions：Described nitrile rubber 5-25 parts, 6-16 parts of erucyl amide, 8-16 parts of Lauryl Alcohol ester, chrome green 2- 18 parts, 3-13 parts of dodecanedioic acid, modified 5-15 parts of kieselguhr, 5-25 parts of epoxy resin latex, 3-17 parts of acrylic acid, aluminium chloride 4-16 parts, 1-11 parts of styrene-acrylic emulsion, 3-15 parts of polyvinyl alcohol, 2-8 parts of mica powder, 4-16 parts of levelling agent, 3-17 parts of bonding agent is closed 5-15 parts of bronze, 4-16 parts of fluxing agent.
A kind of above-mentioned metallic stamping pieces protective coating, is made up of the raw material of following parts by weight：The nitrile rubber 5- 22 parts, 6-12 parts of erucyl amide, 8-14 parts of Lauryl Alcohol ester, 2-15 parts of chrome green, 3-11 parts of dodecanedioic acid, modified silicon 5-12 parts of algae stone, 5-20 parts of epoxy resin latex, 3-15 parts of acrylic acid, 4-12 parts of aluminium chloride, 1-9 parts of styrene-acrylic emulsion, polyethylene 3-12 parts of alcohol, 2-6 parts of mica powder, 4-12 parts of levelling agent, 3-14 parts of bonding agent, 5-12 parts of alloyed powder, 4-12 parts of fluxing agent.
A kind of above-mentioned metallic stamping pieces protective coating, is made up of the raw material of following parts by weight：The nitrile rubber 15 Part, 11 parts of erucyl amide, 12 parts of Lauryl Alcohol ester, 10 parts of chrome green, 8 parts of dodecanedioic acid, modified 10 parts of kieselguhr, ring 15 parts of oxygen tree fat liquor, 10 parts of acrylic acid, 10 parts of aluminium chloride, 6 parts of styrene-acrylic emulsion, 9 parts of polyvinyl alcohol, 5 parts of mica powder, levelling agent 10 parts, 10 parts of bonding agent, 10 parts of alloyed powder, 10 parts of fluxing agent.
A kind of preparation method of above-mentioned metallic stamping pieces protective coating, is comprised the steps of：
（1）The parts by weight of material in claim 3 are weighed, by nitrile rubber, erucyl amide, Lauryl Alcohol ester, three oxidations two Chromium, dodecanedioic acid, modified kieselguhr, epoxy resin latex, acrylic acid, aluminium chloride, styrene-acrylic emulsion, polyvinyl alcohol and mica powder It is placed in mixer and is stirred, mixing time is 2h, and it is heated in whipping process, the heat time is 1.5h, heating-up temperature is 85 DEG C, obtains compound A；
（2）Levelling agent, bonding agent, alloyed powder and fluxing agent will be added in compound A, it is stirred again, stirred Time is 30min, obtains finished product.
In summary the invention has the advantages that：The present invention have anticorrosion effect good with it is easy to use etc. excellent Point, can be effectively protected metal surface, it is to avoid because of metal is chronically exposed to the situation for occurring being corroded in air, extends gold The service life of category.
Embodiment
A kind of metallic stamping pieces protective coating, is made up of the raw material of following parts by weight：Described nitrile rubber 5-25 parts, mustard Sour acid amides 6-16 parts, 8-16 parts of Lauryl Alcohol ester, 2-18 parts of chrome green, 3-13 parts of dodecanedioic acid, modified kieselguhr 5- 15 parts, 5-25 parts of epoxy resin latex, 3-17 parts of acrylic acid, 4-16 parts of aluminium chloride, 1-11 parts of styrene-acrylic emulsion, polyvinyl alcohol 3-15 Part, 2-8 parts of mica powder, 4-16 parts of levelling agent, 3-17 parts of bonding agent, 5-15 parts of alloyed powder, 4-16 parts of fluxing agent.
A kind of above-mentioned metallic stamping pieces protective coating, is made up of the raw material of following parts by weight：The nitrile rubber 5- 22 parts, 6-12 parts of erucyl amide, 8-14 parts of Lauryl Alcohol ester, 2-15 parts of chrome green, 3-11 parts of dodecanedioic acid, modified silicon 5-12 parts of algae stone, 5-20 parts of epoxy resin latex, 3-15 parts of acrylic acid, 4-12 parts of aluminium chloride, 1-9 parts of styrene-acrylic emulsion, polyethylene 3-12 parts of alcohol, 2-6 parts of mica powder, 4-12 parts of levelling agent, 3-14 parts of bonding agent, 5-12 parts of alloyed powder, 4-12 parts of fluxing agent.
A kind of above-mentioned metallic stamping pieces protective coating, is made up of the raw material of following parts by weight：The nitrile rubber 15 Part, 11 parts of erucyl amide, 12 parts of Lauryl Alcohol ester, 10 parts of chrome green, 8 parts of dodecanedioic acid, modified 10 parts of kieselguhr, ring 15 parts of oxygen tree fat liquor, 10 parts of acrylic acid, 10 parts of aluminium chloride, 6 parts of styrene-acrylic emulsion, 9 parts of polyvinyl alcohol, 5 parts of mica powder, levelling agent 10 parts, 10 parts of bonding agent, 10 parts of alloyed powder, 10 parts of fluxing agent.
A kind of preparation method of above-mentioned metallic stamping pieces protective coating, is comprised the steps of：
（1）The parts by weight of material in claim 3 are weighed, by nitrile rubber, erucyl amide, Lauryl Alcohol ester, three oxidations two Chromium, dodecanedioic acid, modified kieselguhr, epoxy resin latex, acrylic acid, aluminium chloride, styrene-acrylic emulsion, polyvinyl alcohol and mica powder It is placed in mixer and is stirred, mixing time is 2h, and it is heated in whipping process, the heat time is 1.5h, heating-up temperature is 85 DEG C, obtains compound A；
（2）Levelling agent, bonding agent, alloyed powder and fluxing agent will be added in compound A, it is stirred again, stirred Time is 30min, obtains finished product.
The present invention has the advantages that anticorrosion effect is good and easy to use, can be effectively protected metal surface, it is to avoid gold Category extends the service life of metal because being chronically exposed to the situation for occurring being corroded in air.
Described above is embodiments of the invention, therefore all construction, feature and principle institutes according to described in the present patent application scope The equivalent change or modification done, is included in the range of present patent application.

Claims (4)

1. a kind of metallic stamping pieces protective coating, it is characterised in that be made up of the raw material of following parts by weight：The nitrile rubber 5-25 parts, 6-16 parts of erucyl amide, 8-16 parts of Lauryl Alcohol ester, 2-18 parts of chrome green, 3-13 parts of dodecanedioic acid is modified 5-15 parts of kieselguhr, 5-25 parts of epoxy resin latex, 3-17 parts of acrylic acid, 4-16 parts of aluminium chloride, 1-11 parts of styrene-acrylic emulsion, poly- second 3-15 parts of enol, 2-8 parts of mica powder, 4-16 parts of levelling agent, 3-17 parts of bonding agent, 5-15 parts of alloyed powder, 4-16 parts of fluxing agent.
2. a kind of metallic stamping pieces protective coating according to claim 1, it is characterised in that by the original of following parts by weight Material composition：Described nitrile rubber 5-22 parts, 6-12 parts of erucyl amide, 8-14 parts of Lauryl Alcohol ester, 2-15 parts of chrome green, ten Two 3-11 parts of docosandioic acids, modified 5-12 parts of kieselguhr, 5-20 parts of epoxy resin latex, 3-15 parts of acrylic acid, 4-12 parts of aluminium chloride, 1-9 parts of styrene-acrylic emulsion, 3-12 parts of polyvinyl alcohol, 2-6 parts of mica powder, 4-12 parts of levelling agent, 3-14 parts of bonding agent, alloyed powder 5-12 Part, 4-12 parts of fluxing agent.
3. a kind of metallic stamping pieces protective coating according to claim 1, it is characterised in that by the original of following parts by weight Material composition：15 parts of the nitrile rubber, 11 parts of erucyl amide, 12 parts of Lauryl Alcohol ester, 10 parts of chrome green, dodecanedioic acid 8 parts, modified 10 parts of kieselguhr, 15 parts of epoxy resin latex, 10 parts of acrylic acid, 10 parts of aluminium chloride, 6 parts of styrene-acrylic emulsion, polyethylene 9 parts of alcohol, 5 parts of mica powder, 10 parts of levelling agent, 10 parts of bonding agent, 10 parts of alloyed powder, 10 parts of fluxing agent.
4. the preparation method of a kind of metallic stamping pieces protective coating according to claim 1-3, it is characterised in that by following Step is constituted：
（1）The parts by weight of material in claim 3 are weighed, by nitrile rubber, erucyl amide, Lauryl Alcohol ester, three oxidations two Chromium, dodecanedioic acid, modified kieselguhr, epoxy resin latex, acrylic acid, aluminium chloride, styrene-acrylic emulsion, polyvinyl alcohol and mica powder It is placed in mixer and is stirred, mixing time is 2h, and it is heated in whipping process, the heat time is 1.5h, heating-up temperature is 85 DEG C, obtains compound A；
（2）Levelling agent, bonding agent, alloyed powder and fluxing agent will be added in compound A, it is stirred again, stirred Time is 30min, obtains finished product.
CN201710314059.1A 2017-05-05 2017-05-05 A kind of metallic stamping pieces protective coating and preparation method thereof Withdrawn CN107090214A (en)