CN106967967A - A kind of surface conditioning agent for automotive oil tank - Google Patents
A kind of surface conditioning agent for automotive oil tank Download PDFInfo
- Publication number
- CN106967967A CN106967967A CN201710065687.0A CN201710065687A CN106967967A CN 106967967 A CN106967967 A CN 106967967A CN 201710065687 A CN201710065687 A CN 201710065687A CN 106967967 A CN106967967 A CN 106967967A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil tank
- conditioning agent
- surface conditioning
- automotive oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to automotive oil tank processing technique field, a kind of surface conditioning agent for automotive oil tank is specifically disclosed, it is characterised in that the described surface conditioning agent for automotive oil tank is made up of following components：10~30 parts of deionized water, 50~80 parts of phosphoric acid, 1~8 part of Mazhev salt, 1~8 part of zinc dihydrogen phosphate, 5~10 parts of citric acid, 0.5~2 part of nickel nitrate, 3~7 parts of sodium chloride, 150~300 parts of 1~5 part of ferric sulfate, 2~6 parts of copper sulphate, 2~8 parts of niter cake and water；When in use, coolant-temperature gage is 45~60 DEG C to the described surface conditioning agent for automotive oil tank.The present invention has derusting and rust-proof effect well, and raw material is cheap, easily operation, and effect is good, accords with the demands of the market, the scope of application is wide.
Description
Technical field
The present invention relates to automotive oil tank manufacture field, a kind of surface conditioning agent for automotive oil tank is specifically disclosed.
Background technology
The main material for manufacturing automotive oil tank assembly is aluminium alloy, stainless steel, zinc-plated carbon steel, plastics, cold-rolled low carbon steel
Deng it is the storage feedway of motor vehicle fuel, and fuel tank is divided into metal and the major class of plastics two, and general cart is metal, dolly
For plastics, safety traffic of its quality to automobile plays vital effect.Particularly carbon steel fuel tank, it is improper to be surface-treated
Corrosion, or coating shedding of the long period of soaking in gasoline or diesel oil are easily produced, fuel oil produces substantial amounts of impurity, occur to block defeated
The phenomenons such as oil pipe line, in order to ensure automotive oil tank quality, are extended the service life of fuel tank, are drawn using rational surface treatment method
The great attention for manufacturing producer is acted.Aluminium alloy, stainless steel due to expensive, fuel tank manufacture the application in field by
Limitation；Plastic fuel tank is easily broken due to strength problem by external shock, so what many automobile production producers still used
It is the fuel tank of carbon steel material.
The content of the invention
In order to solve technical problem present in prior art, it is used for automotive oil tank it is an object of the invention to provide one kind
Surface conditioning agent, with good derusting and rust-proof effect, and raw material is cheap, easily operation, and effect is good, and meeting market needs
Ask, the scope of application is wide.
The technical solution adopted in the present invention is as follows：
A kind of surface conditioning agent for automotive oil tank, the described surface conditioning agent for automotive oil tank is by following components institute structure
Into：10~30 parts of deionized water, 50~80 parts of phosphoric acid, 1~8 part of Mazhev salt, 1~8 part of zinc dihydrogen phosphate, lemon
Sour 5~10 parts, 0.5~2 part of nickel nitrate, 3~7 parts of sodium chloride, 1~5 part of ferric sulfate, 2~6 parts of copper sulphate, niter cake 2
~8 parts and 150~300 parts of water.
It is preferred that, the described surface conditioning agent for automotive oil tank is made up of following components：17 parts of deionized water, phosphorus
65 parts of acid, 4 parts of Mazhev salt, 5 parts of zinc dihydrogen phosphate, 6 parts of citric acid, 1.2 parts of nickel nitrate, 5 parts of sodium chloride, ferric sulfate
3 parts, 4 parts of copper sulphate, 180 parts of 5 parts of niter cake and water.
It is preferred that, the described surface conditioning agent for automotive oil tank is made up of following components：15 parts of deionized water, phosphorus
55 parts of acid, 3 parts of Mazhev salt, 7 parts of zinc dihydrogen phosphate, 6 parts of citric acid, 0.9 part of nickel nitrate, 4.5 parts of sodium chloride, sulphur
280 parts of sour 2.4 parts of iron, 3.7 parts of copper sulphate, 5 parts of niter cake and water.
It is preferred that, when in use, coolant-temperature gage is 45~60 DEG C to the described surface conditioning agent for automotive oil tank.
The present invention is relieved the effect of alcohol the preparation method of liver protection tea bag of helping digestion, and its advantage is shown：
With good derusting and rust-proof effect, and raw material is cheap, easily operation, and effect is good, accords with the demands of the market, the scope of application
It is wide.
Embodiment
The present invention is further illustrated with reference to embodiments.
Embodiment 1
A kind of surface conditioning agent for automotive oil tank, the described surface conditioning agent for automotive oil tank is by following components institute structure
Into：10 parts of deionized water, 50 parts of phosphoric acid, 1 part of Mazhev salt, 1 part of zinc dihydrogen phosphate, 5 parts of citric acid, nickel nitrate
0.5 part, 3 parts of sodium chloride, 1 part of ferric sulfate, 2 parts of copper sulphate, 150 parts of 2 parts of niter cake and water；The described automotive oil tank that is used for
When in use, coolant-temperature gage is 45~60 DEG C to surface conditioning agent.
Embodiment 2
A kind of surface conditioning agent for automotive oil tank, the described surface conditioning agent for automotive oil tank is by following components institute structure
Into：30 parts of deionized water, 80 parts of phosphoric acid, 8 parts of Mazhev salt, 8 parts of zinc dihydrogen phosphate, 10 parts of citric acid, nickel nitrate
2 parts, 7 parts of sodium chloride, 5 parts of ferric sulfate, 6 parts of copper sulphate, 300 parts of 8 parts of niter cake and water；The described automotive oil tank that is used for
When in use, coolant-temperature gage is 45~60 DEG C to surface conditioning agent.
Embodiment 3
A kind of surface conditioning agent for automotive oil tank, the described surface conditioning agent for automotive oil tank is by following components institute structure
Into：17 parts of deionized water, 65 parts of phosphoric acid, 4 parts of Mazhev salt, 5 parts of zinc dihydrogen phosphate, 6 parts of citric acid, nickel nitrate 1.2
180 parts of part, 5 parts of sodium chloride, 3 parts of ferric sulfate, 4 parts of copper sulphate, 5 parts of niter cake and water；The described table for automotive oil tank
When in use, coolant-temperature gage is 45~60 DEG C to face inorganic agent.
Embodiment 4
A kind of surface conditioning agent for automotive oil tank, the described surface conditioning agent for automotive oil tank is by following components institute structure
Into：15 parts of deionized water, 55 parts of phosphoric acid, 3 parts of Mazhev salt, 7 parts of zinc dihydrogen phosphate, 6 parts of citric acid, nickel nitrate
0.9 part, 4.5 parts of sodium chloride, 2.4 parts of ferric sulfate, 3.7 parts of copper sulphate, 280 parts of 5 parts of niter cake and water；Described is used for automobile
When in use, coolant-temperature gage is 45~60 DEG C to the surface conditioning agent of fuel tank.
Above content is only that affiliated those skilled in the art are to being retouched to present inventive concept example and explanation
The specific embodiment stated is made various modifications or supplement or substituted using similar mode, without departing from the design of invention
Or surmount scope defined in the claims, protection scope of the present invention all should be belonged to.
Claims (4)
1. a kind of surface conditioning agent for automotive oil tank, it is characterised in that the described surface conditioning agent for automotive oil tank
It is made up of following components：10~30 parts of deionized water, 50~80 parts of phosphoric acid, 1~8 part of Mazhev salt, zinc dihydrogen phosphate
1~8 part, 5~10 parts of citric acid, 0.5~2 part of nickel nitrate, 3~7 parts of sodium chloride, 1~5 part of ferric sulfate, copper sulphate 2~6
Part, 150~300 parts of 2~8 parts of niter cake and water.
2. a kind of surface conditioning agent for automotive oil tank according to claim 1, it is characterised in that described is used for vapour
The surface conditioning agent of car fuel tank is made up of following components：17 parts of deionized water, 65 parts of phosphoric acid, 4 parts of Mazhev salt, phosphoric acid
5 parts of dihydro zinc, 6 parts of citric acid, 1.2 parts of nickel nitrate, 5 parts of sodium chloride, 3 parts of ferric sulfate, 4 parts of copper sulphate, 5 parts of niter cake
With 180 parts of water.
3. a kind of surface conditioning agent for automotive oil tank according to claim 1, it is characterised in that described is used for vapour
The surface conditioning agent of car fuel tank is made up of following components：15 parts of deionized water, 55 parts of phosphoric acid, 3 parts of Mazhev salt, phosphoric acid
7 parts of dihydro zinc, 6 parts of citric acid, 0.9 part of nickel nitrate, 4.5 parts of sodium chloride, 2.4 parts of ferric sulfate, 3.7 parts of copper sulphate, sulfuric acid
280 parts of 5 parts of hydrogen sodium and water.
4. a kind of surface conditioning agent for automotive oil tank according to any one of claims 1 to 3, it is characterised in that institute
When in use, coolant-temperature gage is 45~60 DEG C to the surface conditioning agent for automotive oil tank stated.