CN107057239A - A kind of weather-proof lamp house cloth and its production technology - Google Patents
A kind of weather-proof lamp house cloth and its production technology Download PDFInfo
- Publication number
- CN107057239A CN107057239A CN201710429289.2A CN201710429289A CN107057239A CN 107057239 A CN107057239 A CN 107057239A CN 201710429289 A CN201710429289 A CN 201710429289A CN 107057239 A CN107057239 A CN 107057239A
- Authority
- CN
- China
- Prior art keywords
- parts
- lamp house
- facial mask
- notacoria
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of weather-proof lamp house cloth, described lamp house cloth is made up of grid cloth, the notacoria and facial mask that are respectively arranged at grid cloth both sides, and described notacoria is made up of the raw material of following parts by weight：46 parts of 100 parts of Corvic, 20 40 parts of epoxy resin, 15 22 parts of calcium carbonate, nanometer calcium 36 50,20 40 parts of phthalic acid ester, 35 parts of epoxidized soybean oil, 6 10 parts of color powder and stabilizer；Described facial mask is made up of the raw material of following parts by weight：46 parts of 100 parts of Corvic, 30 40 parts of epoxy resin, 15 22 parts of calcium carbonate, 48 53 parts of nanometer calcium, 28 55 parts of phthalic acid ester, 35 parts of epoxidized soybean oil, 6 10 parts of color powder and stabilizer.A kind of weather-proof lamp house cloth of the present invention, with good weatherability and pliability.
Description
Technical field
The present invention relates to a kind of weather-proof lamp house cloth and its production technology.
Background technology
As the progress and people of society are to the awareness and understanding of going deep into of advertising, domestic advertising has obtained rapid hair
Exhibition, and outdoor advertising industry receives the green grass or young crops of vast advertisement producer with its strong visual impact and competitive cost
Look at.Lamp house cloth is the lamp house signboard fabric that a kind of grid cloth by two layers of PVC and a floor height intensity is constituted, and is also Pola cloth, point
Two kinds of interior polishing and outer polishing, main production process have knife scraping coating method, rolling process, laminating method.Feature is that thickness, stretching resistance are strong
Degree.With widely using for lamp box advertisement, the lamp box advertisement beautiful in colour of the shape that is seen everywhere form formula.And that it is used is wide
Material is accused to its intensity, rotproofness, the requirement also more and more higher of water resistance.Its pliability of existing lamp house cloth and weatherability are not
It is ideal, it is difficult to use out of doors for a long time and keep original color and luster and toughness.
The content of the invention
The technical problem to be solved in the present invention is：In order to overcome it is above-mentioned present in problem there is provided a kind of weather-proof lamp box
Cloth, with good weatherability and pliability.
The present invention solves its technical problem and provided：A kind of weather-proof lamp house cloth, described lamp house cloth is set by grid cloth, respectively
The notacoria and facial mask composition of grid cloth both sides are placed in, described notacoria is made up of the raw material of following parts by weight：Corvic
100 parts, 20-40 parts of epoxy resin, 15-22 parts of calcium carbonate, nanometer calcium 36-50,20-40 parts of phthalic acid ester, epoxy soybean
4-6 parts of oily 3-5 parts, 6-10 parts of color powder and stabilizer；
Described facial mask is made up of the raw material of following parts by weight：100 parts of Corvic, 30-40 parts of epoxy resin, calcium carbonate
15-22 parts, 48-53 parts of nanometer calcium, 28-55 parts of phthalic acid ester, 3-5 parts of epoxidized soybean oil, 6-10 parts of color powder and stably
4-6 parts of agent.
Preferably, described film is made up of the raw material of following parts by weight：100 parts of Corvic, epoxy resin 35
Part, 17 parts of calcium carbonate, nanometer calcium 40,35 parts of phthalic acid ester, 3 parts of epoxidized soybean oil, 6 parts of color powder and 4 parts of stabilizer；Institute
The facial mask stated is made up of the raw material of following parts by weight：100 parts of Corvic, 30 parts of epoxy resin, calcium carbonate 15 part, nanometer
4 parts of 49 parts of calcium, 29 parts of phthalic acid ester, 35 parts of epoxidized soybean oil, 6 parts of color powder and stabilizer.
Preferably, described epoxy resin be cyclohexanedimethanol epoxy resin and hydrogenated bisphenol A epoxy resin by
1:The mixture of 1 ratio composition.Epoxy resin is one of most important thermosetting polymer classification, and Weather-resistant epoxy coating can
The demand of the finish paint in anticorrosion coating system is eliminated, epoxy resin has good physics, chemical property, it is to metal and non-
The surface of metal material has excellent adhesive strength, and dielectric properties are good, and deformation retract rate is small, and product size stability is good,
Hardness is high, and pliability is preferable, to alkali and most of solvent-stable.
Preferably, described stabilizer is organotin.Organic tin stabilizer has the remarkable transparency, uses organotin
Stabilizer PVC film class formula, can be crystallized as product；With good translucency.
The present invention solves its technical problem and additionally provided：A kind of weather-proof lamp house cloth production technology, the production of described notacoria
Technique is：It is 100 parts of Corvic, 35 parts of epoxy resin, 17 parts of calcium carbonate, nanometer calcium 40, O-phthalic by parts by weight
4 parts of 35 parts of acid esters, 3 parts of epoxidized soybean oil, 6 parts of color powder and stabilizer are mixed, and obtain notacoria major ingredient；To notacoria master
Material is rolled, is embossed, is cooled down and batched, so that notacoria is made；
The production technology of described facial mask is：It is 100 parts of Corvic, 30 parts of epoxy resin, calcium carbonate 15 by parts by weight
Part, 49 parts of nanometer calcium, 29 parts of phthalic acid ester, 35 parts of epoxidized soybean oil, 6 parts of color powder and 4 parts of stabilizer carry out mixing and stirred
Mix, obtain facial mask major ingredient；Facial mask major ingredient is rolled, is embossed, is cooled down and batched, so that facial mask is made；
Notacoria and facial mask are fitted into grid cloth both sides respectively, lamp house cloth is obtained.
Further, the whipping process of the production technology of the notacoria and facial mask includes：
（1）Stirring temperature of charge is increased to 110 degree in heating stirring, whipping process, stirred one minute；
（2）Cooling and stirring, the temperature of reduction stirring material, when stirring temperature of charge is reduced to 50 degree, stops stirring；And by thing
Material and into bulk.
Further, the notacoria major ingredient and facial mask major ingredient are rolled respectively using four rod calenders.
The beneficial effects of the invention are as follows：A kind of weather-proof lamp house cloth, with good weatherability, absorbency, facial mask and notacoria
Plasticizing it is highly uniform, ink absorption is protruded, and each composition is that can produce cooperative effect between organic whole, raw material, is increased
Add the weather-proof and flexility of lamp house cloth, extend the service life of lamp house cloth product.
Embodiment
By embodiment, the present invention is described in detail now.
Embodiment 1
Weather-proof lamp house cloth, described lamp house cloth is made up of grid cloth, the notacoria and facial mask that are respectively arranged at grid cloth both sides, described
Film be made up of the raw material of following parts by weight：100 parts of Corvic, 35 parts of epoxy resin, 17 parts of calcium carbonate, nanometer calcium
40th, 4 parts of 35 parts of phthalic acid ester, 3 parts of epoxidized soybean oil, 6 parts of color powder and stabilizer；Described facial mask is by following parts by weight
Raw material composition：100 parts of Corvic, 30 parts of epoxy resin, 15 parts of calcium carbonate, 49 parts of nanometer calcium, phthalic acid ester
4 parts of 29 parts, 35 parts of epoxidized soybean oil, 6 parts of color powder and stabilizer.
Described epoxy resin is cyclohexanedimethanol epoxy resin and hydrogenated bisphenol A epoxy resin by 1:1 ratio
The mixture of composition.Epoxy resin is one of most important thermosetting polymer classification, and Weather-resistant epoxy coating can eliminate anti-corrosion
The demand of the finish paint in coating system is lost, epoxy resin has good physics, chemical property, and it is to metal and nonmetallic materials
Surface there is excellent adhesive strength, dielectric properties are good, and deformation retract rate is small, and product size stability is good, and hardness is high, soft
Toughness is preferable, to alkali and most of solvent-stable.
Described stabilizer is organotin.Wherein, organic tin stabilizer has the remarkable transparency, uses Organotin Stabilized
Agent PVC film class formula, can be crystallized as product；With good translucency.
A kind of weather-proof lamp house cloth of the present invention, with good weatherability, absorbency, the plasticizing of facial mask and notacoria is non-
Often uniform, ink absorption is protruded, and each composition is that can produce cooperative effect between an organic whole, raw material, adds lamp box
The weather-proof and flexility of cloth, extends the service life of lamp house cloth product.
Embodiment 2
Weather-proof lamp house cloth production technology, the production technology of described notacoria is：It is 100 parts of Corvic, ring by parts by weight
35 parts of oxygen tree fat, 17 parts of calcium carbonate, nanometer calcium 40,35 parts of phthalic acid ester, 3 parts of epoxidized soybean oil, 6 parts of color powder and stably
4 parts of agent is mixed, wherein, whipping process is included（1）Stirring temperature of charge is increased in heating stirring, whipping process
110 degree, stir one minute；（2）Cooling and stirring, the temperature of reduction stirring material, when stirring temperature of charge is reduced to 50 degree, stops
Stirring；Using planet machine by material and into bulk；Using turbine is pounded, by material, thoroughly fully plasticizing is mixed, and obtains notacoria major ingredient；
Notacoria major ingredient is rolled, is embossed, is cooled down and batched using four rod calenders, so that notacoria is made；
The production technology of described facial mask is：It is 100 parts of Corvic, 30 parts of epoxy resin, calcium carbonate 15 by parts by weight
Part, 49 parts of nanometer calcium, 29 parts of phthalic acid ester, 35 parts of epoxidized soybean oil, 6 parts of color powder and 4 parts of stabilizer carry out mixing and stirred
Mix, wherein, whipping process is included（1）Stirring temperature of charge is increased to 110 degree in heating stirring, whipping process, one point is stirred
Clock；（2）Cooling and stirring, the temperature of reduction stirring material, when stirring temperature of charge is reduced to 50 degree, stops stirring；Using planet
Machine is by material and into bulk；Using turbine is pounded, by material, thoroughly fully plasticizing is mixed, and obtains facial mask major ingredient；Using four rod calenders
Facial mask major ingredient is rolled, is embossed, is cooled down and batched, so that facial mask is made.
Notacoria and facial mask are fitted into grid cloth both sides respectively, lamp house cloth is obtained.
Uniformly mixed between obtained lamp house cloth in the present embodiment, raw material, each composition is an organic whole, facial mask
Plasticizing with notacoria is highly uniform, and ink absorption is protruded, and with good weatherability and flexility, extends lamp house cloth product
Service life；Obtained lamp house cloth in the present embodiment, after 2 years, still with original color and luster and toughness.
Using the above-mentioned desirable embodiment according to the present invention as enlightenment, by above-mentioned description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention' entirely.The technology of this invention
Property scope is not limited to the content on specification, it is necessary to its technical scope is determined according to right.
Claims (7)
1. a kind of weather-proof lamp house cloth, described lamp house cloth by grid cloth, be respectively arranged at the notacoria and facial mask group of grid cloth both sides
Into, it is characterised in that described notacoria is made up of the raw material of following parts by weight：100 parts of Corvic, epoxy resin 20-
40 parts, 15-22 parts of calcium carbonate, nanometer calcium 36-50,20-40 parts of phthalic acid ester, 3-5 parts of epoxidized soybean oil, color powder 6-10
4-6 parts of part and stabilizer；
Described facial mask is made up of the raw material of following parts by weight：100 parts of Corvic, 30-40 parts of epoxy resin, calcium carbonate
15-22 parts, 48-53 parts of nanometer calcium, 28-55 parts of phthalic acid ester, 3-5 parts of epoxidized soybean oil, 6-10 parts of color powder and stably
4-6 parts of agent.
2. a kind of weather-proof lamp house cloth according to claim 1, it is characterised in that described film by following parts by weight raw material
Composition：100 parts of Corvic, 35 parts of epoxy resin, 17 parts of calcium carbonate, nanometer calcium 40,35 parts of phthalic acid ester, epoxy
4 parts of 3 parts of soybean oil, 6 parts of color powder and stabilizer；Described facial mask is made up of the raw material of following parts by weight：Corvic
100 parts, 30 parts of epoxy resin, 15 parts of calcium carbonate, 49 parts of nanometer calcium, 29 parts of phthalic acid ester, 35 parts of epoxidized soybean oil, color
4 parts of 6 parts of powder and stabilizer.
3. a kind of weather-proof lamp house cloth according to claim 1 or 2, it is characterised in that described epoxy resin is hexamethylene
Dimethanol epoxy resin is with hydrogenated bisphenol A epoxy resin by 1:The mixture of 1 ratio composition.
4. a kind of weather-proof lamp house cloth according to claim 1 or 2, it is characterised in that described stabilizer is organotin.
5. a kind of weather-proof lamp house cloth production technology, it is characterised in that the production technology of described notacoria is：It is polychlorostyrene by parts by weight
100 parts of vinyl, 35 parts of epoxy resin, 17 parts of calcium carbonate, nanometer calcium 40,35 parts of phthalic acid ester, epoxidized soybean oil 3
4 parts of part, 6 parts of color powder and stabilizer are mixed, and obtain notacoria major ingredient；Notacoria major ingredient is rolled, be embossed, cooled down
With batch so that be made notacoria；
The production technology of described facial mask is：It is 100 parts of Corvic, 30 parts of epoxy resin, calcium carbonate 15 by parts by weight
Part, 49 parts of nanometer calcium, 29 parts of phthalic acid ester, 35 parts of epoxidized soybean oil, 6 parts of color powder and 4 parts of stabilizer carry out mixing and stirred
Mix, obtain facial mask major ingredient；Facial mask major ingredient is rolled, is embossed, is cooled down and batched, so that facial mask is made；
Notacoria and facial mask are fitted into grid cloth both sides respectively, lamp house cloth is obtained.
6. a kind of weather-proof lamp house cloth production technology according to claim 5, it is characterised in that the life of the notacoria and facial mask
The whipping process of production. art includes：
（1）Stirring temperature of charge is increased to 110 degree in heating stirring, whipping process, stirred one minute；
（2）Cooling and stirring, the temperature of reduction stirring material, when stirring temperature of charge is reduced to 50 degree, stops stirring；And by thing
Material and into bulk.
7. a kind of weather-proof lamp house cloth production technology according to claim 5, it is characterised in that using four rod calenders difference
The notacoria major ingredient and facial mask major ingredient are rolled.