CN107056094A - A kind of anti-dewing glass and preparation method thereof, application - Google Patents
A kind of anti-dewing glass and preparation method thereof, application Download PDFInfo
- Publication number
- CN107056094A CN107056094A CN201710463983.6A CN201710463983A CN107056094A CN 107056094 A CN107056094 A CN 107056094A CN 201710463983 A CN201710463983 A CN 201710463983A CN 107056094 A CN107056094 A CN 107056094A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- dewing
- double glazing
- graft material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of anti-dewing glass and preparation method thereof, application, including double glazing matrix, double glazing matrix surrounding uses sealant sealing；Double glazing matrix is internally provided with one layer of glass material film, and graft material is filled between glass material film and the two side of double glazing matrix.Preparation method includes：After each component for constituting graft material is mixed, graft material is made standby；In one layer of glass material film of installed inside of double glazing matrix, and graft material is filled between the two side of glass material film and double glazing matrix；After double glazing matrix surrounding uses sealant sealing, you can.The anti-dewing glass of the embodiment of the present invention in terms of electrical equipment, have in terms of home decoration and be widely applied very much, it is correspondingly processed by three aspects to heat transfer, effectively prevent the transmission of heat, do not heat, do not dry, high degree solves the problem for perplexing everybody now for many years.
Description
Technical field
The present invention relates to glass processing preparation field, in particular to a kind of anti-dewing glass and preparation method thereof, answer
With.
Background technology
Condensation refers to when running into cryogenic object, high temperature, high humidity gas after dropping to below dew-point temperature, surface goes out
The phenomenon of globule condensation is now liquefied as, is mainly together decided on during being somebody's turn to do by internal-external temperature difference, relative humidity and dew-point temperature.
To solve condensation problem, common method uses double glazing, i.e., sealed two pieces or more than two pieces of glass edge
Together, the overall glass structure of static dry gas insulated space is formed between glass, with prominent heat-insulated, sound insulation, anti-
Solidifying frost condensation performance.Double glazing the industries such as building, traffic and refrigeration utilization than wide.
In real life application, because air humidity is big, double glazing surface temperature is big with air themperature difference, can still go out
Existing dew condensation phenomenon.Common way is：1. layer of metal conducting film is covered in outside glass using the method for electroplating film
Sideways, electroplating film is powered using transformer.After electroplating film is powered, electric current uniformly leads in the outside glass inner surface of plated film
Cross, just can reach the purpose of heating, so that outside glass surface temperature is higher than dew-point temperature, effectively to prevent condensation
Produce；2. go out to set high-power fan in glass outer surface, accelerate air flow, reach the effect except condensation.
But use aforesaid way except condensation way there are problems that it is as follows：Increase power consumption, the theory with energy-saving and emission-reduction
Run in the opposite direction；Increase the fault rate of electric equipment, cost is high；Increase noise, reduce comfortableness.
In view of this, it is special to propose the present invention.
The content of the invention
The first object of the present invention is to provide a kind of anti-dewing glass, and the anti-dewing glass passes through three to heat transfer
Individual aspect is correspondingly processed, and effectively prevents the transmission of heat, do not heat, do not dry, and high degree is solved
Perplex everybody problem for many years now, should be widely promoted application.
The second object of the present invention is the preparation method for providing above-mentioned anti-dewing glass, and preparation method is relatively easy, behaviour
Facilitate, operating condition is also relatively gentleer, front and rear step linking is close, and three wastes are produced, safety and environmental protection, belong to preferably a kind of
Preparation method.
The third object of the present invention is the further application for providing above-mentioned anti-dewing glass, and it both can be as daily general
Logical glass is used, it is also possible on electric equipment, such as glass used is just very applicable on the refrigerator showcase of in the market application
In the anti-dewing glass of the present invention, it is seen that application is than wide.
In order to realize the above-mentioned purpose of the present invention, spy uses following technical scheme：
The invention provides a kind of anti-dewing glass, including radiance the double glazing matrix below 0.05, hollow glass
Glass matrix surrounding uses sealant sealing；
In the one layer of glass material film that be internally provided with of double glazing matrix, glass material film and double glazing matrix
Two side between be filled with graft material, graft material is mainly by polyisobutene, alkali metal aluminosilicate and amorphous carbon group
Into.
In the prior art, because air humidity is big, double glazing surface temperature is big with air themperature difference, still occurs solidifying
Reveal phenomenon.Common way is：1. layer of metal conducting film is covered in the medial surface of outside glass using the method for electroplating film,
Electroplating film is powered using transformer.Electroplating film be powered after, electric current plated film outside glass inner surface uniformly through just
The purpose of heating is can reach, so that outside glass surface temperature is higher than dew-point temperature, effectively to prevent the generation of condensation；
2. go out to set high-power fan in glass outer surface, accelerate air flow, reach the effect except condensation.
But use aforesaid way except condensation way there are problems that it is as follows：Increase power consumption, the theory with energy-saving and emission-reduction
Run in the opposite direction；Increase the fault rate of electronic component, cost is high；Increase noise, reduce comfortableness.
The present invention is in order to solve the above technical problems, there is provided a kind of anti-dewing glass, to prevent condensation, seek to
The temperature in glass hot cell is improved, makes it close with air themperature, is actually to improve the thermal insulation of glass, of the invention is anti-
Condensation glass (1. radiation, 2. convection current, 3. conduction) in terms of three of heat transfer has done corresponding processing, effective to solve
The problem of condensation occurs, it is not necessary to any energy consumption, complies fully with the theory of energy-saving and emission-reduction, processing method is also fairly simple, no
Need professional's operation to can be achieved, be easier utilization and extention.
In the present invention, the main innovation for using three kinds of means to be carried out to double glazing necessarily improves anti-condensation to reach
Effect, it is necessary first to using radiance control below 0.05, many silver-layer low-radiation glass are selected typically in actual mechanical process,
Glass heat absorption in itself and heat penetration mistake can so be effectively reduced.
Preferably, the radiance of double glazing is more excellent to be controlled between 0.020-0.025 below 0.03, except this it
External radiation rate can also be 0.021,0.022,0.023 etc..
Then, the knot for being internally provided with one layer of glass material film, instead of in the past using aluminum strip of double glazing matrix
Structure, equivalent to the structure of triplex glass, the setting of glass material film can reduce the thickness of the hollow air layer of glass, so that
Cross-ventilation is effectively reduced, this is also the problem of heat transfer is solved in terms of the convection current of heat transfer.
It should be noted that the glass material film can select the film of general glass material on the market, it is not special
Other limitation, as long as using the film of glass material within protection scope of the present invention.
Finally, graft material is filled between the two side of glass material film and double glazing matrix of the present invention, this is transferred
The component for connecing material is mainly made up of polyisobutene, alkali metal aluminosilicate and amorphous carbon, the nothing that the graft material is included
Machine nonmetallic compound component through after a while and glass contact, have moieties structure and glass and produce chemical reaction
Chemical bonding is formed, so as to effectively prevent heat transfer, additionally by filling graft material, either mechanical performance, bonding
Performance, sealing property, corrosion resistance have the incomparable performance of original double glazing, that is to say, that by filling grafting material
After material, moreover it is possible to improve the corresponding mechanical performance of double glazing, be to kill two birds with one stone, conventional traditional double glazing is to use
Butyl rubber is filled in the cavity of aluminum strip and double glazing, and the present invention replaces conventional fourth using this special graft material
Base rubber is so that performance is more excellent, and secondary seal is as good as with tradition, is also to use common fluid sealant, main improvement is used
Special graft material and the membrane structure of glass material are set up, in the prior art for the anti-of this special construction of the invention
Condensation glass is also recorded without any.
Preferably, in each component of graft material, alkali metal aluminosilicate is included in 3a molecular sieves, hydration 4a molecular sieves
One or two, because molecular sieve has adsorption capacity high, the unexistent advantage of other adsorbents such as heat endurance is strong so that
Molecular sieve is widely applied, here the main strong absorptive energy using molecular sieve in itself.
In addition, the composition of graft material also includes silicyl copolymer, VTES, titanium dioxide
Silicon, calcium carbonate, dibutyl tin laurate and phenyltrimethoxysila,e.
The specific consumption of each component is, in terms of mass fraction, 20-40 parts of polyisobutene, alkali metal aluminosilicate 30-50
Part, 10-20 parts of amorphous carbon, 15-25 parts of VTES, 0-15 parts of silicyl copolymer 1, phenyl trimethoxy
12-18 parts of base silane, 10-15 parts of calcium carbonate, 5-9 parts of silica, 5-8 parts of dibutyl tin laurate.
Preferably, polyisobutene 25-35 parts, 35-45 parts of alkali metal aluminosilicate, 12-18 parts of amorphous carbon, vinyl three
17-20 parts of Ethoxysilane, 2-14 parts of silicyl copolymer 1,13-16 parts of phenyltrimethoxysila,e, calcium carbonate 11-14
Part, 6-8 parts of silica, 6-7 parts of dibutyl tin laurate.
More preferably, 30 parts of polyisobutene, 40 parts of alkali metal aluminosilicate, 16 parts of amorphous carbon, vinyl triethoxyl silicon
18 parts of alkane, 3 parts of silicyl copolymer 1,15 parts of phenyltrimethoxysila,e, 13 parts of calcium carbonate, 7 parts of silica, two bays
Sour 7 parts of dibutyl tin.
In all the components in addition to alkali metal aluminosilicate, other compositions include amorphous carbon, silica these materials
More than stability itself is relatively good, and acidproof, heat resistance is also relatively good, has so virtually also been correspondingly improved glass in itself
Mechanical performance, therefore visible applicant when selecting these materials except with anti-dewing, improving the heat resistance of glass in itself
Effect, can also the corresponding mechanical performance of reinforcing glass in itself, it is each selecting in order to take into account the acquisition of both effects
Plant material and determine that substantial amounts of practice is have passed through during addition just to be obtained, what is be related in a word in the present invention program is every
A kind of component can not lack when constituting graft material, because inventor is had found only by this by substantial amounts of creative experiment
It can be only achieved in the graft material performance that several components mutual 5 are obtained after matching somebody with somebody optimal.
In addition, in terms of raw material dosage, polyisobutene, alkali metal aluminosilicate as major ingredient may dosage than larger, its
He can play the effect of Synergistic by material, so dosage is unsuitable excessive, and if dosage is too big to be also not easy mixing
It is even, it is unfavorable in subsequent applications, performance being optimal by repeatedly groping, adds also unhelpful or may play suitable
Its anti-effect.These materials belong to usual products on the market in itself in fact, but are for the solution of the present invention key
Protection each component between it is this assemble relation mutually, can not because of these materials it is relatively common cannot come interworking composition
The scheme of invention.
In addition, in addition it is also necessary to which explanation is that the treatment measures of three kinds of anti-dewings of the invention are and deposited, indispensable,
And point without sequencing, as long as carried out according to the solution of the present invention using these three treatment measures to double glazing simultaneously
After corresponding processing, the effect of corresponding anti-dewing can be just played.
The present invention additionally provides the specific preparation of the anti-dewing glass except the concrete structure there is provided the anti-dewing glass
Method, comprises the following steps：
After each component for constituting graft material is mixed, graft material is made standby；
In one layer of glass material film of installed inside of double glazing matrix, and in glass material film and double glazing base
Graft material is filled between the two side of body；
After the double glazing matrix surrounding uses sealant sealing, you can.
The preparation method of the embodiment of the present invention is relatively easy, easy to operate, and operating condition is also relatively gentleer, front and rear step rank
Connect close, three wastes are produced, safety and environmental protection, belong to preferably a kind of preparation method, but do not represent without other preparations
Method, if be that by the present invention anti-dewing glass structure preparation method protection scope of the present invention it
It is interior.
Preferably, the temperature control of mixing is at 70-90 DEG C, and the time of mixing is preferably controlled between 1-4h.
It can cause the graft material prepared has preferably to prevent heat transfer by using suitable whipping temp, stir speed (S.S.)
Effect, and more preferable effect is played to the mechanical performance of double glazing in itself.
In addition, temperature control during filling graft material is between 120-130 DEG C.
The anti-dewing glass of the present invention has is widely applied scope very much, such as in terms of electrical equipment, in terms of home decoration, only
If the occasion required to anti-dewing, anti-dewing glass of the invention is applicable, outdoor, indoor, also without specific
The requirement of environmental condition.
Compared with prior art, beneficial effects of the present invention are：
(1) anti-condensation effect of anti-dewing glass of the invention is very good, and by using itself having, low heat conduction, height are airtight
The graft material of property so that the characteristic of double glazing in itself is greatly improved, and reduces condensation；
(2) anti-dewing treatment measures energy-conserving and environment-protective of the invention, not power consumption is substantially reduced the fault rate of electronic component,
Cost is reduced, by domestic well-known Electric company's (Hisense's appearance sound), export-oriented enterprise (victory of Guangdong three, Zhuo Jiao, Ha Shiqi), power
Prestige testing agency (Guangzhou prestige is triumphant) experiment has more preferable effect；
(3) preparation method of anti-dewing glass, preparation method is relatively easy, easy to operate, and operating condition is also relatively gentleer,
Front and rear step linking is close, and three wastes are produced, and safety and environmental protection belongs to preferably a kind of preparation method.
Embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the present invention.It is unreceipted specific in embodiment
Condition person, the condition advised according to normal condition or manufacturer is carried out.Agents useful for same or the unreceipted production firm person of instrument, be
The conventional products that can be obtained by commercially available purchase.
Embodiment 1
The preparation method of anti-dewing glass is as follows：
1) it is mixed with graft material according to following component dispensing：Polyisobutene 20kg, 3a molecular sieve 50kg, amorphous carbon
10kg, VTES 25kg, silicyl copolymer 1 0kg, phenyltrimethoxysila,e 18kg, calcium carbonate
10kg, silica 9kg, dibutyl tin laurate 5kg；
2) many silver-layer low-radiation glass are selected, its radiance is between 0.03-0.05, in the installed inside of double glazing matrix
One layer of glass material film, and between the two side of glass material film and double glazing matrix, between 120-130 DEG C of temperature control
The above-mentioned graft material prepared of filling, last surrounding sealant sealing.
Embodiment 2
The preparation method of anti-dewing glass is as follows：
1) it is mixed with graft material according to following component dispensing：Polyisobutene 40kg, 3a molecular sieve 30kg, amorphous carbon
20kg, VTES 15kg, silicyl copolymer 1 5kg, phenyltrimethoxysila,e 12kg, calcium carbonate
15kg, silica 5kg, dibutyl tin laurate 8kg；
2) many silver-layer low-radiation glass are selected, its radiance is pacified between 0.035-0.045 in the inside of double glazing matrix
If one layer of glass material film, and between the two side of glass material film and double glazing matrix, 120-130 DEG C of temperature control it
Between fill the above-mentioned graft material prepared, last surrounding sealant sealing.
Embodiment 3
The preparation method of anti-dewing glass is as follows：
1) it is mixed with graft material according to following component dispensing：Polyisobutene 25kg, 3a molecular sieve 35kg, amorphous carbon
12kg, VTES 17kg, silicyl copolymer 1 2kg, phenyltrimethoxysila,e 13kg, calcium carbonate
11kg, silica 6kg, dibutyl tin laurate 7kg, said components are put into stirred tank and mixed, temperature control 80-90
DEG C, stir 1-2h；
2) low emissivity glass is selected, its radiance is between 0.02-0.025, in the installed inside one of double glazing matrix
Layer glass material film, and between the two side of glass material film and double glazing matrix, filled out between 120-130 DEG C of temperature control
Fill the graft material stated and prepared, last surrounding sealant sealing with.
Embodiment 4
The preparation method of anti-dewing glass is as follows：
1) it is mixed with graft material according to following component dispensing：Polyisobutene 35kg, is hydrated 4a molecular sieve 45kg, without fixed
Shape carbon 18kg, VTES 20kg, silicyl copolymer 1 4kg, phenyltrimethoxysila,e 16kg, carbonic acid
Calcium 14kg, silica 8kg, dibutyl tin laurate 6kg, said components are put into stirred tank and mixed, temperature control 70-
90 DEG C, stir 3-4h；
2) low emissivity glass is selected, its radiance is between 0.021-0.022, in the installed inside one of double glazing matrix
Layer glass material film, and between the two side of glass material film and double glazing matrix, filled out between 120-130 DEG C of temperature control
Fill the graft material stated and prepared, last surrounding sealant sealing with.
Embodiment 5
The preparation method of anti-dewing glass is as follows：
1) it is mixed with graft material according to following component dispensing：Polyisobutene 30kg, hydration 4a molecular sieve, 3a molecular sieves
40kg, amorphous carbon 16kg, VTES 18kg, silicyl copolymer 1 3kg, phenyltrimethoxysila,e
15kg, calcium carbonate 13kg, silica 7kg, dibutyl tin laurate 7kg, said components are put into mix in stirred tank and stirred
Mix, 70-90 DEG C of temperature control, stir 1-2h；
2) low emissivity glass is selected, its radiance is 0.022, in one layer of glass material of installed inside of double glazing matrix
Film, and between the two side of glass material film and double glazing matrix, above-mentioned preparation is filled between 120-130 DEG C of temperature control
Good graft material, last surrounding sealant sealing.
Above-described embodiment 1-5 anti-dewing glass can be applied in terms of electrical equipment, in terms of home decoration.
Experimental example 1
By the performance progress pair of above-described embodiment 1-5 anti-dewing glass and the ordinary hollow aluminum strip glass sold on the market
Than specific performance test result is as shown in table 1 below：
The performance test results of table 1
Can be seen that the anti-dewing glass of the embodiment of the present invention from the data in upper table 1, not only anticoagulant effect is good, other machines
Tool performance is also more excellent accordingly, and the anti-dewing glass of the embodiment of the present invention has following beneficial effect：
(1) anti-condensation effect of anti-dewing glass of the invention is very good, and by using itself having, low heat conduction, height are airtight
The graft material of property so that the characteristic of double glazing in itself is greatly improved, and reduces condensation；
(2) anti-dewing treatment measures energy-conserving and environment-protective of the invention, not power consumption is substantially reduced the fault rate of electronic component,
Cost is reduced, by domestic well-known Electric company's (Hisense's appearance sound), export-oriented enterprise (victory of Guangdong three, Zhuo Jiao, Ha Shiqi), power
Prestige testing agency (Guangzhou prestige is triumphant) experiment has more preferable effect；
(3) preparation method of anti-dewing glass, preparation method is relatively easy, easy to operate, and operating condition is also relatively gentleer,
Front and rear step linking is close, and three wastes are produced, and safety and environmental protection belongs to preferably a kind of preparation method.
The present invention improves the temperature in glass hot cell to prevent anti-dewing, makes it close with air themperature, actually
Seek to improve glass thermal insulation, in terms of three of heat transfer (1. radiation, 2. convection current, 3. conduct) done from corresponding
Reason, effectively prevents the transmission of heat, does not heat, do not dry, and high degree solves the difficulty for perplexing everybody now for many years
Topic.
Although illustrate and describing the present invention with specific embodiment, but it will be appreciated that without departing substantially from the present invention's
Many other changes and modification can be made in the case of spirit and scope.It is, therefore, intended that in the following claims
Including belonging to all such changes and modifications in the scope of the invention.
Claims (10)
1. a kind of anti-dewing glass, it is characterised in that including double glazing matrix radiance below 0.05, the hollow glass
Glass matrix surrounding uses sealant sealing；
In the one layer of glass material film that be internally provided with of the double glazing matrix, the glass material film and double glazing
Graft material is filled between the two side of matrix, the graft material is main by polyisobutene, alkali metal aluminosilicate and nothing
Shape carbon composition；
Preferably, the alkali metal aluminosilicate includes one or both of 3a molecular sieves, hydration 4a molecular sieves.
2. anti-dewing glass according to claim 1, it is characterised in that the radiance of the double glazing is below 0.03；
Preferably, the radiance of the double glazing is controlled between 0.020-0.025.
3. anti-dewing glass according to claim 1, it is characterised in that the composition of the graft material also includes monosilane
Base co-polymer, VTES, silica, calcium carbonate, dibutyl tin laurate and phenyl trimethoxy silicon
Alkane.
4. anti-dewing glass according to claim 3, it is characterised in that the composition of the graft material includes：With quality
Number meter, 20-40 parts of polyisobutene, 30-50 parts of alkali metal aluminosilicate, 10-20 parts of amorphous carbon, vinyl triethoxyl silicon
15-25 parts of alkane, 0-15 parts of silicyl copolymer 1,12-18 parts of phenyltrimethoxysila,e, 10-15 parts of calcium carbonate, titanium dioxide
5-9 parts of silicon, 5-8 parts of dibutyl tin laurate.
5. anti-dewing glass according to claim 4, it is characterised in that 25-35 parts of polyisobutene, alkali metal aluminosilicate
35-45 parts, 12-18 parts of amorphous carbon, 17-20 parts of VTES, 2-14 parts of silicyl copolymer 1, phenyl
13-16 parts of trimethoxy silane, 11-14 parts of calcium carbonate, 6-8 parts of silica, 6-7 parts of dibutyl tin laurate.
6. anti-dewing glass according to claim 5, it is characterised in that 30 parts of polyisobutene, alkali metal aluminosilicate 40
Part, 16 parts of amorphous carbon, 18 parts of VTES, 3 parts of silicyl copolymer 1, phenyltrimethoxysila,e 15
Part, 13 parts of calcium carbonate, 7 parts of silica, 7 parts of dibutyl tin laurate.
7. the preparation method of the anti-dewing glass described in claim any one of 1-6, it is characterised in that main to include following step
Suddenly：
After each component for constituting graft material is mixed, graft material is made standby；
In one layer of glass material film of installed inside of double glazing matrix, and in glass material film and double glazing matrix
Graft material is filled between two side；
After the double glazing matrix surrounding uses sealant sealing, you can.
8. the preparation method of anti-dewing glass according to claim 7, it is characterised in that the temperature control of mixing exists
70-90℃；
Preferably, the time control of mixing is in 1-4h.
9. the preparation method of anti-dewing glass according to claim 7, it is characterised in that temperature during filling graft material
Control is between 120-130 DEG C.
10. the anti-dewing glass described in claim any one of 1-6 is in terms of electrical equipment, the application in terms of home decoration.