CN107033595A - A kind of new-energy automobile motor radiating piece PP Pipe Compound - Google Patents

A kind of new-energy automobile motor radiating piece PP Pipe Compound Download PDF

Info

Publication number
CN107033595A
CN107033595A CN201710332250.9A CN201710332250A CN107033595A CN 107033595 A CN107033595 A CN 107033595A CN 201710332250 A CN201710332250 A CN 201710332250A CN 107033595 A CN107033595 A CN 107033595A
Authority
CN
China
Prior art keywords
new
energy automobile
radiating piece
motor radiating
automobile motor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710332250.9A
Other languages
Chinese (zh)
Inventor
逯树青
刘敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan Maogao Plastic Technology Co Ltd
Original Assignee
Kunshan Maogao Plastic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Maogao Plastic Technology Co Ltd filed Critical Kunshan Maogao Plastic Technology Co Ltd
Priority to CN201710332250.9A priority Critical patent/CN107033595A/en
Publication of CN107033595A publication Critical patent/CN107033595A/en
Pending legal-status Critical Current

Abstract

The present invention proposes a kind of new-energy automobile motor radiating piece PP Pipe Compound, it is characterized in that, including following components, 45 55 parts of PPS, 3-5 parts of ion toughener, 40 50 parts of thermal conducting agent, 1.0 1.5 parts of filling additive, this material high temperature resistant, this product can be used continuously under the conditions of 300 DEG C of high temperature, while good heat conductivity, thermal conductivity factor reaches 21W/ (K.m)；Heat conduction efficiency is high, reaches 220W/ (K.m).

Description

A kind of new-energy automobile motor radiating piece PP Pipe Compound
Technical field
The present invention relates to plastic material field, more particularly, to a kind of new-energy automobile motor radiating piece PP Pipe Compound.
Background technology
At this stage, new-energy automobile just turns into main trend, and the motor radiating piece tradition for new-energy automobile all makes With the material of aluminium alloy, and the material of aluminium alloy cost itself is high, and difference of hardness, and using effect is not good.(PPS materials are one The thermoplastic special engineering plastic for planting excellent combination property, the characteristics of it is protruded is high temperature resistant, corrosion-resistant and superior mechanicalness Can).
The content of the invention
To solve the problems of the prior art, the present invention proposes a kind of new-energy automobile motor radiating piece PP Pipe Compound, its It is characterised by, including following components,
It is preferred that, the filling additive includes the mixture of talcum powder, calcium carbonate and mica powder.
It is preferred that, the thermal conducting agent is import ceramic powder.
The process of new-energy automobile motor radiating piece PP Pipe Compound is produced, is comprised the following steps：
S1：PPS materials are taken, heated-air drying is used；
S2：Dried PPS materials are put into mixer, entered while adding thermal conducting agent, particle toughening agent and filling additive Row is mixed；
S3：Mixture after mixing passes through screw extruder, carries out extruding pelletization；
S4：It is cooled and shaped after screw extruder discharging through water-carrying groove, and passes through pelleter pelletizing, obtains plastic pellet；
S5：Plastic pellet is screened by vibratory sieve；
S6：Finished product packing.
New-energy automobile motor radiating piece PP Pipe Compound proposed by the present invention has the advantages that：This material high temperature resistant, This product can be used continuously under the conditions of 300 DEG C of high temperature, while good heat conductivity, thermal conductivity factor reaches 21W/ (K.m)；Heat is passed Efficiency high is led, 220W/ (K.m) is reached.
Embodiment
With reference to embodiment, the present invention is furture elucidated.
The process of new-energy automobile motor radiating piece PP Pipe Compound is produced, is comprised the following steps：
S1：PPS materials are taken, heated-air drying is used；
S2：Dried PPS materials are put into mixer, entered while adding thermal conducting agent, particle toughening agent and filling additive Row is mixed；
S3：Mixture after mixing passes through screw extruder, carries out extruding pelletization；
S4：It is cooled and shaped after screw extruder discharging through water-carrying groove, and passes through pelleter pelletizing, obtains plastic pellet；
S5：Plastic pellet is screened by vibratory sieve；
S6：Finished product packing.
By particle made from the above method, different material components ratios are taken, following examples are obtained：
Embodiment 1
A kind of new-energy automobile motor radiating piece PP Pipe Compound, including following components,
Embodiment 2
A kind of new-energy automobile motor radiating piece PP Pipe Compound, including following components,
Embodiment 3
A kind of new-energy automobile motor radiating piece PP Pipe Compound, including following components,
Comparative example 1
A kind of new-energy automobile motor radiating piece PP Pipe Compound, including following components,
Comparative example 2
A kind of new-energy automobile motor radiating piece PP Pipe Compound, including following components,
The sample that above example makes is tested, wherein, include the test of heat conductivility, resistance to elevated temperatures etc..
Above-described embodiment understand, using import ceramic powder as thermal conducting agent, substantially increase material heat distortion temperature and Pyroconductivity, high temperature resistant, this product can be used continuously under the conditions of 300 DEG C of high temperature, and good heat conductivity, thermal conductivity factor reaches 21W/(K.m)；Heat conduction efficiency is high, reaches 220W/ (K.m), meets the use requirement of engine motor.
A variety of modifications to embodiment will be apparent for those skilled in the art, determine herein The General Principle of justice can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, originally Invention is not intended to be limited to the embodiments shown herein, and is to fit to and principles disclosed herein and features of novelty Consistent most wide scope.

Claims (4)

1. a kind of new-energy automobile motor radiating piece PP Pipe Compound, it is characterised in that including following components,
。
2. new-energy automobile motor radiating piece PP Pipe Compound according to claim 1, it is characterised in that the filling additive bag Include the mixture of talcum powder, calcium carbonate and mica powder.
3. new-energy automobile motor radiating piece PP Pipe Compound according to claim 1, it is characterised in that the thermal conducting agent be into Mouth ceramic powder.
4. a kind of process for producing new-energy automobile motor radiating piece PP Pipe Compound, it is characterised in that comprise the following steps：
S1：PPS materials are taken, heated-air drying is used；
S2：Dried PPS materials are put into mixer, mixed while adding thermal conducting agent, particle toughening agent and filling additive Close stirring；
S3：Mixture after mixing passes through screw extruder, carries out extruding pelletization；
S4：It is cooled and shaped after screw extruder discharging through water-carrying groove, and passes through pelleter pelletizing, obtains plastic pellet；
S5：Plastic pellet is screened by vibratory sieve；
S6：Finished product packing.
CN201710332250.9A 2017-05-12 2017-05-12 A kind of new-energy automobile motor radiating piece PP Pipe Compound Pending CN107033595A (en)