CN1070847A - Low-carbon chain hydrocarbon aromatization gallium, zinc, platinum modified HZSM-5 catalyst - Google Patents
Low-carbon chain hydrocarbon aromatization gallium, zinc, platinum modified HZSM-5 catalyst Download PDFInfo
- Publication number
- CN1070847A CN1070847A CN92111467A CN92111467A CN1070847A CN 1070847 A CN1070847 A CN 1070847A CN 92111467 A CN92111467 A CN 92111467A CN 92111467 A CN92111467 A CN 92111467A CN 1070847 A CN1070847 A CN 1070847A
- Authority
- CN
- China
- Prior art keywords
- hzsm
- zinc
- gallium
- catalyzer
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a kind of catalyzer and its preparation method that is used for low-carbon chain hydrocarbon aromatization.It is with HZSM-5 zeolite (SiO
2: Al
2O
3=40～100) be carrier, introduce Ga, Zn, Pt with conventional dipping method, be active ingredient, remove part aluminium in the ZSM-5 skeleton by steam-treated, make the acidic site and the dehydrogenation aromatization active sites number of catalyzer be in correlated state, thereby demonstrate good activity, selectivity and stability.
Description
The present invention relates to a kind of low-carbon chain hydrocarbon aromatization with gallium, zinc, platinum modified HZSM-5 catalyst, especially relate to a kind of catalyzer and its preparation method that makes the low-carbon (LC) chain hydrocarbon be converted into aromatic hydrocarbon.
Low-carbon (LC) chain hydrocarbon (alkane or alkene) is converted into aromatic hydrocarbon such as benzene,toluene,xylene, can be with the HZSM-5 zeolites as catalysts of gallium or zinc modification, active and selectivity is all better, but the loss of gallium or zinc in use takes place easily.For addressing this problem, human gallium sulfates such as the Tomoyuki Inui of Kyoto Univ Japan are handled the ZSM-5 gel, replace wherein al composition, obtain the Ga-ZSM-5 catalyzer; Use Pt(NH again
3)
4Cl
2Carry out ion-exchange, obtain the Pt/Ga-ZSM-5 catalyzer.Once delivered trial run in 1000～1500 hours report, (Petroleum Association of Japan's will, 33(4), 198～207(1990)) but only 6～7 hours running period of its one way are very far away from industrial practicality.People such as Chinese Academy of Sciences's Dalian chemistry Lee of institute great aspirations, Zhao Suqin, active ingredient zinc is directly synthesized on the ZSM-5 skeleton, prepare the Zn-ZSM-5 catalyzer, to one way life-span＞200 of oil field light hydrocarbon aromizing test hour, aromatic hydrocarbon average yield＞45%(weight), through 6 regeneration, accumulative total was reacted 1000 hours, the aromatic hydrocarbon average yield is still in 45%(weight) more than (the 4th national molecular sieve academic meeting paper collection (summary), 1A27 page or leaf, 5A07 page or leaf (1991)).But, this Preparation of catalysts technology more complicated.
The objective of the invention is to provide a kind of catalyzer and its preparation method that is used for low-carbon chain hydrocarbon aromatization, the catalyzer for preparing with the inventive method can make catalyzer have good activity, selectivity and stability, and also technology of preparing is simple.
The object of the present invention is achieved like this: with commercially available HZSM-5(SiO
2/ Al
2O
3=40～100) be raw material, after calcination removes organism,, make Ga/HZSM-5 with gallium salt [gallium nitrate or gallium sulfate] aqueous solution dipping; Above-mentioned Ga/HZSM-5 powder is with γ-Al
2O
3Be tackiness agent, add a small amount of sesbania powder and mix, with deionized water furnishing dough shape, extrusion molding, vacuum-drying; With moulding and the exsiccant Ga/HZSM-5 catalyzer reactor of packing into, carry out dealumination treatment under certain condition with the airflow of moisture vapor; With zinc salt [zinc nitrate, zinc sulfate or zinc chloride], chloroplatinic acid aqueous solution dipping, make the Ga/Zn/Pt/HZSM-5 catalyzer through the Ga/HZSM-5 of dealumination treatment catalyzer; Above-mentioned Ga/Zn/Pt/HZSM-5 catalyzer is carried out air roasting by certain heating schedule to be handled.
Specifically be exactly a kind of low-carbon chain hydrocarbon aromatization gallium, zinc, platinum modified HZSM-5 catalyst, the sial molecular ratio that it is characterized in that carrier HZSM-5 is 40～100, gallium in the catalyzer, zinc, platinum add with conventional dipping method, catalyzer is handled the content of regulating aluminium by the airflow of moisture vapor, the composition weight percent of catalyzer is: gallium 0.5～2.0%, zinc 0.5～2.0%, platinum 0.1～0.5%(is a benchmark with the active ingredient that comprises HZSM-5), comprise active ingredient and the tackiness agent γ-Al of HZSM-5
2O
3With the weight hundred of sesbania powder than being 70: 30, the sesbania powder accounts for 1.5～2.0% of total catalyst weight.
Described Preparation of catalysts method comprises following particular step:
The dipping of a, gallium:
To remove organic HZSM-5 zeolite (SiO through calcination
2: Al
2O
3=40～100) be carrier, the first step makes gallium salt (gallium nitrate or the gallium sulfate) aqueous solution contact with HZSM-5 by the pickling process of routine, preparation Ga/HZSM-5;
B, moulding and dealuminzation
The Ga/HZSM-5 that makes through dipping is with γ-Al
2O
3And a small amount of sesbania powder is a tackiness agent, is moulding in 7: 3 by the active ingredient that comprises HZSM-5 with the binder wt ratio, and in vacuum drying oven 100～105 ℃ of dryings 24 hours, reactor is put in moulding and dried Ga/HZSM-5, and feeding the airflow that contains 15～20% water vapors is 1500～2000 hours at volume space velocity
-1, temperature is to carry out 1～3 hour dealumination treatment under 600～700 ℃ of conditions, is cooled to room temperature with dry air again;
The dipping of c, zinc and platinum
Above-mentioned Ga/HZSM-5 catalyzer is used zinc salt solution (zinc nitrate, zinc sulfate or zinc chloride) and Platinic chloride water liquid dipping again, and introducing zinc and platinum is the activity of such catalysts component, is prepared into the Ga/Zn/Pt/HZSM-5 catalyzer;
D, calcination activation
Above-mentioned Ga/Zn/Pt/HZSM-5 catalyzer is put into muffle furnace, by certain heating schedule furnace temperature is raised to 550 ℃ after, constant temperature 4 hours.
Said HZSM-5 and gallium salt, zinc salt, when platinum salt floods, solution temperature is not higher than 25 ℃, and is dried until soaking, the time is no less than 72 hours.
Catalyst formulation provided by the invention and its preparation method, because only relate to conventional pickling process, preparation process is simple, forms and stablizes, and repeats functional.Because adopting multiple metal is active ingredient, to allocate when suitable when their charge capacity, synergistic effect makes catalyzer show good activity, selectivity and stability.
Best specific implementation process of the present invention and effect are provided by following embodiment and appended testing data.But should be understood that the following examples just further specify of the present invention, rather than limitation of the present invention.
Embodiment: 10ml contains 1.6%Ga, 1.0%Zn/0.5%PtGa/Zn/Pt/HZSM-5 Preparation of catalysts and is used for the effect of oil field light hydrocarbon aromatization.
1. the prescription of catalyzer and preparation process
(1) dipping of gallium: take by weighing through calcination and remove the former powder (SiO of organic HZSM-5
2/ Al
2O
3=40～100) 10 grams are put into culture dish, add deionized water 15ml, add 0.6738mol/dm again
3Ga(NO
3)
3Aqueous solution 3.41ml, solution temperature is not higher than 25 ℃ of furnishing pasty states, under the room temperature dipping 96 hours;
(2) moulding: will pour mortar into from the Ga/HZSM-5 that step (1) obtains, and add 4 gram γ-Al
2O
3With 0.28 gram sesbania powder, mixed grinding is even, with a small amount of deionized water furnishing dough shape, is squeezed into diameter 2mm bar shaped in banded extruder, puts into 105 ℃ of dryings of vacuum drying oven then 24 hours;
(3) steam dealumination: will be cut into the long garden of 4mm post bar from the bar shaped catalyst that step (2) obtain, the reactor of packing into is normal pressure, 600 ℃, during GHSV=2000
-1Under the condition, feed the airflow that contains 15% water vapor and handled 3 hours, feed dry air again and be cooled to room temperature;
(4) dipping of zinc and platinum: take by weighing catalyzer 5.79 grams that obtain from step (3), put into culture dish, add deionized water 12ml, add 0.1000mol/dm again
3Zn(NO
3)
2Aqueous solution 6.32ml adds 0.0386mol/dm at last
3H
2PtCl
6Aqueous solution 2.75ml, solution temperature are not higher than under 25 ℃ of room temperatures dipping 72 hours.
(5) roasting: will put into muffle furnace from the catalyzer that step (4) obtain, by following heating schedule roasting.150 ℃ of constant temperature 1 hour, 250 ℃ of constant temperature 1 hour, 300 ℃ of constant temperature 2 hours, 350 ℃ of constant temperature 2 hours, 450 ℃ of constant temperature 1 hour, 550 ℃ of constant temperature 4 hours.
The catalyzer that makes as stated above contains Ga 1.6%, and Zn 1.0%, and Pt0.5%(is a benchmark with the active ingredient weight that comprises HZSM-5), the weight ratio of active ingredient and binding agent is 7: 3.
2. catalyst runs test: above-mentioned Ga/Zn/Pt/HZSM-5 catalyzer is used for oil field light hydrocarbon (alkane weight percent composition sees Table 1) aromatization, test is carried out in the miniature continuous flowing type fixed-bed reactor in laboratory, reactor inside diameter 10mm, catalyst-assembly 10ml, reaction conditions be normal pressure, 550 ℃, during WHSV=0.5
-1, reaction product is cooled off with frozen water, and gas and product liquid that gas-liquid separation obtains measure respectively, analyze with gas chromatograph.
Table 1 oil field alkane weight percent is gently formed
C
5C
6C
7C
8C
9
16.96 26.89 29.04 17.83 9.27
240 hours test-results of one way running sees Table 2.Can see that from test-results the initial activity of catalyzer and aromizing selectivity ratios are higher, the aromatics yield that reacts initial 48 hours is 51～53(weight); Activity of such catalysts has good stability, and reacts that aromatics yield still maintains 50%(weight after 120 hours) about, keep aromatics yield and be not less than 40%(weight) reaction time be 240 hours, the average yield of aromatic hydrocarbons is a 47.78%(weight in 240 hours).
9 regeneration of this catalyzer experience, accumulative total was reacted 1044 hours, average liquid yield is a 54.29%(weight), total arenes yield is a 45.50%(weight), the catalyzer that present embodiment is described is not only active and selectivity is good, and good stability, experience long-term operation more than 1000 hours, the metal active constituent of institute's load does not have obvious loss.
Claims (4)
1, a kind of low-carbon chain hydrocarbon aromatization gallium, zinc, platinum modified HZSM-5 catalyst, the sial molecular ratio that it is characterized in that carrier HZSM-5 is 40～100, gallium in the catalyzer, zinc, platinum add with conventional dipping method, catalyzer is handled the content of regulating aluminium by the airflow of moisture vapor, the composition weight percent of catalyzer is: gallium 0.5～2.0%, zinc 0.5～2.0%, 1～0.5% (is benchmark with the active ingredient that comprises HZSM-5) comprises active ingredient and the tackiness agent γ-Al of HZSM-5
2O
3With the weight hundred of sesbania powder than being 70: 30, the sesbania powder accounts for 1.5～2.0% of total catalyst weight.
2, the described Preparation of catalysts method of claim 1 is characterized in that described Preparation of catalysts method comprises following particular step:
The dipping of a, gallium:
To remove organic HZSM-5 zeolite (SiO through calcination
2: Al
2O
3=40～100) be carrier,
The first step makes gallium salt (gallium nitrate or the gallium sulfate) aqueous solution contact with HZSM-5 by the pickling process of routine, preparation Ga/HZSM-5;
B, moulding and dealuminzation
The Ga/HZSM-5 that makes through dipping is with γ-Al
2O
3Reaching a small amount of sesbania powder is tackiness agent,
Is moulding in 7: 3 by the active ingredient that comprises HZSM-5 with the binder wt ratio, and in vacuum drying oven 100～105 ℃ of dryings 24 hours, reactor is put in moulding and dried Ga/HZSM-5, and feeding the airflow that contains 15～20% water vapors is 1500～2000 hours at volume space velocity
-1, temperature is to carry out 1～3 hour dealumination treatment under 600～700 ℃ of conditions, is cooled to room temperature with dry air again;
The dipping of c, zinc and platinum
Above-mentioned Ga/HZSM-5 catalyzer is used zinc salt solution (zinc nitrate, zinc sulfate or zinc chloride) and Platinic chloride water liquid dipping again, and introducing zinc and platinum is the activity of such catalysts component, is prepared into the Ga/Zn/Pt/HZSM-5 catalyzer;
D, calcination activation
Above-mentioned Ga/Zn/Pt/HZSM-5 catalyzer is put into muffle furnace, by certain heating schedule furnace temperature is raised to 550 ℃ after, constant temperature 4 hours.
3, method for preparing catalyst according to claim 2 is characterized in that said HZSM-5 and gallium salt, zinc salt, when platinum salt floods, and solution temperature is not higher than 25 ℃, and is dried until soaking, and the time is no less than 72 hours.
4, the described low-carbon chain hydrocarbon aromatization catalyzer of claim 1 more is applicable to positive structure C
5～C
8The aromatization of alkane, especially alkene generates benzene, toluene and dimethylbenzene.