CN107057503A - A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil and preparation method thereof - Google Patents
A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil and preparation method thereof Download PDFInfo
- Publication number
- CN107057503A CN107057503A CN201710010449.XA CN201710010449A CN107057503A CN 107057503 A CN107057503 A CN 107057503A CN 201710010449 A CN201710010449 A CN 201710010449A CN 107057503 A CN107057503 A CN 107057503A
- Authority
- CN
- China
- Prior art keywords
- essential oil
- eyeshield
- sealing wax
- chrysanthemum essential
- containing natural
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil and preparation method thereof, a kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil of the invention, the eyeshield metope sealing wax containing natural chrysanthemum essential oil includes following component by weight：100 400 parts of the net taste resin of the property of water-bearing, 16 parts of defoamer, 26 parts of preservative, 15 parts of wetting agent, 1 10 parts of dispersant, 100 280 parts of pigment titanium white, 810 350 parts of filler, 1 10 parts of thickener, 1 10 parts of levelling agent, natural 8.33 33.33 parts of chrysanthemum essential oil, 10 350 parts of water.Paint film of the present invention has zero VOC, and smell is pure and fresh, and covering power is good, easily construction, the features such as resistant resistance to shampooing, while the eye fatigue that can releive.
Description
Technical field
The present invention relates to functional environment-friendly paint field, a kind of eyeshield metope water containing natural chrysanthemum essential oil is specifically related to
Paint and preparation method thereof.
Background technology
Governance is accounted in the characteristics of interior wall sealing wax has easy construction, performance protrusion, safety and environmental protection, inner wall decoration at home
Status, its market share is more than 70%.Present people's computer and mobile phone time are more and more, are often easily caused eye fatigue,
Conventional latex paint and the function without relieving eye strain, the metope sealing wax that exploitation one has relieving eye strain have very
Important realistic function.Chrysanthemum essential oil has restoring consciouness and the effect of clearing liver and improving vision, and by being compounded with aqueous net taste resin, is made
Environmentally friendly sealing wax after brushing by slowly discharging chrysanthemum essential oil, can preferably alleviate brush indoor user use kopiopia.
At present.Lack eyeshield metope sealing wax containing natural chrysanthemum essential oil and its preparation side of a kind of eye fatigue that can releive
Method.
The content of the invention
Regarding the issue above, the present invention provides a kind of eye fatigue that can releive contains natural chrysanthemum essential oil
Eyeshield metope sealing wax and preparation method thereof.
To reach above-mentioned purpose, present invention employs following technical proposal：The present invention's is a kind of containing natural chrysanthemum essential oil
Eyeshield metope sealing wax, the eyeshield metope sealing wax containing natural chrysanthemum essential oil includes following component by weight：
Further, the eyeshield metope sealing wax containing natural chrysanthemum essential oil includes following component by weight：
Further, the weight ratio of the net taste resin of the property of water-bearing and natural chrysanthemum essential oil is 12：1.Under this ratio situation
Natural chrysanthemum essential oil can reach best stabilized state with aqueous net taste resin.
Further, the net taste resin of the property of water-bearing is aqueous net taste pure acrylate resin；The defoamer is to receive
In rice polysiloxane-polyether copolymer type of latex type, mineral oils or polyethylene glycol-hydrophobic solid-polysiloxane mixture class
One or more of combinations.
Further, the dispersant is Sodium Polyacrylate salt, modified polypropene acid solution class or modified polycarboxylic acid salt
One or more of combinations in class.
Further, the wetting agent is sodium butylnaphthalenesulfonate salt, polyoxyethylated alkyl phenol or polyoxyethylene polyoxy second
One or more of combinations in alkene block copolymer；The thickener is nano nano fumed silica powder body thickener；
The pigment is titanium dioxide.
Further, the filler is calcined kaolin, powdered whiting, diatomite, talcum powder, wollastonite or precipitation
One or more of combinations in barium sulfate.The titanium dioxide is rutile pigment titanium dioxide, and described is rutile pigment
Titanium dioxide chloridising is produced；The levelling agent is cross-linking organosilicon polyoxyalkylene acrylate lipin polymer, dimethyl polysiloxane
One or more of combinations in emulsion or polysiloxane-polyether copolymer class.
Further, the rutile pigment titanium dioxide is Du Pont rutile type titanium white R-706；The aqueous net taste
Pure acrylate resin is BASF styrene-acrylate emulsion ECO；The defoamer is the peaceful defoamer SN-154 of section；Institute
Preservative is stated for Clariant Liquid BPF ipacide GSF；The dispersant is enlightening high score powder TEGO Dispers750W；Institute
Levelling agent is stated for ROHM AND HAAS levelling agent RM-2020；The wetting agent is Clariant wetting agent LCN088.
The preparation method of eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil, comprises the following steps：
(1) each component is accurately weighed by described parts by weight, by water-base resin, natural chrysanthemum essential oil by weight 12：1
Ratio mixing, add wetting agent, stir 1-48 hours, obtain mixture 1；
(2) water, preservative, dispersant and defoamer are mixed, stirs, obtain mixture 2；
(3) added into the mixture 2 under pigment and filler, vacuum state and be distributed to less than 50 microns, obtain mixture 3；
(4) mixture 1, levelling agent and thickener are added into the mixture 3, is stirred, is made containing natural
The eyeshield metope sealing wax of chrysanthemum essential oil.
Beneficial effect：Paint film of the present invention has zero VOC, and smell is pure and fresh, and covering power is good, easily construction, the resistance to shampooing of resistant
The features such as, while the eye fatigue that can releive, is a production for being perfectly combined dicoration, feature, the big theme of the feature of environmental protection three
Product.Eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil is applied to brush, and roller coating and spraying can be painted on metope and wood
On material, during coating decoration, appropriate water regulation viscosity can be added as the case may be.
(1) the eyeshield metope sealing wax containing natural chrysanthemum essential oil of the invention can be painted on metope and timber, paint film tool
There is zero VOC, smell is pure and fresh, covering power is good, easily construction, the features such as resistant resistance to shampooing, be provided simultaneously with relieving eye strain effect
Really, it is a product for being perfectly combined dicoration, feature, the big theme of the feature of environmental protection three.It is an advantage of the current invention that paint film ring
Protect nontoxic, and with sustainability in effect.
(2) the net taste resin of the property of water-bearing of the invention is aqueous net taste pure acrylate resin, its synthetic hollow shell
Nuclear structure, is external plasticizer using water, it is not necessary to add any coalescents can preferable film forming, using special Protection glue
Body, with excellent freeze-thaw resistance, it is not necessary to add antifreezing agent, and by three vacuum diaphragm purifications when synthesis
Reason, free monomer is few, and smell is light.
(3) natural chrysanthemum essential oil is used, using the property of its oleophilic drainage, under the effect of sp act wetting agent, is passed through
Long agitation makes natural chrysanthemum essential oil infiltrate into inside water-base resin, embedding structure is formed, by embedding effect, in interior wall water
When painting drying and volatilizing, natural chrysanthemum essential oil is prevented to be volatilized with moisture.Because natural chrysanthemum essential oil is covered by aqueous tree
Internal in fat, after construction over time, water-base resin progressively degradation with aging is coated on the natural chrysanthemum in water-base resin
Essential oil is just progressively slowly released, so as to be carried out to the harmful bacteria in the room of the interior wall sealing wax for natural chrysanthemum essential oil of having constructed
Kill, protection room owner health.
Embodiment
Following examples only exist in illustrative purpose, without being intended to limit the scope of the present invention.
Embodiment 1
A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil of the present invention, the eyeshield metope containing natural chrysanthemum essential oil
Sealing wax includes following component by weight：
The weight ratio of the BASF styrene-acrylate emulsion ECO338 and natural chrysanthemum essential oil is 12：1.
The defoamer is two kinds of combination in section peaceful defoamer SN-154 and Ke Ning defoamers A-10.
The dispersant is TE parts of O Dispers750W of enlightening high score powder.The wetting agent is Clariant wetting agent
LCN088.The thickener is nano nano fumed silica powder body thickener.The filler is calcined kaolin, heavy carbon
The combination of sour two kinds of calcium.
The titanium dioxide is rutile pigment titanium dioxide, described for the production of rutile pigment titanium dioxide chloridising；Institute
Levelling agent is stated for ROHM AND HAAS levelling agent RM-2020.
The preparation method of eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil, comprises the following steps：
(1) each component is accurately weighed by described parts by weight, by water-base resin, natural chrysanthemum essential oil by weight 12：1
Ratio mixing, add wetting agent, stir 1 hour, obtain mixture 1；
(2) water, Clariant Liquid BPF ipacide GSF, enlightening high score powder TE parts of O Dispers750W and Ke Ning are disappeared
Infusion A-10 is mixed, and is stirred, is obtained mixture 2；
(3) pigment Du Pont's rutile pigment titanium dioxide and filler powdered whiting and calcining are added into the mixture 2
Less than 50 microns are distributed under kaolin, vacuum state, mixture 3 is obtained；
(4) mixture 1, ROHM AND HAAS levelling agent RM-2020 and nano nano-gas-phase are added into the mixture 3
Silicon-dioxide powdery thickener, stirs, and the eyeshield metope sealing wax containing natural chrysanthemum essential oil is made.
The present invention is containing the eyeshield metope sealing wax principle of work and power of natural chrysanthemum essential oil：
Using natural chrysanthemum essential oil, using the property of its oleophilic drainage, under the effect of sp act wetting agent, by it is long when
Between stirring natural chrysanthemum essential oil is infiltrated into inside water-base resin, form embedding structure, it is dry in interior wall sealing wax by embedding effect
During dry volatilization, natural chrysanthemum essential oil is prevented to be volatilized with moisture.
Because natural chrysanthemum essential oil is covered by inside in water-base resin, after construction over time, water-base resin
Progressively degradation with aging, the natural chrysanthemum essential oil being coated in water-base resin is just progressively slowly released, so as to day of having constructed
The harmful bacteria in the room of the interior wall sealing wax of right chrysanthemum essential oil is killed, protection room owner health.
Embodiment 2
The difference of embodiment 2 and embodiment 1 is：
A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil of the present invention, the eyeshield metope containing natural chrysanthemum essential oil
Sealing wax includes following component by weight：
The weight ratio of the BASF styrene-acrylate emulsion ECO338 and natural chrysanthemum essential oil is 12：1.
The defoamer is the peaceful defoamer SN-154 of section.The dispersant is TE parts of ODispers750W of enlightening high score powder.
The wetting agent is Clariant wetting agent LCN088.
The filler is three kinds of combination in calcined kaolin, powdered whiting, diatomite.The levelling agent is sieve door
Haas levelling agent RM-2020.
The preparation method of eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil, comprises the following steps：
In step (1), each component is accurately weighed by described parts by weight, water-base resin, natural chrysanthemum essential oil are pressed
Weight compares 12：1 ratio mixing, adds wetting agent, stirs 20 hours, obtain mixture 1.
Embodiment 3
The difference of embodiment 3 and embodiment 1 is：
A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil of the present invention, the eyeshield metope containing natural chrysanthemum essential oil
Sealing wax includes following component by weight：
The weight ratio of the BASF styrene-acrylate emulsion ECO338 and natural chrysanthemum essential oil is 12：1.
The defoamer is the peaceful defoamer SN-154 of section.The dispersant is enlightening high score powder TEGODispers750W.Institute
Preservative is stated for Clariant Liquid BPF ipacide GSF；
The wetting agent is Clariant wetting agent LCN088.The pigment is Du Pont rutile type titanium white R-706, described
Filler is three kinds of combination in calcined kaolin, powdered whiting, diatomite.
The levelling agent is ROHM AND HAAS levelling agent RM-2020.
The preparation method of eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil, comprises the following steps：In step
Suddenly in (1), each component is accurately weighed by described parts by weight, by water-base resin, natural chrysanthemum essential oil by weight 12：1
Ratio is mixed, and adds wetting agent, is stirred 48 hours, is obtained mixture 1.
Embodiment 4
A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil of the present invention, the eyeshield metope containing natural chrysanthemum essential oil
Sealing wax includes following component by weight：
The weight ratio of the net taste resin of the property of water-bearing and natural chrysanthemum essential oil is 12：1.The defoamer is nano polysilicon oxygen
Two kinds of combination in alkane-copolyether type of latex type, mineral oils.
The dispersant is Sodium Polyacrylate salt.The wetting agent is polyoxyethylated alkyl phenol；The filler is cunning
Stone flour.The levelling agent is two kinds of combination in dimethyl polysiloxane emulsion and polysiloxane-polyether copolymer class.
The preparation method of eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil, comprises the following steps：
In step (1), each component is accurately weighed by described parts by weight, water-base resin, natural chrysanthemum essential oil are pressed
Weight compares 12：1 ratio mixing, adds wetting agent, stirs 1 hour, obtain mixture 1；
In step (2), water, preservative, dispersant and defoamer are mixed, stirs, obtains mixture 2；
In step (3), added into the mixture 2 under pigment and filler, vacuum state and be distributed to less than 50 microns,
Obtain mixture 3；
In step (4), the mixture 1, levelling agent and thickener are added into the mixture 3, is stirred, made
The eyeshield metope sealing wax of natural chrysanthemum essential oil must be contained.
Embodiment 5
The difference of embodiment 5 and embodiment 4 is：
A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil of the present invention, the eyeshield metope containing natural chrysanthemum essential oil
Sealing wax includes following component by weight：
The net taste resin of the property of water-bearing is aqueous net taste pure acrylate resin；The defoamer is polyethylene glycol-hydrophobic
Solid-polysiloxane mixture class.The thickener is nano nano fumed silica powder body thickener；The pigment is titanium
White powder.
The dispersant is two kinds of combination in modified polypropene acid solution class and modified polycarboxylic acid salt.
The wetting agent is two kinds of combination in sodium butylnaphthalenesulfonate salt and polyoxyethylene polyoxyethylene block copolymer；
The thickener is nano nano fumed silica powder body thickener；The pigment is titanium dioxide.
The filler is three kinds of combination in calcined kaolin, wollastonite and blanc fixe.The titanium dioxide is gold
Red stone-type pigment titanium white, it is described for the production of rutile pigment titanium dioxide chloridising；
The levelling agent is cross-linking organosilicon polyoxyalkylene acrylate lipin polymer, dimethyl polysiloxane emulsion or poly- silicon
Three kinds of combination in oxygen alkane-copolyether class.
The preparation method of eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil, comprises the following steps：
(1) each component is accurately weighed by described parts by weight, by water-base resin, natural chrysanthemum essential oil by weight 12：1
Ratio mixing, add wetting agent, stir 25 hours, obtain mixture 1；
(2) water, ipacide parts of SF of Clariant Liquid BPF, enlightening high score powder TE parts of O Dispers750W and Ke Ning are disappeared
Infusion A-10 is mixed, and is stirred, is obtained mixture 2；
(3) pigment Du Pont's rutile pigment titanium dioxide and filler powdered whiting and calcining are added into the mixture 2
Less than 50 microns are distributed under kaolin, vacuum state, mixture 3 is obtained；
(4) mixture 1, ROHM AND HAAS levelling agent RM-2020 and nano nano-gas-phase are added into the mixture 3
Silicon-dioxide powdery thickener, stirs, and the eyeshield metope sealing wax containing natural chrysanthemum essential oil is made.
Embodiment 6
The difference of embodiment 6 and embodiment 4 is：
A kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil of the present invention, the eyeshield metope containing natural chrysanthemum essential oil
Sealing wax includes following component by weight：
The net taste resin of the property of water-bearing is aqueous net taste pure acrylate resin；The defoamer is polyethylene glycol-hydrophobic
Solid-polysiloxane mixture class.
The dispersant is modified polycarboxylic acid salt.
The wetting agent is two kinds of combination in sodium butylnaphthalenesulfonate salt and polyoxyethylene polyoxyethylene block copolymer；
The pigment is titanium dioxide.
The filler is powdered whiting.The titanium dioxide is rutile pigment titanium dioxide, and described is rutile-type face
Expect the production of titanium dioxide chloridising；The levelling agent is polysiloxane-polyether copolymer class.
The preparation method of eyeshield metope sealing wax of the present invention containing natural chrysanthemum essential oil, comprises the following steps：
In step (1), each component is accurately weighed by described parts by weight, water-base resin, natural chrysanthemum essential oil are pressed
Weight compares 12：1 ratio mixing, adds wetting agent, stirs 48 hours, obtain mixture 1.
Experiment 1
The prevailing quality technical indicator of the eyeshield metope sealing wax containing natural chrysanthemum essential oil of the gained of embodiment 1 is as shown in table 1：
Table 1
The prevailing quality technical indicator that the eyeshield metope sealing wax containing natural chrysanthemum essential oil is made in embodiment 2 is as shown in table 2：
Table 2
The prevailing quality technical indicator of the eyeshield metope sealing wax containing natural chrysanthemum essential oil of the gained of embodiment 3 is as shown in table 3：
Table 3
From table 1 to table 3, the properties of the eyeshield metope sealing wax containing natural chrysanthemum essential oil of the invention are excellent, and
And can be with sustained release chrysanthemum essential oil relieving eye strain.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, the present invention
Claimed scope is by appended claims, specification and its equivalent thereof.
Claims (9)
1. a kind of eyeshield metope sealing wax containing natural chrysanthemum essential oil, it is characterised in that：The eyeshield wall containing natural chrysanthemum essential oil
Face sealing wax includes following component by weight：
2. the eyeshield metope sealing wax according to claim 1 containing natural chrysanthemum essential oil, it is characterised in that：It is described to contain natural chrysanthemum
The eyeshield metope sealing wax of flower essential oil includes following component by weight：
3. the eyeshield metope sealing wax according to claim 1 or 2 containing natural chrysanthemum essential oil, it is characterised in that：It is described aqueous
Property net taste resin and natural chrysanthemum essential oil weight ratio be 12：1.
4. the eyeshield metope sealing wax according to claim 3 containing natural chrysanthemum essential oil, it is characterised in that：The property of water-bearing is net
Taste resin is aqueous net taste pure acrylate resin；The defoamer is nano polysilicon oxygen alkane-copolyether type of latex type, mineral
One or more of combinations in oils or polyethylene glycol-hydrophobic solid-polysiloxane mixture class.
5. the eyeshield metope sealing wax according to claim 4 containing natural chrysanthemum essential oil, it is characterised in that：The dispersant is
One or more of combinations in Sodium Polyacrylate salt, modified polypropene acid solution class or modified polycarboxylic acid salt.
6. the eyeshield metope sealing wax according to claim 5 containing natural chrysanthemum essential oil, it is characterised in that：The wetting agent is
Sodium butylnaphthalenesulfonate salt, polyoxyethylated alkyl phenol or the one of which or several in polyoxyethylene polyoxyethylene block copolymer
Combination.
7. the eyeshield metope sealing wax according to claim 6 containing natural chrysanthemum essential oil, it is characterised in that：The filler is to forge
Burn one or more of combinations in kaolin, powdered whiting, diatomite, talcum powder, wollastonite or blanc fixe；It is described
Titanium dioxide is rutile pigment titanium dioxide, described for the production of rutile pigment titanium dioxide chloridising；The levelling agent is friendship
In connection type silicone polyether acrylate analog copolymer, dimethyl polysiloxane emulsion or polysiloxane-polyether copolymer class
One of which or several combinations.
8. the eyeshield metope sealing wax according to claim 7 containing natural chrysanthemum essential oil, it is characterised in that：The rutile-type
Pigment titanium white is Du Pont rutile type titanium white R-706；The aqueous net taste pure acrylate resin be BASF styrene-
Acrylic acid ester emulsion ECO；The defoamer is the peaceful defoamer SN-154 of section；The preservative is Clariant Liquid BPF ipacide
GSF；The dispersant is enlightening high score powder TEGODispers750W；The levelling agent is ROHM AND HAAS levelling agent RM-2020；
The wetting agent is Clariant Clariant wetting agent LCN088.
9. the preparation method of the eyeshield metope sealing wax containing natural chrysanthemum essential oil described in claim any one of 1-8, its feature exists
In comprising the following steps：
(1) parts by weight as described in claim 1 accurately weigh each component, by water-base resin, natural chrysanthemum essential oil by weight
Than 12：1 ratio mixing, adds wetting agent, stirs 1-48 hours, obtain mixture 1；
(2) water, preservative, dispersant and defoamer are mixed, stirs, obtain mixture 2；
(3) added into the mixture 2 under pigment and filler, vacuum state and be distributed to less than 50 microns, obtain mixture 3；
(4) mixture 1, levelling agent and thickener are added into the mixture 3, is stirred, is made and contains natural chrysanthemum
The eyeshield metope sealing wax of essential oil.