CN107033699A - A kind of automobile high brightness protective paint - Google Patents
A kind of automobile high brightness protective paint Download PDFInfo
- Publication number
- CN107033699A CN107033699A CN201710387310.7A CN201710387310A CN107033699A CN 107033699 A CN107033699 A CN 107033699A CN 201710387310 A CN201710387310 A CN 201710387310A CN 107033699 A CN107033699 A CN 107033699A
- Authority
- CN
- China
- Prior art keywords
- parts
- high brightness
- protective paint
- automobile
- automobile high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile high brightness protective paint, consisted of the following composition according to parts by weight：26 parts of 66 78 parts of acrylic resin, 36 50 parts of organic silicon resin, 15 22 parts of tricresyl phosphate, 10 15 parts of zeolite powder, 58 parts of dichloromethane, 10 12 parts of nano diatomite, 7 13 parts of silica, 58 parts of cyclohexanone, 49 parts of stearic acid, 69 parts of glycerine, 36 parts of palm wax, 35 parts of soluble polyurethane levelling agent, 48 parts of defoamer and antirust agent.Automobile of the present invention high brightness protective paint, has good protective action to car surface, prevents automobile from getting rusty, the protective paint basal plane adhesive force is strong, wear-resistant simultaneously and corrosion resistance is strong, do not allow fugitive color and come off, glossiness, brightness preferably, increase automobile aesthetics.
Description
Technical field
Field, particularly a kind of automobile high brightness protective paint are fabricated the present invention relates to automobile.
Background technology
With the development of auto industry, to automobile appearance performance requirement yet more and more higher, automobile exterior paint mask is not required nothing more than
There are preferable brightness and glossiness, should also have preferable metal subunits, Cavitation resistant, Fouling resistant, and it is dirty to environment
Dye is small or free from environmental pollution, and has the combination property in terms of longer service life etc..
But present car surface paint adds the organic solvents such as benzene mostly, and what is had even has certain harm to human body, also can
Environment is affected, anticorrosive, wear resistance is not strong, brilliance degree is poor, wanted as people are attractive in appearance to automobile
More and more higher is sought, this is accomplished by a kind of dependable performance, to human body and environmentally friendly wear-resistant paint.
The content of the invention
It is an object of the invention to provide a kind of automobile high brightness protective paint, above-mentioned technological deficiency is solved.
To achieve the above object, the present invention provides following technical scheme：
A kind of automobile high brightness protective paint, is consisted of the following composition according to parts by weight：66-78 parts of acrylic resin, organosilicon
36-50 parts of resin, 15-22 parts of tricresyl phosphate, 10-15 parts of zeolite powder, 5-8 parts of dichloromethane, nano diatomite 10-12
Part, 7-13 parts of silica, 5-8 parts of cyclohexanone, 4-9 parts of stearic acid, 6-9 parts of glycerine, 3-6 parts of palm wax, water-soluble poly ammonia
2-6 parts of 3-5 parts of ester levelling agent, 4-8 parts of defoamer and antirust agent.
Further, a kind of automobile high brightness protective paint, is consisted of the following composition according to parts by weight：Acrylic acid tree
73-78 parts of fat, organic silicon resin 42-50 parts, 17-20 parts of tricresyl phosphate, 11-14 parts of zeolite powder, 7-8 parts of dichloromethane,
11-12 parts of nano diatomite, 0-13 parts of silica 1,7-8 parts of cyclohexanone, 6-9 parts of stearic acid, 7-9 parts of glycerine, palm wax
4-6 parts of 5-6 parts, 4-5 parts of soluble polyurethane levelling agent, 6-8 parts of defoamer and antirust agent.
Further, a kind of automobile high brightness protective paint, is consisted of the following composition according to parts by weight：Acrylic acid tree
72 parts of fat, 42 parts of organic silicon resin, 17 parts of tricresyl phosphate, 11 parts of zeolite powder, 7 parts of dichloromethane, 12 parts of nano diatomite,
0 part of silica 1,7 parts of cyclohexanone, 6 parts of stearic acid, 7 parts of glycerine, 5 parts of palm wax, 4 parts of soluble polyurethane levelling agent, disappear
4 parts of 6 parts of infusion and antirust agent.
Further, the defoamer is fluorite, sodium carbonate, clinker, coke, the mixture of mineral oil, and it is matched
For 5-10:3-8:4-6:1-3:2-3.
Further, the antirust agent is oiliness wax, phosphate, the mixture of sodium propionate, and it is 5-8 that it, which is matched,:3-6:2-
4。
Compared with prior art, the beneficial effects of the invention are as follows：
Automobile of the present invention high brightness protective paint, has good protective action to car surface, prevents automobile from getting rusty, and simultaneously should
Protective paint basal plane adhesive force is strong, wear-resistant and corrosion resistance is strong, it is not easy to fades and comes off, and glossiness, brightness preferably, increase
Automobile aesthetics.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment 1
A kind of automobile high brightness protective paint, is consisted of the following composition according to parts by weight：66 parts of acrylic resin, organic silicon resin
36 parts, 15 parts of tricresyl phosphate, 10 parts of zeolite powder, 5 parts of dichloromethane, 10 parts of nano diatomite, 7 parts of silica, hexamethylene
5 parts of ketone, 4 parts of stearic acid, 6 parts of glycerine, 3 parts of palm wax, 3 parts of soluble polyurethane levelling agent, 4 parts of defoamer and antirust agent 2
Part.
Wherein, the defoamer be fluorite, sodium carbonate, clinker, coke, the mixture of mineral oil, its proportioning is
5:3:4:1:2。
Wherein, the antirust agent is oiliness wax, phosphate, the mixture of sodium propionate, and it is 5 that it, which is matched,:3:2.
Embodiment 2
A kind of automobile high brightness protective paint, is consisted of the following composition according to parts by weight：78 parts of acrylic resin, organic silicon resin
50 parts, 22 parts of tricresyl phosphate, 15 parts of zeolite powder, 8 parts of dichloromethane, 12 parts of nano diatomite, 3 parts of silica 1, hexamethylene
8 parts of ketone, 9 parts of stearic acid, 9 parts of glycerine, 6 parts of palm wax, 5 parts of soluble polyurethane levelling agent, 8 parts of defoamer and antirust agent 6
Part.
Wherein, the defoamer be fluorite, sodium carbonate, clinker, coke, the mixture of mineral oil, its proportioning is
10:8:6:3:3。
Wherein, the antirust agent is oiliness wax, phosphate, the mixture of sodium propionate, and it is 8 that it, which is matched,:6:4.
Embodiment 3
A kind of automobile high brightness protective paint, is consisted of the following composition according to parts by weight：72 parts of acrylic resin, organic silicon resin
42 parts, 17 parts of tricresyl phosphate, 11 parts of zeolite powder, 7 parts of dichloromethane, 12 parts of nano diatomite, 0 part of silica 1, hexamethylene
7 parts of ketone, 6 parts of stearic acid, 7 parts of glycerine, 5 parts of palm wax, 4 parts of soluble polyurethane levelling agent, 6 parts of defoamer and antirust agent 4
Part.
Wherein, the defoamer is fluorite, sodium carbonate, clinker, coke, the mixture of mineral oil, and it is 7 that it, which is matched,:
6:5:2:2。
Wherein, the antirust agent is oiliness wax, phosphate, the mixture of sodium propionate, and it is 6 that it, which is matched,:4:3.
Automobile of the present invention high brightness protective paint, has good protective action to car surface, prevents automobile from getting rusty, together
When the protective paint basal plane adhesive force it is strong, wear-resistant and corrosion resistance is strong, it is not easy to fade and come off, glossiness, brightness are preferable.
The better embodiment to this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
, can also be on the premise of this patent objective not be departed from formula, the knowledge that one skilled in the relevant art possesses
Make a variety of changes.
Claims (5)
1. a kind of automobile high brightness protective paint, it is characterised in that consisted of the following composition according to parts by weight：Acrylic resin
66-78 parts, organic silicon resin 36-50 parts, 15-22 parts of tricresyl phosphate, 10-15 parts of zeolite powder, 5-8 parts of dichloromethane, receive
10-12 parts of diatomite of rice, 7-13 parts of silica, 5-8 parts of cyclohexanone, 4-9 parts of stearic acid, 6-9 parts of glycerine, palm wax 3-6
Part, 3-5 parts of soluble polyurethane levelling agent, 4-8 parts of defoamer and 2-6 parts of antirust agent.
2. a kind of automobile high brightness protective paint according to claim 1, it is characterised in that according to parts by weight by following component
Composition：73-78 parts of acrylic resin, organic silicon resin 42-50 parts, 17-20 parts of tricresyl phosphate, 11-14 parts of zeolite powder, two
7-8 parts of chloromethanes, 11-12 parts of nano diatomite, 0-13 parts of silica 1,7-8 parts of cyclohexanone, 6-9 parts of stearic acid, glycerine
4-6 parts of 7-9 parts, 5-6 parts of palm wax, 4-5 parts of soluble polyurethane levelling agent, 6-8 parts of defoamer and antirust agent.
3. a kind of automobile high brightness protective paint according to claim 1, it is characterised in that according to parts by weight by following component
Composition：72 parts of acrylic resin, 42 parts of organic silicon resin, 17 parts of tricresyl phosphate, 11 parts of zeolite powder, 7 parts of dichloromethane, receive
12 parts of diatomite of rice, 0 part of silica 1,7 parts of cyclohexanone, 6 parts of stearic acid, 7 parts of glycerine, 5 parts of palm wax, water-soluble poly ammonia
4 parts of 4 parts of ester levelling agent, 6 parts of defoamer and antirust agent.
4. according to a kind of any described automobile high brightness protective paints of claim 1-3, it is characterised in that：The defoamer is
Fluorite, sodium carbonate, clinker, coke, the mixture of mineral oil, it is 5-10 that it, which is matched,:3-8:4-6:1-3:2-3.
5. according to a kind of any described automobile high brightness protective paints of claim 1-3, it is characterised in that：The antirust agent is
Oiliness wax, phosphate, the mixture of sodium propionate, it is 5-8 that it, which is matched,:3-6:2-4.