CN106977842A - A kind of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material and preparation method thereof - Google Patents
A kind of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material and preparation method thereof Download PDFInfo
- Publication number
- CN106977842A CN106977842A CN201710219734.2A CN201710219734A CN106977842A CN 106977842 A CN106977842 A CN 106977842A CN 201710219734 A CN201710219734 A CN 201710219734A CN 106977842 A CN106977842 A CN 106977842A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- wood material
- radiation proof
- radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material, it is characterised in that includes the raw material of following parts by weight:5 10 parts of radiation-resistant glass agent, 46 parts of eaglewood powder, 40 50 parts of timber mill leftover bits, 70 80 parts of Corvic, 13 parts of nano zine oxide, 24 parts of nano titanium oxide, 0.5 3 parts of pyrethrins, 5 15 parts of fire retardant, 5 15 parts of nitrile rubber, 35 parts of ultra-violet absorber, 36 parts of barium zinc stabilizer, 59 parts of antistatic additive, 5 10 parts of coupling agent, 13 parts of lubricant.The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present invention has radiation proof, resisting ultraviolet radiation, ageing-resistant, fire resistance; it is material Sterilized sanitation, high mechanical strength, rub resistance, ageing-resistant; the preparation method of the plastic-wood material of the present invention is using discarded leftover pieces simultaneously; save resource, protect environment; material cost is relatively low, raw material is easy to get and technique concise, has higher practical value and good application prospect as decoration material.
Description
Technical field
The present invention relates to plastic wood sheet material technical field, and in particular to a kind of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material and
Its preparation method.
Background technology
As global resources are increasingly exhausted, social environment consciousness is increasingly surging, and timber and petrochemical industry are produced in production and life
Product application proposes higher requirement.Plastic-wood material is as a kind of emerging environment-friendly materials, and it is mainly with plant fiber material
For major ingredient, plastics synthesis is added, a kind of extensive composite of applicability is formed.Due to modeling wood have concurrently plastics Waterproof corrosion and
Two kinds of characteristics of texture of timber so that it turns into a kind of function admirable and very durable outdoor building materials(Floor, fence, bench,
Gardens or waterfront landscape etc.);Also replace the Wood member that harbour, harbour etc. are used, it may also be used for substitute timber and make various
Packing material, pallet, warehouse pallet etc. are too numerous to enumerate, and purposes is extremely wide.Deserve to be called environmental protection truly, energy-conservation, resource
The novel products of regeneration.
But often because containing more string in plastic-wood material, so that during long-term use, especially
It is that in a humidity environment, plastic-wood material easily causes bacterial growth because moisture is more, so that plastic-wood material goes mouldy
Scrap, and then improve use cost.
Current plastic-wood material also has the deficiency of many aspect of performances, it is impossible to substitute timber completely, makes the sector product
The application in market is restricted at home, and the plastic-wood material density of such as PE, PP base material is larger, big from creepage type, is not suitable for building
Build the application such as exterior wall.After the foaming of the base materials such as PS, ABS, PVC, in outdoor application, weather resistance is poor, is applicable and is greatly limited
Property, while toughness of material is poor, PE, PP base material plastic-wood material are less than in terms of intensity.The co-extruded plastic-wood production of exploitation in other nearly 2 years
Product, although such as Plastic-wood co-extruded metal material, Plastic-wood co-extruded modified plastics can partly solve problem above, production technology is numerous
Trivial, product percent defective is high, there is materials at two layers when in use and peels off risk.Therefore at present on the market plastic-wood material in density, strong
Quality and performance in terms of degree, weatherability also need to be greatly improved and could meet the application in market.
Nowadays electromagnetic radiation pollution is increasingly severe, and we suddenly lack the plastic-wood material of energy radiation-screening.Although nowadays disclosing
Radiation proof building materials in have some broad spectrum type formulas, but the broad spectrum type formula is applied in plastic-wood material radiation-proof effect not
It is good, it is necessary to improve.The Radiation-proof wood-plastic material of prevalence is in the structure of plastic-wood material plus radiation proof currently on the market simultaneously
Layer, to reach radiation-proof effect, cost is big and not easy to operate.
The content of the invention
For the defect of prior art, it is an object of the invention to provide a kind of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material,
The plastic-wood material has radiation proof, resisting ultraviolet radiation, an ageing-resistant, fire resistance, material Sterilized sanitation, high mechanical strength, resistance to
It is friction, ageing-resistant, while the preparation method of the plastic-wood material of the present invention has been saved resource, has been protected ring using discarded leftover pieces
Border, material cost is relatively low, raw material is easy to get and technique concise, has higher practical value and good as decoration material
Application prospect.
The present invention solves technical problem and adopted the following technical scheme that:
The invention provides a kind of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material, include the raw material of following parts by weight:
5-10 parts of radiation-resistant glass agent, 4-6 parts of eaglewood powder, leftover bits 40-50 parts of timber mill, Corvic 70-80
Part, 1-3 parts of nano zine oxide, 2-4 parts of nano titanium oxide, 0.5-3 parts of pyrethrins, 5-15 parts of fire retardant, nitrile rubber 5-
15 parts, 3-5 parts of ultra-violet absorber, 3-6 parts of barium zinc stabilizer, 5-9 parts of antistatic additive, 5-10 parts of coupling agent, lubricant 1-3
Part.
Preferably, the plastic-wood material includes the raw material of following parts by weight:
It is 8 parts of radiation-resistant glass agent, 5 parts of eaglewood powder, 45 parts of timber mill leftover bits, 75 parts of Corvic, nano oxidized
2 parts of zinc, 3 parts of nano titanium oxide, 1.8 parts of pyrethrins, 10 parts of fire retardant, 10 parts of nitrile rubber, 4 parts of ultra-violet absorber,
4.5 parts of barium zinc stabilizer, 7 parts of antistatic additive, 8 parts of coupling agent, 2 parts of lubricant.
Preferably, the radiation-resistant glass agent is the one or more in barium carbonate, strontium carbonate, barium sulfate.
Preferably, the fire retardant is the one or more in eight bromo ether, triphenyl phosphate, APP.
Preferably, the coupling agent is one kind or several in silane coupler, titanate coupling agent, aluminate coupling agent
Kind.
Preferably, the antistatic additive is ethoxylated fat race alkylamine antistatic additive;The ultra-violet absorber is
One kind in ultra-violet absorber UV531, light stabilizer 770;The lubricant is one kind in zinc stearate, calcium stearate.
Present invention also offers a kind of preparation method of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material, comprise the following steps:
Step one, timber mill leftover bits are added in pulverizer and crushed, cross after 200 mesh sieves the mistake for adding that concentration is 15%-25%
Hydrogen peroxide solution is bleached, will dried 2-3 hours at 50-60 DEG C in the wood powder feeding dryer after bleaching, and feeding ultraviolet disappears
Malicious room sterilization obtains wood powder A in 1-2 hours;
Step 2, wood powder A prepared by step one, eaglewood powder, Corvic, nitrile rubber mixing are added in banbury
85-95 DEG C is heated to, after being incubated 8-12 minutes, radiation-resistant glass agent, nano zine oxide, nano titanium oxide, Dalmatian chrysanthemum is added
Ester, fire retardant, ultra-violet absorber, barium zinc stabilizer, antistatic additive, coupling agent, lubricant, are warming up to 115-125 DEG C, mixing
10-15 minutes, obtain mixture B;
Step 3, mixture B is added in feeding double screw extruder and carries out segmented temperature control extrusion, cooling, pelletizing, segmented
Temperature control divides 6 sections of temperature controls, and temperature is respectively:The temperature of section one is 145-155 DEG C, and the temperature of section two is 155-165 DEG C, the temperature of section three
Spend for 165-175 DEG C, the temperature of section four is 175-185 DEG C, the merging area temperature of section five is 185-195 DEG C, the head temperature of section six
Spend for 195 DEG C, screw speed is 140-160r/min, head pressure is 5.5-6.5MPa, is added after extrusion profile cooling is qualitative
The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material invented is cut off in cut-to-length machine.
Preferably, the step is:Step one, timber mill leftover bits are added in pulverizer and crushed, crossed after 200 mesh sieves
Concentration is added to bleach for 20% hydrogenperoxide steam generator, it is small by drying 2.5 at 55 DEG C in the wood powder feeding dryer after bleaching
When, feeding UV sterilizing chamber sterilization obtains wood powder A in 1.5 hours;
Step 2, wood powder A prepared by step one, eaglewood powder, Corvic, nitrile rubber mixing are added in banbury
90 DEG C are heated to, after being incubated 10 minutes, radiation-resistant glass agent, nano zine oxide, nano titanium oxide, pyrethrins, resistance is added
Agent, ultra-violet absorber, barium zinc stabilizer, antistatic additive, coupling agent, lubricant are fired, 120 DEG C are warming up to, kneads 13 minutes, obtains
To mixture B;
Step 3, mixture B is added in feeding double screw extruder and carries out segmented temperature control extrusion, cooling, pelletizing, segmented
Temperature control divides 6 sections of temperature controls, and temperature is respectively:The temperature of section one is 150 DEG C, and the temperature of section two is 160 DEG C, and the temperature of section three is 170
DEG C, the temperature of section four is 180 DEG C, and the merging area temperature of section five is 190 DEG C, and the head temperature of section six is 195 DEG C, and screw speed is
150r/min, head pressure is 6MPa, and the anti-spoke for cutting off and being invented in cut-to-length machine is added after extrusion profile cooling is qualitative
Penetrate weather-resistance flame-retardant environment-protecting plastic wood material.
Compared with prior art, the present invention has following beneficial effect:
(1)The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present invention with the addition of radiation-resistant glass agent, predominantly barium carbonate, carbonic acid
One kind in strontium, barium sulfate, because these additives are to X rays and gamma-ray extremely strong shielding action, therefore, it is possible to significantly
Increase the shielding properties of plastic-wood material.
(2)The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present invention employs timber mill leftover bits coming as wood powder
Source, on the basis of discarded object is made full use of, has saved resource, has protected environment, meets the theory of recycling economy, and realizing can
Sustainable development;Wood powder is bleached and sterilized in preparation process simultaneously, the color for the plank road plate prepared both has been ensure that
Distinctness, causes its safety and sanitation again, sterile nontoxic.
(3)The barium zinc stabilizer of the radiation proof weather-resistance flame-retardant environment-protecting plastic wood material addition of the present invention, it can not only replace
The poisonous stabilizer such as lead cadmium salt class and organic tin, and with fairly good heat endurance, photostability and the transparency and
Color power, can make finer and close Corvic structure, fusion rate increase, improve the mobility of material, extrusion processing work
Skill is good, and product quality stability is high.
(4)Nano zine oxide, the nano titanium oxide energy of the radiation proof weather-resistance flame-retardant environment-protecting plastic wood material addition of the present invention
Enough effective shielding ultraviolet rays, are effectively increased plastic-wood material ageing-resistant performance, and nano titanium oxide also has photocatalysis in addition
It can be catalyzed, photodissociation is attached to the organic matters such as the various formaldehyde of body surface and part inorganic matter, the work(of purification air can be played
Energy.
(5)The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present invention, which with the addition of pyrethrins, can increase plastic-wood material
Expelling parasite killing ability, the generation for the phenomenon that prevents from damaging by worms increases the service life of material, while fire retardant is also added, Neng Gouyou
The fire protection flame retarding ability of effect increase plastic-wood material, has greatly reinforced the ability to ward off risks of plastic-wood material.
(6)The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present invention has saved resource, has protected environment, material cost compared with
Low, raw material is easy to get and technique is concise, has higher practical value and good application prospect as decoration material.
Embodiment
With reference to specific embodiment, the technical scheme in the embodiment of the present invention is clearly and completely described, shown
So, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on the reality in the present invention
Example is applied, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made all belongs to
In the scope of protection of the invention.
Embodiment 1.
The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present embodiment, includes the raw material of following parts by weight:
It is 5 parts of radiation-resistant glass agent, 4 parts of eaglewood powder, 40 parts of timber mill leftover bits, 70 parts of Corvic, nano oxidized
1 part of zinc, 2 parts of nano titanium oxide, 0.5 part of pyrethrins, 5 parts of fire retardant, 5 parts of nitrile rubber, 3 parts of ultra-violet absorber, barium
3 parts of zinc stabilizer, 5 parts of antistatic additive, 5 parts of coupling agent, 1 part of lubricant.
Radiation-resistant glass agent is barium carbonate in the present embodiment.
Fire retardant is eight bromo ether in the present embodiment.
Coupling agent is silane coupler in the present embodiment.
Antistatic additive is ethoxylated fat race alkylamine antistatic additive in the present embodiment;Ultra-violet absorber is ultraviolet
Absorbent UV531;Lubricant is zinc stearate.
The preparation method of the radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present embodiment, comprises the following steps:
Step one, timber mill leftover bits are added in pulverizer and crushed, cross after 200 mesh sieves the peroxidating for adding that concentration is 15%
Hydrogen solution is bleached, and the wood powder after bleaching is sent into dry 2 hours, the feeding UV sterilizing chamber sterilization 1 at 50 DEG C in dryer
Hour obtains wood powder A;
Step 2, wood powder A prepared by step one, eaglewood powder, Corvic, nitrile rubber mixing are added in banbury
It is heated to 85 DEG C, after insulation 8 minutes, adds radiation-resistant glass agent, nano zine oxide, nano titanium oxide, pyrethrins, fire-retardant
Agent, ultra-violet absorber, barium zinc stabilizer, antistatic additive, coupling agent, lubricant, are warming up to 115 DEG C, knead 10 minutes, obtain
Mixture B;
Step 3, mixture B is added in feeding double screw extruder and carries out segmented temperature control extrusion, cooling, pelletizing, segmented
Temperature control divides 6 sections of temperature controls, and temperature is respectively:The temperature of section one is 145 DEG C, and the temperature of section two is 155 DEG C, and the temperature of section three is 165
DEG C, the temperature of section four is 175 DEG C, and the merging area temperature of section five is 185 DEG C, and the head temperature of section six is 195 DEG C, and screw speed is
140r/min, head pressure is 5.5MPa, and add that cut-out in cut-to-length machine invented after extrusion profile cooling is qualitative is anti-
Radiate weather-resistance flame-retardant environment-protecting plastic wood material.
Embodiment 2.
The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present embodiment, includes the raw material of following parts by weight:
It is 10 parts of radiation-resistant glass agent, 6 parts of eaglewood powder, 50 parts of timber mill leftover bits, 80 parts of Corvic, nano oxidized
3 parts of zinc, 4 parts of nano titanium oxide, 3 parts of pyrethrins, 15 parts of fire retardant, 15 parts of nitrile rubber, 5 parts of ultra-violet absorber, barium
6 parts of zinc stabilizer, 9 parts of antistatic additive, 10 parts of coupling agent, 3 parts of lubricant.
Radiation-resistant glass agent is strontium carbonate in the present embodiment.
Fire retardant is triphenyl phosphate in the present embodiment.
Titanate coupling agent in the present embodiment.
Antistatic additive is ethoxylated fat race alkylamine antistatic additive in the present embodiment;Ultra-violet absorber is stable for light
Agent 770;Lubricant is calcium stearate.
The preparation method of the radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present embodiment, comprises the following steps:
Step one, timber mill leftover bits are added in pulverizer and crushed, cross after 200 mesh sieves the peroxidating for adding that concentration is 25%
Hydrogen solution is bleached, and the wood powder after bleaching is sent into dry 3 hours, the feeding UV sterilizing chamber sterilization 2 at 60 DEG C in dryer
Hour obtains wood powder A;
Step 2, wood powder A prepared by step one, eaglewood powder, Corvic, nitrile rubber mixing are added in banbury
95 DEG C are heated to, after being incubated 12 minutes, radiation-resistant glass agent, nano zine oxide, nano titanium oxide, pyrethrins, resistance is added
Agent, ultra-violet absorber, barium zinc stabilizer, antistatic additive, coupling agent, lubricant are fired, 125 DEG C are warming up to, kneads 15 minutes, obtains
To mixture B;
Step 3, mixture B is added in feeding double screw extruder and carries out segmented temperature control extrusion, cooling, pelletizing, segmented
Temperature control divides 6 sections of temperature controls, and temperature is respectively:The temperature of section one is 155 DEG C, and the temperature of section two is 165 DEG C, and the temperature of section three is 175
DEG C, the temperature of section four is 185 DEG C, and the merging area temperature of section five is 195 DEG C, and the head temperature of section six is 195 DEG C, and screw speed is
160r/min, head pressure is 6.5MPa, and add that cut-out in cut-to-length machine invented after extrusion profile cooling is qualitative is anti-
Radiate weather-resistance flame-retardant environment-protecting plastic wood material.
Embodiment 3.
The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present embodiment, includes the raw material of following parts by weight:
It is 8 parts of radiation-resistant glass agent, 5 parts of eaglewood powder, 45 parts of timber mill leftover bits, 75 parts of Corvic, nano oxidized
2 parts of zinc, 3 parts of nano titanium oxide, 1.8 parts of pyrethrins, 10 parts of fire retardant, 10 parts of nitrile rubber, 4 parts of ultra-violet absorber,
4.5 parts of barium zinc stabilizer, 7 parts of antistatic additive, 8 parts of coupling agent, 2 parts of lubricant.
Radiation-resistant glass agent is barium sulfate in the present embodiment.
Fire retardant is APP in the present embodiment.
Coupling agent is aluminate coupling agent in the present embodiment.
Antistatic additive is ethoxylated fat race alkylamine antistatic additive in the present embodiment;Ultra-violet absorber is ultraviolet
Absorbent UV531;Lubricant is zinc stearate.
The preparation method of the radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present embodiment, comprises the following steps:
Step one, timber mill leftover bits are added in pulverizer and crushed, cross after 200 mesh sieves the peroxidating for adding that concentration is 20%
Hydrogen solution is bleached, and the wood powder after bleaching is sent into dry 2.5 hours, the feeding UV sterilizing chamber sterilization at 55 DEG C in dryer
Obtain wood powder A within 1.5 hours;
Step 2, wood powder A prepared by step one, eaglewood powder, Corvic, nitrile rubber mixing are added in banbury
90 DEG C are heated to, after being incubated 10 minutes, radiation-resistant glass agent, nano zine oxide, nano titanium oxide, pyrethrins, resistance is added
Agent, ultra-violet absorber, barium zinc stabilizer, antistatic additive, coupling agent, lubricant are fired, 120 DEG C are warming up to, kneads 13 minutes, obtains
To mixture B;
Step 3, mixture B is added in feeding double screw extruder and carries out segmented temperature control extrusion, cooling, pelletizing, segmented
Temperature control divides 6 sections of temperature controls, and temperature is respectively:The temperature of section one is 150 DEG C, and the temperature of section two is 160 DEG C, and the temperature of section three is 170
DEG C, the temperature of section four is 180 DEG C, and the merging area temperature of section five is 190 DEG C, and the head temperature of section six is 195 DEG C, and screw speed is
150r/min, head pressure is 6MPa, and the anti-spoke for cutting off and being invented in cut-to-length machine is added after extrusion profile cooling is qualitative
Penetrate weather-resistance flame-retardant environment-protecting plastic wood material.
The performance test results of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material are as follows made from various embodiments above:
Tensile strength/MPa | Elongation at break(%) | Fire-protection rating | Environmental protection grade | |
Embodiment 1 | 37 | 10.7 | B1 | E1 |
Embodiment 2 | 36 | 11.5 | B1 | E1 |
Embodiment 3 | 36 | 12.1 | B1 | E1 |
Comparative example | 27 | 8.4 | B2 | E2 |
The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material of the present invention has radiation proof, resisting ultraviolet radiation, ageing-resistant, anti-flammability
Can, it is material Sterilized sanitation, high mechanical strength, rub resistance, ageing-resistant, while the preparation method of the plastic-wood material of the present invention is using useless
Leftover pieces are abandoned, resource has been saved, has protected environment, material cost is relatively low, raw material is easy to get and technique concise, is used as decoration
Material has higher practical value and good application prospect.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It may be appreciated other embodiment.
Claims (8)
1. a kind of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material, it is characterised in that include the raw material of following parts by weight:
5-10 parts of radiation-resistant glass agent, 4-6 parts of eaglewood powder, leftover bits 40-50 parts of timber mill, Corvic 70-80
Part, 1-3 parts of nano zine oxide, 2-4 parts of nano titanium oxide, 0.5-3 parts of pyrethrins, 5-15 parts of fire retardant, nitrile rubber 5-
15 parts, 3-5 parts of ultra-violet absorber, 3-6 parts of barium zinc stabilizer, 5-9 parts of antistatic additive, 5-10 parts of coupling agent, lubricant 1-3
Part.
2. radiation proof weather-resistance flame-retardant environment-protecting plastic wood material according to claim 1, it is characterised in that the plastic-wood material bag
Include the raw material of following parts by weight:
It is 8 parts of radiation-resistant glass agent, 5 parts of eaglewood powder, 45 parts of timber mill leftover bits, 75 parts of Corvic, nano oxidized
2 parts of zinc, 3 parts of nano titanium oxide, 1.8 parts of pyrethrins, 10 parts of fire retardant, 10 parts of nitrile rubber, 4 parts of ultra-violet absorber,
4.5 parts of barium zinc stabilizer, 7 parts of antistatic additive, 8 parts of coupling agent, 2 parts of lubricant.
3. radiation proof weather-resistance flame-retardant environment-protecting plastic wood material according to claim 1 or 2, it is characterised in that the radiation proof
Screener is the one or more in barium carbonate, strontium carbonate, barium sulfate.
4. radiation proof weather-resistance flame-retardant environment-protecting plastic wood material according to claim 1 or 2, it is characterised in that the fire retardant
For the one or more in eight bromo ether, triphenyl phosphate, APP.
5. radiation proof weather-resistance flame-retardant environment-protecting plastic wood material according to claim 1 or 2, it is characterised in that the coupling agent
For the one or more in silane coupler, titanate coupling agent, aluminate coupling agent.
6. radiation proof weather-resistance flame-retardant environment-protecting plastic wood material according to claim 1 or 2, it is characterised in that described antistatic
Agent is ethoxylated fat race alkylamine antistatic additive;The ultra-violet absorber is ultra-violet absorber UV531, light stabilizer
One kind in 770;The lubricant is one kind in zinc stearate, calcium stearate.
7. a kind of preparation method of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material according to claim 1 or 2, its feature exists
In comprising the following steps:
Step one, timber mill leftover bits are added in pulverizer and crushed, cross after 200 mesh sieves the mistake for adding that concentration is 15%-25%
Hydrogen peroxide solution is bleached, and will be dried 2-3 hours at 50-60 DEG C in the wood powder feeding dryer after bleaching, feeding ultraviolet disappears
Malicious room sterilization obtains wood powder A in 1-2 hours;
Step 2, wood powder A prepared by step one, eaglewood powder, Corvic, nitrile rubber mixing are added in banbury
85-95 DEG C is heated to, after being incubated 8-12 minutes, radiation-resistant glass agent, nano zine oxide, nano titanium oxide, Dalmatian chrysanthemum is added
Ester, fire retardant, ultra-violet absorber, barium zinc stabilizer, antistatic additive, coupling agent, lubricant, are warming up to 115-125 DEG C, mixing
10-15 minutes, obtain mixture B;
Step 3, mixture B is added in feeding double screw extruder and carries out segmented temperature control extrusion, cooling, pelletizing, segmented
Temperature control divides 6 sections of temperature controls, and temperature is respectively:The temperature of section one is 145-155 DEG C, and the temperature of section two is 155-165 DEG C, the temperature of section three
Spend for 165-175 DEG C, the temperature of section four is 175-185 DEG C, the merging area temperature of section five is 185-195 DEG C, the head temperature of section six
Spend for 195 DEG C, screw speed is 140-160r/min, head pressure is 5.5-6.5MPa, is added after extrusion profile cooling is qualitative
The radiation proof weather-resistance flame-retardant environment-protecting plastic wood material invented is cut off in cut-to-length machine.
8. the preparation method of radiation proof weather-resistance flame-retardant environment-protecting plastic wood material according to claim 7, it is characterised in that described
Step is:Step one, timber mill leftover bits are added in pulverizer and crushed, cross after 200 mesh sieves the peroxide for adding that concentration is 20%
Change hydrogen solution bleaching, will be dried 2.5 hours at 55 DEG C in the wood powder feeding dryer after bleaching, feeding UV sterilizing chamber disappears
Poison obtains wood powder A in 1.5 hours;
Step 2, wood powder A prepared by step one, eaglewood powder, Corvic, nitrile rubber mixing are added in banbury
90 DEG C are heated to, after being incubated 10 minutes, radiation-resistant glass agent, nano zine oxide, nano titanium oxide, pyrethrins, resistance is added
Agent, ultra-violet absorber, barium zinc stabilizer, antistatic additive, coupling agent, lubricant are fired, 120 DEG C are warming up to, kneads 13 minutes, obtains
To mixture B;
Step 3, mixture B is added in feeding double screw extruder and carries out segmented temperature control extrusion, cooling, pelletizing, segmented
Temperature control divides 6 sections of temperature controls, and temperature is respectively:The temperature of section one is 150 DEG C, and the temperature of section two is 160 DEG C, and the temperature of section three is 170
DEG C, the temperature of section four is 180 DEG C, and the merging area temperature of section five is 190 DEG C, and the head temperature of section six is 195 DEG C, and screw speed is
150r/min, head pressure is 6MPa, and the anti-spoke for cutting off and being invented in cut-to-length machine is added after extrusion profile cooling is qualitative
Penetrate weather-resistance flame-retardant environment-protecting plastic wood material.