CN107034514A - A kind of excellent ruby preparation method of permeability - Google Patents
A kind of excellent ruby preparation method of permeability Download PDFInfo
- Publication number
- CN107034514A CN107034514A CN201710111767.5A CN201710111767A CN107034514A CN 107034514 A CN107034514 A CN 107034514A CN 201710111767 A CN201710111767 A CN 201710111767A CN 107034514 A CN107034514 A CN 107034514A
- Authority
- CN
- China
- Prior art keywords
- ruby
- permeability
- preparation
- pressed compact
- 3min
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to artificial gem field, more particularly to a kind of excellent ruby preparation method of permeability, it is specially:By chrome green, iron oxide, alundum (Al2O3) with 0.5:0.1:99.4 part by weight is mixed, and is put into after pressed compact in arc discharge device, and synthesis 3min is carried out with 150A electric current under the protection of inert gas, obtains color for cerise, the high ruby of jewel entirety permeability.
Description
Technical field
The invention belongs to artificial gem field, more particularly to a kind of excellent ruby preparation method of permeability.
Background technology
It is translucent-sub-translucent in kermesinus or dark pink more than starlight ruby, have six-pointed star.Clearly may be used in jewel
See the tiffany shape inclusion enclave or the different colour band of the depth and twin crystal line of three compositions, 60 °, 120 ° angles of cut.The center of six-pointed star,
There is a bright spot to external diffusion, be tapered per Tiao Xingxianyou centers to edge extension.Existing artificial synthesized ruby is adopted
Synthesized with alundum (Al2O3) and chrome green, be also unable to reach above-mentioned effect.
The content of the invention
It is cerise, high ruby of jewel entirety permeability it is an object of the invention to provide a kind of brand-new color
Preparation method.
In order to realize above-mentioned technique effect, the technical scheme that the present invention is provided is such:A kind of excellent red of permeability
The preparation method of jewel, by chrome green, iron oxide, alundum (Al2O3) with 0.5:0.1:99.4 part by weight is mixed
Close, be put into after pressed compact in arc discharge device, synthesis 3min is carried out with 150A electric current under the protection of inert gas.
In the excellent ruby preparation method of above-mentioned permeability, grain diameter size is 10-11mm after pressed compact.
The present invention has the advantage that compared with conventional method:
The ruby color obtained by the method synthesis of the present invention is cerise, and jewel entirety permeability is high.
Specific embodiment
Claims of the present invention is described further with reference to embodiment, but not constituted to the present invention
Any limitation, it is any with the technical scheme is that made by basis limited number of time modification still fall within the present invention to be protected
The content of shield.
Embodiment 1
The excellent ruby preparation method of a kind of permeability, by chrome green, iron oxide, alundum (Al2O3) with 0.5:
0.1:99.4 part by weight is mixed, and grain diameter size is 10mm after pressed compact, is put into arc discharge device, lazy
Property gas protection under synthesis 3min is carried out with 150A electric current.
Embodiment 2
The excellent ruby preparation method of a kind of permeability, by chrome green, iron oxide, alundum (Al2O3) with 0.5:
0.1:99.4 part by weight is mixed, and grain diameter size is 11mm after pressed compact, is put into arc discharge device, lazy
Property gas protection under synthesis 3min is carried out with 150A electric current.
Embodiment 3
The excellent ruby preparation method of a kind of permeability, by chrome green, iron oxide, alundum (Al2O3) with 0.5:
0.1:99.4 part by weight is mixed, and grain diameter size is 10.5mm after pressed compact, is put into arc discharge device,
Synthesis 3min is carried out with 150A electric current under the protection of inert gas.
Above-described is only presently preferred embodiments of the present invention, all timess made in the range of the spirit and principles in the present invention
What modifications, equivalent substitutions and improvements etc., should be included in the scope of the protection.
Claims (2)
1. the excellent ruby preparation method of a kind of permeability, it is characterised in that by chrome green, iron oxide, three oxidations
Two aluminium are with 0.5:0.1:99.4 part by weight is mixed, and is put into after pressed compact in arc discharge device, in inert gas
Synthesis 3min is carried out with 150A electric current under protection.
2. the excellent ruby preparation method of permeability according to claim 1, it is characterised in that particle after pressed compact
Footpath size is 10-11mm.