CN107020580A - A kind of artificial stone honeycomb is ground material - Google Patents
A kind of artificial stone honeycomb is ground material Download PDFInfo
- Publication number
- CN107020580A CN107020580A CN201710426792.2A CN201710426792A CN107020580A CN 107020580 A CN107020580 A CN 107020580A CN 201710426792 A CN201710426792 A CN 201710426792A CN 107020580 A CN107020580 A CN 107020580A
- Authority
- CN
- China
- Prior art keywords
- mass percent
- artificial stone
- filler
- grinding
- stone honeycomb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Material is ground the invention discloses a kind of artificial stone honeycomb, its each component and mass percent are as follows：Resin：Melamine resin 30%~40%；Diamond 15%~25%；Carborundum 5%~15%；The filler 25%~45% of white fused alumina 5%~10%.The present invention is by changing grinding material composition so that artificial stone honeycomb grinding anti-wear performance, sharpness, stability, mechanical strength and performance are significantly increased.
Description
Technical field
The present invention relates to the technical field of artificial quartz in lump, the small narrow boards polishing processing of artificial hilllock stone semi-finished product, and in particular to
The artificial stone honeycomb grinding that a kind of service life is greatly prolonged.
Background technology
A kind of new composite that artificial stone is made up of resin, filler, pigment and curing agent etc..Compared to natural stone
The traditional construction materials such as material, ceramics, artificial stone is not only vdiverse in function, and various colors, application is also more extensive.Artificial stone is nontoxic
Property, it is "dead", it is fire-retardant, not viscous oil, not permeable dirt, antibacterial and mouldproof, wear-resisting, impact resistance, easily maintenance, it is seamless spliced.
Therefore, artificial stone industry development rapidly, has also driven the development of artificial stone machining tool, processing mode in recent years
It is intended to mechanization, automation.
The main processing artificial stone half-finished product plate of artificial stone honeycomb grinding, this sheet material is cut down from the big plate of artificial stone
, surface is polished by artificial stone metal Bradley, resin Bradley and poliss, simply side cut through by saw blade, it is necessary to
Polish sawing face using the grinding of artificial stone honeycomb, make sawing face have with surface as glossiness, honeycomb has been ground
Finish and be no longer needed for grinding and polishing.
But at present, the common grinding that in the market is used mostly in actual use, is used in manual grinding machine,
The mode of grinding is linear contact lay, and sharpness is poor, and processing efficiency is low, and wearability is weak, short life, the upper equation of light.In the market does not go out also
Existing specialty is directed to the grinding of artificial stone streamline processing.
Therefore, the present inventor makes further research to this, develops a kind of artificial stone honeycomb grinding material, and thus this case produces
It is raw.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of artificial stone honeycomb grinding material, by changing grinding material
Expect composition so that artificial stone honeycomb grinding anti-wear performance, sharpness, stability, mechanical strength and performance are significantly increased,
Using with artificial stone production line machinery, service life greatly prolongs, and polishing effect is good, and grinding and polishing continuity is strong, and efficiency is significantly improved.
In order to solve the above technical problems, the technical solution of the present invention is：
A kind of artificial stone honeycomb is ground material, and its each component and mass percent are as follows：
Further, filler is the one or more in zinc oxide, calcium carbonate, aluminum oxide and nylon powder.
Further, filler is zinc oxide, mass percent 5%~10%；Calcium carbonate, mass percent 5%~10%；Oxygen
Change aluminium, mass percent 7%~15%；Nylon powder, mass percent 10%~15%.
Further, the material, its each component and mass percent are as follows：Resin is melamine resin 40%, diamond
15%, carborundum 5%, white fused alumina 6%, filler 34%, wherein, filler is zinc oxide, and mass percent is 5%, and carbonic acid is calcareous
It is 5% to measure percentage, and nylon powder mass percent is 10%, and quality of alumina percentage is 14%.
Further, the material, its each component and mass percent are as follows：Resin is melamine resin 30%, diamond
12%, carborundum 15%, white fused alumina 8%, filler 35%, wherein, filler is zinc oxide, and mass percent is 10%, nylon powder
Mass percent is 15%, and quality of alumina percentage is 10%.
Further, diamond grit is 100#~1500#.
Wide compared to the big long 1.5m of plate 3m of artificial stone that artificial stone resin Bradley is ground, honeycomb grinding grinding is small in the present invention
Narrow boards is height 4cm or so after the big plate of artificial stone is cut by metal saw blade, width 2cm or so, and length is not limited, because chi
It is very little too small, so grinding grinding and polishing can only be used.Honeycomb grinding is used on automatic machine, and grinding method is face contact grinding, and
Grinding efficiency is high, it requires that honeycomb grinding must have very high sharpness and preferable polishing effect.
After such scheme, general, the abrasive material lower by 10% or so than being commonly ground of honeycomb grinding resin ratio of the invention
Consumption (diamond+white fused alumina+carborundum) can be higher by 15% or so than being commonly ground, and increases the fragility of carcass and the concentration of abrasive material,
Sharpness and luminosity are improved, hollow honeycomb type is made in structure, product can be improved when grinding contacts grinding with sheet side
Sharpness, hollow honeycomb can store water when being ground, and can take away the heat that grinding is produced, and prevent from burning plate.In people
In terms of the polishing effect for making stone, the product luminosity of in the market can only achieve 40~45 degree, and the product luminosity of the present invention can reach
50~55 degree, advantage is apparent.
Embodiment
With reference to specific embodiment, the invention will be further described.Disclosed is a kind of artificial stone honeycomb
Material is ground, because artificial stone is made up of resin, filler, pigment and curing agent etc., because the presence of resin causes artificial stone plate
Material can be softer compared to lithotome, and good toughness, hardness are low, therefore should select the preferable work of sharpness when processing grinding
Tool, it is to avoid produce the problem of burning plate, plate face poor definition in grinding.
Therefore, we select melamine resin, and melamine resin is pure white, is not dyed during grinding and polishing, are lived with larger chemistry
Property, very high adhesive strength, and carcass itself is more crisp, sharpness is especially good during grinding and polishing, is conducive to improving the definition of burnishing surface,
Melamine resin weight, 30%~40%, can give play to sharp characteristic, can increase abrasion resistance again than control.
Diamond is main abrasive material, plays maximum ablation, expensive, mass percent 15%~25%, Buddha's warrior attendant
Stone ratio is bigger, can reach more preferable ground effect.In the present embodiment, diamond grit is 100#~1500#.
Carborundum is in irregular shape, relatively more crisp, and sword is gone out during grinding and polishing soon, the abrasive material of auxiliary diamond, mass percent is used as
5%~15%, can play strengthens sharp effect.
White fused alumina shape is more regular, mass percent 5%~10%, and it can increase the abrasion resistance of chamfering wheel.
Filler accounting 25%~45%, strengthens the performance of carcass each side.
Filler is specifically comprising as follows：Zinc oxide is auxiliary glazing materia, and can increase product abrasion resistance, mass percent
5%~10%.Calcium carbonate can improve sharpness, cheap, reduce production cost, mass percent 5%~10%.Aluminum oxide
For reinforcing material, increase bonding agent intensity and abrasion resistance, mass percent 7%~15%.Nylon powder is toughening material, increase knot
The toughness and impact strength of mixture, mass percent 10%~15%.Embodiment one
In the present embodiment, its each component and mass percent are as follows：
Wherein, filler is zinc oxide, and mass percent is 5%, and calcium carbonate mass percent is 5%, nylon powder quality hundred
Divide than being 10%, quality of alumina percentage is 14%.
Embodiment two
In the present embodiment, its each component and mass percent are as follows：
Wherein, filler is zinc oxide, and mass percent is 10%, and nylon powder mass percent is 15%, quality of alumina
Percentage is 10%.
Embodiment three
In the present embodiment, its each component and mass percent are as follows：
Wherein, filler is zinc oxide, and mass percent is 8%, and calcium carbonate mass percent is 5%, nylon powder quality hundred
Divide than being 10%, quality of alumina percentage is 7%.
The above described is only a preferred embodiment of the present invention, be not intended to limit the scope of the present invention,
Therefore the change or modification that claim under this invention and specification are done in every case, it should all belong to the scope that patent of the present invention covers
Within.
Claims (6)
1. a kind of artificial stone honeycomb is ground material, it is characterised in that：Its each component and mass percent are as follows：
。
2. a kind of artificial stone honeycomb grinding material according to claim 1, it is characterised in that：Filler is zinc oxide, carbonic acid
One or more in calcium, aluminum oxide and nylon powder.
3. a kind of artificial stone honeycomb grinding material according to claim 2, it is characterised in that：Filler is zinc oxide, quality
Percentage 5%~10%；Calcium carbonate, mass percent 5%~10%；Aluminum oxide, mass percent 7%~15%；Nylon powder,
Mass percent 10%~15%.
4. a kind of artificial stone honeycomb grinding material according to claim 3, it is characterised in that：The material, its each component
And mass percent is as follows：Resin be melamine resin 40%, diamond 15%, carborundum 5%, white fused alumina 6%, filler 34%,
Wherein, filler is zinc oxide, and mass percent is 5%, and calcium carbonate mass percent is 5%, and nylon powder mass percent is
10%, quality of alumina percentage is 14%.
5. a kind of artificial stone honeycomb grinding material according to claim 3, it is characterised in that：The material, its each component
And mass percent is as follows：Resin be melamine resin 30%, diamond 12%, carborundum 15%, white fused alumina 8%, filler 35%,
Wherein, filler is zinc oxide, and mass percent is 10%, and nylon powder mass percent is 15%, and quality of alumina percentage is
10%.
6. a kind of artificial stone honeycomb grinding material according to claim 1 to 5 any one, it is characterised in that：Diamond
Granularity is 100#~1500#.