CN107057475A - A kind of water-repellent paint and preparation method - Google Patents
A kind of water-repellent paint and preparation method Download PDFInfo
- Publication number
- CN107057475A CN107057475A CN201710363653.XA CN201710363653A CN107057475A CN 107057475 A CN107057475 A CN 107057475A CN 201710363653 A CN201710363653 A CN 201710363653A CN 107057475 A CN107057475 A CN 107057475A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- repellent paint
- nonionic surfactant
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to water-repellent paint field, a kind of water-repellent paint, including following parts by weight of component are proposed：Solid content is 50% 100 parts of styrene-butadiene latex；50 60 parts of clay；20 30 parts of titanium dioxide；34 parts of zinc oxide；13 parts of antioxidant D；10 12 parts of sodium carboxymethylcellulose；25 parts of nonionic surfactant；100 150 parts of water.The water-repellent paint of the present invention has the advantages that environmental protection and waterproof long lifespan.
Description
Technical field
The present invention relates to paint field, particularly a kind of water-repellent paint and preparation method.
Background technology
Water-repellent paint currently on the market coordinates it using rubber, polyacrylic acid, polyurethane etc. as main component mostly
What his auxiliary agent was obtained has certain ductility, elastoplasticity, impervious new coating.
Existing water-repellent paint is to environmental requirement more and more higher, and water paint is the emphasis of development, but acrylic compounds
Its service life of water-repellent paint is short, and polyurethanes water-repellent paint has toxicity slow release, it is therefore desirable to propose a kind of environmentally friendly and anti-
The water-repellent paint of water long lifespan.
The content of the invention
The present invention is intended to provide the water-repellent paint and preparation method of a kind of environmental protection and waterproof long lifespan.
Its concrete scheme is：A kind of water-repellent paint, including following parts by weight of component：
Solid content is 50% 100 parts of styrene-butadiene latex；
50-60 parts of clay；
20-30 parts of titanium dioxide；
3-4 parts of zinc oxide；
1-3 parts of antioxidant D；
10-12 parts of sodium carboxymethylcellulose；
2-5 parts of nonionic surfactant；
100-150 parts of water.
In above-mentioned water-repellent paint, including following parts by weight of component：
Solid content is 50% 100 parts of styrene-butadiene latex；
55 parts of clay；
25 parts of titanium dioxide；
3.5 parts of zinc oxide；
2 parts of antioxidant D；
11 parts of sodium carboxymethylcellulose；
3 parts of nonionic surfactant；
100-150 parts of water.
In above-mentioned water-repellent paint, described nonionic surfactant is APES, high carbocyclic aliphatic
One or more combinations in alcohol APEO, polyoxyethylene carboxylate, fatty acid methyl ester ethoxylate.
Meanwhile, the invention also discloses the preparation method of above-mentioned water-repellent paint, comprise the following steps：
Step 1：Stirred after other raw materials in addition to water are mixed；
Step 2：Raw material is disperseed by mechanical lapping；
Step 3：Water is added, stirring and filtering produces.
The beneficial effects of the present invention are：
The water-repellent paint of the present invention using styrene-butadiene latex as main body, using clay and titanium dioxide is as filler and brightens
Agent, lives with sodium carboxymethylcellulose in improving the dispersiveness of rubber-like main substance and the relative viscosity of system using table,
It is so comprehensive to reach the coating that matched in excellence or beauty with polyacrylic acid water-repellent paint and polyurethanes water-repellent paint performance.
Embodiment
With reference to embodiment, technical scheme is described in further detail, but not constituted pair
Any limitation of the present invention.
In order to which more clearly the present invention will be described, it is listed below embodiment to illustrate the superiority of the present invention.
Embodiment 1
A kind of water-repellent paint, including following parts by weight of component：
Solid content is 50% 100 parts of styrene-butadiene latex；
55 parts of clay；
25 parts of titanium dioxide；
3.5 parts of zinc oxide；
2 parts of antioxidant D；
11 parts of sodium carboxymethylcellulose；
3 parts of laurate polyoxyethylene ester；
120 parts of water.
Its preparation method comprises the following steps：
Step 1：Stirred after other raw materials in addition to water are mixed；
Step 2：Raw material is disperseed by mechanical lapping；
Step 3：Water is added, stirring and filtering produces.
Embodiment 2
A kind of water-repellent paint, including following parts by weight of component：
Solid content is 50% 100 parts of styrene-butadiene latex；
50 parts of clay；
30 parts of titanium dioxide；
3 parts of zinc oxide；
3 parts of antioxidant D；
10 parts of sodium carboxymethylcellulose；
5 parts of laurate polyoxyethylene ester；
150 parts of water.
Its preparation method comprises the following steps：
Step 1：Stirred after other raw materials in addition to water are mixed；
Step 2：Raw material is disperseed by mechanical lapping；
Step 3：Water is added, stirring and filtering produces.
The water-repellent paint of the present embodiment 1 and 2, as main body, filler is used as using clay and titanium dioxide using styrene-butadiene latex
And brightening agent, lived using table and sodium carboxymethylcellulose glues to improve the dispersiveness of rubber-like main substance and the relative of system
Denseness, it is so comprehensive to reach the coating that matched in excellence or beauty with polyacrylic acid water-repellent paint and polyurethanes water-repellent paint performance.
Its usage amount should reach more than 500g/m2, can reach the effect of preferable waterproof back-fire relief.
Above-described is only presently preferred embodiments of the present invention, all timess made in the range of the spirit and principles in the present invention
What modifications, equivalent substitutions and improvements etc., should be included in the scope of the protection.
Claims (4)
1. a kind of water-repellent paint, it is characterised in that including following parts by weight of component：
Solid content is 50% 100 parts of styrene-butadiene latex；
50-60 parts of clay；
20-30 parts of titanium dioxide；
3-4 parts of zinc oxide；
1-3 parts of antioxidant D；
10-12 parts of sodium carboxymethylcellulose；
2-5 parts of nonionic surfactant；
100-150 parts of water.
2. water-repellent paint according to claim 1, it is characterised in that including following parts by weight of component：
Solid content is 50% 100 parts of styrene-butadiene latex；
55 parts of clay；
25 parts of titanium dioxide；
3.5 parts of zinc oxide；
2 parts of antioxidant D；
11 parts of sodium carboxymethylcellulose；
3 parts of nonionic surfactant；
100-150 parts of water.
3. water-repellent paint according to claim 1 or 2, it is characterised in that described nonionic surfactant is alkyl
One in phenol polyethenoxy ether, high-carbon fatty alcohol polyoxyethylene ether, polyoxyethylene carboxylate, fatty acid methyl ester ethoxylate
Plant or multiple combinations.
4. a kind of preparation method of water-repellent paint as claimed in claim 1 or 2, it is characterised in that comprise the following steps：
Step 1：Stirred after other raw materials in addition to water are mixed；
Step 2：Raw material is disperseed by mechanical lapping；
Step 3：Water is added, stirring and filtering produces.