CN107057229A - A kind of PVC film gloss application sheet - Google Patents
A kind of PVC film gloss application sheet Download PDFInfo
- Publication number
- CN107057229A CN107057229A CN201710334693.1A CN201710334693A CN107057229A CN 107057229 A CN107057229 A CN 107057229A CN 201710334693 A CN201710334693 A CN 201710334693A CN 107057229 A CN107057229 A CN 107057229A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- stabilizer
- application sheet
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of PVC film gloss application sheet, according to the mass fraction, specifically it is made by following component:7 110 120 parts of type PVC resin powders, 12 parts of dispersant, 0.3 0.6 parts of calcium powder, 35 parts of stabilizer, 3 3.5 parts of processing aid, 0.5 1.3 parts of slipping agent, 0.2 0.4 parts of antitack agent, 10 12 parts of impact modifier, 0.5 0.6 parts of ultra-violet absorber.By experiment, a kind of PVC film gloss application sheet for providing of the present invention after being fit together using mode and other PVC films of hot pressing, considerably increases the luminosity of film, it is to avoid the use of UV oil, reduces the cost of enterprise's film glazing.
Description
Technical field
The invention belongs to high-molecular compound technical field, and in particular to a kind of PVC film gloss application sheet.
Background technology
PVC film when in use, generally requires to carry out glazing process, in the prior art, generally applies UV using PVC film Kun
The method of oil polish carries out the glazing of PVC film, but this method needs to buy specific glazing equipment, is only used for PVC thin
The glazing of film can cause great waste.
The content of the invention
In order to solve the above problems, the invention provides a kind of PVC film gloss application sheet, gloss application sheet is attached to PVC film
Surface, reach increase product luminosity effect, without increasing extras, greatly reduce enterprise's production cost.
The present invention is achieved through the following technical solutions:
A kind of PVC film gloss application sheet, according to the mass fraction, is specifically made by following component:7 type PVC resin powder 110-
120 parts, 1-2 parts of dispersant, 0.3-0.6 parts of calcium powder, 3-5 parts of stabilizer, 3-3.5 parts of processing aid, 0.5-1.3 parts of slipping agent,
0.2-0.4 parts of antitack agent, 10-12 parts of impact modifier, 0.5-0.6 parts of ultra-violet absorber;Its preparation method, is specially as follows
Step:
(1) the 7 type PVC resin powder, dispersant, calcium powder are first added into ten thousand horsepowers of high mixers, in T1100-105℃
First it is sufficiently mixed under low temperature 8-12 minutes, facilitates the calcium powder to be uniformly distributed in the presence of the dispersant in PVC;
(2) temperature is promoted to T2118-120 DEG C, add the processing aid, slipping agent, impact modifier, ultraviolet
After light absorbers, 10-12 minutes are incubated;
(3) continue temperature being promoted to T3125-128 DEG C, the stabilizer is added, 3-5 minutes are incubated;
(4) temperature is finally reduced to T4110-113 DEG C, the antitack agent is added, 6-10 minutes are incubated;
(5) preliminary mixed raw material are subjected to further mixing plasticizing using banbury, make its mixing evenly,
Plasticizing is more complete;
(6) use is rolled turbine and plastified again;
(7) raw material after plastifying pass through filter impurity screening;
(8) it is calendered plasticized that the raw material after filtering are delivered to calender progress;
(9) by cooling wheel by film cooling;
(10) calendered film finished product is wound by coiling machine, the mode and other PVC for delivering to make-up machine progress hot pressing are thin
Film fits together.
Further, the calcium powder, by precipitated calcium carbonate, activated Calcium carbonate, hard barium 50-60 in mass ratio:10-13:3-4
It is made after mixing.
Further, the stabilizer, by Methyltin stabiliser, organic tin stabilizer, odium stearate 100- in mass ratio
130:30-50:It is made after 7-11 mixing.
Further, the processing aid, by dibutyl ester, titanate esters 11-14 in mass ratio:It is made after 1-3 mixing.
Compared with prior art, the beneficial effects of the invention are as follows:
Using 7 type PVC resin powders, its degree of polymerization is the most suitable for producing this gloss application sheet 800 or so;Using described
Stabilizer, it is ensured that PVC does not allow degradable, achievable steady production, and the stabilizer combinations color and lustre is pure, and smell is smaller, peace
Full dependable performance, under effect same, the similar organic tin stabilizer of amount ratio of the stabilizer reduces 15-20%, further
Reduce enterprise's production cost;Using the calcium powder, the luminosity of gloss application sheet is considerably increased;Meanwhile, the preparation side that the present invention is provided
Method is also to ensure that product plays the deciding factor of glazing effect, and technique is not right, and auxiliary agent and additive can not be mixed with PVC well
Close, the luminosity of product cannot reach requirement.A kind of PVC film gloss application sheet provided by experiment, the present invention, uses hot pressing
Mode and other PVC films fit together after, considerably increase the luminosity of film, it is to avoid the use of UV oil, reduce
The cost of enterprise's film glazing.
Ultra-violet absorber:Ultra-violet absorber is a kind of light stabilizer, can absorb ultraviolet in sunlight and fluorescence light source
Line part, increases substantially the ageing resistace of product.
Embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
A kind of PVC film gloss application sheet, according to the mass fraction, is specifically made by following component:7 type PVC resin powders 110
It is part, 1 part of dispersant, 0.3 part of calcium powder, 3 parts of stabilizer, 3 parts of processing aid, 0.5 part of slipping agent, 0.2 part of antitack agent, impact-resistant modified
10 parts of agent, 0.5 part of ultra-violet absorber;Its preparation method, specially following steps:
(1) the 7 type PVC resin powder, dispersant, calcium powder are first added into ten thousand horsepowers of high mixers, in T1100 DEG C of low temperature
It is lower to be first sufficiently mixed 8 minutes, facilitate the calcium powder to be uniformly distributed in the presence of the dispersant in PVC;
(2) temperature is promoted to T2118 DEG C, add the processing aid, slipping agent, impact modifier, ultraviolet and inhale
Receive after agent, be incubated 10 minutes;
(3) continue temperature being promoted to T3125 DEG C, the stabilizer is added, 3 minutes are incubated;
(4) temperature is finally reduced to T4110 DEG C, the antitack agent is added, 6 minutes are incubated;
(5) preliminary mixed raw material are subjected to further mixing plasticizing using banbury, make its mixing evenly,
Plasticizing is more complete;
(6) use is rolled turbine and plastified again;
(7) raw material after plastifying pass through filter impurity screening;
(8) it is calendered plasticized that the raw material after filtering are delivered to calender progress;
(9) by cooling wheel by film cooling;
(10) calendered film finished product is wound by coiling machine, the mode and other PVC for delivering to make-up machine progress hot pressing are thin
Film fits together.
Further, the calcium powder, by precipitated calcium carbonate, activated Calcium carbonate, hard barium in mass ratio 50:10:Made after 3 mixing
.
Further, the stabilizer, by Methyltin stabiliser, organic tin stabilizer, odium stearate in mass ratio 100:
30:It is made after 7 mixing.
Further, the processing aid, by dibutyl ester, titanate esters in mass ratio 11:It is made after 1 mixing.
Embodiment 2
A kind of PVC film gloss application sheet, according to the mass fraction, is specifically made by following component:7 type PVC resin powders 120
Part, 2 parts of dispersant, 0.6 part of calcium powder, 5 parts of stabilizer, 3.5 parts of processing aid, 1.3 parts of slipping agent, 0.4 part of antitack agent, anti-impact change
12 parts of agent of property, 0.6 part of ultra-violet absorber;Its preparation method, specially following steps:
(1) the 7 type PVC resin powder, dispersant, calcium powder are first added into ten thousand horsepowers of high mixers, in T1105 DEG C of low temperature
It is lower to be first sufficiently mixed 12 minutes, facilitate the calcium powder to be uniformly distributed in the presence of the dispersant in PVC;
(2) temperature is promoted to T2120 DEG C, add the processing aid, slipping agent, impact modifier, ultraviolet and inhale
Receive after agent, be incubated 12 minutes;
(3) continue temperature being promoted to T3128 DEG C, the stabilizer is added, 5 minutes are incubated;
(4) temperature is finally reduced to T4113 DEG C, the antitack agent is added, 10 minutes are incubated;
(5) preliminary mixed raw material are subjected to further mixing plasticizing using banbury, make its mixing evenly,
Plasticizing is more complete;
(6) use is rolled turbine and plastified again;
(7) raw material after plastifying pass through filter impurity screening;
(8) it is calendered plasticized that the raw material after filtering are delivered to calender progress;
(9) by cooling wheel by film cooling;
(10) calendered film finished product is wound by coiling machine, the mode and other PVC for delivering to make-up machine progress hot pressing are thin
Film fits together.
Further, the calcium powder, by precipitated calcium carbonate, activated Calcium carbonate, hard barium in mass ratio 60:13:Made after 4 mixing
.
Further, the stabilizer, by Methyltin stabiliser, organic tin stabilizer, odium stearate in mass ratio 130:
50:It is made after 11 mixing.
Further, the processing aid, by dibutyl ester, titanate esters in mass ratio 14:It is made after 3 mixing.
Embodiment 3
A kind of PVC film gloss application sheet, according to the mass fraction, is specifically made by following component:7 type PVC resin powders 115
Part, 1.3 parts of dispersant, 0.5 part of calcium powder, 4 parts of stabilizer, 3.2 parts of processing aid, 0.8 part of slipping agent, 0.3 part of antitack agent, anti-impact
11 parts of modifying agent, 0.58 part of ultra-violet absorber;Its preparation method, specially following steps:
(1) the 7 type PVC resin powder, dispersant, calcium powder are first added into ten thousand horsepowers of high mixers, in T1102 DEG C of low temperature
It is lower to be first sufficiently mixed 10 minutes, facilitate the calcium powder to be uniformly distributed in the presence of the dispersant in PVC;
(2) temperature is promoted to T2119 DEG C, add the processing aid, slipping agent, impact modifier, ultraviolet and inhale
Receive after agent, be incubated 11 minutes;
(3) continue temperature being promoted to T3126 DEG C, the stabilizer is added, 4 minutes are incubated;
(4) temperature is finally reduced to T4112 DEG C, the antitack agent is added, 7 minutes are incubated;
(5) preliminary mixed raw material are subjected to further mixing plasticizing using banbury, make its mixing evenly,
Plasticizing is more complete;
(6) use is rolled turbine and plastified again;
(7) raw material after plastifying pass through filter impurity screening;
(8) it is calendered plasticized that the raw material after filtering are delivered to calender progress;
(9) by cooling wheel by film cooling;
(10) calendered film finished product is wound by coiling machine, the mode and other PVC for delivering to make-up machine progress hot pressing are thin
Film fits together.
Further, the calcium powder, by precipitated calcium carbonate, activated Calcium carbonate, hard barium in mass ratio 55:11:Made after 3 mixing
.
Further, the stabilizer, by Methyltin stabiliser, organic tin stabilizer, odium stearate in mass ratio 125:
38:It is made after 10 mixing.
Further, the processing aid, by dibutyl ester, titanate esters in mass ratio 13:It is made after 2 mixing.
Comparative example 1
This comparative example 1 compared with Example 1, without using the calcium powder, using only conventional light calcium carbonate, in addition
Method and step all same.
Comparative example 2
This comparative example 2 compared with Example 1, without using the stabilizer, using only conventional organic tin stabilizer, is removed
In addition method and step all same.
Comparative example 3
This comparative example 3 compared with Example 1, without using the processing aid, is helped using only conventional DOP as processing
Agent, method and step all same in addition.
Comparative example 4
This comparative example 4 compared with Example 1, without step (1)-(4) operation, only by all raw material one
Rise and add high-speed mixer and mixing, method and step all same in addition.
A kind of PVC film gloss application sheet provided by experiment, the present invention, uses mode and other PVC films of hot pressing
After fitting together, considerably increase the luminosity of film, it is to avoid the use of UV oil, reduce the cost of enterprise's film glazing.
And in comparative example 1-4, due to raw material or the difference of processing technology, it is impossible to process qualified gloss application sheet.
Finally it should be noted that:The preferred embodiments of the present invention are these are only, are not intended to limit the invention, although
The present invention is described in detail with reference to embodiment, for those skilled in the art, it still can be to foregoing
Technical scheme described in each embodiment is modified, or to which part technical characteristic carry out equivalent substitution, but it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements made etc. should be included in the protection of the present invention
Within the scope of.
Claims (9)
1. a kind of PVC film gloss application sheet, it is characterised in that according to the mass fraction, is specifically made by following component:7 type PVC trees
110-120 parts of cosmetics, 1-2 parts of dispersant, 0.3-0.6 parts of calcium powder, 3-5 parts of stabilizer, 3-3.5 parts of processing aid, slipping agent
0.5-1.3 parts, 0.2-0.4 parts of antitack agent, 10-12 parts of impact modifier, 0.5-0.6 parts of ultra-violet absorber;Its preparation method,
Specially following steps:
(1) the 7 type PVC resin powder, dispersant, calcium powder are first added into ten thousand horsepowers of high mixers, in T1100-105 DEG C of low temperature
It is lower to be first sufficiently mixed 8-12 minutes;
(2) temperature is promoted to T2118-120 DEG C, add the processing aid, slipping agent, impact modifier, ultraviolet radiation absorption
After agent, 10-12 minutes are incubated;
(3) continue temperature being promoted to T3125-128 DEG C, the stabilizer is added, 3-5 minutes are incubated;
(4) temperature is finally reduced to T4110-113 DEG C, the antitack agent is added, 6-10 minutes are incubated;
(5) preliminary mixed raw material are subjected to further mixing plasticizing using banbury, make its mixing evenly, plasticizing
It is more complete;
(6) use is rolled turbine and plastified again;
(7) raw material after plastifying pass through filter impurity screening;
(8) it is calendered plasticized that the raw material after filtering are delivered to calender progress;
(9) by cooling wheel by film cooling;
(10) calendered film finished product is wound by coiling machine, delivers to mode and other PVC films patch that make-up machine carries out hot pressing
It is combined.
2. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that according to the mass fraction, specifically by such as
Lower component is made:It is 7 115 parts of type PVC resin powders, 1.3 parts of dispersant, 0.5 part of calcium powder, 4 parts of stabilizer, 3.2 parts of processing aid, refreshing
0.8 part of lubrication prescription, 0.3 part of antitack agent, 11 parts of impact modifier, 0.58 part of ultra-violet absorber.
3. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that:The calcium powder, by lightweight carbonic acid
Calcium, activated Calcium carbonate, hard barium 50-60 in mass ratio:10-13:It is made after 3-4 mixing.
4. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that:The calcium powder, by lightweight carbonic acid
Calcium, activated Calcium carbonate, hard barium in mass ratio 55:11:It is made after 3 mixing.
5. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that:The stabilizer is steady by methyl tin
Determine agent, organic tin stabilizer, odium stearate 100-130 in mass ratio:30-50:It is made after 7-11 mixing.
6. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that:The stabilizer is steady by methyl tin
Determine agent, organic tin stabilizer, odium stearate in mass ratio 125:38:It is made after 10 mixing.
7. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that:The processing aid, it is pungent by two
Fat, titanate esters 11-14 in mass ratio:It is made after 1-3 mixing.
8. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that:The processing aid, it is pungent by two
Fat, titanate esters in mass ratio 13:It is made after 2 mixing.
9. a kind of PVC film gloss application sheet according to claim 1, it is characterised in that its preparation method, is specially as follows
Step:
(1) the 7 type PVC resin powder, dispersant, calcium powder are first added into ten thousand horsepowers of high mixers, in T1Under 102 DEG C of low temperature first
It is sufficiently mixed 10 minutes, facilitates the calcium powder to be uniformly distributed in the presence of the dispersant in PVC;
(2) temperature is promoted to T2119 DEG C, add the processing aid, slipping agent, impact modifier, ultra-violet absorber
Afterwards, 11 minutes are incubated;
(3) continue temperature being promoted to T3126 DEG C, the stabilizer is added, 4 minutes are incubated;
(4) temperature is finally reduced to T4112 DEG C, the antitack agent is added, 7 minutes are incubated;
(5) preliminary mixed raw material are subjected to further mixing plasticizing using banbury, make its mixing evenly, plasticizing
It is more complete;
(6) use is rolled turbine and plastified again;
(7) raw material after plastifying pass through filter impurity screening;
(8) it is calendered plasticized that the raw material after filtering are delivered to calender progress;
(9) by cooling wheel by film cooling;
(10) calendered film finished product is wound by coiling machine, delivers to mode and other PVC films patch that make-up machine carries out hot pressing
It is combined.