CN103275440A - Water feeding pipe manufactured by polyvinyl chloride plastics - Google Patents
Water feeding pipe manufactured by polyvinyl chloride plastics Download PDFInfo
- Publication number
- CN103275440A CN103275440A CN2013102512048A CN201310251204A CN103275440A CN 103275440 A CN103275440 A CN 103275440A CN 2013102512048 A CN2013102512048 A CN 2013102512048A CN 201310251204 A CN201310251204 A CN 201310251204A CN 103275440 A CN103275440 A CN 103275440A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- upper hose
- igelite
- polyvinyl
- paraffin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water feeding pipe manufactured by polyvinyl chloride plastics. The composition of raw materials by weight percent is as follows: 85-90% of polyvinyl-chlorid, 0.5-1.5% of stearic acid, 1-2% of di-n-octyl tin and sulfur glycol essien ester, 0.5-1% of paraffin, 2-5% of polyvinyl-chlorid wax, 3.5-4.5% of compound stabilizer, 0.5-1% of titanium dioxide, 0.5-0.7% of calcium stearate, and 0.1-0.2% of light calcium carbonate. Through the adoption of the manner, the polyvinyl-chlorid material is composed of carbon and hydrogen elements, and has no side-effect and good hygiene property, and is safe and reliable in using; water passing through the pipe can not be affected, so as to have no effect for a human body after drinking; the pipe belongs to environment-friendly building material; meanwhile raw materials are cheap and the manufacturing cost is low; and the pipe can be popularized and applied in large-scale.
Description
Technical field
The present invention relates to the plastic pipe field, particularly relate to a kind of igelite upper hose processed.
Background technology
Polyvinyl chloride is one of five big general-purpose plastics kinds in the world at present, and its plastics are widely used in all respects such as industry, agricultural, communications and transportation, national defence, public covil construction and people's lives.Advantages such as polyvinyl chloride is because its raw material sources widely, and production cost is low, the production technology maturation and being used widely.Polyvinyl chloride develops very rapid because it is of many uses, from the nineteen thirties to the middle nineteen sixties, the output of polyvinyl chloride accounts for first of world's plastics output always.
The polyvinyl chloride price is relatively low, can be met the upper hose that water supply needs by formulating of recipe.But the upper hose that tradition is used is not totally nontoxic, and drinking the water that flows through these upper hoses for a long time can damage human body, gives rise to diseases easily, does not meet the standard of safety and sanitation.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of igelite upper hose processed, and described upper hose has no side effect, and sanitation performance is good.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of igelite upper hose processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 85-90%
Stearic acid 0.5-1.5%
Dioctyltin thioglycol monooctyl ester 1-2%
Paraffin 0.5-1%
Polyvinyl chloride wax 2-5%
One package stabilizer 3.5-4.5%
Titanium dioxide 0.5-1%
Calcium stearate 0.5-0.7%
Light calcium carbonate 0.1-0.2%.
In a preferred embodiment of the present invention, by percentage to the quality, the raw material of described igelite upper hose processed consists of:
Polyvinyl chloride 89.2%
Stearic acid 0.7%
Dioctyltin thioglycol monooctyl ester 1.5%
Paraffin 1%
Polyvinyl chloride wax 2.5%
One package stabilizer 3.8%
Titanium dioxide 0.7%
Calcium stearate 0.5%
Light calcium carbonate 0.1%.
In a preferred embodiment of the present invention, by percentage to the quality, the raw material of described igelite upper hose processed consists of:
Polyvinyl chloride 86.8%
Stearic acid 1.5%
Dioctyltin thioglycol monooctyl ester 1%
Paraffin 0.8%
Polyvinyl chloride wax 4.5%
One package stabilizer 4.3%
Titanium dioxide 0.5%
Calcium stearate 0.5%
Light calcium carbonate 0.1%.
In a preferred embodiment of the present invention, by percentage to the quality, the raw material of described igelite upper hose processed consists of:
Polyvinyl chloride 87.2%
Stearic acid 1.5%
Dioctyltin thioglycol monooctyl ester 1%
Paraffin 0.7%
Polyvinyl chloride wax 4%
One package stabilizer 3.9%
Titanium dioxide 0.9%
Calcium stearate 0.6%
Light calcium carbonate 0.2%.
The invention has the beneficial effects as follows: igelite of the present invention upper hose processed, described pvc material is made up of carbon, protium, have no side effect, sanitation performance is good, and is safe and reliable during use, the water that passes through can not polluted, the people drinks the back does not have influence to health, belongs to green building material, and raw material is cheap simultaneously, production cost is low, can apply on a large scale.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
Embodiment one:
Provide a kind of igelite upper hose processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 85-90%
Stearic acid 0.5-1.5%
Dioctyltin thioglycol monooctyl ester 1-2%
Paraffin 0.5-1%
Polyvinyl chloride wax 2-5%
One package stabilizer 3.5-4.5%
Titanium dioxide 0.5-1%
Calcium stearate 0.5-0.7%
Light calcium carbonate 0.1-0.2%.
Embodiment two:
Provide a kind of igelite upper hose processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 85-90%
Stearic acid 0.5-1.5%
Dioctyltin thioglycol monooctyl ester 1-2%
Paraffin 0.5-1%
Polyvinyl chloride wax 2-5%
One package stabilizer 3.5-4.5%
Titanium dioxide 0.5-1%
Calcium stearate 0.5-0.7%
Light calcium carbonate 0.1-0.2%.
Embodiment three:
Provide a kind of igelite upper hose processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 85-90%
Stearic acid 0.5-1.5%
Dioctyltin thioglycol monooctyl ester 1-2%
Paraffin 0.5-1%
Polyvinyl chloride wax 2-5%
One package stabilizer 3.5-4.5%
Titanium dioxide 0.5-1%
Calcium stearate 0.5-0.7%
Light calcium carbonate 0.1-0.2%.
The igelite upper hose processed that the present invention discloses, described pvc material is made up of carbon, protium, have no side effect, sanitation performance is good, and is safe and reliable during use, the water that passes through can not polluted, the people drinks the back does not have influence to health, belongs to green building material, and raw material is cheap simultaneously, production cost is low, can apply on a large scale.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (4)
1. an igelite upper hose processed is characterized in that, by percentage to the quality, the raw material of described igelite upper hose processed consists of:
Polyvinyl chloride 85-90%
Stearic acid 0.5-1.5%
Dioctyltin thioglycol monooctyl ester 1-2%
Paraffin 0.5-1%
Polyvinyl chloride wax 2-5%
One package stabilizer 3.5-4.5%
Titanium dioxide 0.5-1%
Calcium stearate 0.5-0.7%
Light calcium carbonate 0.1-0.2%.
2. igelite according to claim 1 upper hose processed is characterized in that, by percentage to the quality, the raw material of described igelite upper hose processed consists of:
Polyvinyl chloride 89.2%
Stearic acid 0.7%
Dioctyltin thioglycol monooctyl ester 1.5%
Paraffin 1%
Polyvinyl chloride wax 2.5%
One package stabilizer 3.8%
Titanium dioxide 0.7%
Calcium stearate 0.5%
Light calcium carbonate 0.1%.
3. igelite according to claim 1 upper hose processed is characterized in that, by percentage to the quality, the raw material of described igelite upper hose processed consists of:
Polyvinyl chloride 86.8%
Stearic acid 1.5%
Dioctyltin thioglycol monooctyl ester 1%
Paraffin 0.8%
Polyvinyl chloride wax 4.5%
One package stabilizer 4.3%
Titanium dioxide 0.5%
Calcium stearate 0.5%
Light calcium carbonate 0.1%.
4. igelite according to claim 1 upper hose processed is characterized in that, by percentage to the quality, the raw material of described igelite upper hose processed consists of:
Polyvinyl chloride 87.2%
Stearic acid 1.5%
Dioctyltin thioglycol monooctyl ester 1%
Paraffin 0.7%
Polyvinyl chloride wax 4%
One package stabilizer 3.9%
Titanium dioxide 0.9%
Calcium stearate 0.6%
Light calcium carbonate 0.2%.