CN107055639A - A kind of water stabilization material and preparation method and application method - Google Patents
A kind of water stabilization material and preparation method and application method Download PDFInfo
- Publication number
- CN107055639A CN107055639A CN201710220443.5A CN201710220443A CN107055639A CN 107055639 A CN107055639 A CN 107055639A CN 201710220443 A CN201710220443 A CN 201710220443A CN 107055639 A CN107055639 A CN 107055639A
- Authority
- CN
- China
- Prior art keywords
- water
- water stabilization
- stabilization material
- additive
- kinds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water stabilization material and preparation method and application method, belong to field of water quality purification, it is made up of the raw material of following masses percentage composition, additive 4% -15%, the accounting of Brown crake is 85%~96%, and the additive includes 2 kinds or 3 kinds in diatomite, flyash and attapulgite.Of the invention all to use natural material, preparation technology is simple, and using effect is good, and service life is long, will not be because long-time is used and fails, without changing water stabilization material.Operational management is simple, without energy consumption, energy-conserving and environment-protective.The present invention has following beneficial effect：1. convenient material drawing, raw material are cheap and easily-available, manufacture craft is simple, is adapted to large-scale production.2. prepared by water stabilization excellent material performance, easily preserve transport, be easy to onsite application, with very strong promotional value.The purification of water quality for being particularly suitable for use in storm detention tank and reclaimed water storage pond is kept.
Description
Technical field
The invention belongs to field of water quality purification, and in particular to a kind of water stabilization material and preparation method and application method.
Background technology
In recent years, the popularization and construction with country to sponge city, has built increasing storm detention tank with
Water storage pond, but pool inner water matter deteriorates seriously, seriously constrains the reuse of water.
Conventional solution is to set up water treatment system at present, but setting up water treatment system needs increase to take up an area, the energy
Consumption is high, management operating trouble.
Current water quality purification material is mainly used as sorbing material or bio-carrier, be mainly used in water treatment building or
It is continuous the need for having to add water-purifying material in natural water, but all can not as cistern long-lasting aqueous stabilizing material.
The content of the invention
, can not be as cistern to solve existing water quality purification material it is an object of the present invention to provide a kind of water stabilization material
Long-lasting aqueous stabilizing material the problem of.
It is a further object to provide a kind of preparation method of water stabilization material.
It is also another object of the present invention to provide a kind of application method of water stabilization material.
The technical scheme is that：A kind of water stabilization material, is made up of the raw material of following masses percentage composition, addition
Agent 4% -15%, the accounting of Brown crake is 85%~96%, and the additive includes 2 kinds in diatomite, flyash and attapulgite
Or 3 kinds.
It is preferred that, as a kind of a kind of scheme of water stabilization material, additive is diatomite, flyash and attapulgite
In 2 kinds, the weight/mass percentage composition of every kind of additive is 2%~5%.
It is preferred that, as a kind of another scheme of water stabilization material, additive is diatomite, flyash and concave convex rod
Soil, its mass ratio is 1:1:1.
A kind of preparation method of water stabilization material, comprises the following steps：
（1）Brown crake powder and additive agent powder are sieved, be uniformly mixed powder；
（2）Uniform mixed powder is mixed with more than 95 DEG C hot water stirs, wherein the mass ratio of uniform mixed powder and hot water
For 5:1~20:1；Then roll repeatedly 10~60 minutes, the high viscosity water stabilization material using Brown crake as main material is made.
It is preferred that, the purity of Brown crake reaches 90%.
A kind of application method of above-mentioned water stabilization material, scheme is that water stabilization material is coated in cistern
Wall, thickness is 2~15mm.
The application method of above-mentioned water stabilization material, another scheme is to make growth and a width of 1.5~2m with bamboo wood
Matrix substrate, matrix substrate both sides applied thickness be 2~15mm water stabilization material, water stabilization plate is prepared into, finally by water
Matter steadying plate is hung in cistern.
It is preferred that, the surface area of water quality stabilizing material and retaining pool volume in the application method of above-mentioned water stabilization material
Ratio be 0.5:1~5:1.
Of the invention all to use natural material, preparation technology is simple, and using effect is good, and service life is long, will not be because of length
Time uses and failed, without changing water stabilization material.Operational management is simple, without energy consumption, energy-conserving and environment-protective.
The present invention has following beneficial effect：1. convenient material drawing, raw material are cheap and easily-available, manufacture craft is simple, is adapted to scale
Metaplasia is produced.2. prepared by water stabilization excellent material performance, easily preserve transport, be easy to onsite application, with very strong popularization
Value.The purification of water quality for being particularly suitable for use in storm detention tank and reclaimed water storage pond is kept.
Embodiment
The following examples can further illustrate the present invention, but do not limit the invention in any way.
In use, water stabilization material can be applied directly to cistern inwall；Can also bamboo wood be fabricated to matrix substrate, will
Water stabilization material is coated on matrix substrate both sides and water stabilization plate is made, then water stabilization plate is hung in cistern.
Embodiment 1
Dry powdery Brown crake 96kg, diatomite 2kg, flyash 2kg are taken, is well mixed, sieving adds 97 DEG C of hot water 20kg,
Roll repeatedly 60 minutes, be prepared into water stabilization material.Water stabilization material is coated on 2 cubic metres of storm detention tank inwalls,
Applied thickness 5mm, 2 square metres of surface covered.
Embodiment 2
Dry powdery Brown crake 93kg, diatomite 5kg, concave convex rod 2kg are taken, is well mixed, sieving adds 95 DEG C of hot water 5kg, instead
Roll again 10 minutes, be prepared into water stabilization material.1.5m × 1.5m matrix substrate is fabricated to using bamboo wood, by water stabilization material
Material is coated on matrix substrate both sides, and applied thickness 8mm obtains water stabilization plate.3 water are hung in 8m cubic metres of storm detention tanks
Matter steadying plate.
Embodiment 3
Dry powdery Brown crake 90kg, concave convex rod 5kg, flyash 5kg are taken, is well mixed, sieving adds 98 DEG C of hot water 18kg,
Roll repeatedly 20 minutes, be prepared into water stabilization material.Water stabilization material is coated on 2 cubic metres of storm detention tank inwalls,
Applied thickness 10mm, 1.8 square metres of surface covered.
Embodiment 4
Dry powdery Brown crake 85kg, diatomite 5kg, concave convex rod 5kg, flyash 5kg are taken, is well mixed, sieving adds 96 DEG C
Hot water 15kg, rolls 30 minutes, is prepared into water stabilization material repeatedly.2m × 2m matrix substrate is fabricated to using bamboo wood, by water
Matter stabilizing material is coated on matrix substrate both sides, and applied thickness 9mm obtains water stabilization plate.In 15m cubic metres of storm detention tanks
Hang 4 water stabilization plates.
《Brown crake is the performance evaluation of the water stabilization material of main material》
Below by the water quality monitoring to 1~embodiment of embodiment 4, the performance to water stabilization material is evaluated, monitoring knot
Fruit is as shown in table 1.
Claims (9)
1. a kind of water stabilization material, it is characterised in that：It is made up of the raw material of following masses percentage composition, and additive 4%-
15%, the accounting of Brown crake is 85%~96%, and the additive includes 2 kinds or 3 kinds in diatomite, flyash and attapulgite.
2. a kind of water stabilization material according to claim 1, it is characterised in that：Additive be diatomite, flyash and
2 kinds in attapulgite, the weight/mass percentage composition of every kind of additive is 2%~5%.
3. a kind of water stabilization material according to claim 1, it is characterised in that：Additive be diatomite, flyash and
Attapulgite, its mass ratio is 1:1:1.
4. a kind of preparation method of water stabilization material, it is characterised in that comprise the following steps：
（1）Brown crake powder and additive agent powder are sieved, be uniformly mixed powder；
（2）Uniform mixed powder is mixed with more than 95 DEG C hot water stirs, wherein the mass ratio of uniform mixed powder and hot water
For 5:1~20:1；Then roll repeatedly 10~60 minutes, the high viscosity water stabilization material using Brown crake as main material is made.
5. the preparation method of water stabilization material according to claim 4, it is characterised in that：The purity of Brown crake reaches
90%。
6. the application method of the water stabilization material in claim 1-3 described in any one, it is characterised in that：By water stabilization
Material is coated on cistern inwall, and thickness is 2~15mm.
7. the application method of the water stabilization material in claim 1-3 described in any one, it is characterised in that：Made with bamboo wood
Growth and a width of 1.5~2m matrix substrate, matrix substrate both sides applied thickness is 2~15mm water stabilization material, is prepared into water
Matter steadying plate, finally hangs on water stabilization plate in cistern.
8. water stabilization materials'use method as claimed in claim 6, it is characterised in that：The surface area of water stabilization material with
The ratio of retaining pool volume is 0.5:1~5:1.
9. water stabilization materials'use method as claimed in claim 7, it is characterised in that：The surface area of water stabilization material with
The ratio of retaining pool volume is 0.5:1~5:1.