CN107011593A - A kind of expansibility flame-proof polyvinyl chloride cable - Google Patents
A kind of expansibility flame-proof polyvinyl chloride cable Download PDFInfo
- Publication number
- CN107011593A CN107011593A CN201710288426.5A CN201710288426A CN107011593A CN 107011593 A CN107011593 A CN 107011593A CN 201710288426 A CN201710288426 A CN 201710288426A CN 107011593 A CN107011593 A CN 107011593A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- cable
- proof polyvinyl
- expansibility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of expansibility flame-proof polyvinyl chloride cable, the external insulation layer of cable is made up of the raw material of following parts by weight:100 parts of polyvinyl chloride, 20 30 parts of expansion type flame retardant, 15 20 parts of zinc molybdate, 5 10 parts of red phosphorus, 10 20 parts of the molybdenum sesquioxide crystallization water.The present invention is acted on by zinc molybdate, the cooperative flame retardant of red phosphorus and the molybdenum sesquioxide crystallization water and suppression cigarette so that cable can effectively play fire-retardant effect.
Description
Technical field
The present invention relates to power industry field, and in particular to a kind of expansibility flame-proof polyvinyl chloride cable.
Background technology
Electric wire is to transmit electromagnetic energy, information and the wire product for realizing electromagnetic energy conversion.Electric wire and cable is simultaneously
There is no strict boundary.Generally by core number is few, product diameter is small, product simple in construction is referred to as electric wire, what is do not insulated is referred to as
Luodian County, others are referred to as cable.
Cable is more and more diversified in modern use environment, high temperature, low temperature, harsh climate, rugged environment etc.
Use all to normal cable proposes various problems.To tackle the requirement of existing use environment, cable tool of the present invention
There is good fire resistance.
The content of the invention
It is an object of the invention to provide a kind of expansibility flame-proof polyvinyl chloride cable.Expansibility flame-proof polyvinyl chloride electricity
Cable can play good flame retardant effect, be adapted to the use of harsh weather and environment.
The present invention is achieved through the following technical solutions:
A kind of expansibility flame-proof polyvinyl chloride cable, the external insulation layer of cable is made up of the raw material of following parts by weight:Polychlorostyrene
100 parts of ethene, 20-30 parts of expansion type flame retardant, 15-20 parts of zinc molybdate, 5-10 parts of red phosphorus, molybdenum sesquioxide crystallization water 10-20
Part.
The external insulation layer of cable is made up of the raw material of following parts by weight:100 parts of polyvinyl chloride, 20 parts of expansion type flame retardant,
18 parts of zinc molybdate, 8 parts of red phosphorus, 15 parts of the molybdenum sesquioxide crystallization water.
Also include 5-8 parts of antimony oxide.
The expansion type flame retardant is two neopentyl glycol m-phenylene diamine (MPD) phosphates or the phosphonitrile of hydroxyl ring three.
The particle diameter of the zinc molybdate is 300-500 microns.The zinc molybdate of micron grain size more can be contacted with extraneous, and
It will not excessively reunite during cable is prepared, cause material uneven.
The present invention compared with prior art, has the following advantages and advantages:
The present invention is acted on by zinc molybdate, the cooperative flame retardant of red phosphorus and the molybdenum sesquioxide crystallization water and suppression cigarette so that cable
Fire-retardant effect can be effectively played.
Embodiment
For the object, technical solutions and advantages of the present invention are more clearly understood, with reference to embodiment, to present invention work
Further to describe in detail, exemplary embodiment and its explanation of the invention is only used for explaining the present invention, is not intended as to this
The restriction of invention.
Embodiment 1
A kind of expansibility flame-proof polyvinyl chloride cable, the external insulation layer of cable is made up of the raw material of following parts by weight:Polychlorostyrene
100 parts of ethene, 22 parts of expansion type flame retardant, 15 parts of zinc molybdate, 5 parts of red phosphorus, 10 parts of the molybdenum sesquioxide crystallization water.
Embodiment 2
A kind of expansibility flame-proof polyvinyl chloride cable, the external insulation layer of cable is made up of the raw material of following parts by weight:Polychlorostyrene
100 parts of ethene, 20 parts of expansion type flame retardant, 18 parts of zinc molybdate, 8 parts of red phosphorus, 15 parts of the molybdenum sesquioxide crystallization water.
Embodiment 3
A kind of expansibility flame-proof polyvinyl chloride cable, the external insulation layer of cable is made up of the raw material of following parts by weight:Polychlorostyrene
100 parts of ethene, 30 parts of expansion type flame retardant, 20 parts of zinc molybdate, 10 parts of red phosphorus, 20 parts of the molybdenum sesquioxide crystallization water.
Embodiment 4
A kind of expansibility flame-proof polyvinyl chloride cable, the external insulation layer of cable is made up of the raw material of following parts by weight:Polychlorostyrene
100 parts of ethene, 20 parts of expansion type flame retardant, 18 parts of zinc molybdate, 8 parts of red phosphorus, 15 parts of the molybdenum sesquioxide crystallization water, antimony oxide
5 parts.
Embodiment 5
A kind of expansibility flame-proof polyvinyl chloride cable, the external insulation layer of cable is made up of the raw material of following parts by weight:Polychlorostyrene
100 parts of ethene, 20 parts of expansion type flame retardant, 18 parts of zinc molybdate, 8 parts of red phosphorus, 15 parts of the molybdenum sesquioxide crystallization water, antimony oxide
8 parts.
The particle diameter of zinc molybdate is 300-500 microns.
Expansion type flame retardant is two neopentyl glycol m-phenylene diamine (MPD) phosphates or the phosphonitrile of hydroxyl ring three.
Above-described embodiment, has been carried out further to the purpose of the present invention, technical scheme and beneficial effect
Describe in detail, should be understood that the embodiment that the foregoing is only the present invention, be not intended to limit the present invention
Protection domain, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc. all should be included
Within protection scope of the present invention.
Claims (5)
1. a kind of expansibility flame-proof polyvinyl chloride cable, it is characterised in that the external insulation layer of cable by following parts by weight raw material
It is made:100 parts of polyvinyl chloride, 20-30 parts of expansion type flame retardant, 15-20 parts of zinc molybdate, 5-10 parts of red phosphorus, molybdenum sesquioxide knot
Brilliant water 10-20 parts.
2. expansibility flame-proof polyvinyl chloride cable according to claim 1, it is characterised in that the external insulation layer of cable by with
The raw material of lower parts by weight is made:100 parts of polyvinyl chloride, 20 parts of expansion type flame retardant, 18 parts of zinc molybdate, 8 parts of red phosphorus, three oxidations two
15 parts of the molybdenum crystallization water.
3. expansibility flame-proof polyvinyl chloride cable according to claim 1, it is characterised in that also including antimony oxide 5-
8 parts.
4. expansibility flame-proof polyvinyl chloride cable according to claim 1, it is characterised in that the expansion type flame retardant is
Two neopentyl glycol m-phenylene diamine (MPD) phosphates or the phosphonitrile of hydroxyl ring three.
5. expansibility flame-proof polyvinyl chloride cable according to claim 1, it is characterised in that the particle diameter of the zinc molybdate is
300-500 microns.