CN107022187A - A kind of compound polyurethane material of waterproof and its preparation method and application - Google Patents
A kind of compound polyurethane material of waterproof and its preparation method and application Download PDFInfo
- Publication number
- CN107022187A CN107022187A CN201710167805.9A CN201710167805A CN107022187A CN 107022187 A CN107022187 A CN 107022187A CN 201710167805 A CN201710167805 A CN 201710167805A CN 107022187 A CN107022187 A CN 107022187A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyurethane
- mixed
- dibutyltin diacetate
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of compound polyurethane material of waterproof and its preparation method and application, the material is made up of the raw material below according to parts by weight:33 41 parts of polyurethane, 5 12 parts of dibutyltin diacetate, 37 parts of propylene glycol monomethyl ether, 11 19 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, 8 16 parts of cellulose acetate.The present invention is modified using dibutyltin diacetate, propylene glycol monomethyl ether to polyurethane, then mixed with 1-hydroxy ethylidene-1,1-diphosphonic acid with cellulose acetate, ultrasonically treated rear obtained material has longer working life and higher tensile strength, elongation at break and adhesive force, and with excellent impermeability and resistance to ag(e)ing.The present invention is few using raw material, and preparation technology is extremely simple, cost reduction, suitable for use of large-scale production.Easy construction of the present invention;The present invention can be used directly out of doors, and can reach preferably waterproof effect in the case where gross thickness is no more than 100 μm.
Description
Technical field
The present invention relates to field of material technology, specifically a kind of compound polyurethane material of waterproof and preparation method thereof and should
With.
Background technology
Waterproof layer is the important technical for improving the structure durabilities such as bridge pavement.China's concrete-bridge bridge deck water-proof
Three kinds of waterproof layer patterns are defined in layer standard TB/T2965-2011, are respectively:Coiled material adds affixing coating(Or adhesive)Type,
High-polymer modified pitch coiled material type and the coating type without coiled material.First two waterproof layer is used on bridge within protecting wall, and the third is prevented
Water layer is used for beyond protecting wall.These three waterproof layers exposed can not be used, it is necessary to cover 40-60mm admixture third in the above
The C40 pea gravel concreten protective layers of olefin(e) acid nitrile fiber or polypropylene fiber net.At present, usually using polyurea water-proof material, this is prevented
Although water material exposed can be used, tack is poor, the diseases such as discoloration, cracking and large area peeling easily occurs, so as to rise
Less than due waterproof action.Polyurethane high molecule material is due to its peculiar structure and performance, and designability is strong, can extensive use
With every field, with important researching value and wide application prospect.Made although also having in the prior art using polyurethane
For raw material, but its obtained product is more using raw material, prepares complicated, and cost is high, is unsuitable for large-scale use.
The content of the invention
It is an object of the invention to provide a kind of compound polyurethane material of waterproof and its preparation method and application, to solve
The problem of being proposed in above-mentioned background technology.
To achieve the above object, the present invention provides following technical scheme:
A kind of compound polyurethane material of waterproof, is made up of the raw material below according to parts by weight:33-41 parts of polyurethane, two acetic acid
5-12 parts of dibutyl tin, 3-7 parts of propylene glycol monomethyl ether, 11-19 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, 8-16 parts of cellulose acetate.
It is used as further scheme of the invention:The compound polyurethane material of the waterproof, by below according to the original of parts by weight
Material composition:35-39 parts of polyurethane, 7-10 parts of dibutyltin diacetate, 4-6 parts of propylene glycol monomethyl ether, 1-hydroxy ethylidene-1,1-diphosphonic acid 13-17
Part, 10-14 parts of cellulose acetate.
It is used as further scheme of the invention:The compound polyurethane material of the waterproof, by below according to the original of parts by weight
Material composition:37 parts of polyurethane, 8 parts of dibutyltin diacetate, 5 parts of propylene glycol monomethyl ether, 15 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, acetate fiber
12 parts of element.
A kind of preparation method of the compound polyurethane material of waterproof, is comprised the steps of:
1)12.5 times of deionized water of dibutyltin diacetate and its quality is mixed, dibutyltin diacetate solution is made;Will
Polyurethane is crushed, crosses 120 mesh sieves, is then mixed with dibutyltin diacetate solution, is heated to 86 DEG C of stir process 1.6h, then
65 DEG C are cooled to, and adds propylene glycol monomethyl ether, and the stir process 65min at a temperature of 65 DEG C, modified polyurethane is made;
2)1-hydroxy ethylidene-1,1-diphosphonic acid is mixed with cellulose acetate, 71 DEG C and at such a temperature stir process are then heated to
18min, is made mixed material;
3)Mixed material is mixed with modified polyurethane, then the ultrasonically treated 38min at a temperature of 56 DEG C, is down to room temperature and produces
Compound polyurethane material.
Another object of the present invention is to provide application of the compound polyurethane material in underwater paint.
Compared with prior art, the beneficial effects of the invention are as follows:
The present invention is modified using dibutyltin diacetate, propylene glycol monomethyl ether to polyurethane, then with 1-hydroxy ethylidene-1,1-diphosphonic acid
Mixed with cellulose acetate, ultrasonically treated rear obtained material is stretched with longer working life and higher tensile strength, fracture
Long rate and adhesive force, and with excellent impermeability and resistance to ag(e)ing.The present invention is few using raw material, and preparation technology is extremely simple
It is single, cost reduction, suitable for use of large-scale production.The present invention can be coated on concrete by way of spraying, brushing or roller coating
Bridge floor, can be constructed using plurality of devices, be easy to staff to select suitable construction equipment according to actual conditions, be more convenient for
Use;The present invention can be used directly out of doors, and can reach preferably waterproof effect in the case where gross thickness is no more than 100 μm
Really.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of compound polyurethane material of waterproof is made up of the raw material below according to parts by weight:Polyurethane
33 parts, 5 parts of dibutyltin diacetate, 3 parts of propylene glycol monomethyl ether, 11 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, 8 parts of cellulose acetate.
12.5 times of deionized water of dibutyltin diacetate and its quality is mixed, dibutyltin diacetate solution is made;
Polyurethane is crushed, 120 mesh sieves are crossed, is then mixed with dibutyltin diacetate solution, is heated to 86 DEG C of stir process 1.6h, so
After be cooled to 65 DEG C, and add propylene glycol monomethyl ether, and the stir process 65min at a temperature of 65 DEG C, modified polyurethane be made.Will
1-hydroxy ethylidene-1,1-diphosphonic acid is mixed with cellulose acetate, then heats to 71 DEG C and at such a temperature stir process 18min, is made mixed
Compound material.Mixed material is mixed with modified polyurethane, then the ultrasonically treated 38min at a temperature of 56 DEG C, is down to room temperature i.e.
Obtain compound polyurethane material.
Embodiment 2
In the embodiment of the present invention, a kind of compound polyurethane material of waterproof is made up of the raw material below according to parts by weight:Polyurethane
41 parts, 12 parts of dibutyltin diacetate, 7 parts of propylene glycol monomethyl ether, 19 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, 16 parts of cellulose acetate.
12.5 times of deionized water of dibutyltin diacetate and its quality is mixed, dibutyltin diacetate solution is made;
Polyurethane is crushed, 120 mesh sieves are crossed, is then mixed with dibutyltin diacetate solution, is heated to 86 DEG C of stir process 1.6h, so
After be cooled to 65 DEG C, and add propylene glycol monomethyl ether, and the stir process 65min at a temperature of 65 DEG C, modified polyurethane be made.Will
1-hydroxy ethylidene-1,1-diphosphonic acid is mixed with cellulose acetate, then heats to 71 DEG C and at such a temperature stir process 18min, is made mixed
Compound material.Mixed material is mixed with modified polyurethane, then the ultrasonically treated 38min at a temperature of 56 DEG C, is down to room temperature i.e.
Obtain compound polyurethane material.
Embodiment 3
In the embodiment of the present invention, a kind of compound polyurethane material of waterproof is made up of the raw material below according to parts by weight:Polyurethane
35 parts, 7 parts of dibutyltin diacetate, 4 parts of propylene glycol monomethyl ether, 13 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, 10 parts of cellulose acetate.
12.5 times of deionized water of dibutyltin diacetate and its quality is mixed, dibutyltin diacetate solution is made;
Polyurethane is crushed, 120 mesh sieves are crossed, is then mixed with dibutyltin diacetate solution, is heated to 86 DEG C of stir process 1.6h, so
After be cooled to 65 DEG C, and add propylene glycol monomethyl ether, and the stir process 65min at a temperature of 65 DEG C, modified polyurethane be made.Will
1-hydroxy ethylidene-1,1-diphosphonic acid is mixed with cellulose acetate, then heats to 71 DEG C and at such a temperature stir process 18min, is made mixed
Compound material.Mixed material is mixed with modified polyurethane, then the ultrasonically treated 38min at a temperature of 56 DEG C, is down to room temperature i.e.
Obtain compound polyurethane material.
Embodiment 4
In the embodiment of the present invention, a kind of compound polyurethane material of waterproof is made up of the raw material below according to parts by weight:Polyurethane
39 parts, 10 parts of dibutyltin diacetate, 6 parts of propylene glycol monomethyl ether, 17 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, 14 parts of cellulose acetate.
12.5 times of deionized water of dibutyltin diacetate and its quality is mixed, dibutyltin diacetate solution is made;
Polyurethane is crushed, 120 mesh sieves are crossed, is then mixed with dibutyltin diacetate solution, is heated to 86 DEG C of stir process 1.6h, so
After be cooled to 65 DEG C, and add propylene glycol monomethyl ether, and the stir process 65min at a temperature of 65 DEG C, modified polyurethane be made.Will
1-hydroxy ethylidene-1,1-diphosphonic acid is mixed with cellulose acetate, then heats to 71 DEG C and at such a temperature stir process 18min, is made mixed
Compound material.Mixed material is mixed with modified polyurethane, then the ultrasonically treated 38min at a temperature of 56 DEG C, is down to room temperature i.e.
Obtain compound polyurethane material.
Embodiment 5
In the embodiment of the present invention, a kind of compound polyurethane material of waterproof is made up of the raw material below according to parts by weight:Polyurethane
37 parts, 8 parts of dibutyltin diacetate, 5 parts of propylene glycol monomethyl ether, 15 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, 12 parts of cellulose acetate.
12.5 times of deionized water of dibutyltin diacetate and its quality is mixed, dibutyltin diacetate solution is made;
Polyurethane is crushed, 120 mesh sieves are crossed, is then mixed with dibutyltin diacetate solution, is heated to 86 DEG C of stir process 1.6h, so
After be cooled to 65 DEG C, and add propylene glycol monomethyl ether, and the stir process 65min at a temperature of 65 DEG C, modified polyurethane be made.Will
1-hydroxy ethylidene-1,1-diphosphonic acid is mixed with cellulose acetate, then heats to 71 DEG C and at such a temperature stir process 18min, is made mixed
Compound material.Mixed material is mixed with modified polyurethane, then the ultrasonically treated 38min at a temperature of 56 DEG C, is down to room temperature i.e.
Obtain compound polyurethane material.
Comparative example 1
Except by it is ultrasonically treated change stir process into addition to, remaining material content and step are consistent with embodiment 5.
Above-described embodiment 1-5 material is subjected to performance test, as a result as shown in table 1.
Table 1
The thickness of the present embodiment material is just covers basal plane completely, and thickness is 100 μm.As seen from Table 1,1-5 of the embodiment of the present invention
The material prepared using present invention process has longer working life and higher tensile strength, elongation at break and adhesive force,
And with excellent impermeability and resistance to ag(e)ing.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It may be appreciated other embodiment.
Claims (5)
1. a kind of compound polyurethane material of waterproof, it is characterised in that be made up of the raw material below according to parts by weight:Polyurethane
33-41 parts, 5-12 parts of dibutyltin diacetate, 3-7 parts of propylene glycol monomethyl ether, 11-19 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, cellulose acetate
8-16 parts.
2. the compound polyurethane material of waterproof according to claim 1, it is characterised in that by below according to the original of parts by weight
Material composition:35-39 parts of polyurethane, 7-10 parts of dibutyltin diacetate, 4-6 parts of propylene glycol monomethyl ether, 1-hydroxy ethylidene-1,1-diphosphonic acid 13-17
Part, 10-14 parts of cellulose acetate.
3. the compound polyurethane material of waterproof according to claim 1, it is characterised in that by below according to the original of parts by weight
Material composition:37 parts of polyurethane, 8 parts of dibutyltin diacetate, 5 parts of propylene glycol monomethyl ether, 15 parts of 1-hydroxy ethylidene-1,1-diphosphonic acid, acetate fiber
12 parts of element.
4. a kind of preparation method of the compound polyurethane material of waterproof as described in claim 1-3 is any, it is characterised in that by
Following steps are constituted:
1)12.5 times of deionized water of dibutyltin diacetate and its quality is mixed, dibutyltin diacetate solution is made;Will
Polyurethane is crushed, crosses 120 mesh sieves, is then mixed with dibutyltin diacetate solution, is heated to 86 DEG C of stir process 1.6h, then
65 DEG C are cooled to, and adds propylene glycol monomethyl ether, and the stir process 65min at a temperature of 65 DEG C, modified polyurethane is made;
2)1-hydroxy ethylidene-1,1-diphosphonic acid is mixed with cellulose acetate, 71 DEG C and at such a temperature stir process are then heated to
18min, is made mixed material;
3)Mixed material is mixed with modified polyurethane, then the ultrasonically treated 38min at a temperature of 56 DEG C, is down to room temperature and produces
Compound polyurethane material.
5. application of the compound polyurethane material as described in claim 1-3 is any in underwater paint.