CN107057498A - A kind of high coverage rate coating - Google Patents
A kind of high coverage rate coating Download PDFInfo
- Publication number
- CN107057498A CN107057498A CN201710359185.9A CN201710359185A CN107057498A CN 107057498 A CN107057498 A CN 107057498A CN 201710359185 A CN201710359185 A CN 201710359185A CN 107057498 A CN107057498 A CN 107057498A
- Authority
- CN
- China
- Prior art keywords
- coverage rate
- high coverage
- rate coating
- mixtures
- coating according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high coverage rate coating, belong to new material technical field of coatings, include the raw material of mass percentage content:Acrylic resin 20~25%, amino resins 10~12%, auxiliary agent 0.5~2%, adhesive agent 2~2.5%, pigment 10~12%, filler 35~38%, covering polymer 5~8%, solvent 0.5~17.5%.The high coverage rate coating that the invention is provided, the high coverage rate coating prepared has high covering power, and adhesive force is strong, the advantages of water-fast, solvent resistance is good, and meets environmental protection sustainable development requirement.
Description
Technical field
The invention belongs to new material technical field of coatings, and in particular to a kind of high coverage rate coating, the preparation method of coating
And application method.
Background technology
The reasonably combined of color stuffing is adjusted in formulation for coating material system, selection has the pigment of stronger scattering process,
The occasion that pigment can be compounded, pays in the stronger covering of organic pigment by increasing the method for inorganic pigment of high covering power
Power.At present, commercial coating is various in style, complete, but many low coverage rates of coating generally existing (or hiding rare) and disperses
The drawbacks of inefficiency.
The content of the invention
Instant invention overcomes above-mentioned shortcoming, first purpose of the invention is to provide a kind of high coverage rate coating, bag
Include the raw material of mass percentage content:Acrylic resin 20~25%, amino resins 10~12%, auxiliary agent 0.5~2%, adherence
Agent 2~2.5%, pigment 10~12%, filler 35~38%, covering polymer 5~8%, solvent 0.5~17.5%..
It is preferred that, the acrylic resin is in epoxy-modified acrylic acid, polyester modification acrylic acid or thermoset acrylics
Any one or two or more mixtures.
It is preferred that, the amino resins be Lauxite, melamine resin, hydrocarbon-based melamine formaldehyde resin or
Any one in benzoguanamine copolymer resins or two or more mixtures.
It is preferred that, the auxiliary agent is in polycarboxylic acids sodium, polysiloxanes, Sodium Polyacrylate or oleoyl alkylene oxide copolymers
Any one or two or more mixtures.
It is preferred that, the adhesive agent are any in silane coupler, epoxy phosphate ester, polyester modification resin or phosphate
One or more kinds of mixtures.
It is preferred that, the pigment be titanium dioxide, wollastonite powder, pearly-lustre bronze or pearly-lustre silver powder any one or it is two or more
Mixture.
It is preferred that, the covering polymer is methyl methacrylate, methacrylic acid, ethyl acrylate, methyl-prop
Any one or two or more mixtures of the macromolecular compositions such as olefin(e) acid butyl ester, polyene-based insatiable hunger or monomer.
It is preferred that, the solvent is toluene, dimethylbenzene, butanone, acetone, n-butanol, ethanol, propylene glycol monomethyl ether or propane diols
Any one in ether or two or more mixtures.
Second object of the present invention is to provide a kind of preparation method of high coverage rate coating, is specifically by quality percentage
Directly mixed than content, be sufficiently stirred for 3200 revs/min, disperseed 10~15 minutes.
Third object of the present invention is to provide a kind of application method of high coverage rate coating, specifically using 80 mesh machines
Device is polished workpiece surface, and is carried out disposable spray finishing and can be covered ground well.
The beneficial effects of the invention are as follows:
1) each raw material is easily obtained in high coverage rate formulation for coating material of the present invention;2) present invention in high coverage rate coating preparation work
Skill is simple to operation;3) the high coverage rate coating prepared has high covering power, and adhesive force is strong, and water-fast, solvent resistance is good etc.
Advantage, and meet environmental protection sustainable development requirement.
Embodiment
Embodiment 1
Weigh to stir and evenly mix after each raw material by the proportioning of table 1 and can obtain high coverage rate coating;
The composition of raw materials of the high coverage rate coating of table 1
Embodiment 2
Weigh to stir and evenly mix after each raw material by the proportioning of table 2 and can obtain high coverage rate coating;
The composition of raw materials of the high coverage rate coating of table 2
Embodiment 3
Weigh to stir and evenly mix after each raw material by the proportioning of table 3 and can obtain high coverage rate coating;
The composition of raw materials of the high coverage rate coating of table 3
Embodiment 4
Weigh to stir and evenly mix after each raw material by the proportioning of table 4 and can obtain high coverage rate coating;
The composition of raw materials of the high coverage rate coating of table 4
For conventional coating, particle diameter is than larger (except carbon black), it is seen that optical wavelength is about between 380~780nm.It is real
The aggregate particle size that coating is prepared in example 1~4 is applied in below 10um, covering power is good and for the scattered side of coating
Face, scattered is better, and agglomerate is opened more, and covering efficiency is also higher, this high covering power coating, due to resin, face
Material, covering polymer and filler it is reasonably combined, on the hardware ground such as iron material, aluminium, aluminium alloy, kirsite, stainless steel
After being polished with the sand paper of 80 mesh, disposable spray finishing can cover polishing print and material well, and with good performance, city
The coating products sold will be sprayed more than 2 times.
Claims (10)
1. a kind of high coverage rate coating, it is characterised in that the raw material including mass percentage content:Acrylic resin 20~
25%th, amino resins 10~12%, auxiliary agent 0.5~2%, adhesive agent 2~2.5%, pigment 10~12%, filler 35~38%,
Covering polymer 5~8%, solvent 0.5~17.5%.
2. a kind of high coverage rate coating according to claim 1, it is characterised in that the acrylic resin is epoxide modified
Any one in acrylic acid, polyester modification acrylic acid or thermoset acrylics or two or more mixtures.
3. a kind of high coverage rate coating according to claim 1, it is characterised in that the amino resins be Lauxite,
Any one in melamine resin, hydrocarbon-based melamine formaldehyde resin or benzoguanamine copolymer resins or two kinds
Mixture above.
4. a kind of high coverage rate coating according to claim 1, it is characterised in that the auxiliary agent is polycarboxylic acids sodium, poly- silicon
Any one in oxygen alkane, Sodium Polyacrylate or oleoyl alkylene oxide copolymers or two or more mixtures.
5. a kind of high coverage rate coating according to claim 1, it is characterised in that the adhesive agent be silane coupler,
Any one in epoxy phosphate ester, polyester modification resin or phosphate or two or more mixtures.
6. a kind of high coverage rate coating according to claim 1, it is characterised in that the pigment be titanium dioxide, wollastonite powder,
Any one or two or more mixtures of pearly-lustre bronze or pearly-lustre silver powder.
7. a kind of high coverage rate coating according to claim 1, it is characterised in that the covering polymer is methyl-prop
The macromolecular compositions such as e pioic acid methyl ester, methacrylic acid, ethyl acrylate, butyl methacrylate, polyene-based insatiable hunger or monomer
Any one or two or more mixtures.
8. a kind of high coverage rate coating according to claim 1, it is characterised in that the solvent is toluene, dimethylbenzene, fourth
Any one in ketone, acetone, n-butanol, ethanol, propylene glycol monomethyl ether or propylene-glycol ethyl ether or two or more mixtures.
9. a kind of preparation method of high coverage rate coating as described in any one in claim 1~8, it is characterised in that tool
Body is directly to mix mass percentage content, is sufficiently stirred for 3200 revs/min, is disperseed 10~15 minutes.
10. a kind of preparation method of high coverage rate coating as described in any one in claim 1~8, it is characterised in that tool
Body is to use 80 mesh machines polishing workpiece surface, and carries out disposable spray finishing.