CN106974485A - A kind of Concave-convex clay rod health mat blanket - Google Patents
A kind of Concave-convex clay rod health mat blanket Download PDFInfo
- Publication number
- CN106974485A CN106974485A CN201710176533.9A CN201710176533A CN106974485A CN 106974485 A CN106974485 A CN 106974485A CN 201710176533 A CN201710176533 A CN 201710176533A CN 106974485 A CN106974485 A CN 106974485A
- Authority
- CN
- China
- Prior art keywords
- concave
- attapulgite
- convex clay
- clay rod
- sodium carboxymethylcellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of Concave-convex clay rod health mat blanket, weigh water, sodium carboxymethylcellulose, sodium citrate, potassium sorbate respectively according to a certain percentage, it is sufficiently stirred for after mixing, make sodium carboxymethylcellulose fully expanded, add appropriate attapulgite compound, and stir, sticky thickener is made；The thin slice that thickness is 2~5 millimeters is cast or be rolled into this thickener, thin slice 24 26 hours are stood, after drying and dewatering after its abundant gel, you can spongiform gel diaphragm is made.The present invention is using the modified attapulgite clay with strong absorption property as primary raw material, and be equipped with the making of volatile Chinese medicine, make product can not only quick adsorption padding for spring bed release formaldehyde and bed body around benzene, ammonia, TVOC pernicious gases, and making product with building up health, tranquillizing the mind by relieving convulsion, promotion are slept, the function of killing pests and suppressing bacteria.
Description
Technical field
It is exactly a kind of Concave-convex clay rod health mat blanket the present invention relates to pad blanket field.
Background technology
It is reported that the padding for spring bed that people generally use at present contains formaldehyde due to largely having used in process of production
Glue, result in mattress generally existing in use and the problem of Form aldehyde release is exceeded.What the exceeded release of these formaldehyde had can
Up to several years, the healthy of people is seriously endangered, to this problem, the producer of production padding for spring bed also lacks effectively
Solution.For the formaldehyde in air, people can carry out purified treatment using air purifying preparation, still, for seat dream
The formaldehyde of mattress release is thought, because human body is directly contacted with mattress, even if being also difficult to avoid that human body by first using air purifying preparation
The harm of aldehyde.
The content of the invention
It is an object of the invention to produce one kind can quick adsorption formaldehyde, benzene, TVOC pernicious gases, and can adjust
Function of human body, promotes Concave-convex clay rod health mat blanket of sleep and preparation method thereof, is padded on padding for spring bed, can
Directly to adsorb the formaldehyde of mattress release, human body is prevented effectively from by the harm of formaldehyde, health is protected.
In order to realize purpose of the present invention, the present invention have chosen the natural minerals attapulgite with strong absorption property
Clay is main material, to be slept with tranquillizing the mind by relieving convulsion, promotion, the Chinese medicine of desinsection degerming functions, and preservative, gelling
Agent, chelating agent are auxiliary material, are refined through scientific method.
A kind of Concave-convex clay rod health mat blanket, it is characterised in that：Preparation method comprises the following steps：
（1）Mass concentration is equably sprayed on Concave-convex clay rod for 4-6% hydrochloric acid, make its fully soak after feeding pair
Rolled, be rolled into after the sheet that thickness is 1 millimeter, placement is lived for 24-26 hours in roller machine or three-roller
Change, then dry, be calcined 3~4 hours at a temperature of 300 DEG C~400 DEG C, grind to form fineness for 100-200 mesh powders, i.e.,
Obtain modified attapulgite clay standby；
（2）According to following part by weight dispensing：
Modified attapulgite clay 100-110, magnetite 20-25, notopterygium root 15-20, chrysanthemum 10-15, alum 2-4；
Dispensing is put into jointly in homogenizer and stirred, it is sufficiently mixed the uniform attapulgite compound that obtains with standby；
（3）According to 100-110：3-3.5：1-1.2：0.2-0.3 ratio weighs water, sodium carboxymethylcellulose, citric acid respectively
It is sufficiently stirred for after sodium, potassium sorbate, mixing, makes sodium carboxymethylcellulose fully expanded, adds appropriate attapulgite mixing
Material, and stir, sticky thickener is made；The thin slice that thickness is 2~5 millimeters is cast or be rolled into this thickener, by thin slice
24-26 hours are stood, after drying and dewatering after its abundant gel, you can spongiform gel diaphragm is made.
Described a kind of Concave-convex clay rod health mat blanket, it is characterised in that mass concentration is the consumption of 4-6% hydrochloric acid
For the 1-3% of Concave-convex clay rod.
A kind of described Concave-convex clay rod health mat blanket, it is characterised in that the consumption of described attapulgite compound be water,
Sodium carboxymethylcellulose, sodium citrate, the 4-10% of potassium sorbate gross weight.
Its specific method and program are as follows：
A, Concave-convex clay rod processing
Concave-convex clay rod is a kind of natural minerals clay using attapulgite as key component.Attapulgite is with special fibre
Tie up the alumina magnesia silicate containing Shuifu County of Crystal structural morphology.In transmission electron microscope observing, attapulgite is slender rod shaped, needle-like
Crystal habit.Attapulgite has very unique chain layered crystal structure, and have in crystal structure it is many parallel to
Rod chip to nanoscale duct.Thus, Concave-convex clay rod has larger specific surface area and excellent absorption property, concavo-convex
Rod stone clay is in forming process because the presence of law of isomorphism metathesis makes its surface be in elecrtonegativity.The thus absorption to material
With selectivity, the mainly polar molecule that can be adsorbed.This characteristic is activated carbon, and montmorillonite is not had.It is acid-modified to add
Concave-convex clay rod after work has very strong absorption property, can be harmful to the formaldehyde in quick adsorption air, benzene, ammonia, TVOC
Gas, and bacterium, toxin can be adsorbed.
Natural Concave-convex clay rod is a kind of mixture, and its component also often contains calcite, length in addition to attapulgite
Stone, quartz and opal and mica, because its different poor quality strange land of the content of attapulgite is larger, in addition, in concave convex rod
Also often duct is blocked containing substantial amounts of calcium carbonate in the nano pore of stone, the absorption property of attapulgite is have impact on.Therefore, exist
Attapulgite content should be chosen when making product high, the strong Concave-convex clay rod of adsorptivity, while should also remove length as much as possible
Stone, quartz and opal., to increase its specific surface area, its absorption property should not be strengthened through following procedure of processing after ore dressing.
Hydrochloric Acid Modification step：Mass concentration is equably sprayed on the ore deposit of selection soil for 5% hydrochloric acid, it is fully soaked
Progress stone roller mud in twin rollers or three-roller is sent into after wet and is squeezed into the sheet that thickness is 1 millimeter.Roll and placed after 2~4 times
Activated within 24 hours.In this step, hydrochloric acid can remove the carbonate and impurity in attapulgite crystal duct, dredge recessed
Convex rod molecule nano duct.Grinding mud extruding can open the close pencil of Concave-convex clay rod, form fluffy form, make salt
Acid activation is more abundant, makes it have bigger space space.The absorption property of Concave-convex clay rod after being processed through this step
Several times can be improved.
Grinding steps：Roasted after attapulgite clay piece after hydrochloric Acid Modification is dried at a temperature of 300 DEG C~400 DEG C
Burn 3~4 hours, to further enhance its absorption property, by the attapulgite clay slice lapping after roasting into fineness be 200 mesh powder
End can be standby.
B, Chinese medicine selection and processing
To realize tranquillizing the mind by relieving convulsion, promote the purpose of sleep, the present invention have chosen Chinese medicine magnetite, notopterygium root, chrysanthemum and alum and be
Auxiliary material.
Magnetite：The effect relievingd asthma with calming the liver, hearing-improing and eyesight improving, tranquillizing the mind by relieving convulsion, gas of receiving.Magnetite is commonly used for human body magnetic
Treat, its external application can supplement human-body biological magnetic field, improve body immunity.
Chrysanthemum：The niger glucoside containing volatilization, with scattered wind heat-clearing, the function of flat liver improving eyesight can improve microcirculation in human body, centering
Pivot nerve has sedation, to gram-positive bacterium, and humanoid tubercle bacillus and influenza virus have inhibitory action.
Notopterygium root：Containing volatile oil, its volatile oil has inhibitory action to brucella and staphylococcus aureus, also with town
Quiet, hypnosis and the effect of anti-inflammatory.And cold dispelling, wind-dispelling, dehumidifying, the function of analgesic.
Bright inkstone：It is very much mainly alum, there is inhibitory action to various bacteria, external application can detoxifies desinsection.
Several Chinese medicines should be dried respectively before product is made to more than, and grind to form fine powder.
C, modified attapulgite clay are mixed with the proportioning of Chinese medicine
Weighing the modified attapulgite clay prepared, magnetite, notopterygium root, chrysanthemum, alum, the ratio of weighing is：Modified attapulgite
Clay 100, magnetite 20, notopterygium root 15, chrysanthemum 10~15, alum 2~4 are put into stirring in homogenizer, it is fully mixed jointly
Close uniform with standby.
D, making gel diaphragm
According to 100：3：1：0.2 ratio is filled after weighing water, sodium carboxymethylcellulose, sodium citrate, potassium sorbate, mixing respectively
Divide stirring, make sodium carboxymethylcellulose fully expanded, add appropriate mixed modified attapulgite clay and Chinese medicine
Mixed-powder, and stir, sticky pasty state is made.The thin slice that thickness is 2~5 millimeters is cast or be rolled into this thickener,
Thin slice is stood 24 hours, after drying and dewatering after its abundant gel, you can spongiform gel diaphragm is made.
In this step, by gelling agent of sodium carboxymethylcellulose, sodium citrate be chelating agent, potassium sorbate is anti-corrosion
Agent.Sodium carboxymethylcellulose（Abbreviation CMC）, it is a kind of conventional food thickening agent, is the plain glue of topmost ionic cellulose, tool
There are good cohesive and a film forming, the film that the CMC of high viscosity and high relative molecular weight is made has high intensity and high-flexibility.
The CMC solution of higher concentration can be mixed under conditions of the presence of chelator acid citrate salt with the polyvalent cation A13+ in alum
Irreversible spongy jelling structure is formed, this gel has heat irreversible and water-insoluble.Due to making this product
When should consider the intensity of gel diaphragm, again in view of its pliability, therefore, should be selected when to the type selecting of CMC product
Substitution value is 0.6 or so, high relative molecular weight, highly viscous product.It make use of CMC crosslinked action will be modified recessed in this step
Diaphragm is made in convex rod stone clay and Chinese medicine very much, and diaphragm has spongiform porous, both efficiently solves material
Easily flowing, easily accumulate problem, make diaphragm that there is good gas permeability again, without influence modified attapulgite clay adsorptivity with
And Chinese medicine volatile oil is distributed.
The potassium sorbate preservative added in this step, and Chinese medicine alum have inhibitory action to microorganism, to prevent
Degraded of the microorganism to sodium carboxymethylcellulose.
E, making pad blanket
Flannelette or cotton are enclosed respectively as needed in the upper and lower surface for the gel diaphragm produced, and cut into required size,
And carry out bound edge processing can be prepared by health mat blanket, gel diaphragm can also be cut into bulk, be arranged in two layers of cloth
Between, diaphragm junction is sutured cloth with line, so that block diaphragm is separated, is easy to fold pad blanket.
This product has advantages below compared with existing product：
1st, environmental protection and healthcare function, product are equipped with using the modified attapulgite clay with strong absorption property as primary raw material
With volatile Chinese medicine make, make product can not only quick adsorption padding for spring bed release formaldehyde and bed body around
Benzene, ammonia, TVOC pernicious gases, and make product with building up health, tranquillizing the mind by relieving convulsion, promotion are slept, the function of killing pests and suppressing bacteria.
2nd, diaphragm is made in main material and Chinese medicine auxiliary material by the method that product is film-made with gel, efficiently solves material easy
Flowing, easily accumulate and make moist caking the problem of, make product not wrinkle, smooth foldable.
3rd, product can arbitrarily be sheared according to the shape and size of individual demand, can both be made sleeping rug and seat cushion, can also be done
Into shoe-pad, the health care for anti-treating bad smell of feet and tinea pedis, and foot.
4th, product can discharge the pernicious gas of absorption after solar exposure, can be repeatedly used for a long.
5th, product has manufacture craft simple, the advantage of low manufacture cost.
Embodiment
A kind of Concave-convex clay rod health mat blanket, preparation method comprises the following steps：
（1）Mass concentration is equably sprayed on Concave-convex clay rod for 5% hydrochloric acid, it is sent into after fully soaking to roller
Rolled, be rolled into after the sheet that thickness is 1 millimeter, placement is activated for 24 hours, so in machine or three-roller
After dry, be calcined 3 hours at a temperature of 370 DEG C, grind to form fineness for 200 mesh powders, produce modified attapulgite clay
It is standby；The consumption of hydrochloric acid is the 2% of Concave-convex clay rod；
（2）According to following part by weight dispensing：
Modified attapulgite clay 100, magnetite 20, notopterygium root 15, chrysanthemum 10, alum 2；
Dispensing is put into jointly in homogenizer and stirred, it is sufficiently mixed the uniform attapulgite compound that obtains with standby；
（3）According to 100：3：1：0.2 ratio weighs water, sodium carboxymethylcellulose, sodium citrate, potassium sorbate respectively, mixing
After be sufficiently stirred for, make sodium carboxymethylcellulose fully expanded, add attapulgite compound, and stir, be made sticky
Thickener；The thin slice that thickness is 4 millimeters is cast or be rolled into this thickener, thin slice 24 hours are stood, after after its abundant gel
Drying and dewatering, you can spongiform gel diaphragm is made., the consumption of described attapulgite compound is water, carboxymethyl cellulose
Plain sodium, sodium citrate, the 5% of potassium sorbate gross weight.
Claims (3)
1. a kind of Concave-convex clay rod health mat blanket, it is characterised in that：Preparation method comprises the following steps：
（1）Mass concentration is equably sprayed on Concave-convex clay rod for 4-6% hydrochloric acid, make its fully soak after feeding pair
Rolled, be rolled into after the sheet that thickness is 1 millimeter, placement is lived for 24-26 hours in roller machine or three-roller
Change, then dry, be calcined 3~4 hours at a temperature of 300 DEG C~400 DEG C, grind to form fineness for 100-200 mesh powders, i.e.,
Obtain modified attapulgite clay standby；
（2）According to following part by weight dispensing：
Modified attapulgite clay 100-110, magnetite 20-25, notopterygium root 15-20, chrysanthemum 10-15, alum 2-4；
Dispensing is put into jointly in homogenizer and stirred, it is sufficiently mixed the uniform attapulgite compound that obtains with standby；
（3）According to 100-110：3-3.5：1-1.2：0.2-0.3 ratio weighs water, sodium carboxymethylcellulose, citric acid respectively
It is sufficiently stirred for after sodium, potassium sorbate, mixing, makes sodium carboxymethylcellulose fully expanded, adds appropriate attapulgite mixing
Material, and stir, sticky thickener is made；The thin slice that thickness is 2~5 millimeters is cast or be rolled into this thickener, by thin slice
24-26 hours are stood, after drying and dewatering after its abundant gel, you can spongiform gel diaphragm is made.
2. a kind of Concave-convex clay rod health mat blanket according to claim 1, it is characterised in that mass concentration is 4-6%'s
The consumption of hydrochloric acid is the 1-3% of Concave-convex clay rod.
3. a kind of Concave-convex clay rod health mat blanket according to claim 1, it is characterised in that described attapulgite is mixed
The consumption for closing material is water, sodium carboxymethylcellulose, sodium citrate, the 4-10% of potassium sorbate gross weight.