CN107057819A - A kind of machining lubricating and cutting fluid and its production technology - Google Patents
A kind of machining lubricating and cutting fluid and its production technology Download PDFInfo
- Publication number
- CN107057819A CN107057819A CN201710260026.3A CN201710260026A CN107057819A CN 107057819 A CN107057819 A CN 107057819A CN 201710260026 A CN201710260026 A CN 201710260026A CN 107057819 A CN107057819 A CN 107057819A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting fluid
- lubricating
- oil
- viscosity index
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of machining lubricating and cutting fluid and its production technology, it is related to field of machining, the parts by weight of lubricating and cutting fluid are：26 30 parts of base oil, 40 54 parts of petroleum sodium sulfonate, 12 16 parts of polyacrylamide, 16 20 parts of diethanol amine, 14 17 parts of castor oil acid polyester, 17 19 parts of nitromethane, 14 19 parts of turkey red oil, 12 16 parts of glycerin polyoxyethylene ether, 14 parts of dispersant, 8 14 parts of viscosity index improver, 30 50 parts of 6 11 parts of bactericide and water, at the same time, apparatus can be effectively prevented to be damaged, and with good adhesiveness, water can effectively be prevented, influence of the vapor to apparatus, to can directly apply antirust oil after part cleaning treatment after use, due to the addition of bactericide in lubricating and cutting fluid, the bacterium grown in cutting fluid is few, cutting fluid service life length and part is not easy to get rusty.
Description
Technical field
The present invention relates to field of machining, more particularly to a kind of machining lubricating and cutting fluid and its production technology.
Background technology
The paces developed with mechanical automation, requirement of the people to apparatus also making with regard to more and more higher, especially apparatus
With the life-span, it can greatly extend the service life of apparatus using good cutting oil, at present, the species of lubricating oil is various, has
Can not use at high temperature, what is had does not possess good adhesiveness, also have do not have preferable water repelling property, it is impossible to meet
The demand of people.Lubricating and cutting fluid is to be used in machining area in the various machinings of metal to play lubrication, cooling and cleaning workpiece
The industrial type fluid acted on cutter, high performance cutting fluid should possess good processing characteristics, physicochemical property and environmental sanitation performance,
Such as lubrication, cooling, antirust, oil removing cleaning, anti-corrosion, lubricating and cutting fluid are made up of base oil and additive two parts, base oil
The main component for being, decides the fundamental property of lubricating oil, and additive can then make up and improve the deficiency of base oil aspect of performance,
Some new performances are assigned, are the important components of lubricating oil.The operating characteristics and processing characteristics of conventional cutting liquid are poor, machine
Bed, workpiece tarnish protection it is poor, the anti-spalling of paint is poor, and cutting fluid is difficult O＆M, and waste liquid is not disposable, at waste liquid
Reason is costly, and machine maintenance upkeep cost is high, and harmful and environmental pollution is more serious.Oil base cutting fluid can be with storage
Or the continuity of validity period is gradually gone bad because of oxidation and causes acid increase, causes workpiece and cutter to get rusty, or because oxidation and foaming is accounted for
Go out cutting oil spill according to space, also can decline washing (-)off properties because of inappropriate increase that oxidation causes viscosity；If because process is former
Cause or accident are mixed into moisture in oil base cutting fluid, then can increase the adverse consequences such as tool wear.
The Chinese patent application file of Application No. 201410263135.7 is related to technical field of lubricating oil, and it by weight hundred
Fraction meter：To tert-butylbenzene formic acid 1%-3%, diethanol amine 2%-5%, benzoic acid 2%-5%, glycerine 3%-8%, bactericide 0.5%-3%,
Emulsifying agent 3%-5%, water surplus.
The Chinese patent application file of Application No. 201210518622.4 is related to field of lubricant, and in particular to Yi Zhongrun
Lubricating oil cream, includes the raw material of following mass fraction：2-4 parts of p-hydroxy benzaldehyde, 2-3 parts of methyl citrate, citric acid list first
1-3 parts of ester, 3-4 parts of Tetrahydropalmatine, 1-2 parts of birch leaf chrysanthemum terpene, different dehydro-α-curcumene 2-5 parts, 2-4 parts of Lupenyl palmitate
With 1-3 parts of oleanonic acid.
But above-mentioned cutting oil is difficult in use and manufacturing process, complicated, operating characteristics and processing characteristics are poor,
Lathe, workpiece tarnish protection it is poor, the anti-spalling of paint is poor, and cutting fluid is difficult O＆M, and waste liquid is not disposable, waste liquid
Processing cost is high, and machine maintenance upkeep cost is high, and harmful and environmental pollution is more serious, under the high temperature conditions can not
Substantial amounts of heat is enough absorbed, and can not effectively prevent the influence of water, vapor to apparatus.
The content of the invention
The technical problem to be solved of the present invention is to provide a kind of machining lubricating and cutting fluid, to solve existing skill
Caused by art cutting oil using and manufacturing process in it is difficult, complicated, operating characteristics and processing characteristics are poor, lathe,
The tarnish protection of workpiece is poor, and the anti-spalling of paint is poor, and cutting fluid is difficult O＆M, and waste liquid is not disposable, liquid waste processing
Costly, machine maintenance upkeep cost is high, and harmful and environmental pollution is more serious, can not inhale under the high temperature conditions
Substantial amounts of heat is received, and can not effectively prevent the drawbacks described above of the influence of water, vapor to apparatus.
In order to realize the purpose of the present invention, a kind of machining lubricating and cutting fluid that the present invention is provided, it is characterized in that：Profit
The parts by weight of sliding cutting fluid are：26-30 parts of base oil, 40-54 parts of petroleum sodium sulfonate, 12-16 parts of polyacrylamide, diethanol amine
16-20 parts, 14-17 parts of castor oil acid polyester, 17-19 parts of nitromethane, 14-19 parts of turkey red oil, glycerin polyoxyethylene ether
12-16 parts, 1-4 parts of dispersant, 30-50 parts of 8-14 parts of viscosity index improver, 6-11 parts of bactericide and water.
A kind of production technology of machining lubricating and cutting fluid, its production stage is as follows：
（1）Dispensing, weighs petroleum sodium sulfonate, polyacrylamide, glycerin polyoxyethylene ether, diethanol amine, castor oil acid polyester, nitre
Methylmethane, turkey red oil, water and base oil, are uniformly mixed, and be stirring uniformly to obtain mixture according to parts by weight；
（2）System match somebody with somebody material, by the mixture stirred added to reconcile kettle in, stir 10-16 minutes, after again to mediation
Add dispersant in kettle, stir 10-15 minute, obtain material, after will to reconcile temperature in the kettle control be 60-70 DEG C, material is quiet
Put 2-3 hours；
（3）Additive, viscosity index improver and bactericide are added into obtained material, are stirred 3-5 minutes, are obtained blank；
（4）Finished product, obtained blank is tested in laboratory, after qualified product is squeezed into finished pot, carry out canned.
It is preferred that, the step（2）In, when adding dispersant into the material, the temperature in the kettle control that reconciles is 90-
120℃。
It is preferred that, the step（3）In, when adding viscosity index improver and bactericide into the material, reconcile
Temperature in the kettle control is 60-70 DEG C.
It is preferred that, the base oil is I, II, III class base oil of the high viscosity index (HVI) that viscosity index (VI) is more than 100.
It is preferred that, the parts by weight of the viscosity index improver are：1 part of polymethacrylates, 4 parts of polyacrylate,
3 parts of 5 parts of random polypropylene and ethylene-propylene copolymer.
It is preferred that, the parts by weight of the dispersant are：3 parts of glyceryl monostearate, ethylene group is double stearic 2 parts, acid amides three
Stearic 1 part and 2 parts of acid glyceride.
The beneficial effects of the present invention are：
1st, a kind of machining lubricating and cutting fluid that the present invention is provided, can not only effectively prevent apparatus to be damaged, and have
Good adhesiveness, excellent anticorrosive property, substantial amounts of heat can be absorbed under the high temperature conditions, moreover it is possible to effectively prevent water, water from steaming
Influence of the gas to apparatus.
2nd, lubricating and cutting fluid of the present invention do not allow it is perishable, to can directly apply antirust oil after part cleaning treatment after use, i.e.,
Make also not allowing easy-to-rust in the spring part that water south wind is opened more than gas.
3rd, due to the addition of in lubricating and cutting fluid, the bacterium that is grown in bactericide, cutting fluid is few, cutting fluid service life
Long and part is not easy to get rusty.
4th, lubricating and cutting fluid of the invention can solve the problem of existing lubricating oil viscosity index is low, cooling, lubricant effect
Good, frictional force is small when using.
5th, this novel mechanical processing lubricating and cutting fluid and its production craft step are simple, easy to operate, and obtained cut
Cut liquid anti-oxidant, service life is longer, with preferable water proofing property, using also has good security.
Embodiment
The present invention is described in further details with reference to embodiment.
Embodiment 1
A kind of machining lubricating and cutting fluid, the parts by weight of lubricating and cutting fluid are：26 parts of base oil, 40 parts of petroleum sodium sulfonate,
16 parts of polyacrylamide, 20 parts of diethanol amine, 14 parts of castor oil acid polyester, 18 parts of nitromethane, 14 parts of turkey red oil, glycerine
12 parts of APEO, 1 part of dispersant, 30 parts of 14 parts of viscosity index improver, 11 parts of bactericide and water.
A kind of production technology of machining lubricating and cutting fluid, its production stage is as follows：
（1）Dispensing, weighs petroleum sodium sulfonate, polyacrylamide, glycerin polyoxyethylene ether, diethanol amine, castor oil acid polyester, nitre
Methylmethane, turkey red oil, water and base oil, are uniformly mixed according to parts by weight, and are stirring uniformly to obtain mixture, wherein, base
Plinth oil is I, II, III class base oil of the high viscosity index (HVI) that viscosity index (VI) is more than 100；
（2）System match somebody with somebody material, by the mixture stirred added to reconcile kettle in, stir 10 minutes, after again to reconcile kettle
Middle addition dispersant, stir 15 minutes, obtain material, after will reconcile temperature in the kettle control be 70 DEG C, by material stand 3 hours,
Wherein, when adding dispersant into the material, the temperature in the kettle control that reconciles is 120 DEG C, and the parts by weight of dispersant are：It is stearic
Sour 3 parts of monoglyceride, ethylene group is double stearic 2 parts, acid amides three stearic 1 part and 2 parts of acid glyceride.
（3）Additive, viscosity index improver and bactericide are added into obtained material, are stirred 3 minutes, are obtained base
Material, wherein, when adding viscosity index improver and bactericide into the material, the temperature in the kettle control that reconciles is 70 DEG C, is glued
Degree index improver parts by weight be：1 part of polymethacrylates, 4 parts of polyacrylate, 5 parts of random polypropylene and second third are common
3 parts of polymers；
（4）Finished product, obtained blank is tested in laboratory, after qualified product is squeezed into finished pot, carry out canned.
Wherein, a kind of machining lubricating and cutting fluid that the present invention is provided, can not only effectively prevent apparatus to be damaged, and
And there is good adhesiveness, excellent anticorrosive property, substantial amounts of heat can be absorbed under the high temperature conditions, moreover it is possible to effectively prevent
The influence of water, vapor to apparatus, to can directly apply antirust oil after part cleaning treatment after use, opens gas many even in water south wind
Spring part do not allow easy-to-rust yet, the bacterium grown due to the addition of in lubricating and cutting fluid in bactericide, cutting fluid is few, cut
Cut liquid service life length and part is not easy to get rusty, it is low that lubricating and cutting fluid of the invention can solve existing lubricating oil viscosity index
The problem of, cooling, high lubricating effect, frictional force is small when using, and at the same time its production craft step is simple, easy to operate, and
Obtained cutting fluid is anti-oxidant, and service life is longer, with preferable water proofing property, and using also has good security.
Embodiment 2
A kind of machining lubricating and cutting fluid, the parts by weight of lubricating and cutting fluid are：28 parts of base oil, 54 parts of petroleum sodium sulfonate,
12 parts of polyacrylamide, 16 parts of diethanol amine, 15 parts of castor oil acid polyester, 17 parts of nitromethane, 16 parts of turkey red oil, glycerine
14 parts of APEO, 3 parts of dispersant, 40 parts of 7 parts of viscosity index improver, 8 parts of bactericide and water.
A kind of production technology of machining lubricating and cutting fluid, its production stage is as follows：
（1）Dispensing, weighs petroleum sodium sulfonate, polyacrylamide, glycerin polyoxyethylene ether, diethanol amine, castor oil acid polyester, nitre
Methylmethane, turkey red oil, water and base oil, are uniformly mixed according to parts by weight, and are stirring uniformly to obtain mixture, wherein, base
Plinth oil is I, II, III class base oil of the high viscosity index (HVI) that viscosity index (VI) is more than 100；
（2）System match somebody with somebody material, by the mixture stirred added to reconcile kettle in, stir 12 minutes, after again to reconcile kettle
Middle addition dispersant, stirs 12 minutes, obtains material, after will to reconcile temperature in the kettle control be 65 DEG C, material is stood 2.5 small
When, wherein, when adding dispersant into the material, the temperature in the kettle control that reconciles is 90 DEG C, and the parts by weight of dispersant are：Firmly
3 parts of resin acid monoglyceride, ethylene group is double stearic 2 parts, acid amides three stearic 1 part and 2 parts of acid glyceride.
（3）Additive, viscosity index improver and bactericide are added into obtained material, are stirred 4 minutes, are obtained base
Material, wherein, when adding viscosity index improver and bactericide into the material, the temperature in the kettle control that reconciles is 65 DEG C, is glued
Degree index improver parts by weight be：1 part of polymethacrylates, 4 parts of polyacrylate, 5 parts of random polypropylene and second third are common
3 parts of polymers；
（4）Finished product, obtained blank is tested in laboratory, after qualified product is squeezed into finished pot, carry out canned.
Wherein, a kind of machining lubricating and cutting fluid that the present invention is provided, can not only effectively prevent apparatus to be damaged, and
And there is good adhesiveness, excellent anticorrosive property, substantial amounts of heat can be absorbed under the high temperature conditions, moreover it is possible to effectively prevent
The influence of water, vapor to apparatus, to can directly apply antirust oil after part cleaning treatment after use, opens gas many even in water south wind
Spring part do not allow easy-to-rust yet, the bacterium grown due to the addition of in lubricating and cutting fluid in bactericide, cutting fluid is few, cut
Cut liquid service life length and part is not easy to get rusty, it is low that lubricating and cutting fluid of the invention can solve existing lubricating oil viscosity index
The problem of, cooling, high lubricating effect, frictional force is small when using, and at the same time its production craft step is simple, easy to operate, and
Obtained cutting fluid is anti-oxidant, and service life is longer, with preferable water proofing property, and using also has good security.
Embodiment 3
A kind of machining lubricating and cutting fluid, the parts by weight of lubricating and cutting fluid are：30 parts of base oil, 45 parts of petroleum sodium sulfonate,
14 parts of polyacrylamide, 18 parts of diethanol amine, 17 parts of castor oil acid polyester, 19 parts of nitromethane, 19 parts of turkey red oil,
16 parts of glycerin polyoxyethylene ether, 4 parts of dispersant, 50 parts of 8 parts of viscosity index improver, 6 parts of bactericide and water.
A kind of production technology of machining lubricating and cutting fluid, its production stage is as follows：
（1）Dispensing, weighs petroleum sodium sulfonate, polyacrylamide, glycerin polyoxyethylene ether, diethanol amine, castor oil acid polyester, nitre
Methylmethane, turkey red oil, water and base oil, are uniformly mixed according to parts by weight, and are stirring uniformly to obtain mixture, wherein, base
Plinth oil is I, II, III class base oil of the high viscosity index (HVI) that viscosity index (VI) is more than 100；
（2）System match somebody with somebody material, by the mixture stirred added to reconcile kettle in, stir 16 minutes, after again to reconcile kettle
Middle addition dispersant, stir 10 minutes, obtain material, after will reconcile temperature in the kettle control be 60 DEG C, by material stand 2 hours,
Wherein, when adding dispersant into the material, the temperature in the kettle control that reconciles is 100 DEG C, and the parts by weight of dispersant are：It is stearic
Sour 3 parts of monoglyceride, ethylene group is double stearic 2 parts, acid amides three stearic 1 part and 2 parts of acid glyceride.
（3）Additive, viscosity index improver and bactericide are added into obtained material, are stirred 5 minutes, are obtained base
Material, wherein, when adding viscosity index improver and bactericide into the material, the temperature in the kettle control that reconciles is 60 DEG C, is glued
Degree index improver parts by weight be：1 part of polymethacrylates, 4 parts of polyacrylate, 5 parts of random polypropylene and second third are common
3 parts of polymers；
（4）Finished product, obtained blank is tested in laboratory, after qualified product is squeezed into finished pot, carry out canned.
Wherein, a kind of machining lubricating and cutting fluid that the present invention is provided, can not only effectively prevent apparatus to be damaged, and
And there is good adhesiveness, excellent anticorrosive property, substantial amounts of heat can be absorbed under the high temperature conditions, moreover it is possible to effectively prevent
The influence of water, vapor to apparatus, to can directly apply antirust oil after part cleaning treatment after use, opens gas many even in water south wind
Spring part do not allow easy-to-rust yet, the bacterium grown due to the addition of in lubricating and cutting fluid in bactericide, cutting fluid is few, cut
Cut liquid service life length and part is not easy to get rusty, it is low that lubricating and cutting fluid of the invention can solve existing lubricating oil viscosity index
The problem of, cooling, high lubricating effect, frictional force is small when using, and at the same time its production craft step is simple, easy to operate, and
Obtained cutting fluid is anti-oxidant, and service life is longer, with preferable water proofing property, and using also has good security.
As known by the technical knowledge, the present invention can be by the embodiment party of other essence or essential feature without departing from its spirit
Case is realized.Therefore, embodiment disclosed above, for each side, is all merely illustrative, and is not only.Institute
Have within the scope of the present invention or be included in the invention in the change being equal in the scope of the present invention.
Claims (7)
1. a kind of machining lubricating and cutting fluid, it is characterised in that：The parts by weight of lubricating and cutting fluid are：26-30 parts of base oil,
40-54 parts of petroleum sodium sulfonate, 12-16 parts of polyacrylamide, 16-20 parts of diethanol amine, 14-17 parts of castor oil acid polyester, nitro
17-19 parts of methane, 14-19 parts of turkey red oil, 12-16 parts of glycerin polyoxyethylene ether, 1-4 parts of dispersant, viscosity index (VI) is improved
30-50 parts of 8-14 parts of agent, 6-11 parts of bactericide and water.
2. a kind of production technology of machining lubricating and cutting fluid according to claim 1, it is characterised in that：Production step
It is rapid as follows：
（1）Dispensing, weighs petroleum sodium sulfonate, polyacrylamide, glycerin polyoxyethylene ether, diethanol amine, castor oil acid polyester, nitre
Methylmethane, turkey red oil, water and base oil, are uniformly mixed, and be stirring uniformly to obtain mixture according to parts by weight；
（2）System match somebody with somebody material, by the mixture stirred added to reconcile kettle in, stir 10-16 minutes, after again to mediation
Add dispersant in kettle, stir 10-15 minute, obtain material, after will to reconcile temperature in the kettle control be 60-70 DEG C, material is quiet
Put 2-3 hours；
（3）Additive, viscosity index improver and bactericide are added into obtained material, are stirred 3-5 minutes, are obtained blank；
（4）Finished product, obtained blank is tested in laboratory, after qualified product is squeezed into finished pot, carry out canned.
3. a kind of production technology of machining lubricating and cutting fluid according to claim 2, it is characterised in that：The step
Suddenly（2）In, when adding dispersant into the material, the temperature in the kettle control that reconciles is 90-120 DEG C.
4. a kind of production technology of machining lubricating and cutting fluid according to claim 2, it is characterised in that：The step
Suddenly（3）In, when adding viscosity index improver and bactericide into the material, the temperature in the kettle control that reconciles is 60-70 DEG C.
5. a kind of machining lubricating and cutting fluid according to claim 1, it is characterised in that：The base oil is that viscosity refers to
Number is I, II, III class base oil of more than 100 high viscosity index (HVI).
6. a kind of machining lubricating and cutting fluid according to claim 1, it is characterised in that：The viscosity index improver
Parts by weight be：3 parts of 1 part of polymethacrylates, 4 parts of polyacrylate, 5 parts of random polypropylene and ethylene-propylene copolymer.
7. a kind of machining lubricating and cutting fluid according to claim 1, it is characterised in that：The parts by weight of the dispersant
For：3 parts of glyceryl monostearate, ethylene group is double stearic 2 parts, acid amides three stearic 1 part and 2 parts of acid glyceride.