CN107056028A - A kind of anti-dazzle 3D glass and preparation method thereof - Google Patents
A kind of anti-dazzle 3D glass and preparation method thereof Download PDFInfo
- Publication number
- CN107056028A CN107056028A CN201710339475.7A CN201710339475A CN107056028A CN 107056028 A CN107056028 A CN 107056028A CN 201710339475 A CN201710339475 A CN 201710339475A CN 107056028 A CN107056028 A CN 107056028A
- Authority
- CN
- China
- Prior art keywords
- glass
- dazzle
- hot
- preparation
- hot bending
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of anti-dazzle 3D glass, it comprises the following steps:Step 1, one glass bending equipment of offer, it at least includes hot bending fixture, and the hot bending fixture includes upper die and lower die, and the upper mould and/or the surface of lower mould or regional area are provided with coarse structure;Step 2, one flat glass of offer;Step 3, flat glass is placed in hot bending fixture carried out by hot bending equipment it is hot-forming;Step 4, will be hot-forming after glass carry out acid etching processing, produce the 3D glass of anti-dazzle.The preparation method of this anti-dazzle 3D glass, contact surface on hot bending fixture with glass is made coarse structure by it, and then the coarse structure is transferred to glass surface by extruding during hot bending, makes glass surface formation coarse structure, acid etching again, so as to produce anti-dazzle 3D glass;The making of anti-dazzle and 3D glass is merged in a process, cost of manufacture is greatly reduced, simplifies technological process, improve product yield.
Description
Technical field
The present invention relates to 3D glass technologies field, a kind of more particularly to anti-dazzle 3D glass and preparation method thereof.
Background technology
3D bend glasses rely on its excellent performance, can not only improve smart terminal product novel appearance, can be with
Outstanding touch-control feel is brought, 3D bend glasses have greatly the gesture as smart terminal product standard configuration.Current anti-dazzle technology is in 2D
Surface is made by way of etching or spraying, and 3D bend glasses are due to its special tectonic, and traditional anti-dazzle technique is bent in 3D
Surface glass surface runs into many difficult points, such as 1. first does anti-dazzle(AG)Hot bending, i.e., directly use glare proof glass hot bending, then glass again
Glass surface roughness can be by different degrees of infringement;2. being AG after first hot bending, there is the heat-bending glass back side in AG processing procedures difficult
The problem of to protect.Etc..
The content of the invention
The technical problems to be solved by the invention there is provided a kind of anti-dazzle 3D glass and preparation method thereof, and it is by hot bending
Coarse structure is made with the contact surface of glass on fixture, then the coarse structure is transferred to by extruding during hot bending
Glass surface, makes glass surface formation micro-structural, then acid etching, so as to produce anti-dazzle 3D glass;By anti-dazzle and 3D glass
The making fusion of glass ensure that the uniformity of bending area and the anti-dazzle light effect in other regions, drop significantly in a process
Low cost of manufacture, simplifies technological process, improves product yield.
The technical problems to be solved by the invention are achieved by the following technical programs:
A kind of preparation method of anti-dazzle 3D glass, it comprises the following steps:
Step 1, one glass bending equipment of offer, it at least includes hot bending fixture, and the hot bending fixture includes upper die and lower die, institute
State mould and/or the surface of lower mould or regional area is provided with coarse structure;
Step 2, one flat glass of offer;
Step 3, flat glass is placed in hot bending fixture and carried out by hot bending equipment hot-forming, obtaining surface has micro-structural
3D glass;
Step 4, will be hot-forming after glass carry out acid etching processing, produce the 3D glass of anti-dazzle.
The acid etching carries out carrying out acid etching to the 3D glass after hot bending using fluorine-containing solution, and acid etching depth is preferably high
In 5 μm.The acid etching processing not only acts as the effect gently changed to 3D glass surface micro-structurals, corrects AG specifications, enters simultaneously
The effect of row surface passivation reinforcing glass intensity.When implementing, only the micro-structural face of 3D glass can be entered according to actual needs
Row acid etching, can also carry out acid etching to the two-sided of 3D glass.The present invention handles fluorine-containing solution used not to acid etching
Do specific restriction, commercially available fluorine-containing solution.
Improved as a kind of the of preparation method of the anti-dazzle 3D glass of the present invention, the roughness of the coarse structure is
0.02~2μm。
To be improved as a kind of the of preparation method of the anti-dazzle 3D glass of the present invention, the hot-forming temperature is 500 ~
900℃。
Improved as a kind of the of preparation method of the anti-dazzle 3D glass of the present invention, the hot bending clamp material be graphite or
Ceramics.
Improved as a kind of the of preparation method of the anti-dazzle 3D glass of the present invention, it is described hot-forming under protective atmosphere
Carry out.
Improved as a kind of the of preparation method of the anti-dazzle 3D glass of the present invention, the protective gas is nitrogen or argon
Gas.
A kind of anti-dazzle 3D glass, it is made by any above-mentioned preparation method.
The present invention has the advantages that:This merges the making of anti-dazzle and 3D glass in a process, Neng Goubao
The uniformity of bending area and the anti-dazzle light effect in other regions is demonstrate,proved, cost of manufacture is greatly reduced, simplifies technological process, carry
High product yield;The 3D glass of local anti-dazzle or overall anti-dazzle light effect can be produced according to actual needs, meet different
User's request, further expands its application and improves competitiveness.3D glass surfaces after hot-forming have micro-structural,
But micro-structural corner angle are obvious, be excessively sharp, it is impossible to realize anti-dazzle light effect, and surface has micro-crack generation to have a strong impact on glass
Intensity, and the present invention is entered the 3D glass with micro-structural using the hot-forming synergy both with acid etching of micro-structural
The processing of one step etching, makes its tending towards stability of microstructure area, while being modified AG specifications, also glass surface is passivated
Play a part of reinforcing glass intensity.
Brief description of the drawings
Fig. 1 is the structural representation of the anti-dazzle 3D glass of the embodiment of the present invention 1;
Fig. 2 is the structural representation of the anti-dazzle 3D glass of the embodiment of the present invention 2;
Fig. 3 is the structural representation of the anti-dazzle 3D glass of the embodiment of the present invention 3;
Fig. 4 is the structural representation of the anti-dazzle 3D glass of the embodiment of the present invention 4.
Embodiment
With reference to embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention,
It is not limitation of the invention.
Embodiment 1
As shown in figure 1, a kind of anti-dazzle 3D glass 1, its upper surface has the micro-structural 2 of anti-dazzle.
Specifically, the preparation method of the present embodiment anti-dazzle 3D glass 1, it comprises the following steps:
Step 11, one glass bending equipment of offer.The hot bending fixture of the hot bending equipment is improved, in the upper of hot bending fixture
The lower surface of mould(With the contact surface of flat glass upper surface)Produce the coarse structure of about 0.05 μm of roughness;
Step 12, one flat glass of offer;It can be 2D or 2.5D flat glass;
Step 13, the flat glass of step 12 is placed in hot bending fixture by hot bending equipment, the hot pressing under nitrogen protective gas
In the environment of about 600 DEG C of temperature, progress is hot-forming, and obtaining surface has the 3D glass of micro-structural;
Step 14, the glass of step 13 by fluorine-containing solution is subjected to acid etching processing, the main function of fluorine-containing solution processing is
The micro-crack passivation that hot pressing is produced, corrects AG specifications, surface micro-structure is gently changed, and the one side control of acid etching processing exists
5 μm, produce anti-dazzle 3D glass 1.
Embodiment 2
As shown in Fig. 2 a kind of anti-dazzle 3D glass 1, its lower surface has the micro-structural 2 of anti-dazzle.
Specifically, the preparation method of the present embodiment anti-dazzle 3D glass 1, it comprises the following steps:
Step 21, one glass bending equipment of offer.The hot bending fixture of the hot bending equipment is improved, under hot bending fixture
The upper surface of mould(With the contact surface of flat glass lower surface)Produce the coarse structure of about 0.1 μm of roughness;
Step 22, one flat glass of offer;It can be 2D or 2.5D flat glass;
Step 23, the flat glass of step 22 is placed in hot bending fixture by hot bending equipment, the hot pressing under argon gas protective gas
In the environment of about 700 DEG C of temperature, progress is hot-forming, and obtaining surface has the 3D glass of micro-structural;
Step 24, the glass of step 23 by fluorine-containing solution is subjected to acid etching processing, the main function of fluorine-containing solution processing is
The micro-crack passivation that hot pressing is produced, corrects AG specifications, surface micro-structure is gently changed, and the one side control of acid etching processing exists
5 μm, produce anti-dazzle 3D glass 1.
Embodiment 3
As shown in figure 3, a kind of anti-dazzle 3D glass 1, its pair of surface has the micro-structural 2 of anti-dazzle.
Specifically, the preparation method of the present embodiment anti-dazzle 3D glass 1, it comprises the following steps:
Step 31, one glass bending equipment of offer.The hot bending fixture of the hot bending equipment is improved, under hot bending fixture
The upper surface of mould(With the contact surface of flat glass lower surface)Produce the coarse structure of about 0.15 μm of roughness;In hot bending fixture
Lower mould upper surface(With the contact surface of flat glass lower surface)Produce the coarse structure of about 0.1 μm of roughness;
Step 32, one flat glass of offer;It can be 2D or 2.5D flat glass;
Step 33, the flat glass of step 32 is placed in hot bending fixture by hot bending equipment, the hot pressing under argon gas protective gas
In the environment of about 800 DEG C of temperature, progress is hot-forming, and obtaining surface has the 3D glass of micro-structural;
Step 34, the glass of step 33 by fluorine-containing solution is subjected to acid etching processing, the main function of fluorine-containing solution processing is
The micro-crack passivation that hot pressing is produced, corrects AG specifications, surface micro-structure is gently changed, and the one side control of acid etching processing exists
8 μm, produce anti-dazzle 3D glass 1.
Embodiment 4
As shown in figure 4, a kind of anti-dazzle 3D glass 1, its surface locally has the micro-structural 2 of anti-dazzle.
Specifically, the preparation method of the present embodiment anti-dazzle 3D glass 1, it comprises the following steps:
Step 41, one glass bending equipment of offer.The hot bending fixture of the hot bending equipment is improved, under hot bending fixture
Produce the coarse structure of about 0.2 μm of roughness in the part of horizontal face of the upper surface of mould;
Step 42, one flat glass of offer;It can be 2D or 2.5D flat glass;
Step 43, the flat glass of step 42 is placed in hot bending fixture by hot bending equipment, the hot pressing under argon gas protective gas
In the environment of about 900 DEG C of temperature, progress is hot-forming, and obtaining surface has the 3D glass of micro-structural;
Step 44, the glass of step 43 by fluorine-containing solution is subjected to acid etching processing, the main function of fluorine-containing solution processing is
The micro-crack passivation that hot pressing is produced, corrects AG specifications, surface micro-structure is gently changed, and the one side control of acid etching processing exists
10 μm, produce anti-dazzle 3D glass 1.
It should be noted that amendment AG specifications are mainly so that coarse structure reaches preferable requirement:Glossiness:15~
140GU;Mist degree:1~30%;Surface roughness Ra:0.02~1μm.
Embodiment described above only expresses embodiments of the present invention, and it describes more specific and detailed, but can not
Therefore the limitation to the scope of the claims of the present invention is interpreted as, as long as the skill obtained using the form of equivalent substitution or equivalent transformation
Art scheme, all should fall within the scope and spirit of the invention.
Claims (7)
1. a kind of preparation method of anti-dazzle 3D glass, it comprises the following steps:
Step 1, one glass bending equipment of offer, it at least includes hot bending fixture, and the hot bending fixture includes upper die and lower die, institute
State mould and/or the surface of lower mould or regional area is provided with coarse structure;
Step 2, one flat glass of offer;
Step 3, flat glass is placed in hot bending fixture and carried out by hot bending equipment hot-forming, obtaining surface has micro-structural
3D glass;
Step 4, will be hot-forming after glass carry out acid etching processing, produce the 3D glass of anti-dazzle.
2. the preparation method of anti-dazzle 3D glass according to claim 1, it is characterised in that the coarse structure it is coarse
Spend for 0.02 ~ 2 μm.
3. the preparation method of anti-dazzle 3D glass according to claim 2, it is characterised in that the hot-forming temperature
For 500 ~ 900 DEG C.
4. the preparation method of anti-dazzle 3D glass according to claim 3, it is characterised in that the hot bending clamp material is
Graphite or ceramics.
5. the preparation method of anti-dazzle 3D glass according to claim 3, it is characterised in that described hot-forming in protection
Carried out under atmosphere.
6. the preparation method of anti-dazzle 3D glass according to claim 6, it is characterised in that the protective gas is nitrogen
Or argon gas.
7. a kind of anti-dazzle 3D glass, it is characterised in that be made by the preparation method as described in claim 1 to 6 is any.