CN107088642A - A kind of slack wax preparation method of cast steel gear model casting - Google Patents
A kind of slack wax preparation method of cast steel gear model casting Download PDFInfo
- Publication number
- CN107088642A CN107088642A CN201710214679.8A CN201710214679A CN107088642A CN 107088642 A CN107088642 A CN 107088642A CN 201710214679 A CN201710214679 A CN 201710214679A CN 107088642 A CN107088642 A CN 107088642A
- Authority
- CN
- China
- Prior art keywords
- wax
- slack
- cast steel
- machine
- model casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of slack wax preparation method of cast steel gear model casting, comprise the following steps：（1）Change wax：Cerul mould material is placed in water-bath wax cylinder, regulation temperature is at 85 95 DEG C；（2）Plane wax is cut：The material in wax cylinder will be changed, pour into horizontal wax disk(-sc) machine, prepare wax ingot, its sectional dimension 135mm × 135mm；（3）Stir slack wax：By obtained wax ingot, it is placed in and stirs the obtained slack waxs of 1 2h in wax machine；（4）Hui Xing：Slack wax is placed in insulating box, 0.5 1h is incubated, technique is simple, cost-effective, shaping is fast, and the material after use can also be reused, more fine using slack wax casting die made from this method.
Description
Technical field
The present invention relates to the slack wax technical field of model casting, prepared by the slack wax of specially a kind of cast steel gear model casting
Method.
Background technology
At present, the method for preparing close mould is more, such as：Directly add resin etc. with wax or gypsum, but, these methods will
It is slow in mould molding, or shaping rear mold is easily deformed, or the defect such as can not reclaim after mould molding.
Prior art although solve after mould molding be unlikely to deform, the advantage of not cracky, but this mode by
In mainly employing gypsum as paraffin and the mixed liquor of resin, therefore, mould can not be recycled using after finishing, such as mould
Breakage, to implement repairing can be more difficult, also, the above method is used as raw material, therefore, this mode as a result of land plaster
Obtained mould fineness not enough, and then influences the accuracy of mould, moreover, technique is complex.
The content of the invention
In order to overcome the shortcomings of prior art, the present invention provides a kind of slack wax of cast steel gear model casting and prepared
Method, technique is simple, and cost-effective, shaping is fast, and the material after use can also be reused, using this method
Obtained slack wax casting die is more fine.
The technical solution adopted for the present invention to solve the technical problems is：It is prepared by a kind of slack wax of cast steel gear model casting
Method, comprises the following steps：
（1）Change wax：Cerul mould material is placed in water-bath wax cylinder, regulation temperature is at 85-95 DEG C；
（2）Plane wax is cut：The material in wax cylinder will be changed, pour into horizontal wax disk(-sc) machine, prepare wax ingot, its sectional dimension 135mm ×
135mm；
（3）Stir slack wax：By obtained wax ingot, it is placed in and stirs the obtained slack waxs of 1-2h in wax machine；
（4）Hui Xing：Slack wax is placed in insulating box, 0.5-1h is incubated.
As a kind of preferred technical scheme of the present invention, the wax liquid temperature for stirring wax machine is controlled at 65~80 DEG C.
As a kind of preferred technical scheme of the present invention, the water temperature for stirring wax machine is controlled at 48~52 DEG C.
As a kind of preferred technical scheme of the present invention, the temperature control of the insulating box is at 48~52 DEG C.
Compared with prior art, the beneficial effects of the invention are as follows：Present invention process is simple, and cost-effective, shaping is fast, and
Material after use can also be reused, it is more fine using slack wax casting die made from this method.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment：
The invention provides a kind of technical scheme：A kind of slack wax preparation method of cast steel gear model casting, comprises the following steps：
（1）Change wax：Cerul mould material is placed in water-bath wax cylinder, regulation temperature is at 85-95 DEG C；
（2）Plane wax is cut：The material in wax cylinder will be changed, pour into horizontal wax disk(-sc) machine, prepare wax ingot, its sectional dimension 135mm ×
135mm；
（3）Stir slack wax：By obtained wax ingot, it is placed in and stirs the obtained slack waxs of 1-2h in wax machine；
（4）Hui Xing：Slack wax is placed in insulating box, 0.5-1h is incubated.
The wax liquid temperature for stirring wax machine is controlled at 65~80 DEG C；The water temperature for stirring wax machine is controlled at 48~52 DEG C；Institute
The temperature control of insulating box is stated at 48~52 DEG C.
Present invention process is simple, and cost-effective, shaping is fast, and the material after use can also be reused,
It is more fine using slack wax casting die made from this method.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.Any mark in claim should not be considered as to the claim involved by limitation.
Claims (4)
1. a kind of slack wax preparation method of cast steel gear model casting, it is characterised in that：Comprise the following steps：
（1）Change wax：Cerul mould material is placed in water-bath wax cylinder, regulation temperature is at 85-95 DEG C；
（2）Plane wax is cut：The material in wax cylinder will be changed, pour into horizontal wax disk(-sc) machine, prepare wax ingot, its sectional dimension 135mm ×
135mm；
（3）Stir slack wax：By obtained wax ingot, it is placed in and stirs the obtained slack waxs of 1-2h in wax machine；
（4）Hui Xing：Slack wax is placed in insulating box, 0.5-1h is incubated.
2. a kind of slack wax preparation method of cast steel gear model casting according to claim 1, it is characterised in that：It is described to stir
The wax liquid temperature of wax machine is controlled at 65~80 DEG C.
3. a kind of slack wax preparation method of cast steel gear model casting according to claim 1, it is characterised in that：It is described to stir
The water temperature of wax machine is controlled at 48~52 DEG C.
4. a kind of slack wax preparation method of cast steel gear model casting according to claim 1, it is characterised in that：The perseverance
The temperature control of incubator is at 48~52 DEG C.