CN107082622A - A kind of wall body building material and preparation method thereof - Google Patents
A kind of wall body building material and preparation method thereof Download PDFInfo
- Publication number
- CN107082622A CN107082622A CN201710472023.6A CN201710472023A CN107082622A CN 107082622 A CN107082622 A CN 107082622A CN 201710472023 A CN201710472023 A CN 201710472023A CN 107082622 A CN107082622 A CN 107082622A
- Authority
- CN
- China
- Prior art keywords
- parts
- wall body
- building material
- body building
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of wall body building material and preparation method thereof, is related to building material field, wall body building material is made up of the raw material of following parts by weight：55 70 parts of waste ceramic material, 45 60 parts of rock wool board waste material, 10 20 parts of stalk waste residue, 10 15 parts of anti-crack fiber, 10 15 parts of Paris white, 15 20 parts of perlite, 12 16 parts of diatomite in powder, 0.5 1.5 parts of defoamer, 0.5 1 parts of mortar water-loss reducer, 0.2 0.5 parts of water reducer, 10 14 parts of mineral wool, 30 40 parts of vermiculite, 5 10 parts, 24 parts of dispersant；Preparation method weighs waste ceramic material, rock wool board waste material, stalk waste residue, anti-crack fiber, Paris white, perlite, diatomite in powder, defoamer, mortar water-loss reducer, water reducer, mineral wool, vermiculite according to parts by weight for (1) and loads stirring in mixer, obtains solid mixture；(2) toward addition water and dispersant in solid mixture, 20 30min are stirred, are well mixed；The present invention has the advantages that good effect of heat insulation, intensity are high, refuse reclamation rate is high, sound-absorbing effect is good and corrosion resistance is strong.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of wall body building material and preparation method thereof.
Background technology
As social economy continues to develop with scientific and technical, the living standard of the people is quickly improved, to construction material
It is required that more prominent, New Building Materials kind is numerous, and form is different, lead modern building technology innovation development and
Improve.
The effort of more than 30 years is passed through in China's heat-insulating fireproof material industry, particularly by high speed development in recent years, from list
One to variation, and from low to high, but existing construction material is in insulation, intensity, refuse reclamation, sound-absorbing and corrosion resistant for quality
Effect is far from reaching the desired value of people in corrosion.
A kind of wall body building material of Chinese patent literature of on 2 17th, 2016 bulletins and preparation method thereof (Granted publication
Number CN103896619B), include the component of following parts by weight：Ceramic polished 50~80 parts of slag, 0~30 part of feldspar, calcining are slided
2~10 parts of stone, 10~20 parts of red soil, 0~10 part of lithium feldspar, dickite 0~15,0.5~2 part of carborundum, stabilizer 1.5~3
40~50 parts of part and water.The invention also proposed the preparation method of above-mentioned wall body building material, including ball milling, drying, dress cellar for storing things, burning
Into and cutting processing.The wall body building material of the invention is from heavy and light, anti seismic efficiency is good, heat-insulating property is high, soundproof effect good.
But the invention is in the intensity of wall body building material, refuse reclamation, energy-conserving and environment-protective, insulation, sound-absorbing and corrosion resistant
It is still not good enough in corrosion, have much room for improvement.
The content of the invention
It is not fine, low intensity, refuse reclamation to solve existing wall body building material to there is heat insulating effect
Rate is low, sound-absorbing effect is poor and the problem of corrosion-resistant, it is an object of the invention to provide a kind of wall body building material and its preparation
Method, has the advantages that good effect of heat insulation, intensity are high, refuse reclamation rate is high, sound-absorbing effect is good and corrosion resistance is strong.
The invention provides following technical scheme：
A kind of wall body building material, it is made up of the raw material of following parts by weight：
Solve existing wall body building material and preparation method thereof exist heat insulating effect be not very well, low intensity,
Refuse reclamation rate is low, sound-absorbing effect is poor and the problem of corrosion-resistant.
Preferably, it is made up of the raw material of following parts by weight：
Preferably, it is made up of the raw material of following parts by weight：
Preferably, the mineral wool is one kind in mineral wool, mineral wool and aluminium silicate wool, and mineral wool has sound-absorbing, subtracted
Shake, heat-insulated advantage.
Preferably, the mineral wool is mineral wool, and mineral wool has small forming, bulk density, low thermal conductivity, thermal insulation separation
Heat, sound-absorbing effect are good, good corrosion resistance advantage.
A kind of preparation method of wall body building material, comprises the following steps：
(1) 55-70 parts of waste ceramic material, 45-60 parts of rock wool board waste material, stalk waste residue 10-20 are weighed according to parts by weight
Part, 10-15 parts of anti-crack fiber, 10-15 parts of Paris white, 15-20 parts of perlite, 12-16 parts of diatomite in powder, defoamer 0.5-
1.5 parts, 0.5-1 parts of mortar water-loss reducer, 0.2-0.5 parts of water reducer, 10-14 parts of mineral wool, 30-40 parts of loading mixers of vermiculite
Interior, it is 120-160r/min to control revolution, stirs 30-40min, is well mixed, obtains solid mixture；
(2) 2-4 parts of 5-10 parts of water and dispersant are added according to parts by weight in the solid mixture obtained toward step (1),
It is 60-80r/min to control revolution, stirs 20-30min, is well mixed, obtains required wall body building material.
Preferably, comprise the following steps：
(1) 55-65 parts of waste ceramic material, 45-55 parts of rock wool board waste material, stalk waste residue 10-18 are weighed according to parts by weight
Part, 10-14 parts of anti-crack fiber, 10-13 parts of Paris white, 15-18 parts of perlite, 12-15 parts of diatomite in powder, defoamer 0.5-1
Part, 0.5-0.8 parts of mortar water-loss reducer, 0.2-0.4 parts of water reducer, 10-12 parts of mineral wool, in 30-35 parts of loading mixers of vermiculite,
It is 120-160r/min to control revolution, stirs 30-40min, is well mixed, obtains solid mixture；
(2) 2-3 parts of 5-8 parts of water and dispersant, control are added according to parts by weight in the solid mixture obtained toward step (1)
Revolution processed is 60-80r/min, stirs 20-30min, is well mixed, obtains required wall body building material.
Preferably, comprise the following steps：
(1) 65 parts of waste ceramic material, 55 parts of rock wool board waste material, 18 parts of stalk waste residue, cracking resistance fibre are weighed according to parts by weight
14 parts of dimension, 13 parts of Paris white, 18 parts of perlite, 15 parts of diatomite in powder, 1 part of defoamer, 0.8 part of mortar water-loss reducer, water reducer
0.4 part, 12 parts of mineral wool, in 35 parts of loading mixers of vermiculite, it is 120-160r/min to control revolution, stirs 30-40min, is mixed
Close uniform, obtain solid mixture；
(2) 3 parts of 8 parts of water and dispersant are added according to parts by weight in the solid mixture obtained toward step (1), control turns
Number is 60-80r/min, stirs 20-30min, is well mixed, obtains required wall body building material.
The beneficial effects of the invention are as follows：
1st, it is not fine, low intensity, waste that the present invention, which solves existing wall body building material and there is heat insulating effect,
Reuse ratio is low, sound-absorbing effect is poor and the problem of corrosion-resistant.
2nd, anti-crack fiber is added in the present invention, anti-crack fiber tensile strength is high；Waste ceramic material, rock cotton board is added to give up
Material, stalk waste residue so that waste can be recycled, energy-conserving and environment-protective；Vermiculite is added, the performance that can possess fire-proof and thermal-insulation.
3rd, the mineral wool in the present invention is one kind in mineral wool, mineral wool and aluminium silicate wool, and mineral wool, which has, to be inhaled
Sound, damping, heat-insulated advantage.
4th, the present invention in the mineral wool be mineral wool, mineral wool have small forming, bulk density, low thermal conductivity,
Insulation, sound-absorbing effect are good, the advantage of good corrosion resistance.
5th, simple production process of the present invention, control easy to implement and control, cost are low, beneficial to industrialized production and use.
Embodiment
Embodiment 1
A kind of wall body building material, it is made up of the raw material of following parts by weight：
Mineral wool is mineral wool, and mineral wool has small forming, bulk density, low thermal conductivity, insulation, sound-absorbing effect
The good, advantage of good corrosion resistance.
A kind of preparation method of wall body building material, comprises the following steps：
(1) 65 parts of waste ceramic material, 55 parts of rock wool board waste material, 18 parts of stalk waste residue, cracking resistance fibre are weighed according to parts by weight
14 parts of dimension, 13 parts of Paris white, 18 parts of perlite, 15 parts of diatomite in powder, 1 part of defoamer, 0.8 part of mortar water-loss reducer, water reducer
0.4 part, 12 parts of mineral wool, in 35 parts of loading mixers of vermiculite, it is 160r/min to control revolution, stirs 40min, is well mixed,
Obtain solid mixture；
(2) 3 parts of 8 parts of water and dispersant are added according to parts by weight in the solid mixture obtained toward step (1), control turns
Number is 80r/min, stirs 30min, is well mixed, obtains required wall body building material.
Properties of product test, the survey of wall body building material made from above-described embodiment are carried out according to DB34/T1279-2010
Test result is as follows：
Thermal conductivity factor (w/m ﹒ k)：0.023；
Unit weight (kg/m3)：276；
Compression strength (Mpa)：3.21.
Embodiment 2
A kind of wall body building material, it is made up of the raw material of following parts by weight：
Mineral wool is mineral wool, and mineral wool has small forming, bulk density, low thermal conductivity, insulation, sound-absorbing effect
The good, advantage of good corrosion resistance.
A kind of preparation method of wall body building material, comprises the following steps：
(1) 60 parts of waste ceramic material, 50 parts of rock wool board waste material, 15 parts of stalk waste residue, cracking resistance fibre are weighed according to parts by weight
12 parts of dimension, 12 parts of Paris white, 16 parts of perlite, 14 parts of diatomite in powder, 0.8 part of defoamer, 0.6 part of mortar water-loss reducer, diminishing
0.3 part of agent, 11 parts of mineral wool, in 32 parts of loading mixers of vermiculite, it is 160r/min to control revolution, stirs 40min, and mixing is equal
It is even, obtain solid mixture；
(2) 3 parts of 7 parts of water and dispersant are added according to parts by weight in the solid mixture obtained toward step (1), control turns
Number is 80r/min, stirs 30min, is well mixed, obtains required wall body building material.
Properties of product test, the survey of wall body building material made from above-described embodiment are carried out according to DB34/T1279-2010
Test result is as follows：
Thermal conductivity factor (w/m ﹒ k)：0.027；
Unit weight (kg/m3)：286；
Compression strength (Mpa)：3.01.
Embodiment 3
A kind of wall body building material, it is made up of the raw material of following parts by weight：
Mineral wool is mineral wool, and mineral wool has small forming, bulk density, low thermal conductivity, insulation, sound-absorbing effect
The good, advantage of good corrosion resistance.
A kind of preparation method of wall body building material, comprises the following steps：
(1) 55 parts of waste ceramic material, 45 parts of rock wool board waste material, 10 parts of stalk waste residue, cracking resistance fibre are weighed according to parts by weight
10 parts of dimension, 10 parts of Paris white, 15 parts of perlite, 12 parts of diatomite in powder, 0.5 part of defoamer, 0.5 part of mortar water-loss reducer, diminishing
0.2 part of agent, 10 parts of mineral wool, in 30 parts of loading mixers of vermiculite, it is 160r/min to control revolution, stirs 40min, and mixing is equal
It is even, obtain solid mixture；
(2) 2 parts of 5 parts of water and dispersant are added according to parts by weight in the solid mixture obtained toward step (1), control turns
Number is 80r/min, stirs 30min, is well mixed, obtains required wall body building material.
Properties of product test, the survey of wall body building material made from above-described embodiment are carried out according to DB34/T1279-2010
Test result is as follows：
Thermal conductivity factor (w/m ﹒ k)：0.033；
Unit weight (kg/m3)：301；
Compression strength (Mpa)：2.86.
Embodiment 4
A kind of wall body building material, it is made up of the raw material of following parts by weight：
Mineral wool is mineral wool, and mineral wool has small forming, bulk density, low thermal conductivity, insulation, sound-absorbing effect
The good, advantage of good corrosion resistance.
A kind of preparation method of wall body building material, comprises the following steps：
(it is fine that (1) weighs 70 parts of waste ceramic material, 60 parts of rock wool board waste material, 20 parts of stalk waste residue, cracking resistance according to parts by weight
15 parts of dimension, 15 parts of Paris white, 20 parts of perlite, 16 parts of diatomite in powder, 1.5 parts of defoamer, 1 part of mortar water-loss reducer, water reducer
0.5 part, 14 parts of mineral wool, in 40 parts of loading mixers of vermiculite, it is 160r/min to control revolution, stirs 40min, is well mixed,
Obtain solid mixture；
(2) 4 parts of 10 parts of water and dispersant, control are added according to parts by weight in the solid mixture obtained toward step (1)
Revolution is 80r/min, stirs 30min, is well mixed, obtains required wall body building material.
Properties of product test, the survey of wall body building material made from above-described embodiment are carried out according to DB34/T1279-2010
Test result is as follows：
Thermal conductivity factor (w/m ﹒ k)：0.038；
Unit weight (kg/m3)：324；
Compression strength (Mpa)：2.73.
Comparative example
A kind of wall body building material, it is made up of the raw material of following parts by weight：
Mineral wool is mineral wool, and mineral wool has small forming, bulk density, low thermal conductivity, insulation, sound-absorbing effect
The good, advantage of good corrosion resistance.
A kind of preparation method of wall body building material, comprises the following steps：
(it is fine that (1) weighs 75 parts of waste ceramic material, 65 parts of rock wool board waste material, 25 parts of stalk waste residue, cracking resistance according to parts by weight
20 parts of dimension, 20 parts of Paris white, 25 parts of perlite, 20 parts of diatomite in powder, 2 parts of defoamer, 2 parts of mortar water-loss reducer, water reducer 1
Part, 15 parts of mineral wool, in 45 parts of loading mixers of vermiculite, it is 160r/min to control revolution, stirs 40min, is well mixed, obtains
Solid mixture；
(2) 5 parts of 12 parts of water and dispersant, control are added according to parts by weight in the solid mixture obtained toward step (1)
Revolution is 80r/min, stirs 30min, is well mixed, obtains required wall body building material.
Properties of product test, the survey of wall body building material made from above-mentioned comparative example are carried out according to DB34/T1279-2010
Test result is as follows：
Thermal conductivity factor (w/m ﹒ k)：0.042；
Unit weight (kg/m3)：350；
Compression strength (Mpa)：2.25.
Embodiment 1 is below the thermal conductivity factor of comparative example to the thermal conductivity factor of the wall body building material of embodiment 4, and implements
The thermal conductivity factor of example 1 is minimum, illustrates that its heat insulation effect is best.Embodiment 1 to the wall body building material of embodiment 4 compression strength
It is above comparative example, and the compression strength highest of embodiment 1.Embodiment 1 is low to the unit weight of the wall body building material of embodiment 4
In comparative example, and the unit weight of embodiment 1 is minimum.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or equivalent substitution, all essences in the present invention are carried out to which part technical characteristic
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of wall body building material, it is characterised in that it is made up of the raw material of following parts by weight：
2. wall body building material according to claim 1, it is characterised in that it is made up of the raw material of following parts by weight：
3. wall body building material according to claim 2, it is characterised in that it is made up of the raw material of following parts by weight：
4. wall body building material according to claim 1, it is characterised in that：The mineral wool be mineral wool, mineral wool and
One kind in aluminium silicate wool.
5. wall body building material according to claim 1, it is characterised in that：The mineral wool is mineral wool.
6. a kind of preparation method of wall body building material as claimed in claim 1, it is characterised in that comprise the following steps：
(1) weigh 55-70 parts of waste ceramic material according to parts by weight, it is 45-60 parts of rock wool board waste material, 10-20 parts of stalk waste residue, anti-
Split 10-15 parts of fiber, 10-15 parts of Paris white, 15-20 parts of perlite, 12-16 parts of diatomite in powder, 0.5-1.5 parts of defoamer,
0.5-1 parts of mortar water-loss reducer, 0.2-0.5 parts of water reducer, 10-14 parts of mineral wool, in 30-40 parts of loading mixers of vermiculite, control
Revolution is 120-160r/min, stirs 30-40min, is well mixed, obtains solid mixture；
(2) 2-4 parts of 5-10 parts of water and dispersant, control are added according to parts by weight in the solid mixture obtained toward step (1)
Revolution is 60-80r/min, stirs 20-30min, is well mixed, obtains required wall body building material.
7. the preparation method of wall body building material according to claim 6, it is characterised in that comprise the following steps：
(1) weigh 55-65 parts of waste ceramic material according to parts by weight, it is 45-55 parts of rock wool board waste material, 10-18 parts of stalk waste residue, anti-
Split 10-14 parts of fiber, 10-13 parts of Paris white, 15-18 parts of perlite, 12-15 parts of diatomite in powder, 0.5-1 parts of defoamer, sand
Starch 0.5-0.8 part of water-loss reducer, 0.2-0.4 parts of water reducer, 10-12 parts of mineral wool, in 30-35 parts of loading mixers of vermiculite, control
Revolution is 120-160r/min, stirs 30-40min, is well mixed, obtains solid mixture；
(2) 2-3 parts of 5-8 parts of water and dispersant are added according to parts by weight in the solid mixture obtained toward step (1), control turns
Number is 60-80r/min, stirs 20-30min, is well mixed, obtains required wall body building material.
8. the preparation method of wall body building material according to claim 7, it is characterised in that comprise the following steps：
(1) 65 parts of waste ceramic material, 55 parts of rock wool board waste material, 18 parts of stalk waste residue, anti-crack fiber 14 are weighed according to parts by weight
Part, 13 parts of Paris white, 18 parts of perlite, 15 parts of diatomite in powder, 1 part of defoamer, 0.8 part of mortar water-loss reducer, water reducer 0.4
Part, 12 parts of mineral wool, in 35 parts of loading mixers of vermiculite, it is 120-160r/min to control revolution, stirs 30-40min, and mixing is equal
It is even, obtain solid mixture；
(2) 3 parts of 8 parts of water and dispersant are added according to parts by weight in the solid mixture obtained toward step (1), controls the revolution to be
60-80r/min, stirs 20-30min, is well mixed, obtains required wall body building material.