CN107022251A - Disposable net white carbon printing coating and preparation method thereof - Google Patents
Disposable net white carbon printing coating and preparation method thereof Download PDFInfo
- Publication number
- CN107022251A CN107022251A CN201710372234.2A CN201710372234A CN107022251A CN 107022251 A CN107022251 A CN 107022251A CN 201710372234 A CN201710372234 A CN 201710372234A CN 107022251 A CN107022251 A CN 107022251A
- Authority
- CN
- China
- Prior art keywords
- parts
- white carbon
- agent
- printing coating
- carbon printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to disposable net white carbon printing coating and preparation method thereof, described disposable net white carbon printing coating includes the raw material of following parts by weight：40 parts~50 parts of water, 0.1 part~0.2 part of cellulose, 3 parts~4 parts of organosilicon slipping agent, 0.15 part~0.2 part of bactericide, 0.2 part~0.3 part of dispersant, 0.15 part~0.2 part of wetting agent, 95 0.15 parts~0.2 part of multifunctional assistant AMP, 0.15 part~0.2 part of defoamer, 1 part~2 parts of antifreezing agent, 2 parts~3 parts of titanium dioxide, 2 parts~3 parts of aerosil, 8 parts~10 parts of diatomite, 10 parts~15 parts of nanometer calcium, 0.3 part~0.5 part of levelling agent, 15 parts~20 parts of 1.5 parts~2 parts of thickener and the net taste emulsion of purified petroleum benzin.The disposable net white carbon printing coating environmental protection of the present invention, preparation method is simple, is difficult to be infected with dust, saving washes the net time, improves efficiency of construction.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of disposable net white carbon printing coating and preparation method thereof.
Background technology
With the raising of expanding economy people's living standard and cultural quality, the art of indoor wall fitted up into when
Still, such as wall covering fabric, adherent picture, printed wallpaper flower.But wall paper, mural painting be it is viscous with glue, not environmentally, seam, easy alice, no
Set fire；Common wallpaper stamp material exist it is dry soon, easy network blocking, the shortcomings of decorative pattern is unintelligible, color is not vivid.
The content of the invention
It is an object of the present invention to propose a kind of disposable net white carbon printing coating.
The disposable net white carbon printing coating of the present invention, includes the raw material of following parts by weight：40 parts~50 parts of water, fiber
0.1 part~0.2 part of element, 3 parts~4 parts of organosilicon slipping agent, 0.15 part~0.2 part of bactericide, 0.2 part~0.3 part of dispersant, profit
0.15 part~0.2 part of humectant, 0.15 part~0.2 part of multifunctional assistant AMP-95,0.15 part~0.2 part of defoamer, antifreezing agent 1
Part~2 parts, 2 parts~3 parts of titanium dioxide, 2 parts~3 parts of aerosil, 8 parts~10 parts of diatomite, 10 parts~15 parts of nanometer calcium,
15 parts~20 parts of 0.3 part~0.5 part of levelling agent, 1.5 parts~2 parts of thickener and the net taste emulsion of purified petroleum benzin.
The disposable net white carbon printing coating environmental protection of the present invention, its preparation method is simple, easy construction, is difficult contamination
The net time is washed in dust, saving, substantially increases efficiency of construction, reduces cost of labor.
In addition, disposable net white carbon printing coating according to the above embodiment of the present invention, can also have what is added as follows
Technical characteristic：
As the preferred embodiment of the present invention, described disposable net white carbon printing coating, including following parts by weight
Raw material：40 parts of water, 0.2 part of cellulose, 3 parts of organosilicon slipping agent, 0.2 part of bactericide, 0.2 part of dispersant, wetting agent 0.2
Part, 0.15 part of multifunctional assistant AMP-95,0.2 part of defoamer, 1 part of antifreezing agent, 3 parts of titanium dioxide, 2 parts of aerosil, silicon
20 parts of 10 parts of diatomaceous earth, 10 parts of nanometer calcium, 0.3 part of levelling agent, 1.5 parts of thickener and the net taste emulsion of purified petroleum benzin.
As the preferred embodiment of the present invention, described disposable net white carbon printing coating, including following parts by weight
Raw material：50 parts of water, 0.1 part of cellulose, 4 parts of organosilicon slipping agent, 0.15 part of bactericide, 0.3 part of dispersant, wetting agent 0.15
Part, 0.2 part of multifunctional assistant AMP-95,0.15 part of defoamer, 2 parts of antifreezing agent, 2 parts of titanium dioxide, 3 parts of aerosil, silicon
15 parts of 8 parts of diatomaceous earth, 15 parts of nanometer calcium, 0.5 part of levelling agent, 2 parts of thickener and the net taste emulsion of purified petroleum benzin.
Further, the dispersant at least includes sodium tripolyphosphate, calgon, sodium pyrophosphate, triethyl group hexyl
Phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, cellulose derivative, polyacrylamide, guar gum and fatty acid polyethylene glycol ester
In one kind.
Further, the wetting agent at least includes ethanol, propane diols, glycerine, dimethyl sulfoxide (DMSO), linear alkyl benzene sulfonic acid
Sodium, sodium sulfate of polyethenoxy ether of fatty alcohol, AESA, sldium lauryl sulfate, lauroyl glutamate,
One kind in diglycollic amide glycerol stearate monoesters, lignosulfonates, heavy alkylbenzene sulfonate and alkylsulfonate.
Further, the defoamer at least includes silicone emulsion, polyoxyethylene, polyoxypropylene, pentaerythrite ether, polyoxy
One kind in propyl alcohol amidogen ether, polypropylene glycerol aether and dimethyl silicone polymer.
Further, the bactericide is bromo- 2- nitropropanes -1, the 3- glycol of 2-.
Further, the antifreezing agent is propane diols.
It is another object of the present invention to the preparation method for proposing described disposable net white carbon printing coating.
The preparation method of described disposable net white carbon printing coating, comprises the following steps：S101：The water is added first
Enter in stainless steel dispersion tank, be put into suspension type high speed dispersor；S102：Adjust the rotating speed of the dispersion machine to 350r/min~
450r/min, then by the cellulose, the organosilicon slipping agent, the bactericide, the dispersant, the antifreezing agent,
The wetting agent, the multifunctional assistant AMP-95 and the defoamer add the dispersion tank, then stir 10min~
20min；S103：The titanium dioxide, the aerosil, the diatomite and the nanometer calcium are added to described scattered
In machine, it is 550r/min~650r/min then to adjust rotating speed, stirs 25min~35min；S104：Adjust the dispersion machine
Then rotating speed adds after the net taste emulsion of the purified petroleum benzin, stirring 3min~8min to 250r/min~350r/min and filters and collect
Filtrate；S105：The thickener is added into the filtrate and the levelling agent is modulated into paste, disposable net white carbon print is obtained
Flower coating.
The additional aspect and advantage of the present invention will be set forth in part in the description, and will partly become from the following description
Obtain substantially, or recognized by the practice of the present invention.
Embodiment
Embodiments of the invention are described below in detail, the embodiment is exemplary, it is intended to for explaining the present invention, and
It is not considered as limiting the invention.
Embodiment 1
Embodiment 1 proposes a kind of disposable net white carbon printing coating, includes the raw material of following parts by weight：40 parts of water,
0.2 part of cellulose, 3 parts of organosilicon slipping agent, 0.2 part of the bromo- 2- nitropropanes -1,3- glycol of 2-, 0.2 part of sodium tripolyphosphate, third
1.2 parts of glycol, 0.15 part of multifunctional assistant AMP-95,0.2 part of silicone emulsion, 3 parts of titanium dioxide, 2 parts of aerosil, silicon
10 parts of diatomaceous earth, 10 parts of nanometer calcium, 0.3 part of levelling agent, 1.5 parts of polyacrylate alkali swelling type thickener and the net taste emulsion 20 of purified petroleum benzin
Part.
The preparation method of the disposable net white carbon printing coating of embodiment 1, comprises the following steps：
(1) water is added in stainless steel dispersion tank first, is put into suspension type high speed dispersor
(2) adjust the rotating speed of the dispersion machine to 350r/min, then by the cellulose, the organosilicon slipping agent,
The bromo- 2- nitropropanes -1,3- glycol of 2-, the sodium tripolyphosphate, the propane diols, the multifunctional assistant AMP-95 and
The silicone emulsion adds the dispersion tank, then stirs 20min.
(3) titanium dioxide, the aerosil, the diatomite and the nanometer calcium are added to described scattered
In machine, it is 550r/min then to adjust rotating speed, stirs 35min.
(4) rotating speed of the dispersion machine is adjusted to 250r/min, is then added after the net taste emulsion of the purified petroleum benzin, stirring 8min
Filter and collect filtrate.
(5) levelling agent is added into the filtrate and the thickener is modulated into paste, disposable net white carbon is obtained
Printing coating.
Embodiment 2
Embodiment 2 proposes a kind of disposable net white carbon printing coating, includes the raw material of following parts by weight：50 parts of water,
0.1 part of cellulose, 4 parts of organosilicon slipping agent, 0.15 part of the bromo- 2- nitropropanes -1,3- glycol of 2-, 0.3 part of methyl anyl alcohol, diformazan
0.15 part of base sulfoxide, 2 parts of propane diols, 0.2 part of multifunctional assistant AMP-95,0.15 part of polyoxyethylene, 2 parts of titanium dioxide, gas phase two
3 parts of silica, 8 parts of diatomite, 15 parts of nanometer calcium, 0.3 part of levelling agent, 2 parts of polyacrylate alkali swelling type thickener and purified petroleum benzin
Net 15 parts of taste emulsion.
The preparation method of the disposable net white carbon printing coating of embodiment 2, comprises the following steps：
(1) water is added in stainless steel dispersion tank first, is put into suspension type high speed dispersor
(2) adjust the rotating speed of the dispersion machine to 450r/min, then by the cellulose, the organosilicon slipping agent,
The bromo- 2- nitropropanes -1,3- glycol of 2-, the methyl anyl alcohol, the propane diols, the multifunctional assistant AMP-95, institute
State dimethyl sulfoxide (DMSO) and the polyoxyethylene adds the dispersion tank, then stir 10min.
(3) titanium dioxide, the aerosil, the diatomite and the nanometer calcium are added to described scattered
In machine, it is 650r/min then to adjust rotating speed, stirs 25min.
(4) rotating speed of the dispersion machine is adjusted to 350r/min, is then added after the net taste emulsion of the purified petroleum benzin, stirring 3min
Filter and collect filtrate.
(5) levelling agent is added into the filtrate and the thickener is modulated into paste, disposable net white carbon is obtained
Printing coating.
Embodiment 3
Embodiment 3 proposes a kind of disposable net white carbon printing coating, includes the raw material of following parts by weight：40 parts of water,
0.2 part of cellulose, 3 parts of organosilicon slipping agent, 0.2 part of bactericide, 0.2 part of polyacrylamide, 0.2 part of lauroyl glutamate,
0.2 part of polyoxypropylene, 1 part of propane diols, AMP-950.15 parts of multifunctional assistant, 3 parts of titanium dioxide, 2 parts of aerosil, diatom
10 parts of soil, 10 parts of nanometer calcium, 0.4 part of levelling agent, 1.5 parts of polyacrylate alkali swelling type thickener and the net taste emulsion 20 of purified petroleum benzin
Part.
The preparation method of the disposable net white carbon printing coating of embodiment 3, comprises the following steps：
(1) water is added in stainless steel dispersion tank first, is put into suspension type high speed dispersor
(2) adjust the rotating speed of the dispersion machine to 400r/min, then by the cellulose, the organosilicon slipping agent,
The bactericide, the polyacrylamide, the propane diols, the lauroyl glutamate, the multifunctional assistant AMP-95
The dispersion tank is added with the polyoxypropylene, 15min is then stirred.
(3) titanium dioxide, the aerosil, the diatomite and the nanometer calcium are added to described scattered
In machine, it is 600r/min then to adjust rotating speed, stirs 30min.
(4) rotating speed of the dispersion machine is adjusted to 300r/min, is then added after the net taste emulsion of the purified petroleum benzin, stirring 5min
Filter and collect filtrate.
(5) levelling agent is added into the filtrate and the thickener is modulated into paste, disposable net white carbon is obtained
Printing coating.
Embodiment 4
Embodiment 4 proposes a kind of disposable net white carbon printing coating, includes the raw material of following parts by weight：50 parts of water,
0.1 part of cellulose, 4 parts of organosilicon slipping agent, 0.15 part of bactericide, 0.3 part of sodium pyrophosphate, 0.15 part of sldium lauryl sulfate, season
Penta 4 0.15 part of alcohol ethers, 2 parts of propane diols, AMP-950.2 parts of multifunctional assistant, 2 parts of titanium dioxide, 3 parts of aerosil, diatom
15 parts of 8 parts of soil, 15 parts of nanometer calcium, 0.3 part of levelling agent, 2 parts of polyacrylate alkali swelling type thickener and the net taste emulsion of purified petroleum benzin.
The preparation method of the disposable net white carbon printing coating of embodiment 4, comprises the following steps：
(1) water is added in stainless steel dispersion tank first, is put into suspension type high speed dispersor
(2) adjust the rotating speed of the dispersion machine to 380r/min, then by the cellulose, the organosilicon slipping agent,
The bactericide, the propane diols, the multifunctional assistant AMP-95, the sodium pyrophosphate, the sldium lauryl sulfate and institute
State pentaerythrite ether and add the dispersion tank, then stir 13min.
(3) titanium dioxide, the aerosil, the diatomite and the nanometer calcium are added to described scattered
In machine, it is 580r/min then to adjust rotating speed, stirs 28min.
(4) rotating speed of the dispersion machine is adjusted to 270r/min, is then added after the net taste emulsion of the purified petroleum benzin, stirring 4min
Filter and collect filtrate.
(5) levelling agent is added into the filtrate and the thickener is modulated into paste, disposable net white carbon is obtained
Printing coating.
Embodiment 5
Embodiment 5 proposes a kind of disposable net white carbon printing coating, includes the raw material of following parts by weight：50 parts of water,
0.1 part of cellulose, 4 parts of organosilicon slipping agent, 0.15 part of bactericide, 1 part of propane diols, 0.15 part of multifunctional assistant AMP-95, fat
0.3 part of fat acid polyethylene glycol ester, 0.15 part of diglycollic amide glycerol stearate monoesters, 0.15 part of polypropylene glycerol aether, titanium white
2 parts of powder, 3 parts of aerosil, 8 parts of diatomite, 15 parts of nanometer calcium, 0.5 part of levelling agent, 2 parts of thickener and the net taste breast of purified petroleum benzin
15 parts of liquid.
The preparation method of the disposable net white carbon printing coating of embodiment 5, comprises the following steps：
(1) water is added in stainless steel dispersion tank first, is put into suspension type high speed dispersor
(2) adjust the rotating speed of the dispersion machine to 420r/min, then by the cellulose, the organosilicon slipping agent,
The bactericide, the fatty acid polyethylene glycol ester, the propane diols, the multifunctional assistant AMP-95, the diethanol acyl
Amine glycerol stearate monoesters and the polypropylene glycerol aether add the dispersion tank, then stir 18min.
(3) titanium dioxide, the aerosil, the diatomite and the nanometer calcium are added to described scattered
In machine, it is 620r/min then to adjust rotating speed, stirs 32min.
(4) rotating speed of the dispersion machine is adjusted to 320r/min, is then added after the net taste emulsion of the purified petroleum benzin, stirring 7min
Filter and collect filtrate.
(5) levelling agent is added into the filtrate and the thickener is modulated into paste, disposable net white carbon is obtained
Printing coating.
The disposable net white carbon printing coating environmental protection of the present invention, its preparation method is simple, easy construction, is difficult contamination
The net time is washed in dust, saving, substantially increases efficiency of construction, reduces cost of labor.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means to combine specific features, structure, material or the spy that the embodiment or example are described
Point is contained at least one embodiment of the present invention or example.In this manual, to the schematic representation of above-mentioned term not
Identical embodiment or example must be directed to.Moreover, specific features, structure, material or the feature of description can be with office
Combined in an appropriate manner in one or more embodiments or example.In addition, in the case of not conflicting, the skill of this area
Art personnel can be tied the not be the same as Example or the feature of example and non-be the same as Example or example described in this specification
Close and combine.
Although embodiments of the invention have been shown and described above, it is to be understood that above-described embodiment is example
Property, it is impossible to limitation of the present invention is interpreted as, one of ordinary skill in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, changed, replacing and modification.
Claims (9)
1. a kind of disposable net white carbon printing coating, it is characterised in that include the raw material of following parts by weight：Water 40 parts~50
Part, 0.1 part~0.2 part of cellulose, 3 parts~4 parts of organosilicon slipping agent, 0.15 part~0.2 part of bactericide, 0.2 part of dispersant~
0.3 part, 0.15 part~0.2 part of wetting agent, 0.15 part~0.2 part of multifunctional assistant AMP-95,0.15 part~0.2 part of defoamer,
1 part~2 parts of antifreezing agent, 2 parts~3 parts of titanium dioxide, 2 parts~3 parts of aerosil, 8 parts~10 parts of diatomite, 10 parts of nanometer calcium
15 parts~20 parts of~15 parts, 0.3 part~0.5 part of levelling agent, 1.5 parts~2 parts of thickener and the net taste emulsion of purified petroleum benzin.
2. disposable net white carbon printing coating according to claim 1, it is characterised in that include the original of following parts by weight
Material：It is 40 parts of water, 0.2 part of cellulose, 3 parts of organosilicon slipping agent, 0.2 part of bactericide, 0.2 part of dispersant, 0.2 part of wetting agent, many
0.15 part of function additive AMP-95,0.2 part of defoamer, 1 part of antifreezing agent, 3 parts of titanium dioxide, 2 parts of aerosil, diatomite
20 parts of 10 parts, 10 parts of nanometer calcium, 0.3 part of levelling agent, 1.5 parts of thickener and the net taste emulsion of purified petroleum benzin.
3. disposable net white carbon printing coating according to claim 1, it is characterised in that include the original of following parts by weight
Material：50 parts of water, 0.1 part of cellulose, 4 parts of organosilicon slipping agent, 0.15 part of bactericide, 0.3 part of dispersant, 0.15 part of wetting agent,
0.2 part of multifunctional assistant AMP-95,0.15 part of defoamer, 2 parts of antifreezing agent, 2 parts of titanium dioxide, 3 parts of aerosil, diatom
15 parts of 8 parts of soil, 15 parts of nanometer calcium, 0.5 part of levelling agent, 2 parts of thickener and the net taste emulsion of purified petroleum benzin.
4. the disposable net white carbon printing coating according to claim any one of 1-3, it is characterised in that the dispersant is extremely
Less include sodium tripolyphosphate, calgon, sodium pyrophosphate, triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol,
One kind in cellulose derivative, polyacrylamide, guar gum and fatty acid polyethylene glycol ester.
5. the disposable net white carbon printing coating according to claim any one of 1-3, it is characterised in that the wetting agent is extremely
Include ethanol, propane diols, glycerine, dimethyl sulfoxide (DMSO), sodium n-alkylbenzenesulfonate, sodium sulfate of polyethenoxy ether of fatty alcohol, fat less
Fat alcohol polyoxyethylene ether ammonium sulfate, sldium lauryl sulfate, lauroyl glutamate, diglycollic amide glycerol stearate monoesters, wood
One kind in mahogany sulfonate, heavy alkylbenzene sulfonate and alkylsulfonate.
6. the disposable net white carbon printing coating according to claim any one of 1-3, it is characterised in that the defoamer is extremely
Include silicone emulsion, polyoxyethylene, polyoxypropylene, pentaerythrite ether, polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and poly- two less
One kind in methylsiloxane.
7. the disposable net white carbon printing coating according to claim any one of 1-3, it is characterised in that the bactericide is
The bromo- 2- nitropropanes -1,3- glycol of 2-.
8. the disposable net white carbon printing coating according to claim any one of 1-3, it is characterised in that the antifreezing agent is
Propane diols.
9. the preparation method of the disposable net white carbon printing coating described in claim any one of 1-8, it is characterised in that including such as
Lower step：
S101：The water is added in stainless steel dispersion tank first, is put into suspension type high speed dispersor；
S102：The rotating speed of the dispersion machine is adjusted to 350r/min~450r/min, then by the cellulose, the organosilicon
Slipping agent, the bactericide, the dispersant, the antifreezing agent, the wetting agent, the multifunctional assistant AMP-95 and described
Defoamer adds the dispersion tank, then stirs 10min~20min；
S103：The titanium dioxide, the aerosil, the diatomite and the nanometer calcium are added to the dispersion machine
In, it is 550r/min~650r/min then to adjust rotating speed, stirs 25min~35min；
S104：The rotating speed of the dispersion machine is adjusted to 250r/min~350r/min, the net taste emulsion of the purified petroleum benzin is then added, stirs
Mix and filtrate is filtered and collected after 3min~8min；
S105：The thickener is added into the filtrate and the levelling agent is modulated into paste, disposable net white carbon print is obtained
Flower coating.