CN107055595A - A kind of preparation method of lithium cell cathode material - Google Patents
A kind of preparation method of lithium cell cathode material Download PDFInfo
- Publication number
- CN107055595A CN107055595A CN201710250504.2A CN201710250504A CN107055595A CN 107055595 A CN107055595 A CN 107055595A CN 201710250504 A CN201710250504 A CN 201710250504A CN 107055595 A CN107055595 A CN 107055595A
- Authority
- CN
- China
- Prior art keywords
- tio
- lithium
- preparation
- cathode material
- cell cathode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of lithium cell cathode material, comprises the following steps:S1, the K by 5 10g2TiO3Mixed with 150 200ml 0.1mol/L acid solutions, carry out ion exchange, filtered after 23 hours, obtain compound H2TiO3;S2, by 3 4g H2TiO3It is placed in 0.2mol/L lithium salt solution, stirs;S3, the reactant after being sufficiently mixed is placed in water heating kettle, after being put into Muffle furnace 110 120 DEG C of insulations 10 12 hours, suction filtration, washing obtain Li4Ti5O12.The present invention obtains bigger serface Li4Ti5O12Specific surface area is big, as the lithium excellent electrical property of negative material, with environmental protection, the simple advantage of technique.
Description
Technical field
The present invention relates to the technical field of battery, more particularly to a kind of lithium cell cathode material.
Background technology
Lithium titanate is widely used in new-energy automobile, electric motorcycle as the negative material of lithium ion battery of new generation
Car and require high security, high stability and macrocyclic application field.The lithium titanate of the loose structure of high-specific surface area, favorably
In the contact area for improving electrode and electrolyte, so as to lift the performance of lithium titanate.Existing lithium titanate preparation technology, high temperature is anti-
Product grain should be descended easily to grow up, pore structure is easily caved in, lithium titanate specific surface area can be caused very small.
The content of the invention
It is an object of the invention to provide a kind of lithium cell cathode material, solve one in above-mentioned prior art problem or
It is multiple.
The present invention provides a kind of preparation method of lithium cell cathode material, comprises the following steps:
S1, the K by 5-10g2TiO3Mixed with 150-200ml 0.1mol/L acid solutions, carry out ion exchange, 2-3 hours
After filter, obtain compound H2TiO3;
S2, by 3-4g H2TiO3It is placed in 0.2mol/L lithium salt solution, stirs;
S3, the reactant after being sufficiently mixed is placed in water heating kettle, is put into 110-120 DEG C of insulation 10-12 in Muffle furnace small
Shi Hou, suction filtration, washing, obtains Li4Ti5O12。
In some embodiments, acid solution is the one or more in hydrochloric acid or nitric acid.
In some embodiments, lithium salt solution is the one or more in lithium hydroxide or lithium nitrate.
Embodiment
Following case study on implementation, the present invention is described in more detail.
Case study on implementation 1:
A1, the K by 5g2TiO3Mixed with 150ml 0.1mol/L hydrochloric acid solutions, carry out ion exchange, filtered after 2 hours,
Obtain compound H2TiO3;
A2, by 3g H2TiO3It is placed in 0.2mol/L lithium hydroxide salting liquid, stirs;
A3, the reactant after being sufficiently mixed is placed in water heating kettle, after being put into Muffle furnace 110 DEG C of insulations 12 hours, taken out
Filter, washing, obtain Li4Ti5O12
Case study on implementation 2:
B1, the K by 10g2TiO3Mixed with 200ml 0.1mol/L salpeter solutions, carry out ion exchange, mistake after 3 hours
Filter, obtains compound H2TiO3;
B2, by 4g H2TiO3It is placed in 0.2mol/L nitric acid lithium salt solution, stirs;
B3, the reactant after being sufficiently mixed is placed in water heating kettle, after being put into Muffle furnace 120 DEG C of insulations 10 hours, taken out
Filter, washing, obtain Li4Ti5O12
Case study on implementation 3:
C1, by 8 K2TiO3Mixed with 180ml 0.1mol/L hydrochloric acid solutions, carry out ion exchange, mistake after 2.5 hours
Filter, obtains compound H2TiO3;
C2, by 3.5g H2TiO3It is placed in 0.2mol/L lithium hydroxide salting liquid, stirs;
C3, the reactant after being sufficiently mixed is placed in water heating kettle, after being put into Muffle furnace 115 DEG C of insulations 11 hours, taken out
Filter, washing, obtain Li4Ti5O12
Following table is that case study on implementation obtains Li4Ti5O12Physical parameter.
Batch | Product/specific surface area m2/g |
Case study on implementation 1 | 140 |
Case study on implementation 2 | 150 |
Case study on implementation 3 | 145 |
The embodiment that the present invention is provided, the present invention obtains bigger serface Li4Ti5O12Specific surface area is big, as negative
The lithium excellent electrical property of pole material, with environmental protection, the simple advantage of technique.
Presented above is only the preferred embodiment of the present invention, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, various modifications and improvements can be made, these also should be regarded as the protection model of invention
Within enclosing.
Claims (3)
1. a kind of preparation method of lithium cell cathode material, it is characterised in that comprise the following steps:
S1, the K by 5-10g2TiO3Mixed with 150-200ml 0.1mol/L acid solutions, carry out ion exchange, mistake after 2-3 hours
Filter, obtains compound H2TiO3;
S2, by 3-4g H2TiO3It is placed in 0.2mol/L lithium salt solution, stirs;
S3, the reactant after being sufficiently mixed is placed in water heating kettle, after being put into Muffle furnace 110-120 DEG C of insulation 10-12 hours,
Suction filtration, washing, obtain Li4Ti5O12。
2. a kind of preparation method of lithium cell cathode material according to claim 1, it is characterised in that the acid solution is
One or more in hydrochloric acid or nitric acid.
3. a kind of preparation method of lithium cell cathode material according to claim 1, it is characterised in that the lithium salt solution
For the one or more in lithium hydroxide or lithium nitrate.