CN107053409A - A kind of Rattan does old processing method - Google Patents
A kind of Rattan does old processing method Download PDFInfo
- Publication number
- CN107053409A CN107053409A CN201710226008.3A CN201710226008A CN107053409A CN 107053409 A CN107053409 A CN 107053409A CN 201710226008 A CN201710226008 A CN 201710226008A CN 107053409 A CN107053409 A CN 107053409A
- Authority
- CN
- China
- Prior art keywords
- parts
- rattan
- temperature
- takes out
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to rattan processing technique field, especially a kind of Rattan does old processing method, and specific method is as follows：（1）Boiling, drying, immersion and fermentation process；（2）Surface size, baking, wetting, fermentation and drying process；The present invention is first through boiling, drying, immersion and fermentation process, it is not only able to effectively eliminate the impurity on Rattan surface, strengthen its surface gloss, and can effectively suppress the growth of Rattan harmful bacteria, improve its antibacterial ability, strengthen its anticorrosive mildewproof ability, effectively extend the service life of its knitting；Then through surface size, baking, wetting, fermentation and drying process, the toughness of effectively enhancing Rattan is not only able to, its fragility is reduced, effectively improve its Resisting fractre ability, and cause Rattan color and luster thick and heavy uniform, fragrance is pure and fresh persistently, lifts it and uses quality.
Description
Technical field
The invention belongs to rattan processing technique field, especially a kind of Rattan does old processing method.
Background technology
Rattan, Palmae vine plant, rattan is the ideal material for making furniture and handicraft, strong but pliable in texture, figure
Extremely long, crust is bright in luster, and feel is smooth, and elasticity is splendid, seemingly slights rather than slights, and also commonly uses the days such as this establishment rattan chair, rattan case and commonly uses
Tool；Simultaneously as rattan feel is smooth, the characteristics of elastic splendid, therefore it is very suitable for for being woven into variously-shaped technique
Product or other more practical daily necessitiess；But its to do old handling process relatively difficult, deal with improperly not only so that it does old
Color and luster is uneven, and is easily caused the cracking of Rattan, is even broken, and smell is pungent after its processing in addition；Therefore invent a kind of
The old processing method of doing of Rattan is current urgent problem to be solved.
The content of the invention
In view of the above-mentioned problems, the present invention is intended to provide a kind of Rattan does old processing method.
The present invention is achieved through the following technical solutions：
A kind of Rattan does old processing method, and specific method is as follows：
（1）Boiling, drying, immersion and fermentation process
Rattan is inserted into constant temperature 18 ~ 20min of boiling in the Vacuum cooker that temperature is 125 ~ 127 DEG C, with 5.2 ~ 5.4 DEG C/min
Heating rate be warming up to 166 ~ 168 DEG C of constant temperature 34 ~ 36min of boiling, take out, frequency be 330 ~ 340MHz under conditions of microwave
It is 17% ~ 18% to dry to moisture, is immersed in 350 ~ 360min of immersion in soak, takes out, and it is 40 ~ 41 DEG C to insert temperature
26 ~ 27h of fermentation in fermenting case, takes out, and is cleaned 2 ~ 3 times for 45 ~ 47 DEG C of water with temperature；
Described treatment fluid, is made up of the raw material of following parts by weight：3.2 ~ 3.4 parts of metasilicate pentahydrate sodium, tertiary sodium phosphate 2.1 ~ 2.3
Part, 1.6 ~ 1.8 parts of Sodium acetate trihydrate, 2.7 ~ 2.9 parts of Sodium Polyacrylate, 0.56 ~ 0.58 part of Cortex Acanthopancis extract, black cohosh root are extracted
0.71 ~ 0.73 part of thing, 94 ~ 96 parts of water；
（2）Surface size, baking, wetting, fermentation and drying process
Will be through step（1）Rattan after processing, which is immersed in smearing slurry, makes its surface be completely covered by smearing slurry, takes out, inserts temperature
Spend constant temperature in the baking box for 58 ~ 59 DEG C and toast 590 ~ 600s, 93 ~ 94 DEG C are warming up to 2.3 ~ 2.4 DEG C/min heating rate
Constant temperature toasts 470 ~ 480s, and being cooled to 65 ~ 66 DEG C of constant temperature with 3.4 ~ 3.5 DEG C/min rate of temperature fall toasts 360 ~ 370s, takes out,
It is that constant temperature soaks 95 ~ 100min in 4 ~ 5 DEG C of water to be immersed in temperature, takes out, washes away the smearing slurry on surface, insert temperature for 40 ~
26 ~ 27h of fermentation in 41 DEG C of fermenting case, takes out, and microwave drying to moisture is under conditions of frequency is 450 ~ 460MHz
10%~11%；
Described smearing slurry, is made up of the raw material of following parts by weight：85 ~ 87 parts of bentonite, 34 ~ 36 parts of fire clay, gamboge 2.6
~ 2.8 parts, 1.5 ~ 1.7 parts of dragon's blood, 3.1 ~ 3.3 parts of asarum, 2.3 ~ 2.5 parts of, Bi Collettiis, 4.3 ~ 4.5 parts of the root of three-nerved spicebush, loguat leaf 3.1 ~ 3.3
Part, 5.7 ~ 5.9 parts of fresh Heliotropium arborescens petal, 155 ~ 160 parts of water.
It is used as the further scheme of invention：Step（2）The preparation method of described smearing slurry, specifically includes following steps：
A. asarum, Bi Collettiis, the root of three-nerved spicebush and loguat leaf are put into rotating speed to crush 13 ~ 14min in 1300 ~ 1400r/min pulverizer,
Take out, be boiled by fire in input water, slow fire 15 ~ 17min of infusion adds gamboge and the dragon's blood for being crushed to 130 ~ 140 mesh, continues text
Fiery 43 ~ 45min of infusion is simultaneously constantly stirred with rotating speed for 110 ~ 120r/min agitator, and room temperature natural cooling obtains Chinese medicine
Infusion liquid；
B. fresh Heliotropium arborescens petal is put into rotating speed to be beaten 20 ~ 22min in 950 ~ 970r/min beater, takes out, obtain colored slurry；
C. bentonite and fire clay are put into Chinese medicine infusion liquid, with rotating speed for 180 ~ 190r/min agitator stirring 13 ~
14min, is heated to temperature for 64 ~ 66 DEG C, and input flower slurry rotating speed continues to stir 8 ~ 9min for 180 ~ 190r/min agitator,
Slurry must be smeared.
Beneficial effects of the present invention：A kind of Rattan that the present invention is provided does old processing method, first through boiling, drying,
Immersion and fermentation process, are not only able to effectively eliminate the impurity on Rattan surface, strengthen its surface gloss, and can be effective
Suppress the growth of Rattan harmful bacteria, improve its antibacterial ability, strengthen its anticorrosive mildewproof ability, effectively extend making for its knitting
Use the life-span；Then through surface size, baking, wetting, fermentation and drying process, the toughness of effectively enhancing Rattan is not only able to,
Its fragility is reduced, its Resisting fractre ability is effectively improved, and causes Rattan color and luster thick and heavy uniform, fragrance is pure and fresh persistently, lifting
It uses quality.
Embodiment
Illustrate the present invention with specific embodiment below, but be not limitation of the present invention.
Embodiment 1
In the embodiment of the present invention, a kind of Rattan does old processing method, and specific method is as follows：
（1）Boiling, drying, immersion and fermentation process
Rattan is inserted into constant temperature boiling 18min in the Vacuum cooker that temperature is 125 DEG C, with 5.2 DEG C/min heating rate
166 DEG C of constant temperature boiling 34min are warming up to, are taken out, microwave drying to moisture is 17% under conditions of frequency is 330MHz,
It is immersed in soak and soaks 350min, take out, inserts fermentation 26h in the fermenting case that temperature is 40 DEG C, take out, be 45 with temperature
DEG C water clean 2 ~ 3 times；
Described treatment fluid, is made up of the raw material of following parts by weight：3.2 parts of metasilicate pentahydrate sodium, 2.1 parts of tertiary sodium phosphate, three water
1.6 parts of sodium acetate, 2.7 parts of Sodium Polyacrylate, 0.56 part of Cortex Acanthopancis extract, 0.71 part of Black Cohosh P.E, 94 parts of water；
（2）Surface size, baking, wetting, fermentation and drying process
Will be through step（1）Rattan after processing, which is immersed in smearing slurry, makes its surface be completely covered by smearing slurry, takes out, inserts temperature
Spend constant temperature in the baking box for 58 DEG C and toast 590s, 93 DEG C of constant temperature baking 470s are warming up to 2.3 DEG C/min heating rate, with
3.4 DEG C/min rate of temperature fall is cooled to 65 DEG C of constant temperature baking 360s, takes out, and is immersed in constant temperature in the water that temperature is 4 DEG C and soaks
95min, takes out, and washes away the smearing slurry on surface, inserts fermentation 26h in the fermenting case that temperature is 40 DEG C, takes out, be in frequency
Microwave drying to moisture is 10% under conditions of 450MHz；
Described smearing slurry, is made up of the raw material of following parts by weight：85 parts of bentonite, 34 parts of fire clay, 2.6 parts of gamboge, blood
Exhaust 1.5 parts, 3.1 parts of asarum, 2.3 parts of, Bi Collettiis, 4.3 parts of the root of three-nerved spicebush, 3.1 parts of loguat leaf, 5.7 parts of fresh Heliotropium arborescens petal, 155 parts of water.
It is used as the further scheme of invention：Step（2）The preparation method of described smearing slurry, specifically includes following steps：
A. asarum, Bi Collettiis, the root of three-nerved spicebush and loguat leaf are put into rotating speed to crush 13min in 1300r/min pulverizer, takes out, throw
Enter in water and be boiled by fire, slow fire infusion 15min adds gamboge and the dragon's blood for being crushed to 130 mesh, continues 43 ~ 45min of slow fire infusion
And constantly be 110r/min with rotating speed agitator be stirred, room temperature natural cooling obtains Chinese medicine infusion liquid；
B. fresh Heliotropium arborescens petal is put into rotating speed to be beaten 20min in 950r/min beater, takes out, obtain colored slurry；
C. bentonite and fire clay are put into Chinese medicine infusion liquid, the agitator for being 180r/min with rotating speed stirring 13min, plus
Heat to temperature is 64 DEG C, and the agitator that input flower slurry is 180r/min with rotating speed continues to stir 8min, must smear slurry.
Embodiment 2
In the embodiment of the present invention, a kind of Rattan does old processing method, and specific method is as follows：
（1）Boiling, drying, immersion and fermentation process
Rattan is inserted into constant temperature boiling 19min in the Vacuum cooker that temperature is 126 DEG C, with 5.3 DEG C/min heating rate
167 DEG C of constant temperature boiling 35min are warming up to, are taken out, microwave drying to moisture is under conditions of frequency is 335MHz
17.5%, it is immersed in soak and soaks 355min, take out, inserts fermentation 26.5h in the fermenting case that temperature is 40.5 DEG C, take out,
Cleaned 2 ~ 3 times for 46 DEG C of water with temperature；
Described treatment fluid, is made up of the raw material of following parts by weight：3.3 parts of metasilicate pentahydrate sodium, 2.2 parts of tertiary sodium phosphate, three water
1.7 parts of sodium acetate, 2.8 parts of Sodium Polyacrylate, 0.57 part of Cortex Acanthopancis extract, 0.71 ~ 0.73 part of Black Cohosh P.E, water 95
Part；
（2）Surface size, baking, wetting, fermentation and drying process
Will be through step（1）Rattan after processing, which is immersed in smearing slurry, makes its surface be completely covered by smearing slurry, takes out, inserts temperature
Spend constant temperature in the baking box for 58.5 DEG C and toast 595s, 93.5 DEG C of constant temperature bakings are warming up to 2.35 DEG C/min heating rate
475s, is cooled to 65.5 DEG C of constant temperature baking 365s with 3.45 DEG C/min rate of temperature fall, takes out, it is 4.5 DEG C to be immersed in temperature
Constant temperature soaks 98min in water, takes out, and washes away the smearing slurry on surface, inserts fermentation 26.5h in the fermenting case that temperature is 40.5 DEG C,
Take out, microwave drying to moisture is 10.5% under conditions of frequency is 455MHz；
Described smearing slurry, is made up of the raw material of following parts by weight：86 parts of bentonite, 35 parts of fire clay, 2.7 parts of gamboge, blood
Exhaust 1.6 parts, 3.2 parts of asarum, 2.4 parts of, Bi Collettiis, 4.4 parts of the root of three-nerved spicebush, 3.2 parts of loguat leaf, 5.8 parts of fresh Heliotropium arborescens petal, 158 parts of water.
It is used as the further scheme of invention：Step（2）The preparation method of described smearing slurry, specifically includes following steps：
A. asarum, Bi Collettiis, the root of three-nerved spicebush and loguat leaf are put into rotating speed to crush 13.5min in 1350r/min pulverizer, taken out,
It is boiled by fire in input water, slow fire infusion 16min adds gamboge and the dragon's blood for being crushed to 135 mesh, continues slow fire infusion 44min
And constantly be 115r/min with rotating speed agitator be stirred, room temperature natural cooling obtains Chinese medicine infusion liquid；
B. fresh Heliotropium arborescens petal is put into rotating speed to be beaten 21min in 960r/min beater, takes out, obtain colored slurry；
C. bentonite and fire clay are put into Chinese medicine infusion liquid, the agitator for being 185r/min with rotating speed stirring 13.5min,
Temperature is heated to for 65 DEG C, the agitator that input flower slurry is 185r/min with rotating speed continues to stir 8.5min, must smear slurry.
Embodiment 3
In the embodiment of the present invention, a kind of Rattan does old processing method, and specific method is as follows：
（1）Boiling, drying, immersion and fermentation process
Rattan is inserted into constant temperature boiling 20min in the Vacuum cooker that temperature is 127 DEG C, with 5.4 DEG C/min heating rate
168 DEG C of constant temperature boiling 36min are warming up to, are taken out, microwave drying to moisture is 18% under conditions of frequency is 340MHz,
It is immersed in soak and soaks 360min, take out, inserts fermentation 27h in the fermenting case that temperature is 41 DEG C, take out, be 47 with temperature
DEG C water clean 2 ~ 3 times；
Described treatment fluid, is made up of the raw material of following parts by weight：3.4 parts of metasilicate pentahydrate sodium, 2.3 parts of tertiary sodium phosphate, three water
1.8 parts of sodium acetate, 2.9 parts of Sodium Polyacrylate, 0.58 part of Cortex Acanthopancis extract, 0.73 part of Black Cohosh P.E, 96 parts of water；
（2）Surface size, baking, wetting, fermentation and drying process
Will be through step（1）Rattan after processing, which is immersed in smearing slurry, makes its surface be completely covered by smearing slurry, takes out, inserts temperature
Spend constant temperature in the baking box for 59 DEG C and toast 600s, 94 DEG C of constant temperature baking 480s are warming up to 2.4 DEG C/min heating rate, with
3.5 DEG C/min rate of temperature fall is cooled to 66 DEG C of constant temperature baking 370s, takes out, and is immersed in constant temperature in the water that temperature is 5 DEG C and soaks
100min, takes out, and washes away the smearing slurry on surface, inserts fermentation 27h in the fermenting case that temperature is 41 DEG C, takes out, be in frequency
Microwave drying to moisture is 11% under conditions of 460MHz；
Described smearing slurry, is made up of the raw material of following parts by weight：87 parts of bentonite, 36 parts of fire clay, 2.8 parts of gamboge, blood
Exhaust 1.7 parts, 3.3 parts of asarum, 2.5 parts of, Bi Collettiis, 4.5 parts of the root of three-nerved spicebush, 3.3 parts of loguat leaf, 5.9 parts of fresh Heliotropium arborescens petal, 160 parts of water.
It is used as the further scheme of invention：Step（2）The preparation method of described smearing slurry, specifically includes following steps：
A. asarum, Bi Collettiis, the root of three-nerved spicebush and loguat leaf are put into rotating speed to crush 14min in 1400r/min pulverizer, takes out, throw
Enter in water and be boiled by fire, slow fire infusion 17min adds gamboge and the dragon's blood for being crushed to 140 mesh, continues slow fire infusion 45min simultaneously
The agitator for being constantly 120r/min with rotating speed is stirred, and room temperature natural cooling obtains Chinese medicine infusion liquid；
B. fresh Heliotropium arborescens petal is put into rotating speed to be beaten 22min in 970r/min beater, takes out, obtain colored slurry；
C. bentonite and fire clay are put into Chinese medicine infusion liquid, the agitator for being 190r/min with rotating speed stirring 14min, plus
Heat to temperature is 66 DEG C, and the agitator that input flower slurry is 190r/min with rotating speed continues to stir 9min, must smear slurry.
Claims (2)
1. a kind of Rattan does old processing method, it is characterised in that specific method is as follows：
（1）Boiling, drying, immersion and fermentation process
Rattan is inserted into constant temperature 18 ~ 20min of boiling in the Vacuum cooker that temperature is 125 ~ 127 DEG C, with 5.2 ~ 5.4 DEG C/min
Heating rate be warming up to 166 ~ 168 DEG C of constant temperature 34 ~ 36min of boiling, take out, frequency be 330 ~ 340MHz under conditions of microwave
It is 17% ~ 18% to dry to moisture, is immersed in 350 ~ 360min of immersion in soak, takes out, and it is 40 ~ 41 DEG C to insert temperature
26 ~ 27h of fermentation in fermenting case, takes out, and is cleaned 2 ~ 3 times for 45 ~ 47 DEG C of water with temperature；
Described treatment fluid, is made up of the raw material of following parts by weight：3.2 ~ 3.4 parts of metasilicate pentahydrate sodium, tertiary sodium phosphate 2.1 ~ 2.3
Part, 1.6 ~ 1.8 parts of Sodium acetate trihydrate, 2.7 ~ 2.9 parts of Sodium Polyacrylate, 0.56 ~ 0.58 part of Cortex Acanthopancis extract, black cohosh root are extracted
0.71 ~ 0.73 part of thing, 94 ~ 96 parts of water；
（2）Surface size, baking, wetting, fermentation and drying process
Will be through step（1）Rattan after processing, which is immersed in smearing slurry, makes its surface be completely covered by smearing slurry, takes out, inserts temperature
Spend constant temperature in the baking box for 58 ~ 59 DEG C and toast 590 ~ 600s, 93 ~ 94 DEG C are warming up to 2.3 ~ 2.4 DEG C/min heating rate
Constant temperature toasts 470 ~ 480s, and being cooled to 65 ~ 66 DEG C of constant temperature with 3.4 ~ 3.5 DEG C/min rate of temperature fall toasts 360 ~ 370s, takes out,
It is that constant temperature soaks 95 ~ 100min in 4 ~ 5 DEG C of water to be immersed in temperature, takes out, washes away the smearing slurry on surface, insert temperature for 40 ~
26 ~ 27h of fermentation in 41 DEG C of fermenting case, takes out, and microwave drying to moisture is under conditions of frequency is 450 ~ 460MHz
10%~11%；
Described smearing slurry, is made up of the raw material of following parts by weight：85 ~ 87 parts of bentonite, 34 ~ 36 parts of fire clay, gamboge 2.6
~ 2.8 parts, 1.5 ~ 1.7 parts of dragon's blood, 3.1 ~ 3.3 parts of asarum, 2.3 ~ 2.5 parts of, Bi Collettiis, 4.3 ~ 4.5 parts of the root of three-nerved spicebush, loguat leaf 3.1 ~ 3.3
Part, 5.7 ~ 5.9 parts of fresh Heliotropium arborescens petal, 155 ~ 160 parts of water.
2. Rattan according to claim 1 does old processing method, it is characterised in that step（2）Described smearing slurry
Preparation method, specifically include following steps：
A. asarum, Bi Collettiis, the root of three-nerved spicebush and loguat leaf are put into rotating speed to crush 13 ~ 14min in 1300 ~ 1400r/min pulverizer,
Take out, be boiled by fire in input water, slow fire 15 ~ 17min of infusion adds gamboge and the dragon's blood for being crushed to 130 ~ 140 mesh, continues text
Fiery 43 ~ 45min of infusion is simultaneously constantly stirred with rotating speed for 110 ~ 120r/min agitator, and room temperature natural cooling obtains Chinese medicine
Infusion liquid；
B. fresh Heliotropium arborescens petal is put into rotating speed to be beaten 20 ~ 22min in 950 ~ 970r/min beater, takes out, obtain colored slurry；
C. bentonite and fire clay are put into Chinese medicine infusion liquid, with rotating speed for 180 ~ 190r/min agitator stirring 13 ~
14min, is heated to temperature for 64 ~ 66 DEG C, and input flower slurry rotating speed continues to stir 8 ~ 9min for 180 ~ 190r/min agitator,
Slurry must be smeared.