CN107007861A - Nano deodorized powder and preparation method thereof - Google Patents
Nano deodorized powder and preparation method thereof Download PDFInfo
- Publication number
- CN107007861A CN107007861A CN201710200021.1A CN201710200021A CN107007861A CN 107007861 A CN107007861 A CN 107007861A CN 201710200021 A CN201710200021 A CN 201710200021A CN 107007861 A CN107007861 A CN 107007861A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- nano
- weight
- deodorized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of deodorant powder, more particularly to a kind of nano deodorized powder and preparation method thereof, it belongs to daily-use chemical industry technical field by killing bacterium, suppressing growth of microorganism so as to go to eliminate the unusual smell.Nano deodorized powder, it is mainly prepared from by following raw materials by institute's parts by weight:27 31 parts of nano zine oxide, 0.1 0.2 parts of nano-silver powder, 37 parts of negative ion powder, 37 parts of alum, 0.5 1.5 parts of Tea Polyphenols, 50 60 parts of talcum powder.Deodorant powder of the present invention is that a kind of nontoxic, environmentally friendly, use cost is low, usage amount is small, rapid-action, good deodorization effect, effect keep permanent nano deodorized powder.
Description
Technical field
The present invention relates to a kind of deodorant powder, more particularly to a kind of nano deodorized powder and preparation method thereof, it is by killing
Bacterium, suppress growth of microorganism so as to going to eliminate the unusual smell, belong to daily-use chemical industry technical field.
Background technology
In daily life, shoes socks are indispensable articles for use, go out be required for daily, but the problem of shoes socks peculiar smell
Or the unreasonable insoluble technical problem of a comparison.Footgear is smelly, foot odour is due to that arch of the foot sweat gland is more, easily perspires, sweat
In except moisture content, salt exceptionally, also containing lactic acid and urea.Under the conditions of hidrosis, bacterium amount reproduction on pin simultaneously decomposes cutin
Albumen, along with the urea in sweat, lactic acid, can thus send a kind of stink.If shoes are airtight, atmosphere draught-free is smelly
Taste will be more long-pending denseer, and foul smell is extremely strong.
Mainly there is following several method to shoes, socks, shoe chest deodorization at present:The first is ablution, can be with after cleaning
Most of stink is removed, but needing to have worn every time all cleans, this makes troubles to user, while also strong influence footwear
The service life of socks;The cleaning of shoe chest is then wasted time and energy, and effect is poor.Second is, using the method adsorbed, to be entered using activated carbon
Row absorption, such a method is simple and convenient, but its adsorption effect it is poor, it is necessary to time it is long, it is impossible to fundamentally solve footgear
Bad-smell problem.The third is to carry out deodorization using spray, and such a method is simple, and wide using scope, this method is mainly divided
The following two kinds:One kind is liquid sprays class, and Publication No. CN1256872A Chinese patent discloses a kind of footwear deodorization and sterilization
Agent, it is formulated by a certain percentage by benzalkonium bromide, borneol, peppermint, alcohol, essence, distilled water, can be seen by its composition
Go out, based on it is mainly covered with aromatic essence, containing a small amount of bactericide, can only so play the effect that fragrance covers stink
Really, its sterilization persistently and does not increase humidity in footwear, finally again without the bad-smell problem for fundamentally solving footgear, during effect
Between it is short;Another is powder agent, and Publication No. CN1654076A Chinese patent discloses a kind of foot deodorant powder, and it is by Huang
Pellet, camphor, kuh-seng, alum, chlorite schist are prepared from, and its main component is Chinese medicine, individually to suppress pin sweat as action principle, are led to
Cross Chinese medicine odor and cover stink, deodorizing effect is poor, work extremely slow, usage amount is big, once need 2.5 grams, effect keeps not long
Long.
The content of the invention
It is an object of the invention to provide a kind of nontoxic, environmentally friendly, use cost it is low, usage amount is small, rapid-action, deodorizing effect
Good, effect keeps permanent nano deodorized powder and preparation method thereof.
In order to achieve the above object, the present invention is achieved through the following technical solutions:
Nano deodorized powder, it is mainly prepared from by following raw materials by institute's parts by weight:27-31 parts of nano zine oxide, nanometer
0.1-0.2 parts of silver powder, 3-7 parts of negative ion powder, 3-7 parts of alum, 0.5-1.5 parts of Tea Polyphenols, 50-60 parts of talcum powder.
Above-mentioned nano deodorized powder, it is to be prepared from by following raw materials by institute's parts by weight:28-30 parts of nano zine oxide,
0.13-0.17 parts of nano-silver powder, 4-6 parts of negative ion powder, 4-6 parts of aloe powder, 4-6 parts of alum, 4-6 parts of Herba Menthae powder, Tea Polyphenols
0.7-1.2 parts, 53-56 parts of talcum powder.
Above-mentioned nano deodorized powder, it is to be prepared from by following raw materials by institute's parts by weight:Nano zine oxide 29 part, nanometer
0.15 part of silver powder, 5 parts of negative ion powder, 5 parts of aloe powder, 5 parts of alum, 5 parts of Herba Menthae powder, 1 part of Tea Polyphenols, 54.85 parts of talcum powder.
The preparation method of above-mentioned nano deodorized powder is as follows:Take the nano-silver powder for meeting the parts by weight, it is negative ion powder, bright
Alum, Tea Polyphenols are added in mixed at high speed mixer to be stirred 20-40 seconds with 10,000 turns, obtains mixed powder, and mixed powder is described with meeting
The nano zine oxide and talcum powder of parts by weight are together added in tub mixer 800 mesh of mistake after 100 turns of stirrings 8-12 minute
Sieve to obtain nano deodorized powder.
The preparation method of above-mentioned nano deodorized powder is as follows:Take the nano-silver powder for meeting the parts by weight, negative ion powder, reed
Luxuriant growth powder, alum, Herba Menthae powder, Tea Polyphenols are added in mixed at high speed mixer to be stirred 20-40 seconds with 10,000 turns, obtains mixed powder, will be mixed
Close powder and be together added to 100 turns of stirring 8-12 in tub mixer with meeting the nano zine oxide and talcum powder of the parts by weight
800 mesh sieves are crossed after minute and obtain nano deodorized powder.
Due to using above-mentioned technical proposal so that the invention has the advantages that and effect:
In view of the reason for stink causes in footwear is the bacterium amount reproduction on pin and decomposes contained in keratoprotein and sweat
Lactic acid, urea, the present invention use nano zine oxide, Nano Silver for main deodorization and sterilization raw material, and asepsis environment-protecting is stingless to skin
Swash material.The nano materials such as nano zine oxide, Nano Silver, greatly, huge surface area effectively destroys memebrane protein knot to the volume on surface
Structure, makes it lose activity, and nano material is had extremely strong adsorption capacity, and plus negative ion powder Synergistic biocidal deodorization, this makes
Nano-particle is obtained for either promoting the corrupt oxygen atom of material, oxygen radical, the alkanes point of other peculiar smell are still produced
Son etc., be respectively provided with it is extremely strong grab prisoner's ability, the synergy for being subject to alum makes it have durable antibiotic sterilizing and deodorizing function and energy
Restrain skin to suppress to perspire, with durable antibiotic, sterilization, deodorization functions.Further aloe powder, Tea Polyphenols play guarantor to skin
The skin care effect such as foster, anti-aging, Herba Menthae powder can improve the comfort level of user.
Use cost of the present invention is low, and usage amount is small, one time 0.25 gram, through test 6 hours sterilizing rates reach 99.81-
99.85%, taste substantially mitigates the same day in practical application, and deodorizing effect can be kept 3 months or so, clean many using rear footgear
Secondary rear sterilizing rate still can reach 98%, and the present invention can effectively prevent by bacterial foot's skin problem such as tinea pedis, the ringworm of the foot
Deng.
Embodiment
Next step description is carried out to the present invention with reference to embodiment.Following examples are only the specific implementation of the present invention
Example, in order that the objects, technical solutions and advantages of the present invention are very clear, following examples carry out further detailed to the present invention
Explanation.
Embodiment 1
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:27 parts of nano zine oxide, nano-silver powder 0.2
Part, 7 parts of negative ion powder, 7 parts of alum, 1.5 parts of Tea Polyphenols, 60 parts of talcum powder.
Its preparation method is as follows:The nano-silver powder for meeting the parts by weight, negative ion powder, alum, Tea Polyphenols is taken to add
Stirred 20 seconds with 10,000 turns in mixed at high speed mixer, mixed powder is obtained, by mixed powder and the nano oxygen for meeting the parts by weight
Change and cross 800 mesh sieves after zinc and talcum powder are together added in tub mixer 100 turns of stirrings 12 minutes and obtain nano deodorized powder.
Embodiment 2
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:31 parts of nano zine oxide, 0.1 part of nano-silver powder, 3 parts of negative ion powder, 3 parts of alum, 0.5 part of Tea Polyphenols, talcum powder 50
Part.
Its preparation method is as follows:The nano-silver powder for meeting the parts by weight, negative ion powder, alum, Tea Polyphenols is taken to add
Stirred 40 seconds with 10,000 turns in mixed at high speed mixer, mixed powder is obtained, by mixed powder and the nano oxygen for meeting the parts by weight
Change and cross 800 mesh sieves after zinc and talcum powder are together added in tub mixer 100 turns of stirrings 8 minutes and obtain nano deodorized powder.
Embodiment 3
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:27.6 parts of nano zine oxide, 0.12 part of nano-silver powder, 3.8 parts of negative ion powder, 6.7 parts of alum, 0.65 part of Tea Polyphenols,
57.8 parts of talcum powder.
Its preparation method is as follows:The nano-silver powder for meeting the parts by weight, negative ion powder, alum, Tea Polyphenols is taken to add
Stirred 25 seconds with 10,000 turns in mixed at high speed mixer, mixed powder is obtained, by mixed powder and the nano oxygen for meeting the parts by weight
Change and cross 800 mesh sieves after zinc and talcum powder are together added in tub mixer 100 turns of stirrings 9 minutes and obtain nano deodorized powder.
Embodiment 4
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:29.2 parts of nano zine oxide, 0.18 part of nano-silver powder, 5.9 parts of negative ion powder, 4.2 parts of alum, 1.37 parts of Tea Polyphenols,
53.7 parts of talcum powder.
Its preparation method is as follows:The nano-silver powder for meeting the parts by weight, negative ion powder, alum, Tea Polyphenols is taken to add
Stirred 35 seconds with 10,000 turns in mixed at high speed mixer, mixed powder is obtained, by mixed powder and the nano oxygen for meeting the parts by weight
Change and cross 800 mesh sieves after zinc and talcum powder are together added in tub mixer 100 turns of stirrings 11 minutes and obtain nano deodorized powder.
Embodiment 5
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:28 parts of nano zine oxide, 0.17 part of nano-silver powder, 6 parts of negative ion powder, 6 parts of aloe powder, 6 parts of alum, 6 parts of Herba Menthae powder,
1.2 parts of Tea Polyphenols, 56 parts of talcum powder.
The preparation method of above-mentioned nano deodorized powder is as follows:Take the nano-silver powder for meeting the parts by weight, negative ion powder, reed
Luxuriant growth powder, alum, Herba Menthae powder, Tea Polyphenols are added in mixed at high speed mixer to be stirred 27 seconds with 10,000 turns, is obtained mixed powder, will be mixed
Powder and meet the nano zine oxide and talcum powder of the parts by weight and be together added in tub mixer 100 turns and stir 8 minutes
800 mesh sieves are crossed afterwards obtains nano deodorized powder.
Embodiment 6
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:30 parts of nano zine oxide, 0.13 part of nano-silver powder, 4 parts of negative ion powder, 4 parts of aloe powder, 4 parts of alum, 4 parts of Herba Menthae powder,
0.7 part of Tea Polyphenols, 53 parts of talcum powder.
The preparation method of above-mentioned nano deodorized powder is as follows:Take the nano-silver powder for meeting the parts by weight, negative ion powder, reed
Luxuriant growth powder, alum, Herba Menthae powder, Tea Polyphenols are added in mixed at high speed mixer to be stirred 32 seconds with 10,000 turns, is obtained mixed powder, will be mixed
Powder and meet the nano zine oxide and talcum powder of the parts by weight and be together added in tub mixer 100 turns and stir 12 minutes
800 mesh sieves are crossed afterwards obtains nano deodorized powder.
Embodiment 7
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:28.5 parts of nano zine oxide, 0.14 part of nano-silver powder, 4.5 parts of negative ion powder, 5.5 parts of aloe powder, 4.5 parts of alum are thin
5.5 parts of lotus powder, 1.4 parts of Tea Polyphenols, 54 parts of talcum powder.
The preparation method of above-mentioned nano deodorized powder is as follows:Take the nano-silver powder for meeting the parts by weight, negative ion powder, reed
Luxuriant growth powder, alum, Herba Menthae powder, Tea Polyphenols are added in mixed at high speed mixer to be stirred 30 seconds with 10,000 turns, is obtained mixed powder, will be mixed
Powder and meet the nano zine oxide and talcum powder of the parts by weight and be together added in tub mixer 100 turns and stir 9 minutes
800 mesh sieves are crossed afterwards obtains nano deodorized powder.
Embodiment 8
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:29.5 parts of nano zine oxide, 0.13 part of nano-silver powder, 5.5 parts of negative ion powder, 4.5 parts of aloe powder, 5.5 parts of alum are thin
4.5 parts of lotus powder, 1.2 parts of Tea Polyphenols, 55 parts of talcum powder.
The preparation method of above-mentioned nano deodorized powder is as follows:Take the nano-silver powder for meeting the parts by weight, negative ion powder, reed
Luxuriant growth powder, alum, Herba Menthae powder, Tea Polyphenols are added in mixed at high speed mixer to be stirred 32 seconds with 10,000 turns, is obtained mixed powder, will be mixed
Powder and meet the nano zine oxide and talcum powder of the parts by weight and be together added in tub mixer 100 turns and stir 11 minutes
800 mesh sieves are crossed afterwards obtains nano deodorized powder.
Embodiment 9
Nano deodorized powder it be to be prepared from by following raw materials by institute's parts by weight:It is by institute's parts by weight numeral system by following raw materials
It is standby to form:29 parts of nano zine oxide, 0.15 part of nano-silver powder, 5 parts of negative ion powder, 5 parts of aloe powder, 5 parts of alum, 5 parts of Herba Menthae powder,
1 part of Tea Polyphenols, 54.85 parts of talcum powder.
The preparation method of above-mentioned nano deodorized powder is as follows:Take the nano-silver powder for meeting the parts by weight, negative ion powder, reed
Luxuriant growth powder, alum, Herba Menthae powder, Tea Polyphenols are added in mixed at high speed mixer to be stirred 30 seconds with 10,000 turns, is obtained mixed powder, will be mixed
Powder and meet the nano zine oxide and talcum powder of the parts by weight and be together added in tub mixer 100 turns and stir 10 minutes
800 mesh sieves are crossed afterwards obtains nano deodorized powder.
Nano deodorized powder prepared by 1-9 of the embodiment of the present invention, it uses nano zine oxide, Nano Silver to be removed for main sterilization
Smelly raw material, adds anion collaboration assisting sterilisation deodorization, effect and the spy of the present invention is further illustrated below by way of experimental data
Point:
Experimental data is as follows:
Experimental raw:Nano deodorized powder prepared by 1-9 of embodiment of the present invention methods.
Experimental method:Just history value 9191412- is drawn using ATP fluorescence detector hygiena pi202 measuring and calculations
9191677【A variety of bacterium sums】, nano deodorized powder is sprinkling upon in the footwear for producing foul smell respectively in 9,0.25 gram of the equal usage amount of every footwear,
A variety of bacterium sums are 37691-83633 in footwear after being detected three hours through ATP fluorescence detectors, a variety of bacterium sums in footwear after six hours
For 1361-1785.
Result of the test:99.81-99.85% is reached through testing 6 hours sterilizing rates, taste is obvious on the day of using effect after tested
Mitigate, can keep 3 months or so, because the excellent bactericidal action of product is same to there is the bacterium sense of the foot such as pin tinea pedis, ringworm of the foot
Symptom caused by dye has prevention effect, and 6 hour sterilizations are basically completed.The effect of wherein embodiment 9 is the most notable, embodiment 9
The bactericidal effect of three hours is optimal, and a variety of bacterium sums are 37691 in footwear after three hours.
Claims (5)
1. nano deodorized powder, it is characterised in that it is mainly prepared from by following raw materials by the parts by weight:It is nano oxidized
27-31 parts of zinc, 0.1-0.2 parts of nano-silver powder, 3-7 parts of negative ion powder, 3-7 parts of alum, 0.5-1.5 parts of Tea Polyphenols, talcum powder 50-
60 parts.
2. nano deodorized powder according to claim 1, it is characterised in that it is to be prepared by following raw materials by institute's parts by weight
Form:28-30 parts of nano zine oxide, 0.13-0.17 parts of nano-silver powder, 4-6 parts of negative ion powder, 4-6 parts of aloe powder, alum 4-6
Part, 4-6 parts of Herba Menthae powder, 0.7-1.2 parts of Tea Polyphenols, 53-56 parts of talcum powder.
3. nano deodorized powder according to claim 2, it is characterised in that above-mentioned nano deodorized powder and preparation method thereof, it is
It is prepared from by following raw materials by institute's parts by weight:29 parts of nano zine oxide, 0.15 part of nano-silver powder, 5 parts of negative ion powder, aloe
5 parts of powder, 5 parts of alum, 5 parts of Herba Menthae powder, 1 part of Tea Polyphenols, 54.85 parts of talcum powder.
4. the preparation method of the nano deodorized powder described in a kind of claim 1, it is characterised in that take and meet the parts by weight
Nano-silver powder, negative ion powder, alum, Tea Polyphenols are added in mixed at high speed mixer to be stirred 20-40 seconds with 10,000 turns, must be mixed
Powder, 100 turns are together added in tub mixer by mixed powder and the nano zine oxide and talcum powder that meet the parts by weight
Stirring crosses 800 mesh sieves after 8-12 minutes and obtains nano deodorized powder.
5. the preparation method of the nano deodorized powder described in a kind of claim 2 and 3, it is characterised in that take and meet the parts by weight
Nano-silver powder, negative ion powder, aloe powder, alum, Herba Menthae powder, Tea Polyphenols be added in mixed at high speed mixer and stirred with 10,000 turns
Mix 20-40 seconds, obtain mixed powder, mixed powder and the nano zine oxide and talcum powder that meet the parts by weight are together added to bucket
In formula mixer 100 turns stirring 8-12 minute after mistake 800 mesh sieves obtain nano deodorized powder.