CN107021599A - A kind of sludge solidifying agent - Google Patents
A kind of sludge solidifying agent Download PDFInfo
- Publication number
- CN107021599A CN107021599A CN201710403159.1A CN201710403159A CN107021599A CN 107021599 A CN107021599 A CN 107021599A CN 201710403159 A CN201710403159 A CN 201710403159A CN 107021599 A CN107021599 A CN 107021599A
- Authority
- CN
- China
- Prior art keywords
- solidifying agent
- sludge
- sludge solidifying
- polyacrylamide
- sodium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sludge solidifying agent, it is characterised in that the sludge solidifying agent is mixed by two or three of component in polyacrylamide, anhydrous sodium sulfate, magnesia, calcium oxide;Wherein, the sludge solidifying agent is pressed:The weight proportion mixing of polyacrylamide 20% 80% and anhydrous sodium sulfate 20% 80%;Or, sludge solidifying agent is pressed:The weight proportion mixing of polyacrylamide 20% 50%, anhydrous sodium sulfate 30% 70% and magnesia 10% 20%;Or, sludge solidifying agent is pressed:The weight proportion mixing of polyacrylamide 20% 70%, anhydrous sodium sulfate 20% 60% and calcium oxide 10% 20%;Or, sludge solidifying agent is pressed:The weight proportion mixing of polyacrylamide 20% 70%, magnesia 20% 70% and calcium oxide 10%.The present invention is easy to use, does not return water after solidification sludge impermeable;It is with low cost, it is adapted to use in the large-scale sludge handling process for building base and sewage treatment plant of repairing the roads.
Description
Technical field
The present invention relates to environmental technology field, and in particular to a kind of sludge solidifying agent.
Background technology
When building subway, tunnel and mining area construction, shield machine can excavate the higher sludge of moisture content, its moisture content
Calcium, magnesium ion content are exceeded in 30%-60% or so, and sludge.At present, the sludge solidifying agent of in the market enters to this sludge
Effect is all undesirable during row solidification, and has that cost is too high, hardening time is short, be difficult to control to and pollute larger etc. ask
Topic.Therefore need a kind of cost badly controllable, prepare simple, solidification effect is good and sludge solidifying agent of environmental protection.
The content of the invention
For problems of the prior art, it is an object of the invention to provide one kind moisture content can be made high, calcium, magnesium from
The sludge of sub- content overproof realizes the sludge solidifying agent for not returning water after solidification, and solidification in a short time.
To achieve the above object, concrete technical scheme of the invention is:
A kind of sludge solidifying agent, the sludge solidifying agent is in polyacrylamide, anhydrous sodium sulfate, magnesia, calcium oxide
Two or three of component is mixed;Wherein,
The sludge solidifying agent is pressed:Polyacrylamide 20%-80% and anhydrous sodium sulfate 20%-80% weight proportion are mixed
Close;Or,
Sludge solidifying agent is pressed:Polyacrylamide 20%-50%, anhydrous sodium sulfate 30%-70% and magnesia 10%-20%
Weight proportion mixing;Or,
Sludge solidifying agent is pressed:Polyacrylamide 20%-70%, anhydrous sodium sulfate 20%-60% and calcium oxide 10%-20%
Weight proportion mixing;Or,
Sludge solidifying agent is pressed:Polyacrylamide 20%-70%, magnesia 20%-70% and calcium oxide 10% weight are matched somebody with somebody
Than mixing.
Further,
Technical scheme has the advantages that:Instant component is easily obtained, and it is easy to prepare, by each component
It is made by certain percentage by weight stirring, it is easy to use, water is not returned after solidification sludge impermeable;It is with low cost, it is adapted to big rule
Used in the sludge handling process for building base and sewage treatment plant of repairing the roads of mould, 50% soil and 50% water system can also be will be equivalent to
Into mixing mud weight one thousandth to 5/1000ths sludge solidifying agent add mixing mud in be used for block coal seam
Mining area goaf, can both ensure the mobility at initial stage, can fill up goaf solidify afterwards completely again, oxygen is added in the application
When changing magnesium and calcium oxide, the also effect with improved soil, with very strong practicality.
Embodiment
The present invention is more fully illustrated below with embodiment.The present invention can be presented as a variety of multi-forms,
It is not construed as the exemplary embodiment for being confined to describe here.
Embodiment 1:
A kind of sludge solidifying agent, weighs the anhydrous sulphur of each raw material, the polyacrylamide of 2 parts by weight and 8 parts by weight respectively
Sour sodium, it is well mixed to can obtain the sludge solidifying agent.
In use, being stood after sludge solidifying agent and sludge are mixed.
Embodiment 2:
A kind of sludge solidifying agent, weighs the anhydrous sulphur of each raw material, the polyacrylamide of 8 parts by weight and 2 parts by weight respectively
Sour sodium, it is well mixed to can obtain the sludge solidifying agent.
Embodiment 3:
A kind of sludge solidifying agent, weighs each raw material, the polyacrylamide of 5 parts by weight, the anhydrous sodium sulfate of 3 parts by weight respectively
And 2 parts by weight magnesia, it is well mixed to can obtain the sludge solidifying agent.
Embodiment 4:
A kind of sludge solidifying agent, weighs each raw material, the polyacrylamide of 2 parts by weight, the anhydrous sodium sulfate of 7 parts by weight respectively
And 1 parts by weight magnesia, it is well mixed to can obtain the sludge solidifying agent.
Embodiment 5:
A kind of sludge solidifying agent, weighs each raw material, the polyacrylamide of 2 parts by weight, the anhydrous sodium sulfate of 6 parts by weight respectively
And 2 parts by weight calcium oxide, it is well mixed to can obtain the sludge solidifying agent.
Embodiment 6:
A kind of sludge solidifying agent, weighs each raw material, the polyacrylamide of 7 parts by weight, the anhydrous sodium sulfate of 2 parts by weight respectively
And 1 parts by weight calcium oxide, it is well mixed to can obtain the sludge solidifying agent.
Embodiment 7:
A kind of sludge solidifying agent, weighs each raw material respectively, the polyacrylamide of 2 parts by weight, the magnesia of 7 parts by weight and
The calcium oxide of 1 parts by weight, it is well mixed to can obtain the sludge solidifying agent.
Embodiment 8:
A kind of sludge solidifying agent, weighs each raw material respectively, the polyacrylamide of 7 parts by weight, the magnesia of 2 parts by weight and
The calcium oxide of 1 parts by weight, it is well mixed to can obtain the sludge solidifying agent.
Above-mentioned example is only intended to the explanation present invention, in addition, also a variety of different embodiments, and these are implemented
Mode be all those skilled in the art after comprehension inventive concept it is also envisioned that therefore, will not enumerate herein.
Claims (1)
1. a kind of sludge solidifying agent, it is characterised in that the sludge solidifying agent is by polyacrylamide, anhydrous sodium sulfate, magnesia, oxygen
Two or three of the component changed in calcium is mixed;Wherein,
The sludge solidifying agent is pressed:Polyacrylamide 20%-80% and anhydrous sodium sulfate 20%-80% weight proportion mixing;
Or,
Sludge solidifying agent is pressed:Polyacrylamide 20%-50%, anhydrous sodium sulfate 30%-70% and magnesia 10%-20% weight
Amount proportioning mixing;Or,
Sludge solidifying agent is pressed:Polyacrylamide 20%-70%, anhydrous sodium sulfate 20%-60% and calcium oxide 10%-20% weight
Amount proportioning mixing;Or,
Sludge solidifying agent is pressed:Polyacrylamide 20%-70%, magnesia 20%-70% and calcium oxide 10% weight proportion are mixed
Close.