CN106987479A - A kind of concave convex rod lampblack absorber cleaning agent and preparation method thereof - Google Patents
A kind of concave convex rod lampblack absorber cleaning agent and preparation method thereof Download PDFInfo
- Publication number
- CN106987479A CN106987479A CN201710231505.2A CN201710231505A CN106987479A CN 106987479 A CN106987479 A CN 106987479A CN 201710231505 A CN201710231505 A CN 201710231505A CN 106987479 A CN106987479 A CN 106987479A
- Authority
- CN
- China
- Prior art keywords
- parts
- cleaning agent
- lampblack absorber
- convex rod
- concave convex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of concave convex rod lampblack absorber cleaning agent, it is characterised in that includes the raw material of following parts by weight：30 40 parts of attapulgite, 20 30 parts of inorganic adsorbent body, 12 parts of isostearoyl base isopropyl titanate, 5 10 parts of neopelex, 5 10 parts of glycine betaine, 0.1 2 parts of plant essence, 0.5 2.5 parts of sodium citrate, 5 15 parts of cocoanut fatty acid diethanolamide, 13 parts of triethanolamine, 5 20 parts of aliphatic acid polyethenoxy ether, 5 15 parts of APG APG, 0.5 4 parts of enuatrol, 0.1 1 parts of ethylparaben alcohol, 26 parts of activating agent, 50 80 parts of deionized water.The concave convex rod lampblack absorber cleaning agent dirt-removing power of the present invention is strong, biological degradability is good, non-corrosiveness, nontoxic nonirritant, while material cost is relatively low, raw material is easy to get and preparation method simple, with higher use value and good application prospect.
Description
Technical field
The present invention relates to cleaning agent technical field, and in particular to a kind of concave convex rod lampblack absorber cleaning agent and preparation method thereof.
Background technology
With the development of science and technology and the people's material and cultural life level raising, increasing people enters city
Life, the problem of kitchen fume problem has become the most headache of the sanitation and hygiene in family, restaurant etc..
Oil smoke spot extremely stubbornness is difficult to clear up, but we have to come into contacts with therewith everyday, if cleaned for a long time
Not will result in the corrosion of the ironwares such as kitchen appliance totally, but also can breed bacteria, when be carved with contaminated food
Danger, so as to cause the event of " misfortune enters from mouth " to occur.And the cleaning agent of commercial type is often containing substantial amounts of to ring at present
There is pollution in border, the highly basic or acidic materials for having injury to body, is injured when we clean kitchen fume and kitchen appliance
Our skin, has especially injured our skin on hand, if things go on like this results in pachylosis, lackluster, and skin line becomes
Slightly, chap decortication, easy infection should not fully recover, and serious meeting causes the arthralgia of both hands or even fester to wait to endanger.And it is strong acid, strong
Alkali also has corrosiveness in itself to ironware, the material in the cleaning agent remained on some tablewares slowly threaten everybody
Health.
Smoke exhaust ventilator is also known as range hood, is a kind of kitchen appliance for purifying kitchen environment.It is arranged on kitchen health section
Above energy range hood cooking stove, the harmful oil smoke produced in cooking stove can burn waste and cooking process is taken out rapidly
Walk, discharge is outdoor, reduce pollution, purify air, and have gas defence, explosion-proof safety guarantee effect.Smoke exhaust ventilator needs fixed
Phase is cleaned, and simple cleaning handles to fall greasy dirt, and it is existing that cleaning fan of sucking oil fume must use the cleaning agent of specialty to carry out
Cleaning agent majority belong to solid particulate compound, it is necessary to unpick and wash lampblack absorber when cleaning, and it is a large amount of to need client to prepare
Boiling water, such working costs is laborious, and smell is pungent.
The content of the invention
For the defect of prior art, it is an object of the invention to provide a kind of concave convex rod lampblack absorber cleaning agent, the concave convex rod
Lampblack absorber cleaning agent dirt-removing power is strong, biological degradability is good, non-corrosiveness, nontoxic nonirritant, while material cost is relatively low, original
Material is easy to get and preparation method is simple, has a good application prospect.
The present invention solves technical problem and adopted the following technical scheme that：
The invention provides a kind of concave convex rod lampblack absorber cleaning agent, include the raw material of following parts by weight：
30-40 parts of attapulgite, 20-30 parts of inorganic adsorbent body, 1-2 parts of isostearoyl base isopropyl titanate, detergent alkylate sulphur
Sour sodium 5-10 parts, 5-10 parts of glycine betaine, 0.1-2 parts of plant essence, 0.5-2.5 parts of sodium citrate, coco-nut oil fatty acid diethanol
5-15 parts of acid amides, 1-3 parts of triethanolamine, 5-20 parts of aliphatic acid polyethenoxy ether, 5-15 parts of APG APG, enuatrol 0.5-
4 parts, 0.1-1 parts of ethylparaben alcohol, 2-6 parts of activating agent, 50-80 parts of deionized water.
Preferably, the inorganic adsorbent body is the one or more in mica, vermiculite, montmorillonite, serpentine.
Preferably, the plant essence be lemon extract, peach flavor, lily essence, osmanthus flower fragrance, flavoring rose essence,
One or more in cucumber essence, flavoring pineapple essence.
Preferably, the activating agent be Sodium Polyacrylate, sodium tetraborate decahydrate, polyethenoxy ether sodium sulfate, polyoxyalkylene-
One or more in polysiloxane polymer.
Preferably, the concave convex rod lampblack absorber cleaning agent includes the raw material of following parts by weight：
35 parts of attapulgite, 25 parts of inorganic adsorbent body, 1.5 parts of isostearoyl base isopropyl titanate, neopelex 7.5
Part, 7.5 parts of glycine betaine, 1 part of plant essence, 1.5 parts of sodium citrate, 10 parts of cocoanut fatty acid diethanolamide, triethanolamine 2
Part, 12 parts of aliphatic acid polyethenoxy ether, 10 parts of APG APG, 2 parts of enuatrol, 0.5 part of ethylparaben alcohol, activating agent 4
Part, 65 parts of deionized water.
Present invention also offers a kind of preparation method of concave convex rod lampblack absorber cleaning agent, comprise the following steps：
Step one, deionized water is placed in 90 DEG C of water-baths of water-bath 60- and heated, sodium citrate is added into water, is constantly stirred
Mix, it is to be dissolved completely after sequentially add alkyl sugar APG, cocoanut fatty acid diethanolamide, it is to be dissolved completely after, add fatty
Sour APEO obtains mixed liquor A；
Step 2, triethanolamine is added in mixed liquor A made from step one, and detergent alkylate sulphur is added until completely dissolved
Sour sodium, it is to be dissolved to add enuatrol completely, continue to stir, after stirring, add essence, ethylparaben alcohol, mixed
Liquid B；
Step 3, attapulgite, inorganic adsorbent body, isostearoyl base isopropyl titanate and glycine betaine are added in pulverizing mill, if
Determine 80-100 DEG C of pulverizing mill temperature, with 1200-1600 r/min rotating speed high speed dispersing and disintegrating 10-20min, promote microfibre powder
Body boundling is dispersed throughout refinement, then adds activating agent, continues to activate 3-5min, obtains active fine mixture C；
Step 4, addition homogenizer is mixed with fine mixture C made from step 3 by mixed liquid B made from step 2
In, mixing time 1-2 hours, speed of agitator 800-1000r/min obtain finished product concave convex rod lampblack absorber cleaning agent.
Preferably, water-bath temperature is 75 DEG C in the step one.
Preferably, in the step 3 pulverizing mill temperature be 90 DEG C, the r/min of rotating speed 5 1400, refinement time 15min, work
In change time 4min, step 4 mixing time be 1.5 hours, speed of agitator be 900 r/min.
Compared with prior art, the present invention has following beneficial effect：
（1）The concave convex rod lampblack absorber cleaning agent of the present invention, can be by all kinds of stubbornnesses using attapulgite, inorganic adsorbent body as main component
Adhesion is cleaned out soon for fouling, possesses the characteristics of cleaning is thorough, cleaning speed is fast.
（2）The present invention concave convex rod lampblack absorber cleaning agent with isostearoyl base isopropyl titanate, neopelex,
Glycine betaine, sodium citrate, cocoanut fatty acid diethanolamide, triethanolamine, aliphatic acid polyethenoxy ether, APG APG,
Enuatrol, ethylparaben alcohol, activating agent are slave part so that product has that dirt-removing power is strong, water-soluble speed fast, to grease
Solubilising power is strong, to no skin irritation the characteristics of, while making the biodegradation of product becomes more preferable, environmental pollution is small.
（3）The concave convex rod lampblack absorber cleaning agent of the present invention with the addition of different types of essence, and the use of essence makes cleaning agent
With exhilarating breath, while can cover when stink makes to wash lampblack absorber has pure and fresh sensation.
（4）The preparation method of the concave convex rod lampblack absorber cleaning agent of the present invention, its material cost is relatively low, raw material is easy to get and prepares
Method is simple, and technique is concise, is adapted to large-scale industrial production, is clipped and good application prospect with higher practicality.
Embodiment
With reference to specific embodiment, the technical scheme in the embodiment of the present invention is clearly and completely described, shown
So, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on the reality in the present invention
Example is applied, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made all belongs to
In the scope of protection of the invention.
Embodiment 1.
The concave convex rod lampblack absorber cleaning agent of the present embodiment, includes the raw material of following parts by weight：
30 parts of attapulgite, 20 parts of vermiculite, 1 part of isostearoyl base isopropyl titanate, 5 parts of neopelex, glycine betaine 5
Part, 0.1 part of flavoring pineapple essence, 0.5 part of sodium citrate, 5 parts of cocoanut fatty acid diethanolamide, 1 part of triethanolamine, fatty acid polyglycol
5 parts of oxygen vinethene, 5 parts of APG APG, 0.5 part of enuatrol, 0.1 part of ethylparaben alcohol, polyethenoxy ether sodium sulfate 2
Part, 50 parts of deionized water.
The preparation method of the concave convex rod lampblack absorber cleaning agent of the present embodiment, comprises the following steps：
Step one, deionized water is placed in 60 DEG C of water-baths of water-bath and heated, sodium citrate is added into water, is stirred continuously, is treated
Sequentially add fatty alcohol, alkyl sugar APG, cocoanut fatty acid diethanolamide after dissolving completely, it is to be dissolved completely after, addition fat
Fat acid APEO obtains mixed liquor A；
Step 2, triethanolamine is added in mixed liquor A made from step one, and detergent alkylate sulphur is added until completely dissolved
Sour sodium, it is to be dissolved to add enuatrol completely, continue to stir, after stirring, add essence, ethylparaben alcohol, mixed
Liquid B；
Step 3, attapulgite, inorganic adsorbent body, isostearoyl base isopropyl titanate and glycine betaine are added in pulverizing mill, if
Determine 80 DEG C of pulverizing mill temperature, with 1200r/min rotating speed high speed dispersing and disintegrating 10min, promote microfibre powder boundling abundant
Dispersing and disintegrating, then adds polyethenoxy ether sodium sulfate, continues to activate 3min, obtains active fine mixture C；
Step 4, addition homogenizer is mixed with fine mixture C made from step 3 by mixed liquid B made from step 2
In, mixing time 1 hour, speed of agitator 800r/min obtain finished product concave convex rod lampblack absorber cleaning agent.
Embodiment 2.
The concave convex rod lampblack absorber cleaning agent of the present embodiment, includes the raw material of following parts by weight：
40 parts of attapulgite, 30 parts of mica, 2 parts of isostearoyl base isopropyl titanate, 10 parts of neopelex, glycine betaine
10 parts, 2 parts of osmanthus flower fragrance, 2.5 parts of sodium citrate, 15 parts of cocoanut fatty acid diethanolamide, 3 parts of triethanolamine, aliphatic acid
20 parts of APEO, APG15 parts of APG, 4 parts of enuatrol, 1 part of ethylparaben alcohol, 6 parts of Sodium Polyacrylate, deionization
80 parts of water.
The preparation method of the concave convex rod lampblack absorber cleaning agent of the present embodiment, comprises the following steps：
Step one, deionized water is placed in 90 DEG C of water-baths of water-bath and heated, sodium citrate is added into water, is stirred continuously, is treated
Sequentially add fatty alcohol, alkyl sugar APG, cocoanut fatty acid diethanolamide after dissolving completely, it is to be dissolved completely after, addition fat
Fat acid APEO obtains mixed liquor A；
Step 2, triethanolamine is added in mixed liquor A made from step one, and detergent alkylate sulphur is added until completely dissolved
Sour sodium, it is to be dissolved to add enuatrol completely, continue to stir, after stirring, add essence, ethylparaben alcohol, mixed
Liquid B；
Step 3, attapulgite, inorganic adsorbent body, isostearoyl base isopropyl titanate and glycine betaine are added in pulverizing mill, if
Determine 100 DEG C of pulverizing mill temperature, with 1600 r/min rotating speed high speed dispersing and disintegrating 20min, promote microfibre powder boundling to be filled
Divide dispersing and disintegrating, then add Sodium Polyacrylate, continue to activate 5min, obtain active fine mixture C；
Step 4, addition homogenizer is mixed with fine mixture C made from step 3 by mixed liquid B made from step 2
In, mixing time 2 hours, speed of agitator 1000r/min obtain finished product concave convex rod lampblack absorber cleaning agent.
Embodiment 3.
The concave convex rod lampblack absorber cleaning agent of the present embodiment, includes the raw material of following parts by weight：
35 parts of attapulgite, 25 parts of inorganic adsorbent body, 1.5 parts of isostearoyl base isopropyl titanate, neopelex 7.5
Part, 7.5 parts of glycine betaine, 1 part of plant essence, 1.5 parts of sodium citrate, 10 parts of cocoanut fatty acid diethanolamide, triethanolamine 2
Part, 12 parts of aliphatic acid polyethenoxy ether, 10 parts of APG APG, 2 parts of enuatrol, 0.5 part of ethylparaben alcohol, the boron of ten water four
Sour 4 parts of sodium, 65 parts of deionized water.
The preparation method of the concave convex rod lampblack absorber cleaning agent of the present embodiment, comprises the following steps：
Step one, deionized water is placed in 75 DEG C of water-baths of water-bath and heated, sodium citrate is added into water, is stirred continuously, is treated
Sequentially add fatty alcohol, alkyl sugar APG, cocoanut fatty acid diethanolamide after dissolving completely, it is to be dissolved completely after, addition fat
Fat acid APEO obtains mixed liquor A；
Step 2, triethanolamine is added in mixed liquor A made from step one, and detergent alkylate sulphur is added until completely dissolved
Sour sodium, it is to be dissolved to add enuatrol completely, continue to stir, after stirring, add essence, ethylparaben alcohol, mixed
Liquid B；
Step 3, attapulgite, inorganic adsorbent body, isostearoyl base isopropyl titanate and glycine betaine are added in pulverizing mill, if
Determine 90 DEG C of pulverizing mill temperature, with 1400 r/min rotating speed high speed dispersing and disintegrating 15min, promote microfibre powder boundling abundant
Dispersing and disintegrating, then adds sodium tetraborate decahydrate, continues to activate 4min, obtains active fine mixture C；
Step 4, addition homogenizer is mixed with fine mixture C made from step 3 by mixed liquid B made from step 2
In, mixing time 1.5 hours, speed of agitator 900r/min obtain finished product concave convex rod lampblack absorber cleaning agent.
A kind of concave convex rod lampblack absorber cleaning agent of the present invention have it is green, efficient, harmless, sterilize, do not hurt hands, it is antirust, slow
The features such as erosion, cleaning agent viscosity is suitable, and denseness is suitable, and stability is good, and smell is pleasant, can efficiently go to degrease, environmental protection is right
Environment is nontoxic, and cost performance is high, it is easy to clean, and the lampblack absorber cleaning agent can remove the stain on lampblack absorber,
Removal that also can be effective to the yellow rust staining on its surface.While the preparation method of the concave convex rod lampblack absorber cleaning agent of the present invention, its material
The simple and easy to get, cost of material is relatively low, method is simple, is adapted to industrialized production, is with a wide range of applications.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It may be appreciated other embodiment.
Claims (8)
1. a kind of concave convex rod lampblack absorber cleaning agent, it is characterised in that include the raw material of following parts by weight：
30-40 parts of attapulgite, 20-30 parts of inorganic adsorbent body, 1-2 parts of isostearoyl base isopropyl titanate, detergent alkylate sulphur
Sour sodium 5-10 parts, 5-10 parts of glycine betaine, 0.1-2 parts of plant essence, 0.5-2.5 parts of sodium citrate, coco-nut oil fatty acid diethanol
5-15 parts of acid amides, 1-3 parts of triethanolamine, 5-20 parts of aliphatic acid polyethenoxy ether, 5-15 parts of APG APG, enuatrol 0.5-
4 parts, 0.1-1 parts of ethylparaben alcohol, 2-6 parts of activating agent, 50-80 parts of deionized water.
2. concave convex rod lampblack absorber cleaning agent according to claim 1, it is characterised in that the concave convex rod lampblack absorber cleaning agent
Include the raw material of following parts by weight：
35 parts of attapulgite, 25 parts of inorganic adsorbent body, 1.5 parts of isostearoyl base isopropyl titanate, neopelex 7.5
Part, 7.5 parts of glycine betaine, 1 part of plant essence, 1.5 parts of sodium citrate, 10 parts of cocoanut fatty acid diethanolamide, triethanolamine 2
Part, 12 parts of aliphatic acid polyethenoxy ether, 10 parts of APG APG, 2 parts of enuatrol, 0.5 part of ethylparaben alcohol, activating agent 4
Part, 65 parts of deionized water.
3. concave convex rod lampblack absorber cleaning agent according to claim 1 or 2, it is characterised in that the inorganic adsorbent body is cloud
One or more in mother, vermiculite, montmorillonite, serpentine.
4. concave convex rod lampblack absorber cleaning agent according to claim 1 or 2, it is characterised in that the plant essence is lemon
One or more in essence, peach flavor, lily essence, osmanthus flower fragrance, flavoring rose essence, cucumber essence, flavoring pineapple essence.
5. concave convex rod lampblack absorber cleaning agent according to claim 1 or 2, it is characterised in that the activating agent is polypropylene
One or more in sour sodium, sodium tetraborate decahydrate, polyethenoxy ether sodium sulfate, polyoxyalkylene-polysiloxane polymer.
6. a kind of preparation method of concave convex rod lampblack absorber cleaning agent according to claim 1 or 2, it is characterised in that including
Following steps：
Step one, deionized water is placed in 60~90 DEG C of water-baths of water-bath and heated, sodium citrate is added into water, is constantly stirred
Mix, it is to be dissolved completely after sequentially add alkyl sugar APG, cocoanut fatty acid diethanolamide, it is to be dissolved completely after, add fatty
Sour APEO obtains mixed liquor A；
Step 2, triethanolamine is added in mixed liquor A made from step one, and detergent alkylate sulphur is added until completely dissolved
Sour sodium, it is to be dissolved to add enuatrol completely, continue to stir, after stirring, add essence, ethylparaben alcohol, mixed
Liquid B；
Step 3, attapulgite, inorganic adsorbent body, isostearoyl base isopropyl titanate and glycine betaine are added in pulverizing mill, if
Determine 80-100 DEG C of pulverizing mill temperature, with 1200-1600 r/min rotating speed high speed dispersing and disintegrating 10-20min, promote microfibre powder
Body boundling is dispersed throughout refinement, then adds activating agent, continues to activate 3-5min, obtains active fine mixture C；
Step 4, addition homogenizer is mixed with fine mixture C made from step 3 by mixed liquid B made from step 2
In, mixing time 1-2 hours, speed of agitator 800-1000r/min obtain finished product concave convex rod lampblack absorber cleaning agent.
7. the preparation method of concave convex rod lampblack absorber cleaning agent according to claim 6, it is characterised in that in the step one
Water-bath pot temperature is 75 DEG C.
8. the preparation method of concave convex rod lampblack absorber cleaning agent according to claim 6, it is characterised in that in the step 3
Pulverizing mill temperature is 90 DEG C, the r/min of rotating speed 5 1400, refinement time 15min, soak time 4min, mixing time in step 4
It is 900 r/min for 1.5 hours, speed of agitator.