CN107022905B - A kind of terylene cotton elastic knitting fabric dyeing - Google Patents
A kind of terylene cotton elastic knitting fabric dyeing Download PDFInfo
- Publication number
- CN107022905B CN107022905B CN201710299602.5A CN201710299602A CN107022905B CN 107022905 B CN107022905 B CN 107022905B CN 201710299602 A CN201710299602 A CN 201710299602A CN 107022905 B CN107022905 B CN 107022905B
- Authority
- CN
- China
- Prior art keywords
- cloth
- parts
- fabric dyeing
- knitted fabric
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of terylene cotton elastics to be knitted fabric dyeing, including step 1: polyester-cotton blend cloth being dipped in disperse dyes, a leaching one is carried out and pricks；Step 2: by one leaching one prick after polyester-cotton blend cloth 80 ~ 90 DEG C at a temperature of dry；Step 3: by the cloth after drying 190 DEG C at a temperature of carry out bake 90 seconds；Step 4: the cloth for baking completion is dipped and carries out secondary dip in reduction cleaning liquid；Step 5: the cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；Step 6: wash ventilative, and soap boiling dries again later.The fabric of present invention process preparation has the characteristic for being not easy pilling.
Description
Technical field
The present invention relates to cloth dyeing, more particularly to a kind of terylene cotton elastic is knitted fabric dyeing.
Background technique
Polyester-cotton blend refers to the general designation of the blended fabric of terylene and cotton, mixes yarn using the cotton of 65% -67% terylene and 33% -35%
The textile that line is made into is commonly called as " dacron ".
Visually, polyester-cotton blend is more vivider than the color of pure cotton；If it is calico, the front and back sides color density pair of pure cotton cloth
Than larger, and the front and back sides color of polyester-mixed cotton cloth is closer to.
In feel, pure cotton cloth is soft but unsmooth, and polyester-mixed cotton cloth hand, which is felt, feels that some are smooth.
Better to skin, pure cotton, 100% cotton goods, feel touches up very soft comfortable to pure cotton.Polyester-cotton blend is to wash
The mixture of synthetic fibre and cotton, feel are comfortable not as good as cotton.Pure cotton absorbing sweat is worn and is not so good as, it is blended with terylene short fiber peacekeeping cotton fiber
The various fabrics that yarn is made into, are commonly called as cotton dacron.
Polyester-cotton blend is entangled with cotton fiber filoplume since the strength of polyester fiber is larger, it is very difficult to fall off, thus be formed
Pilling effect seen by us.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of terylene cotton elastic knitting for being not easy pilling
Dyeing fabric technique.
To achieve the above object, the present invention provides the following technical scheme that
A kind of terylene cotton elastic knitting fabric dyeing,
Including step 1:
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2:
By one leaching one prick after polyester-cotton blend cloth 80 ~ 90 DEG C at a temperature of dry；
Step 3:
By the cloth after drying 190 DEG C at a temperature of carry out bake 90 seconds；
Step 4:
The cloth for baking completion is dipped and carries out secondary dip in reduction cleaning liquid；
Step 5:
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6:
Wash ventilative, soap boiling dries again later；
The disperse dyes include following composition:
Dyestuff: 6g/L
Dispersing agent: 3 g/L
Anti- swimming agent: 12 g/L
Softener: 5 g/L；
The softener includes following parts by weight composition:
3- (isobutene acyl-oxygen) propyl trimethoxy silicane: 2 parts
3- (trimethyl silyl) ethyl propionate: 5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde: 5 parts
Four (2- hydroxyl-oxethyl) silane;: 10 parts.
As a further improvement of the present invention,
In the step 1, dipping temperature is 25 DEG C, and pick-up is 60 ~ 70%.
As a further improvement of the present invention,
The reduction cleaning liquid includes following composition:
Sodium hydroxide: 20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol: 2g/L.
As a further improvement of the present invention,
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
As a further improvement of the present invention,
It further include having bleeding agent 3g/L in the disperse dyes.
As a further improvement of the present invention,
The bleeding agent includes following weight parts composition:
3- [(methylol) methyl amine] propane sulfonic acid: 2 parts
Disecoctylmaleate sodium sulfonate: 10 parts
Hydroxy ethylene diphosphonic acid sylvite: 2 parts.
In the present invention, by the way that softener is added in dyeing course, entirety can be enhanced directly in dyeing course
Anti pilling ability is not necessarily to subsequent arrangement step.
The key of we's invention is in the selection of softener that four (2- hydroxyl-oxethyl) silane in softener are in entirety
In play the role of compatilizer, other softener ingredients are well dispersed in entire disperse dyes, while 3- (methacryloyl
Oxygen) propyl trimethoxy silicane and 3- (trimethyl silyl) ethyl propionate addition, increase considerably subsequent polyester-cotton blend material
Anti-pilling property, be eventually adding 3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde and play one
The effect of a fixative, so that last polyester-cotton blend after long-time is cleaned, still has preferable anti pilling effect, by submissive
The synergy of each component in agent, is further ensured that during routine use, and good anti pilling ability can still be maintained.
It especially joined homemade bleeding agent, enable to shortening the processing time, and obtain preferable anti pilling effect
Fruit.
Specific embodiment
Embodiment one:
A kind of terylene cotton elastic knitting fabric dyeing,
Including step 1:
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2:
By one leaching one prick after polyester-cotton blend cloth 80 ~ 90 DEG C at a temperature of dry；
Step 3:
By the cloth after drying 190 DEG C at a temperature of carry out bake 90 seconds；
Step 4:
The cloth for baking completion is dipped and carries out secondary dip in reduction cleaning liquid；
Step 5:
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6:
Wash ventilative, soap boiling dries again later；
The disperse dyes include following composition:
Dyestuff: 6g/L
Dispersing agent: 3 g/L
Anti- swimming agent: 12 g/L
Softener: 5 g/L；
The softener includes following parts by weight composition:
3- (isobutene acyl-oxygen) propyl trimethoxy silicane: 2 parts
3- (trimethyl silyl) ethyl propionate: 5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde: 5 parts
Four (2- hydroxyl-oxethyl) silane;: 10 parts.
In the step 1, dipping temperature is 25 DEG C, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition:
Sodium hydroxide: 20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol: 2g/L.
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
It further include having bleeding agent 3g/L in the disperse dyes.
The bleeding agent includes following weight parts composition:
3- [(methylol) methyl amine] propane sulfonic acid: 2 parts
Disecoctylmaleate sodium sulfonate: 10 parts
Hydroxy ethylene diphosphonic acid sylvite: 2 parts.
Embodiment two:
A kind of terylene cotton elastic knitting fabric dyeing,
Including step 1:
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2:
By one leaching one prick after polyester-cotton blend cloth 80 ~ 90 DEG C at a temperature of dry；
Step 3:
By the cloth after drying 190 DEG C at a temperature of carry out bake 90 seconds；
Step 4:
The cloth for baking completion is dipped and carries out secondary dip in reduction cleaning liquid；
Step 5:
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6:
Wash ventilative, soap boiling dries again later；
The disperse dyes include following composition:
Dyestuff: 6g/L
Dispersing agent: 3 g/L
Anti- swimming agent: 12 g/L
Softener: 5 g/L；
The softener includes following parts by weight composition:
3- (isobutene acyl-oxygen) propyl trimethoxy silicane: 2 parts
3- (trimethyl silyl) ethyl propionate: 5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde: 5 parts
Four (2- hydroxyl-oxethyl) silane;: 10 parts.
In the step 1, dipping temperature is 25 DEG C, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition:
Sodium hydroxide: 20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol: 2g/L.
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
Embodiment three:
A kind of terylene cotton elastic knitting fabric dyeing,
Including step 1:
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2:
By one leaching one prick after polyester-cotton blend cloth 80 ~ 90 DEG C at a temperature of dry；
Step 3:
By the cloth after drying 190 DEG C at a temperature of carry out bake 90 seconds；
Step 4:
The cloth for baking completion is dipped and carries out secondary dip in reduction cleaning liquid；
Step 5:
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6:
Wash ventilative, soap boiling dries again later；
The disperse dyes include following composition:
Dyestuff: 6g/L
Dispersing agent: 3 g/L
Anti- swimming agent: 12 g/L
Softener: 5 g/L；
The softener includes following parts by weight composition:
3- (isobutene acyl-oxygen) propyl trimethoxy silicane: 2 parts
3- (trimethyl silyl) ethyl propionate: 5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde: 5 parts
Four (2- hydroxyl-oxethyl) silane;: 10 parts.
In the step 1, dipping temperature is 25 DEG C, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition:
Sodium hydroxide: 20g/L
85% sodium hydrosulfite 20g/L
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
It further include having bleeding agent 3g/L in the disperse dyes.
The bleeding agent includes following weight parts composition:
3- [(methylol) methyl amine] propane sulfonic acid: 2 parts
Disecoctylmaleate sodium sulfonate: 10 parts
Hydroxy ethylene diphosphonic acid sylvite: 2 parts.
Comparative example one:
A kind of terylene cotton elastic knitting fabric dyeing,
Including step 1:
Polyester-cotton blend cloth is dipped in disperse dyes, a leaching one is carried out and pricks；
Step 2:
By one leaching one prick after polyester-cotton blend cloth 80 ~ 90 DEG C at a temperature of dry；
Step 3:
By the cloth after drying 190 DEG C at a temperature of carry out bake 90 seconds；
Step 4:
The cloth for baking completion is dipped and carries out secondary dip in reduction cleaning liquid；
Step 5:
Cloth after secondary dip is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6:
Wash ventilative, soap boiling dries again later；
The disperse dyes include following composition:
Dyestuff: 6g/L
Dispersing agent: 3 g/L
Anti- swimming agent: 12 g/L
In the step 1, dipping temperature is 25 DEG C, and pick-up is 60 ~ 70%.
The reduction cleaning liquid includes following composition:
Sodium hydroxide: 20g/L
85% sodium hydrosulfite 20g/L
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
Examination criteria:
Anti-pilling detection is detected according to the standard of GB/T4802.3-1997；
Antistatic test is detected according to 12703.3 standard of GB/T.
In the present invention, by the way that softener is added in dyeing course, entirety can be enhanced directly in dyeing course
Anti pilling ability is not necessarily to subsequent arrangement step.
The key of we's invention is in the selection of softener that four (2- hydroxyl-oxethyl) silane in softener are in entirety
In play the role of compatilizer, other softener ingredients are well dispersed in entire disperse dyes, while 3- (methacryloyl
Oxygen) propyl trimethoxy silicane and 3- (trimethyl silyl) ethyl propionate addition, increase considerably subsequent polyester-cotton blend material
Anti-pilling property, be eventually adding 3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde and play one
The effect of a fixative, so that last polyester-cotton blend after long-time is cleaned, still has preferable anti pilling effect, by submissive
The synergy of each component in agent, is further ensured that during routine use, and good anti pilling ability can still be maintained.
It especially joined homemade bleeding agent, enable to shortening the processing time, and obtain preferable anti pilling effect
Fruit.
Pass through above-mentioned experimental data, it can be deduced that, for (N-Boc-2- pyrrole radicals) dimethylsilane is added in reducing agent
Alcohol plays preferable effect.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of terylene cotton elastic is knitted fabric dyeing, it is characterised in that:
Including step 1:
Polyester-cotton blend cloth is padded in disperse dyes, an immersing and rolling is carried out；
Step 2:
By the polyester-cotton blend cloth after an immersing and rolling 80 ~ 90 DEG C at a temperature of dry；
Step 3:
By the cloth after drying 190 DEG C at a temperature of carry out bake 90 seconds；
Step 4:
The cloth for baking completion is padded and carries out secondary pad in reduction cleaning liquid；
Step 5:
Cloth after secondary pad is wrapped with plastic foil, decatize 2 minutes under 100 DEG C of vapor；
Step 6:
Wash ventilative, soap boiling dries again later；
The disperse dyes include following composition:
Dyestuff: 6g/L
Dispersing agent: 3 g/L
Anti- swimming agent: 12 g/L
Softener: 5 g/L；
The softener includes following parts by weight composition:
3- (isobutene acyl-oxygen) propyl trimethoxy silicane: 2 parts
3- (trimethyl silyl) ethyl propionate: 5 parts
3,4- bis--O- acetyl group -6-O- (t-butyl-dimethylsilyl)-D- grape aldehyde: 5 parts
Four (2- hydroxyl-oxethyl) silane;: 10 parts.
2. a kind of terylene cotton elastic according to claim 1 is knitted fabric dyeing, it is characterised in that: the step 1
In, padding temperature is 25 DEG C, and pick-up is 60 ~ 70%.
3. a kind of terylene cotton elastic according to claim 2 is knitted fabric dyeing, it is characterised in that:
The reduction cleaning liquid includes following composition:
Sodium hydroxide: 20g/L
85% sodium hydrosulfite 20g/L
(N-Boc-2- pyrrole radicals) dimethyl-silicon alkanol: 2g/L.
4. a kind of terylene cotton elastic according to claim 3 is knitted fabric dyeing, it is characterised in that:
Washing temperature is 40 DEG C in the step 6, and the time is 1 ~ 5 minute.
5. a kind of terylene cotton elastic according to claim 4 is knitted fabric dyeing, it is characterised in that:
It further include having bleeding agent 3g/L in the disperse dyes.
6. a kind of terylene cotton elastic according to claim 5 is knitted fabric dyeing, it is characterised in that:
The bleeding agent includes following weight parts composition:
3- [(methylol) methyl amine] propane sulfonic acid: 2 parts
Disecoctylmaleate sodium sulfonate: 10 parts
Hydroxy ethylene diphosphonic acid sylvite: 2 parts.