CN107034736A - A kind of high gloss endures with all one's will wrapping paper - Google Patents
A kind of high gloss endures with all one's will wrapping paper Download PDFInfo
- Publication number
- CN107034736A CN107034736A CN201710315515.4A CN201710315515A CN107034736A CN 107034736 A CN107034736 A CN 107034736A CN 201710315515 A CN201710315515 A CN 201710315515A CN 107034736 A CN107034736 A CN 107034736A
- Authority
- CN
- China
- Prior art keywords
- paper
- oar
- added
- high gloss
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Endure with all one's will wrapping paper the present invention relates to a kind of high gloss, it is characterised in that:Using waste paper as raw pulp, waste paper is wastepaper, and technological process includes:Oar is ground in immersion, broken oar of washing by water, slurrying, purification, and homogenate, copy paper is dried, cutting;2.0~3.0wt% wet strength agent, 2.5~5.0 wt % AKD sizing agents is added during mill oar, with 0.05~0.6 wt % softening agent, 0.1~1.0 organosilicon quaternary ammonium salts of the wt % with chain alkyl and 0.2~1.6 wt % sodium tripolyphosphates are added in homogenization process, wherein drying temperature is using the increase of three phase temperature gradient types.Organosilicon quaternary ammonium salt is added in homogenization process of the present invention, absorption is formed between the hydroxyl on methoxyl group and fiber on its molecular end chain, equivalent to fibre length is increased, fiber is effectively kept, the cohesive force of reinforcing fiber, the effect for making acquisition stiffening.
Description
Technical field
Endure with all one's will the present invention relates to a kind of wrapping paper, more particularly to a kind of high gloss on commodity, hardware article
Wrapping paper.Belong to daily living article technical field.
Background technology
As paper is in the extensive application in the fields such as packaging, demand is increasing.Particularly art post paperboard is in packaging field
Application include medicine, health products, cosmetics, electronic product, handbag, clothes box, jack-in-a-box, cigarette pack, dixie cup, conveniently
The substantial amounts of application art post paperboard of the packagings for foodstuff such as face box, hamburger box, cake box, causes art post paperboard demand sharp increase.Current electronics
Commercial affairs, logistics are fast-developing, have further promoted carton, carton etc. to pack the rush of demand of paper product.
Due to the resource contradiction of production drawback and the wood pulp paper of traditional pulp based paper, preventing it, species is various and need from meeting
Huge Packaging Industry is sought, the need for social sustainable development can not being met.Particularly current conventional paper is in order to meet packaging
Demand, it is necessary to further surface coating processing, increase the cost of wrapping paper.
Current paper is low for showing as well-pressed degree when making carton, carton, paper bag.It is used for using part mineral fibres
The deflection of stone paper can be improved by preparing stone paper, but because stone is processed by thermoplastic flowing, mineral fibres it is netted
Structure is difficult to be sufficiently reserved, so that mineral fibres is difficult to the mesh-supported for playing fiber in stone paper, so as to cause
Stone paper is used for the presence of well-pressed degree low defect during wrapping paper.In addition in order to which the glossiness for improving wrapper surface is needed in its table
Face carries out aluminum coated steel, adds processing step, improves processing cost.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of high gloss for above-mentioned prior art to endure with all one's will wrapping paper,
Increase the cohesive force of paper fibre, the effect for making it obtain stiffening and high gloss.
The present invention the used technical scheme that solves the above problems is:A kind of high gloss endures with all one's will wrapping paper, using waste paper as
Raw pulp, waste paper is wastepaper, and technological process includes:Oar is ground in immersion, broken oar of washing by water, slurrying, purification, is homogenized, copy paper,
Drying, cutting;2.0~3.0wt% wet strength agent, 2.5~5.0 wt % AKD sizing agents is added during mill oar, and
0.05~0.6 wt % softening agent, adds 0.1~1.0 organosilicon quaternary ammonium salts of the wt % with chain alkyl in homogenization process
With 0.2~1.6 wt % sodium tripolyphosphates, added after homogenate terminates 0.08~0.1wt % polydiorganosiloxanepolyurea glycol and
0.02~0.1wt % water-soluble poly ammonium phosphate, wherein drying temperature are using the increase of three phase temperature gradient types.
Preferably, the organosilicon quaternary ammonium salt is selected from 3-(Trihydroxy silicyl)Propyl-dimethyl-octadecyl chloride
Change ammonium or 3-(Trihydroxy silicyl)Propyl-dimethyl-cetyl chloride ammonium.
Preferably, the drying tube temperature of the drying temperature first stage is 55 DEG C, 60 DEG C, 65 DEG C, 70 DEG C, second stage
Drying tube temperature is 65 DEG C, 70 DEG C, 75 DEG C, 75 DEG C, and the drying tube temperature of phase III is 80 DEG C, 85 DEG C, 90 DEG C, most 90 DEG C, after-blow
It is cooled to room temperature.Compared with prior art, the advantage of the invention is that:
Organosilicon quaternary ammonium salt is added in homogenization process of the present invention, shape between the hydroxyl on methoxyl group and fiber on its molecular end chain
Into absorption, equivalent to fibre length is increased, fiber is effectively kept, the cohesive force of reinforcing fiber, the effect for making acquisition stiffening;
Polydiorganosiloxanepolyurea glycol is added in homogenization process, it is good with Miscibility, can tend in copy paper operating process
In top layer arrangement, so as to reach the effect for improving sheet gloss.
Embodiment
Embodiment 1
Using waste paper as raw pulp, waste paper is wastepaper, and technological process includes:Immersion, broken oar of washing by water, slurrying is purified, mill
Oar, homogenate, copy paper is dried, cutting;Added during mill oar 2.0wt% wet strength agent, 2.5 wt % AKD sizing agents and
0.05 wt % softening agent, adds 3-s of the 0.1wt % with chain alkyl in homogenization process(Trihydroxy silicyl)Propyl group two
Methyl-octadecyl ammonium chloride and 0.2 wt % sodium tripolyphosphates(Homogenisation systems), 0.08wt % are added after homogenate terminates
Polydimethylsiloxanediols diols (polydiorganosiloxanepolyurea glycol) and 0.02 wt % water-soluble poly ammonium phosphate, wherein drying temperature
The drying tube temperature for spending the first stage is 55 DEG C, and the drying tube temperature of second stage is 65 DEG C, and the drying tube temperature of phase III is 80 DEG C,
Most after-blow is cooled to room temperature.
Embodiment 2
Using waste paper as raw pulp, waste paper is wastepaper, and technological process includes:Immersion, broken oar of washing by water, slurrying is purified, mill
Oar, homogenate, copy paper is dried, cutting;2.5wt% wet strength agent, 4 wt % AKD sizing agents and 0.3 is added during mill oar
Wt % softening agent, adds 3-s of the 0.5wt % with chain alkyl in homogenization process(Trihydroxy silicyl)Propyl-dimethyl
- cetyl chloride ammonium and 0.2 wt % sodium tripolyphosphates(Homogenisation systems), poly- the two of 0.09wt % is added after homogenate terminates
Methylsiloxane glycol and 0.06 wt % water-soluble poly ammonium phosphate, the wherein drying tube temperature of drying temperature first stage are 60 DEG C,
The drying tube temperature of second stage is 70 DEG C, and the drying tube temperature of phase III is 85 DEG C, and most after-blow is cooled to room temperature.
Embodiment 3
Using waste paper as raw pulp, waste paper is wastepaper, and technological process includes:Immersion, broken oar of washing by water, slurrying is purified, mill
Oar, homogenate, copy paper is dried, cutting;Added during mill oar 3.0wt% wet strength agent, 5.0wt % AKD sizing agents and
0.6 wt % softening agent, adds 3-s of the 1.0wt % with chain alkyl in homogenization process(Trihydroxy silicyl)Propyl group two
Methyl-octadecyl ammonium chloride and 1.0wt % sodium tripolyphosphates(Homogenisation systems), add 0.08wt %'s after homogenate terminates
Polydimethylsiloxanediols diols (polydiorganosiloxanepolyurea glycol) and 0.1 wt % water-soluble poly ammonium phosphate, wherein drying temperature
The drying tube temperature in one stage is 70 DEG C, and the drying tube temperature of second stage is 75 DEG C, and the drying tube temperature of phase III is 90 DEG C, finally
Blow and be cooled to room temperature.
A kind of preferable implementation of the present invention is the foregoing is only, is not intended to limit the invention, it is all in this hair
Non-essential modification, replacement, improvement for being made in bright spirit etc., should be included in the scope of the protection.
Claims (3)
1. a kind of high gloss endures with all one's will wrapping paper, it is characterised in that:Using waste paper as raw pulp, waste paper is wastepaper, technique
Flow includes:Oar is ground in immersion, broken oar of washing by water, slurrying, purification, and homogenate, copy paper is dried, cutting;2.0 are added during mill oar
The AKD sizing agents of~3.0wt% wet strength agent, 2.5~5.0 wt %, and 0.05~0.6 wt % softening agent, be homogenized
0.1~1.0 organosilicon quaternary ammonium salts of the wt % with chain alkyl and 0.2~1.6 wt % sodium tripolyphosphates are added in journey, in homogenate
0.08~0.1wt % polydiorganosiloxanepolyurea glycol and 0.02~0.1wt % water-soluble poly ammonium phosphate is added after end, wherein
Drying temperature is using the increase of three phase temperature gradient types.
2. high gloss according to claim 1 endures with all one's will wrapping paper, it is characterised in that:The organosilicon quaternary ammonium salt is selected from 3-
(Trihydroxy silicyl)Propyl-dimethyl-octadecyl ammonium chloride or 3-(Trihydroxy silicyl)Propyl-dimethyl-
Cetyl chloride ammonium.
3. high gloss according to claim 1 endures with all one's will wrapping paper, it is characterised in that:The drying temperature first stage
Drying tube temperature is 55 DEG C, 60 DEG C, 65 DEG C, 70 DEG C, and the drying tube temperature of second stage is 65 DEG C, 70 DEG C, 75 DEG C, 75 DEG C, the 3rd rank
The drying tube temperature of section is 80 DEG C, 85 DEG C, 90 DEG C, 90 DEG C, and most after-blow is cooled to room temperature.