CN107012582A - A kind of processing method of high-strength polyethylene twist net slice - Google Patents
A kind of processing method of high-strength polyethylene twist net slice Download PDFInfo
- Publication number
- CN107012582A CN107012582A CN201710390579.0A CN201710390579A CN107012582A CN 107012582 A CN107012582 A CN 107012582A CN 201710390579 A CN201710390579 A CN 201710390579A CN 107012582 A CN107012582 A CN 107012582A
- Authority
- CN
- China
- Prior art keywords
- strength
- kettle
- sizing
- mesh sheet
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Apparatus processing technique field is fished for the invention belongs to fishery, and in particular to a kind of processing method of high-strength polyethylene twist net slice, including a benzene vapor sizing, cooling and second heat steam shaping.The present invention has advantages below compared with prior art:By adding composite assistant in high-strength polythene filament raw material in the present invention, make it in the case where line density is increased slightly, tensile mechanical properties also improve, first shape of mesh sheet one-off drawing and benzene vapor of knitting forming is modified to mesh sheet simultaneously, make its space structure more complicated, molecular structure is closer, increases intensity;Mesh sheet succeeding stretch and the mode of vapours sizing coordinate, and reduce the relaxation shrinkage of mesh sheet, it is ensured that the product quality of fishing net, the ultimate strength compared to same specification mesh sheet adds 3.5% or so, and the scope of application is wider.
Description
Technical field
Apparatus processing technique field is fished for the invention belongs to fishery, and in particular to a kind of high-strength polyethylene twist net slice
Processing method.
Background technology
Due to the design feature of twist net slice, twist net slice strength depends primarily on the strength character of monofilament, for superelevation
Molecular weight polyethylene, the braided construction of superpower performance and high-strength utilization rate due to itself having, so that mesh sheet possesses Zhuo
Strength character more, however, due to however, due to the special process needed for superhigh molecular weight polyethylene fibers fabrication processes and
High production cost, expensive price seriously constrains its popularization, and fishery is big to the demand of high intensity mesh sheet, and requires valency
Lattice are cheap, it is necessary to use the high reinforcing fiber of cost performance as mesh sheet matrix material, high-strength polythene filament has price
The advantage such as the low, ratio of performance to price is high, compared with common polythene, with intensity is high, lightweight, wear-resisting, ageing-resistant and performance valency
Lattice than it is high the advantages of, therefore, be widely used to the fish production such as trawlnet, net cage and sea anchor rope field, achieve good make
With effect, but with fast developments such as deep-water net cage culture industry and tuna seines, to the intensity and combination property of twist net slice
Higher requirement is proposed, and China is less to relation technological researching, accordingly, it would be desirable to enter to the intensity for how strengthening twist net slice
Row further investigation.
The content of the invention
The purpose of the present invention is that there is provided a kind of processing side of high-strength polyethylene twist net slice the problem of being directed to existing
Method.
The present invention is achieved by the following technical solutions:A kind of processing method of high-strength polyethylene twist net slice, will
High-strength polyethylene twist net slice makes its length reach the 102-104% of product specification by mechanical stretching, then by rack with drawing
The mesh sheet stretched is shaped while being pushed into sizing kettle, and particular content is that after closing sizing kettle, nitrogen is passed through into sizing kettle,
Opposite side extracts air out, can stop until not oxygenous in detection sizing kettle;Then benzene vapor is passed through into sizing kettle, until
Stop when pressure reaches 300-320kPa in sizing kettle, be warming up to 114-118 DEG C, after being kept for 8 minutes, open air bleeding valve discharge kettle
Interior benzene vapour;Then mesh sheet is taken out, soaked 10-15 minutes in temperature is 10-15 DEG C of water, then by after above-mentioned one-step building
The stretching of high-strength polyethylene twist net slice its length is reached the 106-108% of product specification, then by after rack and stretching
Mesh sheet is shaped again, is passed through vapours, and it is 120-140kPa to make pressure in sizing kettle, and holding temperature in the kettle is 105-115
DEG C, after being kept for 2-3 minutes, discharge steam, you can complete;
The high-strength polyethylene twist net slice is woven by high-strength polythene filament, and number of share of stock is 36 strands;The poly- second of high intensity
Alkene monofilament raw material includes the raw material of following parts by weight:It is 80-85 parts of high-strength polyethylene, 8-14 parts of low density polyethylene (LDPE), compound strong
Change 3-6 parts of auxiliary agent.
As further improvement of these options, the tensile mechanical properties of the high-strength polythene filament are diameter
0.2mm, line density 34.5tex, ultimate strength 23.854N, elongation at break 16.64%, single line knot strength 13.854N, fracture are strong
Spend 7.25cN/dtex, knot strength 4.32cN/dtex.
As further improvement of these options, the temperature of the benzene vapor is 101-105 DEG C.
As further improvement of these options, the tolysulfonyl amino acid is N-p-tolysulfonyl glycine and right
Tosyl alanine.
As further improvement of these options, the complex intensifying auxiliary agent includes:3,5- dinitrobenzoic acid imidazoles
2-3 parts of cobalt, 1-2 parts of 4- bromobenzaldehyde semicarbazones, 0.2-0.8 parts of tolysulfonyl amino acid, fatty alcohol sulfate 1.3-1.8
Part, 1.4-2.2 parts of diethylaluminum ethoxide sulfonic acid sodium succinate, 0.4-1 parts of benzoic acid.
As further improvement of these options, the benzene vapor of the air bleeding valve discharge is cooled back with cooling tube to be stored up
Deposit.
The present invention has advantages below compared with prior art:By adding in high-strength polythene filament raw material in the present invention
Plus composite assistant, make it in the case where line density is increased slightly, tensile mechanical properties also improve, while to being woven into
Sizing is modified the mesh sheet one-off drawing and benzene vapor of type to mesh sheet for the first time, makes its space structure more complicated, molecule knot
Structure is closer, increases intensity;Mesh sheet succeeding stretch and the mode of vapours sizing coordinate, and reduce the relaxation shrinkage of mesh sheet, protect
The product quality of fishing net is demonstrate,proved, the ultimate strength compared to same specification mesh sheet adds 3.5% or so, and the scope of application is wider.
Embodiment
Embodiment 1
A kind of processing method of high-strength polyethylene twist net slice, makes it by high-strength polyethylene twist net slice by mechanical stretching
Length reaches the 103% of product specification, and then the mesh sheet of rack and stretching is pushed into sizing kettle simultaneously and shaped, specific interior
After Rong Wei, closing sizing kettle, nitrogen is passed through into sizing kettle, opposite side extracts air out, until not oxygenous in detection sizing kettle
It can stop;Then benzene vapor is passed through into sizing kettle, stops when pressure reaches 300kPa in kettle of shaping, be warming up to 116
DEG C, after being kept for 8 minutes, open benzene vapour in air bleeding valve discharge kettle;Then mesh sheet is taken out, soaked in temperature is 12 DEG C of water
14 minutes, then its length is reached product specification the high-strength polyethylene twist net slice stretching after above-mentioned one-step building
107%, then the mesh sheet after rack and stretching is shaped again, vapours is passed through, it is 130kPa to make pressure in sizing kettle,
It is 110 DEG C to keep temperature in the kettle, after being kept for 3 minutes, discharges steam, you can completed;
The high-strength polyethylene twist net slice is woven by high-strength polythene filament, and number of share of stock is 36 strands;The poly- second of high intensity
Alkene monofilament raw material includes the raw material of following parts by weight:83 parts of high-strength polyethylene, 12 parts of low density polyethylene (LDPE), complex intensifying auxiliary agent
5 parts;
Wherein, the complex intensifying auxiliary agent includes:2 parts of 3,5- dinitrobenzoic acid imidazoles cobalt, 4- bromobenzaldehydes semicarbazones 1
Part, 0.5 part of tolysulfonyl amino acid, 1.5 parts of fatty alcohol sulfate, 1.8 parts of diethylaluminum ethoxide sulfonic acid sodium succinate, benzoic acid
0.7 part.
After testing, the tensile mechanical properties of the high-strength polythene filament are diameter 0.2mm, line density 34.5tex, are broken
Split strength 23.854N, elongation at break 16.64%, single line knot strength 13.854N, fracture strength 7.25cN/dtex, knot strength
4.32cN/dtex。
Wherein, the temperature of the benzene vapor is 101-105 DEG C;The tolysulfonyl amino acid is the sweet ammonia of tolysulfonyl
Acid and tolysulfonyl alanine;The benzene vapor of the air bleeding valve discharge is cooled back to store up with cooling tube to be deposited.
Embodiment 2
A kind of processing method of high-strength polyethylene twist net slice, makes it by high-strength polyethylene twist net slice by mechanical stretching
Length reaches the 102% of product specification, and then the mesh sheet of rack and stretching is pushed into sizing kettle simultaneously and shaped, specific interior
After Rong Wei, closing sizing kettle, nitrogen is passed through into sizing kettle, opposite side extracts air out, until not oxygenous in detection sizing kettle
It can stop;Then benzene vapor is passed through into sizing kettle, stops when pressure reaches 320kPa in kettle of shaping, be warming up to 114
DEG C, after being kept for 8 minutes, open benzene vapour in air bleeding valve discharge kettle;Then mesh sheet is taken out, soaked in temperature is 15 DEG C of water
10 minutes, then its length is reached product specification the high-strength polyethylene twist net slice stretching after above-mentioned one-step building
106%, then the mesh sheet after rack and stretching is shaped again, vapours is passed through, it is 140kPa to make pressure in sizing kettle,
It is 115 DEG C to keep temperature in the kettle, after being kept for 2 minutes, discharges steam, you can completed;
The high-strength polyethylene twist net slice is woven by high-strength polythene filament, and number of share of stock is 36 strands;The poly- second of high intensity
Alkene monofilament raw material includes the raw material of following parts by weight:80 parts of high-strength polyethylene, 14 parts of low density polyethylene (LDPE), complex intensifying auxiliary agent
3 parts;
Wherein, the complex intensifying auxiliary agent includes:2 parts of 3,5- dinitrobenzoic acid imidazoles cobalt, 4- bromobenzaldehydes semicarbazones 1
Part, 0.2 part of tolysulfonyl amino acid, 1.8 parts of fatty alcohol sulfate, 2.2 parts of diethylaluminum ethoxide sulfonic acid sodium succinate, benzoic acid
0.4 part.
Embodiment 3
A kind of processing method of high-strength polyethylene twist net slice, makes it by high-strength polyethylene twist net slice by mechanical stretching
Length reaches the 104% of product specification, and then the mesh sheet of rack and stretching is pushed into sizing kettle simultaneously and shaped, specific interior
After Rong Wei, closing sizing kettle, nitrogen is passed through into sizing kettle, opposite side extracts air out, until not oxygenous in detection sizing kettle
It can stop;Then benzene vapor is passed through into sizing kettle, stops when pressure reaches 300kPa in kettle of shaping, be warming up to 114
DEG C, after being kept for 8 minutes, open benzene vapour in air bleeding valve discharge kettle;Then mesh sheet is taken out, soaked in temperature is 15 DEG C of water
10 minutes, then its length is reached product specification the high-strength polyethylene twist net slice stretching after above-mentioned one-step building
106%, then the mesh sheet after rack and stretching is shaped again, vapours is passed through, it is 120kPa to make pressure in sizing kettle,
It is 115 DEG C to keep temperature in the kettle, after being kept for 3 minutes, discharges steam, you can completed;
The high-strength polyethylene twist net slice is woven by high-strength polythene filament, and number of share of stock is 36 strands;The poly- second of high intensity
Alkene monofilament raw material includes the raw material of following parts by weight:85 parts of high-strength polyethylene, 8 parts of low density polyethylene (LDPE), complex intensifying auxiliary agent 6
Part;
Wherein, the complex intensifying auxiliary agent includes:3 parts of 3,5- dinitrobenzoic acid imidazoles cobalt, 4- bromobenzaldehydes semicarbazones 2
Part, 0.8 part of tolysulfonyl amino acid, 1.3 parts of fatty alcohol sulfate, 1.4 parts of diethylaluminum ethoxide sulfonic acid sodium succinate, benzoic acid
1 part.
Embodiment 4
A kind of processing method of high-strength polyethylene twist net slice, makes it by high-strength polyethylene twist net slice by mechanical stretching
Length reaches the 106% of product specification, and then the mesh sheet after rack and stretching is shaped again, vapours is passed through, makes sizing
Pressure is 120-140kPa in kettle, and it is 105-115 DEG C to keep temperature in the kettle, after being kept for 2-3 minutes, discharges steam, you can completed;
Remaining content is in the same manner as in Example 1.
Embodiment 5
A kind of processing method of high-strength polyethylene twist net slice, makes it by high-strength polyethylene twist net slice by mechanical stretching
Length reaches the 103% of product specification, and then the mesh sheet of rack and stretching is pushed into sizing kettle simultaneously and shaped, specific interior
After Rong Wei, closing sizing kettle, nitrogen is passed through into sizing kettle, opposite side extracts air out, until not oxygenous in detection sizing kettle
It can stop;Then benzene vapor is passed through into sizing kettle, stops when pressure reaches 300kPa in kettle of shaping, be warming up to 116
DEG C, after being kept for 8 minutes, open benzene vapour in air bleeding valve discharge kettle;Then mesh sheet is taken out, soaked in temperature is 30 DEG C of water
14 minutes, then its length is reached product specification the high-strength polyethylene twist net slice stretching after above-mentioned one-step building
107%, then the mesh sheet after rack and stretching is shaped again, vapours is passed through, it is 130kPa to make pressure in sizing kettle,
It is 110 DEG C to keep temperature in the kettle, after being kept for 3 minutes, discharges steam, you can completed;Remaining content is in the same manner as in Example 1.
Embodiment 6
A kind of processing method of high-strength polyethylene twist net slice, the high-strength polyethylene twist net slice is by high-strength polyethylene
Monofilament weaves, and number of share of stock is 36 strands;The high-strength polythene filament raw material includes the raw material of following parts by weight:High-strength polyethylene
83 parts, 12 parts of low density polyethylene (LDPE), 2 parts of benzoic acid;Remaining content is in the same manner as in Example 1.
It is measured from tester INSTRON-4466 types strength tester in the case where being separated by 2 days, obtains each
The measure of twist net slice mesh rupture strength in embodiment, the high-strength polyethylene twist net slice that existing market is purchased is used as reality
The specification for testing mesh sheet in group, each embodiment is HSPE-36tex × 36 gang -50mm, and concrete outcome is as follows:
Table 1
Group | Mesh pin diameter(mm) | Mesh tie point ultimate strength(N) | Mesh sheet single line ultimate strength(N) | The mesh mesh sheet weight of 10 mesh × 10 | Mesh sheet price(Member/kg) |
Embodiment 1 | 2.01 | 1192.5 | 652.8 | 16.7 | 46.8 |
Embodiment 2 | 2.02 | 1208.3 | 653.4 | 17.3 | 46.8 |
Embodiment 3 | 2.01 | 1198.7 | 655.2 | 17.2 | 46.8 |
Embodiment 4 | 2.03 | 1168.5 | 641.8 | 19.4 | 46.2 |
Embodiment 5 | 2.02 | 1184.5 | 647.2 | 18.6 | 46.5 |
Embodiment 6 | 2.01 | 1162.8 | 635.4 | 20.8 | 46.3 |
Control group | 2.02 | 1174.2 | 643.2 | 21.8 | 46 |
Twist net slice plus money slightly above control group in the present invention are can be seen that by data in table 1, but its mesh tie point is disconnected
Resistance to spalling is significantly improved, and application is wider in fish production;Condition control and mesh sheet in type-approval process is former
The selection synergy of material produces certain influence to the strength character of mesh sheet, can be according to required performance and valency in actual production
Money is than carrying out appropriate selection.
Claims (6)
1. a kind of processing method of high-strength polyethylene twist net slice, it is characterised in that lead to high-strength polyethylene twist net slice
The 102-104% that mechanical stretching makes its length reach product specification is crossed, rack and the mesh sheet of stretching are then pushed into sizing kettle simultaneously
Middle to be shaped, particular content is after closing sizing kettle, nitrogen to be passed through into sizing kettle, opposite side extracts air out, until detection
It is not oxygenous in sizing kettle to stop;Then benzene vapor is passed through into sizing kettle, until pressure reaches 300- in sizing kettle
Stop during 320kPa, be warming up to 114-118 DEG C, after being kept for 8 minutes, open benzene vapour in air bleeding valve discharge kettle;Then by mesh sheet
Take out, soaked 10-15 minutes in temperature is 10-15 DEG C of water, then the high-strength polyethylene after above-mentioned one-step building is twisted into sth. made by twisting
Mesh sheet stretching makes its length reach the 106-108% of product specification, and then the mesh sheet after rack and stretching is shaped again,
Vapours is passed through, it is 120-140kPa to make pressure in sizing kettle, and it is 105-115 DEG C to keep temperature in the kettle, after being kept for 2-3 minutes,
Discharge steam, you can complete;
The high-strength polyethylene twist net slice is woven by high-strength polythene filament, and number of share of stock is 36 strands;The poly- second of high intensity
Alkene monofilament raw material includes the raw material of following parts by weight:It is 80-85 parts of high-strength polyethylene, 8-14 parts of low density polyethylene (LDPE), compound strong
Change 3-6 parts of auxiliary agent.
2. a kind of processing method of high-strength polyethylene twist net slice as claimed in claim 1, it is characterised in that the high intensity
The tensile mechanical properties of polyethylene monofilament are diameter 0.2mm, line density 34.5tex, ultimate strength 23.854N, elongation at break
16.64%, single line knot strength 13.854N, fracture strength 7.25cN/dtex, knot strength 4.32cN/dtex.
3. a kind of processing method of high-strength polyethylene twist net slice as claimed in claim 1, it is characterised in that the benzene vapor
Temperature be 101-105 DEG C.
4. a kind of processing method of high-strength polyethylene twist net slice as claimed in claim 1, it is characterised in that described to toluene
Sulfonamino acid is N-p-tolysulfonyl glycine and tolysulfonyl alanine.
5. a kind of processing method of high-strength polyethylene twist net slice as claimed in claim 1, it is characterised in that described compound strong
Changing auxiliary agent includes:2-3 parts of 3,5- dinitrobenzoic acids imidazoles cobalt, 1-2 parts of 4- bromobenzaldehyde semicarbazones, tolysulfonyl amino
Sour 0.2-0.8 parts, 1.3-1.8 parts of fatty alcohol sulfate, 1.4-2.2 parts of diethylaluminum ethoxide sulfonic acid sodium succinate, benzoic acid 0.4-1
Part.
6. a kind of processing method of high-strength polyethylene twist net slice as claimed in claim 1, it is characterised in that the air bleeding valve
The benzene vapor of discharge is cooled back to store up with cooling tube and deposited.