CN107083029A - A kind of lavatory lid and preparation method thereof - Google Patents
A kind of lavatory lid and preparation method thereof Download PDFInfo
- Publication number
- CN107083029A CN107083029A CN201710344970.7A CN201710344970A CN107083029A CN 107083029 A CN107083029 A CN 107083029A CN 201710344970 A CN201710344970 A CN 201710344970A CN 107083029 A CN107083029 A CN 107083029A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- lavatory lid
- weight
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of lavatory lid and preparation method thereof, by weight, raw material includes:100 parts~200 parts of polybutylene terephthalate (PBT), 10 parts~30 parts of magnesium hydroxide, 20 parts~50 parts of MMB methyl methacrylate butadiene styrol copolymer, 5 parts~10 parts of calcium carbonate.The beneficial effects of the invention are as follows:Ageing resistace is high, is difficult jaundice, can keep profile fair and clear attractive in appearance for a long time, with high intensity, be difficult to scratch, and is difficult embrittlement, and decay resistance is high, and service life is long, and preparation method is simple, and the cost of raw material is cheap.
Description
Technical field
The invention belongs to sanitary ware technical field, and in particular to a kind of lavatory lid and preparation method thereof.
Background technology
As the improvement of people's living standards, closestool becomes a kind of daily necessities become increasingly popular.It is best in quality, make
There is high market appealing degree and huge market potential with the closestool product of convenient, clean hygiene.Bathroom is applied at present
Lavatory lid material mainly include the traditional material such as acrylonitrile-butadiene-styrene (ABS) plastics, polypropylene, ureaformaldehyde.Wherein, third
The easy aging jaundice of alkene nitrile-butadiene-styrene plastics, corrosion-resistant;Polypropylene material surface is easily scratched, and influence is beautiful
See, while ageing resistace is poor;Embrittlement easily occurs for ureaformaldehyde, and service life is short.
Therefore, research and develop that a kind of ageing resistace is good, the lavatory lid that surface is difficult to scratch, good corrosion resistance, intensity are high, tool
It is of great significance.
The content of the invention
Turn to be yellow, easily scratch to solve the easy aging of Conventional toilets cover plate, corrosion-resistant, easy embrittlement the problems such as, it is of the invention
Purpose is to provide a kind of lavatory lid and preparation method thereof.
The present invention is achieved through the following technical solutions:A kind of lavatory lid, by weight, raw material includes:It is poly-
100 parts~200 parts of mutual-phenenyl two acid bromide two alcohol ester, 10 parts~30 parts of magnesium hydroxide, methyl methacrylate-butadiene-benzene second
20 parts~50 parts of alkene copolymer, 5 parts~10 parts of calcium carbonate.
Preferably, by weight, above-mentioned raw materials also include the present invention:10 parts~20 parts of phenyl salicylate.
Preferably, by weight, above-mentioned raw materials also include the present invention:15 parts~25 parts of APP.
Preferably, by weight, above-mentioned raw materials also include the present invention:5 parts~10 parts of sodium metasilicate.
A kind of preparation method of lavatory lid, step includes:
S1. above-mentioned raw materials are mixed in proportion, is heated at 150 DEG C~200 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
Preferably, in above-mentioned steps S1, the heat time to above-mentioned raw materials is 2 hours~4 hours to the present invention.
Polybutylene terephthalate (PBT), which is that milky is translucent, arrives opaque, semicrystalline thermoplastic polyester, with height
Heat resistance, can the long-term work at 140 DEG C, toughness, fatigue durability, self-lubricating, low-friction coefficient.Magnesium hydroxide has good
Shock-absorbing capacity, adsorptivity power, be a kind of fire retardant of environmental protection.MBS
With higher intensity, it still is able to keep very high rigidity at 85 DEG C~90 DEG C, lavatory lid material can be significantly improved not
The performance easily scratched, still has good toughness at -40 DEG C, lavatory lid is not susceptible to embrittlement, and oil resistant, it is acidproof,
Alkaline-resisting, ultraviolet resistance aging.Calcium carbonate can strengthen the intensity of lavatory lid.
Phenyl salicylate can absorb ultraviolet light, it is possible to increase the performance of the anti-aging jaundice of lavatory lid.
APP is nonpoisonous and tasteless, does not produce etchant gas, and heat endurance is high, it is possible to increase the intensity of lavatory lid and resistance to
Corrosion.
Sodium metasilicate cohesive force is strong, with higher intensity, it is possible to increase the corrosion resistance of lavatory lid, heat resistance and water-fast
Property, improve anti-aging, the erosion-resisting performance of lavatory lid.
The present invention can at least reach less than one beneficial effect:
1. ageing resistace is high, jaundice is difficult, can keep profile fair and clear attractive in appearance for a long time;
2. with high intensity, it is difficult to scratch, is difficult embrittlement;
3. decay resistance is high, service life is long;
4. preparation method is simple, the cost of raw material is cheap.
Embodiment
With reference to embodiment the present invention will be further explained explanation.
Embodiment 1
By weight, raw material includes:100 parts of polybutylene terephthalate (PBT), 10 parts of magnesium hydroxide, methacrylic acid
20 parts of methyl esters-BS, 5 parts of calcium carbonate.
By weight, raw material also includes:10 parts of phenyl salicylate.
By weight, raw material also includes:15 parts of APP.
By weight, raw material also includes:5 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 150 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 2 hours.
Embodiment 2
By weight, raw material includes:110 parts of polybutylene terephthalate (PBT), 12 parts of magnesium hydroxide, methacrylic acid
23 parts of methyl esters-BS, 5 parts of calcium carbonate.
By weight, raw material also includes:11 parts of phenyl salicylate.
By weight, raw material also includes:16 parts of APP.
By weight, raw material also includes:5 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 155 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 2 hours.
Embodiment 3
By weight, raw material includes:120 parts of polybutylene terephthalate (PBT), 14 parts of magnesium hydroxide, methacrylic acid
26 parts of methyl esters-BS, 6 parts of calcium carbonate.
By weight, raw material also includes:12 parts of phenyl salicylate.
By weight, raw material also includes:17 parts of APP.
By weight, raw material also includes:6 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 160 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 2 hours.
Embodiment 4
By weight, raw material includes:130 parts of polybutylene terephthalate (PBT), 16 parts of magnesium hydroxide, methacrylic acid
29 parts of methyl esters-BS, 6 parts of calcium carbonate.
By weight, raw material also includes:13 parts of phenyl salicylate.
By weight, raw material also includes:18 parts of APP.
By weight, raw material also includes:6 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 165 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 2 hours.
Embodiment 5
By weight, raw material includes:140 parts of polybutylene terephthalate (PBT), 18 parts of magnesium hydroxide, methacrylic acid
32 parts of methyl esters-BS, 7 parts of calcium carbonate.
By weight, raw material also includes:14 parts of phenyl salicylate.
By weight, raw material also includes:19 parts of APP.
By weight, raw material also includes:7 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 170 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 3 hours.
Embodiment 6
By weight, raw material includes:160 parts of polybutylene terephthalate (PBT), 20 parts of magnesium hydroxide, methacrylic acid
35 parts of methyl esters-BS, 7 parts of calcium carbonate.
By weight, raw material also includes:15 parts of phenyl salicylate.
By weight, raw material also includes:20 parts of APP.
By weight, raw material also includes:7 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 175 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 3 hours.
Embodiment 7
By weight, raw material includes:170 parts of polybutylene terephthalate (PBT), 25 parts of magnesium hydroxide, methacrylic acid
40 parts of methyl esters-BS, 8 parts of calcium carbonate.
By weight, raw material also includes:16 parts of phenyl salicylate.
By weight, raw material also includes:22 parts of APP.
By weight, raw material also includes:8 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 180 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 3 hours.
Embodiment 8
By weight, raw material includes:180 parts of polybutylene terephthalate (PBT), 26 parts of magnesium hydroxide, methacrylic acid
45 parts of methyl esters-BS, 8 parts of calcium carbonate.
By weight, raw material also includes:18 parts of phenyl salicylate.
By weight, raw material also includes:22 parts of APP.
By weight, raw material also includes:8 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 185 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 4 hours.
Embodiment 9
By weight, raw material includes:190 parts of polybutylene terephthalate (PBT), 28 parts of magnesium hydroxide, methacrylic acid
48 parts of methyl esters-BS, 9 parts of calcium carbonate.
By weight, raw material also includes:18 parts of phenyl salicylate.
By weight, raw material also includes:18 parts of APP.
By weight, raw material also includes:9 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 190 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 4 hours.
Embodiment 10
By weight, raw material includes:200 parts of polybutylene terephthalate (PBT), 30 parts of magnesium hydroxide, methacrylic acid
50 parts of methyl esters-BS, 10 parts of calcium carbonate.
By weight, raw material also includes:20 parts of phenyl salicylate.
By weight, raw material also includes:25 parts of APP.
By weight, raw material also includes:10 parts of sodium metasilicate.
Making step includes:
S1. raw material is mixed in proportion, is heated at 200 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
In step S1, the heat time to raw material is 4 hours.
The property indices of the lavatory lid made by repetition test, the present invention are as shown in the table:
Tensile strength (MPa) | 132~155 |
Bending strength (MPa) | 189~211 |
Acid corrosion mass loss rate (%) | 14~33 |
Caustic corrosion mass loss rate (%) | 5~12 |
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, is not being taken off
On the premise of from spirit and scope of the invention, various changes and modifications of the present invention are possible, and these changes and improvements are regarded as
Fall into scope of the claimed invention.
Claims (6)
1. a kind of lavatory lid, it is characterised in that:By weight, raw material includes:100 parts of polybutylene terephthalate (PBT)~
200 parts, 10 parts~30 parts of magnesium hydroxide, 20 parts~50 parts of MBS, calcium carbonate 5
Part~10 parts.
2. a kind of lavatory lid according to claim 1, it is characterised in that:By weight, the raw material also includes:Water
10 parts~20 parts of poplar acid phenenyl ester.
3. a kind of lavatory lid according to claim 2, it is characterised in that:By weight, the raw material also includes:It is poly-
15 parts~25 parts of ammonium phosphate.
4. a kind of lavatory lid according to claim 3, it is characterised in that:By weight, the raw material also includes:Silicon
Sour 5 parts~10 parts of sodium.
5. a kind of preparation method of lavatory lid, it is characterised in that:Step includes:
S1. the raw material is mixed in proportion, is heated at 150 DEG C~200 DEG C, obtain fused materials;
S2. fused materials are molded into lavatory lid mould, cooled down, the demoulding produces lavatory lid finished product.
6. a kind of preparation method of lavatory lid according to claim 5, it is characterised in that:In the step S1, to institute
The heat time for stating raw material is 2 hours~4 hours.