CN107057489A - It is a kind of for fire-proof and thermal-insulation coating of interior wall and preparation method thereof - Google Patents
It is a kind of for fire-proof and thermal-insulation coating of interior wall and preparation method thereof Download PDFInfo
- Publication number
- CN107057489A CN107057489A CN201611165401.8A CN201611165401A CN107057489A CN 107057489 A CN107057489 A CN 107057489A CN 201611165401 A CN201611165401 A CN 201611165401A CN 107057489 A CN107057489 A CN 107057489A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- proof
- thermal
- interior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of fire-proof and thermal-insulation coating for interior wall, the raw material containing following parts by weight:30 40 parts of aqueous acrylic emulsion, 35 parts of hydroxypropyl methyl cellulose, 12 parts of silane coupler, 5 10 parts of glass bead, 15 20 parts of silicate mineral powder, 5 10 parts of haydite, 12 parts of MethylethoxylsiliconFluid Fluid, 58 parts of fire retardant, 15 20 parts of deionized water, 24 parts of coalescents, the invention also discloses its preparation method.Coating prepared by the present invention has insulation, heat-proof quality, and excellent fire protecting performance well.Conventional coating is compared on the market, and summer coating of the present invention can effectively reduce indoor temperature more than 3 DEG C, energy-conservation, and coating quality produced by the present invention is stable, and adhesive force is strong, with good application prospect.
Description
Technical field
The present invention relates to technical field of coatings, and in particular to a kind of fire-proof and thermal-insulation coating and its preparation side for interior wall
Method.
Background technology
Energy-conserving and environment-protective have become the key subjects that the 21 century whole mankind must face, and also have become our building trades
Have to the important topic for putting forth effort to solve.The thermal and insulating performance for improving house is one of building energy-saving consumption reduction and important arranged
Apply, many new buildings and many old buildings in exterior wall and interior wall by sticking heat insulation layer under the advocating of country
Method in the hope of reaching the heat insulation and preservation effect in room:I.e. hot summer by the heat-barrier material of inner-outer wall prevent heat radiation to
Transmit within doors, reduce the energy consumption of the household electrical appliance such as air-conditioning, cold winter also by the heat-barrier material of inner-outer wall prevent it is indoor compared with
High-temperature is transmitted to the outdoor of cold.In addition, heat-resisting, the heat-proof quality that improve existing coating are to solve fireproof root problem.
At present, on the market the heat-insulated heat resistance of fireproof coating is general.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of anti-fire screen for interior wall of heat-insulated Good Heat-resistance
Hot coating and preparation method thereof.
To realize object above, the present invention is achieved by the following technical programs:
A kind of fire-proof and thermal-insulation coating for interior wall, the raw material containing following parts by weight:Aqueous acrylic emulsion 30-40
Part, 3-5 parts of hydroxypropyl methyl cellulose, 1-2 parts of silane coupler, 5-10 parts of glass bead, 15-20 parts of silicate mineral powder,
5-10 parts of haydite, 1-2 parts of MethylethoxylsiliconFluid Fluid, 5-8 parts of fire retardant, 15-20 parts of deionized water, 2-4 parts of coalescents.
Preferably, the raw material containing following parts by weight:35 parts of aqueous acrylic emulsion, 4.5 parts of hydroxypropyl methyl cellulose,
Silane coupler 1.5,8 parts of glass bead, 16 parts of silicate mineral powder, 6 parts of haydite, 1.2 parts of MethylethoxylsiliconFluid Fluid, fire retardant
7 parts, 18 parts of deionized water, 3 parts of coalescents.
Preferably, the solid content of the aqueous acrylic emulsion is 30-40%.
Preferably, the silicate mineral powder is in talcum powder, diatomite, kaolin, montmorillonite, vermiculite, sepiolite
At least one.
Preferably, the haydite is lytag.
Preferably, the fire retardant by magnesium hydroxide, aluminium hydroxide and APP according to 2:2:3 mass ratio composition.
Preferably, the coalescents are butyl acetate and ethylene glycol according to 1:1 mass ratio composition.
For the preparation method of the fire-proof and thermal-insulation coating of interior wall, step is as follows:Aqueous acrylic emulsion and suitable quantity of water are added
Enter into container, dispersed with stirring 5-10min, silicate mineral powder, glass bead and haydite are added thereto, at a high speed scattered 10-
3-4h is ground after 15min again, then adds coalescents, hydroxypropyl methyl cellulose, fire retardant, silane coupler, first thereto
Base oxethyl silicone oil and balance deionized water, dispersed with stirring 20-30min, are produced.
Beneficial effect of the present invention:Silicate mineral powder and haydite in instant component, with porosity height, heat transfer coefficient
Low the characteristics of so that obtained coating has other component collective effects in insulation, heat-proof quality, and formula well, tool
There is excellent fire protecting performance.Conventional coating is compared on the market, summer coating of the present invention can effectively reduce by 3 DEG C of indoor temperature with
On, energy-conservation, and coating quality produced by the present invention is stable, adhesive force is strong, water-tolerant, with good application prospect.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making
The every other embodiment obtained under the premise of creative work, belongs to the scope of protection of the invention.
Embodiment 1:
A kind of fire-proof and thermal-insulation coating for interior wall, the raw material containing following parts by weight:Aqueous acrylic emulsion (solid content
For 32%) 35 parts, 4.5 parts of hydroxypropyl methyl cellulose, 1.5 parts of silane coupler, 8 parts of glass bead, 8 parts of talcum powder, vermiculite 8
Part, 6 parts of lytag, 1.2 parts of MethylethoxylsiliconFluid Fluid, 7 parts of fire retardant, 18 parts of deionized water, 1.5 parts of butyl acetate, second
1.5 parts of glycol.Wherein, fire retardant by magnesium hydroxide, aluminium hydroxide and APP according to 2:2:3 mass ratio composition.
For the preparation method of the fire-proof and thermal-insulation coating of interior wall, step is as follows:Aqueous acrylic emulsion and suitable quantity of water are added
Enter into container, dispersed with stirring 8min, silicate mineral powder, glass bead and haydite are added thereto, at a high speed after scattered 15min
3.5h is ground again, then adds coalescents, hydroxypropyl methyl cellulose, fire retardant, silane coupler, methyl ethoxy thereto
Silicone oil and balance deionized water, dispersed with stirring 25min, are produced.
Embodiment 2:
A kind of fire-proof and thermal-insulation coating for interior wall, the raw material containing following parts by weight:Aqueous acrylic emulsion (solid content
For 35%) 32 parts, 4 parts of hydroxypropyl methyl cellulose, 1.8 parts of silane coupler, 7 parts of glass bead, 9 parts of diatomite, sepiolite 9
Part, 7 parts of lytag, 1.5 parts of MethylethoxylsiliconFluid Fluid, 8 parts of fire retardant, 20 parts of deionized water, 1.5 parts of butyl acetate, second
1.5 parts of glycol.Wherein, fire retardant by magnesium hydroxide, aluminium hydroxide and APP according to 2:2:3 mass ratio composition.
For the preparation method of the fire-proof and thermal-insulation coating of interior wall, step is as follows:Aqueous acrylic emulsion and suitable quantity of water are added
Enter into container, dispersed with stirring 10min, silicate mineral powder, glass bead and haydite are added thereto, at a high speed scattered 10min
Grind 4h again afterwards, then add coalescents, hydroxypropyl methyl cellulose, fire retardant, silane coupler, methyl ethoxy thereto
Silicone oil and balance deionized water, dispersed with stirring 30min, are produced.
Embodiment 3:
A kind of fire-proof and thermal-insulation coating for interior wall, the raw material containing following parts by weight:Aqueous acrylic emulsion (solid content
For 30%) 40 parts, 3 parts of hydroxypropyl methyl cellulose, 2 parts of silane coupler, 5 parts of glass bead, 10 parts of kaolin, vermiculite 10
Part, 5 parts of lytag, 2 parts of MethylethoxylsiliconFluid Fluid, 5 parts of fire retardant, 20 parts of deionized water, 1 part of butyl acetate, ethylene glycol 2
Part.Wherein, fire retardant by magnesium hydroxide, aluminium hydroxide and APP according to 2:2:3 mass ratio composition.
For the preparation method of the fire-proof and thermal-insulation coating of interior wall, step is as follows:Aqueous acrylic emulsion and suitable quantity of water are added
Enter into container, dispersed with stirring 10min, silicate mineral powder, glass bead and haydite are added thereto, at a high speed scattered 15min
Grind 3h again afterwards, then add coalescents, hydroxypropyl methyl cellulose, fire retardant, silane coupler, methyl ethoxy thereto
Silicone oil and balance deionized water, dispersed with stirring 20min, are produced.
Embodiment 4:
A kind of fire-proof and thermal-insulation coating for interior wall, the raw material containing following parts by weight:Aqueous acrylic emulsion (solid content
For 40%) 30 parts, 5 parts of hydroxypropyl methyl cellulose, 1 part of silane coupler, 10 parts of glass bead, 5 parts of diatomite, montmorillonite 10
Part, 10 parts of lytag, 1 part of MethylethoxylsiliconFluid Fluid, 8 parts of fire retardant, 15 parts of deionized water, 2 parts of butyl acetate, ethylene glycol
2 parts.Wherein, fire retardant by magnesium hydroxide, aluminium hydroxide and APP according to 2:2:3 mass ratio composition.
For the preparation method of the fire-proof and thermal-insulation coating of interior wall, step is as follows:Aqueous acrylic emulsion and suitable quantity of water are added
Enter into container, dispersed with stirring 7min, silicate mineral powder, glass bead and haydite are added thereto, at a high speed after scattered 12min
3.5h is ground again, then adds coalescents, hydroxypropyl methyl cellulose, fire retardant, silane coupler, methyl ethoxy thereto
Silicone oil and balance deionized water, dispersed with stirring 30min, are produced.
Embodiment 5:
A kind of fire-proof and thermal-insulation coating for interior wall, the raw material containing following parts by weight:Aqueous acrylic emulsion (solid content
For 36%) 38 parts, 4.5 parts of hydroxypropyl methyl cellulose, 1.7 parts of silane coupler, 8 parts of glass bead, 7 parts of diatomite, Hai Pao
10 parts of stone, 10 parts of lytag, 1.5 parts of MethylethoxylsiliconFluid Fluid, 8 parts of fire retardant, 20 parts of deionized water, butyl acetate 1.5
Part, 1.5 parts of ethylene glycol.Wherein, fire retardant by magnesium hydroxide, aluminium hydroxide and APP according to 2:2:3 mass ratio composition.
For the preparation method of the fire-proof and thermal-insulation coating of interior wall, step is as follows:Aqueous acrylic emulsion and suitable quantity of water are added
Enter into container, dispersed with stirring 10min, silicate mineral powder, glass bead and haydite are added thereto, at a high speed scattered 15min
Grind 4h again afterwards, then add coalescents, hydroxypropyl methyl cellulose, fire retardant, silane coupler, methyl ethoxy thereto
Silicone oil and balance deionized water, dispersed with stirring 20min, are produced.
Performance test, its adhesive force≤1 are carried out to the obtained fire-proof and thermal-insulation coating for interior wall of the embodiment of the present invention 1
Level, when coating layer thickness is 10mm, its resistance to combustion limit >=100min.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that:It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic;And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (8)
1. a kind of fire-proof and thermal-insulation coating for interior wall, it is characterised in that the raw material containing following parts by weight:Aqueous acrylamide yogurt
30-40 parts of liquid, 3-5 parts of hydroxypropyl methyl cellulose, 1-2 parts of silane coupler, 5-10 parts of glass bead, silicate mineral powder
15-20 parts, 5-10 parts of haydite, 1-2 parts of MethylethoxylsiliconFluid Fluid, 5-8 parts of fire retardant, 15-20 parts of deionized water, coalescents 2-
4 parts.
2. it is used for the fire-proof and thermal-insulation coating of interior wall as claimed in claim 1, it is characterised in that the original containing following parts by weight
Material:35 parts of aqueous acrylic emulsion, 4.5 parts of hydroxypropyl methyl cellulose, silane coupler 1.5,8 parts of glass bead, silicate
16 parts of mineral powder, 6 parts of haydite, 1.2 parts of MethylethoxylsiliconFluid Fluid, 7 parts of fire retardant, 18 parts of deionized water, 3 parts of coalescents.
3. it is used for the fire-proof and thermal-insulation coating of interior wall as claimed in claim 2, it is characterised in that the aqueous acrylic emulsion
Solid content is 30-40%.
4. it is used for the fire-proof and thermal-insulation coating of interior wall as claimed in claim 2, it is characterised in that the silicate mineral powder is selected from
At least one of talcum powder, diatomite, kaolin, montmorillonite, vermiculite, sepiolite.
5. it is used for the fire-proof and thermal-insulation coating of interior wall as claimed in claim 2, it is characterised in that the haydite is flyash ceramic
Grain.
6. it is used for the fire-proof and thermal-insulation coating of interior wall as claimed in claim 2, it is characterised in that the fire retardant is by hydroxide
Magnesium, aluminium hydroxide and APP are according to 2:2:3 mass ratio composition.
7. it is used for the fire-proof and thermal-insulation coating of interior wall as claimed in claim 2, it is characterised in that the coalescents are acetic acid fourth
Ester and ethylene glycol are according to 1:1 mass ratio composition.
8. the preparation method of the fire-proof and thermal-insulation coating for interior wall as described in claim 1-7 is any, it is characterised in that step
It is as follows:Aqueous acrylic emulsion and suitable quantity of water are added in container, dispersed with stirring 5-10min adds silicate mine thereto
Thing powder, glass bead and haydite, grind 3-4h, then add coalescents, hydroxypropyl thereto again after scattered 10-15min at a high speed
Methylcellulose, fire retardant, silane coupler, MethylethoxylsiliconFluid Fluid and balance deionized water, dispersed with stirring 20-30min, i.e.,
.