CN107033326A - A kind of preparation method of the mining injecting paste material of two-component - Google Patents
A kind of preparation method of the mining injecting paste material of two-component Download PDFInfo
- Publication number
- CN107033326A CN107033326A CN201710337133.1A CN201710337133A CN107033326A CN 107033326 A CN107033326 A CN 107033326A CN 201710337133 A CN201710337133 A CN 201710337133A CN 107033326 A CN107033326 A CN 107033326A
- Authority
- CN
- China
- Prior art keywords
- component
- mining
- paste material
- injecting paste
- saline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of the mining injecting paste material of two-component, belong to reinforcement material preparing technical field.High-temperature activation is handled after the present invention first sieves kaolin particle ball milling, cooling, which is collected, must activate kaolin powder, then it will heat and centrifuge with deionized water after saline-alkali soil grinding sieving, collect supernatant liquor and mix ultrasonic disperse with activating kaolin powder etc., it is prepared into component A, choose again polyethers 330N vacuum drying after with toluene di-isocyanate(TDI) heat, 4 are added dropwise again, 4' methyl diphenylene diisocyanates carry out ultrasonic disperse, collect to obtain component B, last component A is stirred at room temperature with component B when in use mixes, the mining injecting paste material of two-component can be prepared into, mining injecting paste material produced by the present invention has viscosity low, good fluidity, the characteristics of setting time is short, and after solidification 7 days rupture strengths up to 28~32MPa, compression strength is up to 46~52MPa, preferable impervious leakage-stopping effect can be played.
Description
Technical field
The invention discloses a kind of preparation method of the mining injecting paste material of two-component, belong to reinforcement material technology of preparing neck
Domain.
Background technology
Coal and rock tunnel generally there are following safety problem in exploitation and tunneling process:1. seriously crushed in coal and rock
Location, roadway roof coal and part directly withstand on inbreak on full span length, and wall caving depth is big, and difficulty of construction is big, and safe condition is poor,
Easily cause accident;2. emit to fall behind at the top of tunnel and form cavity, accumulate a large amount of gas, bring many tired to ventilation and gas administration
, there is accident potential in difficulty;3. extremely hazardous in the empty in-cavity construction grillage hook top operation of inbreak, the grillage of local construction connects top effect
Difference does not connect top, and support is in instability status because of back timber sky branch, when meeting head on roof fall, easily causes support and smashes or push away and collapse.And it is right
Broken coal petrography is effectively treated, and common processing method one kind is increase support material, and another is exactly cement injection.Increase
Support material carrys out very big influence to the moving belt of coal mining support, and roof fall can not be fundamentally solved the problems, such as again;Cement mortar again because
The engineering properties such as its property noted difference influence, and do not reach grouting consolidation effect.
Chemical grouting technology is a kind of indispensable strengthening of foundation, impervious leakage-stopping, reparation concrete defect in modern project
Sunken advanced technology.It is by certain chemical material(Inorganic or organic material)The solution of low-viscosity is configured to, with chemistry filling
Stock pump(Single liquid pump or biliquid pump), the force feed equipment such as simple stirrup pump poured into stratum or gap, with increase formation strength,
Reduce permeability, prevent stratum deformation and increase concrete density.Polyurethane injecting paste material is to be applied to water conservancy, water power, tunnel
Antiseepage, leak stopping, the important injecting paste material of reinforcement effect are played in the engineerings such as road, subway, mine, people's air defense, industry and civil buildings.It is logical
After engineer applied for many years and screening, the Polyurethane injecting paste material used at present in reinforcing for grouting in coal mine technology mainly has
Two major classes a, class is one pack system injecting paste material, is polymerized in advance containing certain free isocyanate groups base by polyethers and polyisocyanates
The performed polymer of group, then adds the constitutional chemistry slurries such as solvent, catalyst, surfactant, is by single liquid pump as needed
Slip casting can be carried out;Another kind of is two-component injecting paste material, and a component is the polyol based on polyethers, and another component is
Polyisocyanate compound, is mixed by bi-component grouting pump in construction part.
However, either any injecting paste material, it is higher all to there is viscosity, the problem of poor fluidity, is suitable only for crushing
Coal body working face is met head on local short distance(<5m)Injection slip casting, be not suitable for the long drilled holes slip casting in return airway and air intake lane, pin
Overall slip casting to large working area, its consolidation effect is restricted significantly, and existing injecting paste material exist it is inflammable, explosive potential
Danger, easily lights coal seam or other underground combustibles, forms underground fire.So, find new slip casting and reach reinforcing coal petrography tool
There is important Research Significance.
The content of the invention
Present invention mainly solves technical problem:It is higher for existing mining injecting paste material viscosity, poor fluidity lack
It is sunken that there is provided a kind of preparation method of the mining injecting paste material of two-component.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is:
(1)Kaolin ball milling is taken, 250 mesh sieves is crossed, obtains kaolin powder, kaolin powder high-temperature activation is handled after 2~3h, it is quiet
Put and be cooled to room temperature, obtain activation kaolin powder;
(2)Saline-alkali soil is collected, grinds and crosses 50 mesh sieves, obtain saline and alkaline soil particle, saline and alkaline soil particle is mixed with deionized water, through water
After bath heating, standing is cooled to after room temperature, is centrifuged and is collected supernatant liquor, must excite modification liquid;
(3)Count by weight, 45~50 parts are weighed respectively and excites modification liquid, 10~15 parts of activation kaolin powders and 2~3 parts
Gamma-aminopropyl-triethoxy-silane is mixed, heating stirring and 10~15min of ultrasonic disperse, and standing, which is cooled to after room temperature, obtains component
A;
(4)Polyethers 330N must be dried by taking polyethers 330N to be dried in vacuo, and toluene di-isocyanate(TDI) is stirred into mixed with drying polyethers 330N
Merging is placed in three-necked flask, and 4, the 4'- hexichol for drying polyethers 330N mass 25% is added dropwise after heating water bath into three-necked flask again
Dicyclohexylmethane diisocyanate;
(5)After being added dropwise to complete, ultrasonic disperse and 1~2h of heating water bath, standing are cooled to room temperature and obtain component B, when in use, will
Component A is stirred at room temperature with component B and mixed, you can be prepared into a kind of mining injecting paste material of two-component.
Step(1)Described activation temperature is 150~200 DEG C.
Step(2)Described saline-alkali soil is moderate saline-alkali soil saline-alkali soil.
Step(2)Described saline and alkaline soil particle is mass ratio 1 with deionized water mixed proportion:10.
Step(4)Described toluene di-isocyanate(TDI) is mass ratio 1 with drying polyethers 330N mixed proportions:10.
Step(4)Described 4,4'- methyl diphenylene diisocyanates time for adding is controlled in 10~15min.
Step(5)Described component A and component B mixed proportions are mass ratio 1:3.
The beneficial effects of the invention are as follows:
The present invention carries out leaching process by alignment degree salt-soda soil saline-alkali soil, because moderate saline-alkali soil pH is 8.5~9.5, in it
A large amount of water-soluble alkaline salt are contained in portion, by collecting leachate as the alkali-activator of slip casting binder materials, pass through the alkali-activated carbonatite
Agent and kaolin reagentia, make Si-O in mixed material, and Al-O keys are broken and recombinated again, shape under alkali-activator effect
Into gelatin polymer, the inorganic polymeric macromolecular of the solidifying O-Si-O-Al-O three-dimensional network-like structures of gelatin polymer reaction generation, drop
Secondary hydrogen bond formation rate between low inorganic polymeric macromolecular so that inorganic polymer molecule can be rotated freely, and then reduce note
Pulp material viscosity, so as to improve injecting paste material mobile performance, fully meets use and the safety requirements of coal and rock water reinforcement, together
When the obtained injecting paste material of the present invention and coal seam bonding force be excellent, concretion body strength is high, be a kind of preferable mining water reinforcement
Learn injecting paste material.
Embodiment
Kaolin particle is taken to be placed in ball grinder, 3~5h of ball milling under the conditions of 250~300r/min crosses 250 mesh sieves, obtained
Kaolin powder is placed in 150~200 DEG C of Muffle furnace high temperature activation process 2~3h, it is to be activated after the completion of, standing is cooled to room
Temperature, obtains activation kaolin powder, collects moderate saline-alkali soil saline-alkali soil, is placed in mortar and grinds and cross 50 mesh sieves, obtains saline and alkaline
Soil particle, in mass ratio 1:10, saline and alkaline soil particle is mixed with deionized water and is placed in 3~5h of heating water bath at 45~50 DEG C,
Treat after the completion of heating water bath, standing is cooled to room temperature, is centrifuged under 4500~5500r/min and collects supernatant liquor, make
It is standby to excite modification liquid, then count by weight, 45~50 parts are weighed respectively excites modification liquid, 10~15 parts of activation kaolin powder
End and 2~3 parts of gamma-aminopropyl-triethoxy-silanes be placed in beaker, at 45~50 DEG C heating water bath and stir mixing 25~
30min, then 10~15min of ultrasonic disperse under 200~300W, stop heating and standing being cooled to room temperature, are prepared into component A,
Polyethers 330N is chosen again and 2~3h of vacuum drying at 110~120 DEG C is placed on, and standing is cooled to after room temperature, is collected after drying
Polyethers 330N, in mass ratio 1:10, toluene di-isocyanate(TDI) is mixed with dried polyethers 330N stirrings and is placed in three mouthfuls
In flask, three-necked flask is placed in 3~5h of heating water bath at 55~65 DEG C, after the completion for the treatment of heating water bath, then three-necked flask dripped
Plus 4, the 4'- methyl diphenylene diisocyanates of dried polyethers 330N mass 25%, it is 10~15min to control time for adding,
After being added dropwise to complete, under 200~300r/min after 10~15min of ultrasonic disperse, 1~2h of heating water bath at 75~80 DEG C,
Stop heating and standing being cooled to room temperature, component B, when in use, in mass ratio 1 are collected to obtain finally:3, by component A and component B
Mixing is stirred at room temperature, you can be prepared into a kind of mining injecting paste material of two-component.
Example 1
Kaolin particle is taken to be placed in ball grinder, the ball milling 3h under the conditions of 250r/min crosses 250 mesh sieves, obtains kaolin powder simultaneously
Be placed in 150 DEG C of Muffle furnace high temperature activation process 2h, it is to be activated after the completion of, standing is cooled to room temperature, obtains activation kaolin powder,
Moderate saline-alkali soil saline-alkali soil is collected, is placed in mortar and grinds and cross 50 mesh sieves, obtain saline and alkaline soil particle, in mass ratio 1:10,
Saline and alkaline soil particle is mixed with deionized water and is placed in heating water bath 3h at 45 DEG C, is treated after the completion of heating water bath, standing is cooled to
Room temperature, centrifuges under 4500r/min and collects supernatant liquor, is prepared into and excites modification liquid, then counts by weight, respectively
Weighing 45 parts excites modification liquid, 10 parts of activation kaolin powders and 2 parts of gamma-aminopropyl-triethoxy-silanes to be placed in beaker,
Heating water bath and mixing 25min, then the ultrasonic disperse 10min under 200W are stirred at 45 DEG C, stop heating and standing being cooled to room
Temperature, is prepared into component A, then chooses polyethers 330N and be placed at 110 DEG C and be dried in vacuo 2h, and standing is cooled to after room temperature, receives
Collect dried polyethers 330N, in mass ratio 1:10, toluene di-isocyanate(TDI) is mixed simultaneously with dried polyethers 330N stirrings
It is placed in three-necked flask, three-necked flask is placed in heating water bath 3h at 55 DEG C, after the completion for the treatment of heating water bath, then three-necked flask is dripped
Plus 4, the 4'- methyl diphenylene diisocyanates of dried polyethers 330N mass 25%, it is 10~15min to control time for adding,
After being added dropwise to complete, under 200r/min after ultrasonic disperse 10min, the heating water bath 12h at 75 DEG C stops heating and standing cold
But to room temperature, component B, when in use, in mass ratio 1 are collected to obtain finally:3, component A is stirred at room temperature with component B and mixed,
A kind of mining injecting paste material of two-component can be prepared into.
The mining injecting paste material of the two-component low-viscosity high-fluidity produced by the present invention being uniformly mixed is noted first
Stock pump is pushed down into the coal rock layer crack for carrying out closing measure in 0.5MPa pump pressure, is treated after the completion of whole crack fillings, is made note
Pulp material stands solidification at 20 DEG C.After testing, the mining slip casting material of two-component low-viscosity high-fluidity produced by the present invention
Material viscosity is 10mPas, and initial flow degree is 14s, and viscosity is relatively low, mobility is preferable, while having good volume stability
Property, the shrinkage factor after material solidification is only 0.012%, and 7 days rupture strengths reach 28MPa, and compression strength reaches 46MPa, and anti-folding is strong within 28 days
Degree reaches 45MPa, and compression strength reaches 74MPa, with preferable filling reinforcement effect.
Example 2
Kaolin particle is taken to be placed in ball grinder, 3~5h of ball milling under the conditions of 250~300r/min crosses 250 mesh sieves, obtains kaolinite
Native powder is placed in 150~200 DEG C of Muffle furnace high temperature activation process 2~3h, it is to be activated after the completion of, standing is cooled to room temperature,
Kaolin powder must be activated, moderate saline-alkali soil saline-alkali soil is collected, is placed in mortar and grinds and cross 50 mesh sieves, obtain saline-alkali soil
Grain, in mass ratio 1:10, saline and alkaline soil particle is mixed with deionized water and is placed in 3~5h of heating water bath at 45~50 DEG C, water is treated
After the completion of bath heating, standing is cooled to room temperature, is centrifuged under 4500~5500r/min and collects supernatant liquor, is prepared into
Excite modification liquid, then count by weight, respectively weigh 45~50 parts excite modification liquid, 10~15 parts activation kaolin powders and
2~3 parts of gamma-aminopropyl-triethoxy-silanes are placed in beaker, at 45~50 DEG C heating water bath and stir mixing 25~
30min, then 10~15min of ultrasonic disperse under 200~300W, stop heating and standing being cooled to room temperature, are prepared into component A,
Polyethers 330N is chosen again and 2~3h of vacuum drying at 110~120 DEG C is placed on, and standing is cooled to after room temperature, is collected after drying
Polyethers 330N, in mass ratio 1:10, toluene di-isocyanate(TDI) is mixed with dried polyethers 330N stirrings and is placed in three mouthfuls
In flask, three-necked flask is placed in 3~5h of heating water bath at 55~65 DEG C, after the completion for the treatment of heating water bath, then three-necked flask dripped
Plus 4, the 4'- methyl diphenylene diisocyanates of dried polyethers 330N mass 25%, it is 10~15min to control time for adding,
After being added dropwise to complete, under 250r/min after ultrasonic disperse 13min, the heating water bath 1h at 78 DEG C stops heating and standing cold
But to room temperature, component B is obtained, when in use finally, in mass ratio 1:3, component A is stirred at room temperature with component B and mixed, you can
It is prepared into a kind of mining injecting paste material of two-component.
First by the mining injecting paste material grouting pump of the two-component produced by the present invention being uniformly mixed 0.6MPa's
Pump pressure is pushed down into the coal rock layer crack for carrying out closing measure, is treated after the completion of whole crack fillings, is made injecting paste material at 30 DEG C
Stand solidification.After testing, the mining injecting paste material viscosity of two-component produced by the present invention is 15mPas, and initial flow degree is
156s, viscosity is relatively low, mobility is preferable, while having the shrinkage factor after good volume stability, material solidification to be only
0.015%, 7 days rupture strengths reach 30MPa, and compression strength reaches 49MPa, and rupture strength reaches 48MPa within 28 days, and compression strength reaches
80MPa, with preferable filling reinforcement effect.
Example 3
Kaolin particle is taken to be placed in ball grinder, the ball milling 5h under the conditions of 300r/min crosses 250 mesh sieves, obtains kaolin powder simultaneously
Be placed in 200 DEG C of Muffle furnace high temperature activation process 3h, it is to be activated after the completion of, standing is cooled to room temperature, obtains activation kaolin powder,
Moderate saline-alkali soil saline-alkali soil is collected, is placed in mortar and grinds and cross 50 mesh sieves, obtain saline and alkaline soil particle, in mass ratio 1:10,
Saline and alkaline soil particle is mixed with deionized water and is placed in heating water bath 5h at 50 DEG C, is treated after the completion of heating water bath, standing is cooled to
Room temperature, centrifuges under 5500r/min and collects supernatant liquor, is prepared into and excites modification liquid, then counts by weight, respectively
Weighing 50 parts excites modification liquid, 15 parts of activation kaolin powders and 3 parts of gamma-aminopropyl-triethoxy-silanes to be placed in beaker,
Heating water bath and mixing 30min, then the ultrasonic disperse 15min under 200~300W are stirred at 50 DEG C, stop heating and simultaneously stands cooling
To room temperature, component A is prepared into, then chooses polyethers 330N and is placed at 120 DEG C and be dried in vacuo 3h, standing is cooled to room temperature
Afterwards, dried polyethers 330N, in mass ratio 1 are collected:10, toluene di-isocyanate(TDI) and dried polyethers 330N are stirred mixed
Merging is placed in three-necked flask, and three-necked flask is placed in into heating water bath 5h at 65 DEG C, after the completion for the treatment of heating water bath, then three mouthfuls are burnt
4, the 4'- methyl diphenylene diisocyanates of dried polyethers 330N mass 25% are added dropwise in bottle, and it is 15min to control time for adding,
After being added dropwise to complete, under 300r/min after ultrasonic disperse 15min, the heating water bath 2h at 80 DEG C stops heating and standing cold
But to room temperature, component B, when in use, in mass ratio 1 are collected to obtain finally:3, component A is stirred at room temperature with component B and mixed,
A kind of mining injecting paste material of two-component can be prepared into.
First by the mining injecting paste material grouting pump of the two-component produced by the present invention being uniformly mixed 0.7MPa's
Pump pressure is pushed down into the coal rock layer crack for carrying out closing measure, is treated after the completion of whole crack fillings, is made injecting paste material at 40 DEG C
Stand solidification.After testing, the mining injecting paste material viscosity of two-component produced by the present invention is 20mPas, and initial flow degree is
16s, viscosity is relatively low, mobility is preferable, while having the shrinkage factor after good volume stability, material solidification to be only
0.018%, 7 days rupture strengths reach 32MPa, and compression strength reaches 52MPa, and rupture strength reaches 52MPa within 28 days, and compression strength reaches
86MPa, with preferable filling reinforcement effect.
Claims (7)
1. a kind of preparation method of the mining injecting paste material of two-component, it is characterised in that specifically preparation process is:
(1)Kaolin ball milling is taken, 250 mesh sieves is crossed, obtains kaolin powder, kaolin powder high-temperature activation is handled after 2~3h, it is quiet
Put and be cooled to room temperature, obtain activation kaolin powder;
(2)Saline-alkali soil is collected, grinds and crosses 50 mesh sieves, obtain saline and alkaline soil particle, saline and alkaline soil particle is mixed with deionized water, through water
After bath heating, standing is cooled to after room temperature, is centrifuged and is collected supernatant liquor, must excite modification liquid;
(3)Count by weight, 45~50 parts are weighed respectively and excites modification liquid, 10~15 parts of activation kaolin powders and 2~3 parts
Gamma-aminopropyl-triethoxy-silane is mixed, heating stirring and 10~15min of ultrasonic disperse, and standing, which is cooled to after room temperature, obtains component
A;
(4)Polyethers 330N must be dried by taking polyethers 330N to be dried in vacuo, and toluene di-isocyanate(TDI) is stirred into mixed with drying polyethers 330N
Merging is placed in three-necked flask, and 4, the 4'- hexichol for drying polyethers 330N mass 25% is added dropwise after heating water bath into three-necked flask again
Dicyclohexylmethane diisocyanate;
(5)After being added dropwise to complete, ultrasonic disperse and 1~2h of heating water bath, standing are cooled to room temperature and obtain component B, when in use, will
Component A is stirred at room temperature with component B and mixed, you can be prepared into a kind of mining injecting paste material of two-component.
2. a kind of preparation method of the mining injecting paste material of two-component according to claim 1, it is characterised in that:Step(1)
Described activation temperature is 150~200 DEG C.
3. a kind of preparation method of the mining injecting paste material of two-component according to claim 1, it is characterised in that:Step(2)
Described saline-alkali soil is moderate saline-alkali soil saline-alkali soil.
4. a kind of preparation method of the mining injecting paste material of two-component according to claim 1, it is characterised in that:Step(2)
Described saline and alkaline soil particle is mass ratio 1 with deionized water mixed proportion:10.
5. a kind of preparation method of the mining injecting paste material of two-component according to claim 1, it is characterised in that:Step(4)
Described toluene di-isocyanate(TDI) is mass ratio 1 with drying polyethers 330N mixed proportions:10.
6. a kind of preparation method of the mining injecting paste material of two-component according to claim 1, it is characterised in that:Step(4)
Described 4,4'- methyl diphenylene diisocyanates time for adding is controlled in 10~15min.
7. a kind of preparation method of the mining injecting paste material of two-component according to claim 1, it is characterised in that:Step(5)
Described component A and component B mixed proportions are mass ratio 1:3.