CN106966654A - The method that a kind of utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick - Google Patents
The method that a kind of utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick Download PDFInfo
- Publication number
- CN106966654A CN106966654A CN201710205991.0A CN201710205991A CN106966654A CN 106966654 A CN106966654 A CN 106966654A CN 201710205991 A CN201710205991 A CN 201710205991A CN 106966654 A CN106966654 A CN 106966654A
- Authority
- CN
- China
- Prior art keywords
- water
- boehmite
- industrial residue
- permeable brick
- aluminosilicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method that utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick, aluminosilicate industrial residue is respectively adopted in the present invention and boehmite is raw material, Ludox and Alumina gel is made, then Ludox is well mixed, add sodium carbonate, carbon black, the stirring mixing of the foaming agents such as DBSA triethanolamine salt, it is thermally treated, sintering processes produce high mechanical strength, the wide porous silica alumina composite ceramic of pore size distribution range, then using porous silica alumina composite ceramic as aggregate, portland cement is adhesive, carbon mineral wool is reinforcing agent, there is high mechanical strength through hydrostatic profile and the obtained water-permeable brick of maintenance, water penetration is strong, the features such as good endurance, service life is long, have a wide range of application, aluminosilicate industrial waste residue resourceization is recycled simultaneously, greatly reduce production cost, with good economic benefit and social benefit.
Description
Technical field
Sponge urban construction is prepared with permeable using aluminosilicate industrial residue and boehmite the present invention relates to one kind
The method of brick, belongs to building material technical field.
Background technology
The earth's surface of modern city is progressively covered by material water-proof materials such as building and concrete, so as to form ecology
" artificial desert " on.Fluid-tight concrete and pitch etc. are as the main ground surface material in city so that decline naturally
Rainwater can not be natural and tripping permeate the ground;Thus be cause lack to urban surface temperature, humidity regulation ability it is main
Reason, " tropical island effect " for causing to produce so-called city or causes to see the waterlogging problem in sea in rainy season city.In order to alleviate to environment
Infringement, and the stable ecological environment in city can have fundamentally been administered, so as to propose the new general of construction " sponge city "
Read." sponge city ", is that metaphor city possesses the same function of sponge, is adapting to seasonal climate environmental change and reply nature
There is good " elasticity " in terms of disaster.Water suction, retaining, infiltration, water purification when raining, need " to release the water stored when arid
Put " and it is used, so as to allow migratory movement of the water in city more " nature ".
Natural way is combined by sponge urban construction with artificial measures, is ensuring the premise of municipal drainage prevention waterlogging safety
Under, realize that rainwater accumulates in urban area, permeates and purified to greatest extent, improve Rainwater Resources level, protecting ecology ring
Border.Build sponge city and seek to that there is " cavernous body ";" cavernous body " both includes the water system such as river, lake, pond, also including greenery patches,
City auxiliary facility as garden, permeable pavior brick.Rainwater by being oozed under these " cavernous bodies ", it is stagnant store, purification, reuse,
Last remainder runoff, so as to effectively improve the standard of sewerage system, is extenuated in city by being arranged outside pipe network, pumping plant
The pressure of flood.Sponge urban construction is a systemic engineering, but each critical component of systemic requirement of engineering is next organic
Combine, water-permeable brick is exactly one of sponge urban construction crucial organism.
Water-permeable brick is also seepage brick, Dutch brick etc., belongs to Green environmental-protection building material product.Raw material are generally to use water
Based on the concrete materials such as mud, sand, stone, vibrate pressurization product forming process to carry out mass production by mechanization orientation
Floor tile;Full sized brick forms for disposable compression, forms the not stratified homogeneity brick of global density uniformity.Water-permeable brick is for exploitation
Rainfall produced by the difference in functionality regions such as road, garden, square in construction area, takes appropriate measures, or at collection
Reason is recycled, or the recharging groundwater that permeates the ground, and rainwater resource, the raising self-purification ability of enviroment, improvement garden are made full use of to reach
Area's ecological environment, the purpose for adjusting Partial little climate.Water-permeable brick can be widely used in laying pavement or lightweight traffic garage
The road surface in road etc. and ground surface works, it may also be used for cell, garden, parking lot, shop, block, square, waterside bank protection, in park
The paving such as road and level land, airport and harbour.
At present, two major classes can be divided into from material and production technology in the water-permeable brick seen on the market.One class is with solid
Industrial waste, house refuse and building waste be primary raw material, by crush, shaping, high-temperature firing have water-permeable brick
Performance, meets the building and ornament materials of water-permeable brick standard, and it is called ceramic water-permeable brick by we;Another kind of is with inorganic non-metallic
Material is primary raw material, using organic or inorganic binding agent by shaping, solidifying with water-permeable brick performance, meet permeable
The building and ornament materials of brick standard.Because it need not burn till, so we are called non-ceramic water-permeable brick.Dai Wubin, Zeng Lingke,
Wang Hui et al. is at it《The present Research and development prospect of water-permeable brick》The method that several water-permeable bricks are described in one text:(1)Utilize
Shraff, cullet and clay develop environment-friendly ceramic water-permeable brick as primary raw material;(2)It is main former using gold tailings
Material, makees pore former with gangue, prepares Porous permeable bricks;(3)Be primary raw material using flyash, broken useless floor tile be bone
Material, clay make binding agent, prepare flyash water-permeable brick.As can be seen here, gangue, fine coal are used water-permeable brick in the market more
The solid industrial waste material such as ash, shraff, cullet, useless floor tile, gold tailings makees raw material, also seldom sees and uses aluminosilicate
Industrial residue and boehmite are water-permeable brick prepared by primary raw material.
The content of the invention
Sponge urban construction is prepared with thoroughly using aluminosilicate industrial residue and boehmite the invention discloses one kind
The method of water brick.Water-permeable brick produced by the present invention has a high mechanical strength, and water penetration is strong, the features such as good endurance, service life
It is long, have a wide range of application.
To achieve the above object, the present invention is adopted the following technical scheme that:
The method that a kind of utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick, including with
Lower step:
(1)Aluminosilicate industrial residue is crushed, 150-250 mesh sieves are crossed, then according to mass ratio 1:0.7-0.9 is by after sieving
Aluminosilicate industrial residue and sodium carbonate mixing, 2000-4000r/min high speed ball milling 10-30min, then forged at 820-880 DEG C
1-2h is burnt, grind into powder after room temperature is cooled to, then according to solid-to-liquid ratio 1:Powder after calcining is added to mole dense by 8-10
Spend in the sulfuric acid solution for 5mol/L, stir 1-2h, filtering is concentrated into the 1/3-1/2 of original volume, produces Ludox;
(2)Boehmite is crushed, 100-200 mesh sieves are crossed, matter is made in the boehmite powder stirring that adds water after then sieving
The suspension that amount fraction is 40-50%, ultrasonic disperse 15-20min, it is 20% that mass fraction is then slowly added under magnetic stirring
Salpeter solution, control H+Mol ratio with Al produces Alumina gel between 0.03-0.07;
(3)It is middle after stirring to add equivalent to mixed sols quality 0.8- by mass mixings such as Ludox and Alumina gels
1.6% sodium carbonate, 2-3% carbon black, 3-5% DBSA triethanolamine salt and 1.5-2.5% coconut oleoyl amine third
Base hydroxy sulfo lycine, stands 15-30min in 35-45 DEG C of water-bath after stirring, in 400-600r/min rotating speed
Lower stirring no longer increases to foam volume, and 24-48h is then stood in 30-40 DEG C of water-bath, then stands 7-10d at room temperature, then
5-8d is stood in 115-130 DEG C of oil bath, then 770-830 DEG C is warming up to 3-5 DEG C/min speed, 3-5h is incubated, then with
1-3 DEG C/min speed is cooled to 400-450 DEG C, is incubated 4-6h, then be warming up to 880-920 DEG C, guarantor with 2-4 DEG C/min speed
Warm 2-4h, then 1060-1120 DEG C is warming up to 1-2 DEG C/min speed, 1-3h is incubated, then cool with 3-5 DEG C/min speed
To 520-580 DEG C, 4-6h is incubated, room temperature is air-cooled to, crushed, produce porous silica-alumina composite ceramic;
(4)According to mass ratio 3-5:5-8:It is fine that 2-4 weighs portland cement, porous silica-alumina composite ceramic and carbon stone
Dimension, then by portland cement, porous silica-alumina composite ceramic and the dry-mixed 5-8min of carbon mineral wool, is then added
Appropriate water wet mixing 7-9min, control wet feed water content is in 10-15%;
(5)Wet feed obtained above is added to hydrostatic profile in mould, stands and is stripped after 3-4d, it is natural after steam curing
7-14d is conserved, required water-permeable brick is produced.
Step(2)Described in aluminosilicate industrial residue for kaolin by processing extract the remaining Industry Waste of aluminum sulfate
Slag.
Step(2)Described in ultrasonic power be 300-350W.
Step(4)Described in portland cement be 52.5 grades of portland cements.
Step(5)Described in briquetting pressure be 3-5MPa, the dwell time is 80-100s.
Step(5)Described in steam curing system for heating 2-4h, constant temperature time is 8-10h, cool 3-5h, constant temperature temperature
Spend for 70-90 DEG C.
Beneficial effects of the present invention:
Aluminosilicate industrial residue is respectively adopted in the present invention and boehmite is raw material, Ludox and Alumina gel is made, then
Ludox is well mixed, the stirring mixing of the foaming agents such as sodium carbonate, carbon black, DBSA triethanolamine salt is added,
Thermally treated, sintering processes produce the wide porous silica-alumina composite ceramic of high mechanical strength, pore size distribution range, so
Afterwards using porous silica-alumina composite ceramic as aggregate, portland cement is adhesive, and carbon mineral wool is reinforcing agent, through quiet
The molded and obtained water-permeable brick of maintenance has high mechanical strength, and water penetration is strong, the features such as good endurance, and service life is long, should
It is wide with scope, while aluminosilicate industrial waste residue resourceization is recycled, production cost is greatly reduced, with good economy
Benefit and social benefit.
Embodiment
Embodiment 1
The method that a kind of utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick, including with
Lower step:
(1)Aluminosilicate industrial residue is crushed, 150 mesh sieves are crossed, then according to mass ratio 1:0.7 by the aluminosilicate after sieving
Industrial residue and sodium carbonate mixing, 2000r/min high speed ball milling 30min, then 2h is calcined at 820 DEG C, it is cooled to after room temperature and grinds
Clay into power, then according to solid-to-liquid ratio 1:8 are added to the powder after calcining in the sulfuric acid solution that molar concentration is 5mol/L, stir
1h is mixed, is filtered, is concentrated into the 1/3 of original volume, produces Ludox;
(2)Boehmite is crushed, 100 mesh sieves are crossed, quality point is made in the stirring that adds water of the boehmite powder after then sieving
Number is 40% suspension, and then ultrasonic disperse 15min is slowly added to the nitric acid that mass fraction is 20% molten under magnetic stirring
Liquid, controls H+Mol ratio with Al produces Alumina gel 0.03;
(3)It is middle after stirring to add equivalent to mixed sols quality 0.8-% by mass mixings such as Ludox and Alumina gels
Sodium carbonate, 2% carbon black, 3% DBSA triethanolamine salt and 1.5% cocamidopropyl propyl amide hydroxyl sulfobetaines
Alkali, 30min is stood after stirring in 35 DEG C of water-baths, is stirred to foam volume and is no longer increased under 400r/min rotating speed
Greatly, 48h is then stood in 30 DEG C of water-baths, then stands 7d at room temperature, then stands in 115 DEG C of oil baths 8d, then with 3 DEG C/
Min speed is warming up to 770 DEG C, is incubated 5h, then is cooled to 400 DEG C with 1 DEG C/min speed, is incubated 6h, then with 2 DEG C/min's
Speed is warming up to 880 DEG C, is incubated 4h, then is warming up to 1060 DEG C with 1 DEG C/min speed, is incubated 3h, then with 3 DEG C/min speed
520 DEG C are cooled to, 6h is incubated, is air-cooled to room temperature, crushes, produces porous silica-alumina composite ceramic;
(4)According to mass ratio 3:5:2 weigh portland cement, porous silica-alumina composite ceramic and carbon mineral wool, then
By portland cement, porous silica-alumina composite ceramic and the dry-mixed 5min of carbon mineral wool, appropriate water is then added wet
Mixed 7min, control wet feed water content is 10%;
(5)Wet feed obtained above is added to hydrostatic profile in mould, stands and is stripped after 3d, supported naturally after steam curing
7d is protected, required water-permeable brick is produced.
Step(2)Described in aluminosilicate industrial residue for kaolin by processing extract the remaining Industry Waste of aluminum sulfate
Slag.
Step(2)Described in ultrasonic power be 350W.
Step(4)Described in portland cement be 52.5 grades of portland cements.
Step(5)Described in briquetting pressure be 3MPa, the dwell time is 100s.
Step(5)Described in steam curing system for heating 2h, constant temperature time is 8h, cool 3h, thermostat temperature is 90
℃。
Embodiment 2
The method that a kind of utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick, including with
Lower step:
(1)Aluminosilicate industrial residue is crushed, 200 mesh sieves are crossed, then according to mass ratio 1:0.8 by the aluminosilicate after sieving
Industrial residue and sodium carbonate mixing, 3000r/min high speed ball milling 20min, then 1.5h is calcined at 850 DEG C, it is cooled to after room temperature
Grind into powder, then according to solid-to-liquid ratio 1:9 are added to the powder after calcining in the sulfuric acid solution that molar concentration is 5mol/L,
1.5h is stirred, filtering is concentrated into the 1/3 of original volume, produces Ludox;
(2)Boehmite is crushed, 150 mesh sieves are crossed, quality point is made in the stirring that adds water of the boehmite powder after then sieving
Number is 45% suspension, and then ultrasonic disperse 18min is slowly added to the nitric acid that mass fraction is 20% molten under magnetic stirring
Liquid, controls H+Mol ratio with Al produces Alumina gel 0.05;
(3)It is middle after stirring to add equivalent to mixed sols quality 1.2% by mass mixings such as Ludox and Alumina gels
Sodium carbonate, 2.5% carbon black, 4% DBSA triethanolamine salt and 2% cocamidopropyl propyl amide hydroxyl sulfobetaines
Alkali, 25min is stood after stirring in 40 DEG C of water-baths, is stirred to foam volume and is no longer increased under 500r/min rotating speed
Greatly, 36h is then stood in 35 DEG C of water-baths, then stands 8d at room temperature, then stands in 125 DEG C of oil baths 6d, then with 4 DEG C/
Min speed is warming up to 800 DEG C, is incubated 4h, then is cooled to 420 DEG C with 2 DEG C/min speed, is incubated 5h, then with 3 DEG C/min's
Speed is warming up to 900 DEG C, is incubated 3h, then is warming up to 1090 DEG C with 1.5 DEG C/min speed, is incubated 2h, then with 4 DEG C/min speed
Rate is cooled to 550 DEG C, is incubated 5h, is air-cooled to room temperature, crushes, produces porous silica-alumina composite ceramic;
(4)According to mass ratio 4:6:3 weigh portland cement, porous silica-alumina composite ceramic and carbon mineral wool, then
By portland cement, porous silica-alumina composite ceramic and the dry-mixed 6min of carbon mineral wool, appropriate water is then added wet
Mixed 8min, control wet feed water content is 12%;
(5)Wet feed obtained above is added to hydrostatic profile in mould, stands and is stripped after 3d, supported naturally after steam curing
10d is protected, required water-permeable brick is produced.
Step(2)Described in aluminosilicate industrial residue for kaolin by processing extract the remaining Industry Waste of aluminum sulfate
Slag.
Step(2)Described in ultrasonic power be 320W.
Step(4)Described in portland cement be 52.5 grades of portland cements.
Step(5)Described in briquetting pressure be 4MPa, the dwell time is 90s.
Step(5)Described in steam curing system for heating 3h, constant temperature time is 9h, cool 4h, thermostat temperature is 80
℃。
Embodiment 3
The method that a kind of utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick, including with
Lower step:
(1)Aluminosilicate industrial residue is crushed, 250 mesh sieves are crossed, then according to mass ratio 1:0.9 by the aluminosilicate after sieving
Industrial residue and sodium carbonate mixing, 4000r/min high speed ball milling 10min, then 1h is calcined at 880 DEG C, it is cooled to after room temperature and grinds
Clay into power, then according to solid-to-liquid ratio 1:10 are added to the powder after calcining in the sulfuric acid solution that molar concentration is 5mol/L,
2h is stirred, filtering is concentrated into the 1/2 of original volume, produces Ludox;
(2)Boehmite is crushed, 200 mesh sieves are crossed, quality point is made in the stirring that adds water of the boehmite powder after then sieving
Number is 50% suspension, and then ultrasonic disperse 20min is slowly added to the nitric acid that mass fraction is 20% molten under magnetic stirring
Liquid, controls H+Mol ratio with Al produces Alumina gel 0.07;
(3)It is middle after stirring to add equivalent to mixed sols quality 1.6% by mass mixings such as Ludox and Alumina gels
Sodium carbonate, 3% carbon black, 5% DBSA triethanolamine salt and 2.5% cocamidopropyl propyl amide hydroxyl sulfobetaines
Alkali, 15min is stood after stirring in 45 DEG C of water-baths, is stirred to foam volume and is no longer increased under 600r/min rotating speed
Greatly, 24h is then stood in 40 DEG C of water-baths, then stands 10d at room temperature, then stands in 130 DEG C of oil baths 5d, then with 5 DEG C/
Min speed is warming up to 830 DEG C, is incubated 3h, then is cooled to 450 DEG C with 3 DEG C/min speed, is incubated 4h, then with 4 DEG C/min's
Speed is warming up to 920 DEG C, is incubated 2h, then is warming up to 1120 DEG C with 2 DEG C/min speed, is incubated 1h, then with 5 DEG C/min speed
580 DEG C are cooled to, 4h is incubated, is air-cooled to room temperature, crushes, produces porous silica-alumina composite ceramic;
(4)According to mass ratio 5:8:4 weigh portland cement, porous silica-alumina composite ceramic and carbon mineral wool, then
By portland cement, porous silica-alumina composite ceramic and the dry-mixed 8min of carbon mineral wool, appropriate water is then added wet
Mixed 9min, control wet feed water content is 15%;
(5)Wet feed obtained above is added to hydrostatic profile in mould, stands and is stripped after 4d, supported naturally after steam curing
14d is protected, required water-permeable brick is produced.
Step(2)Described in aluminosilicate industrial residue for kaolin by processing extract the remaining Industry Waste of aluminum sulfate
Slag.
Step(2)Described in ultrasonic power be 300W.
Step(4)Described in portland cement be 52.5 grades of portland cements.
Step(5)Described in briquetting pressure be 5MPa, the dwell time is 80s.
Step(5)Described in steam curing system for heating 4h, constant temperature time is 10h, cool 5h, thermostat temperature is 70
℃。
Claims (6)
1. a kind of method that utilization aluminosilicate industrial residue and boehmite prepare sponge urban construction water-permeable brick, it is special
Levy and be, comprise the following steps:
(1)Aluminosilicate industrial residue is crushed, 150-250 mesh sieves are crossed, then according to mass ratio 1:0.7-0.9 is by after sieving
Aluminosilicate industrial residue and sodium carbonate mixing, 2000-4000r/min high speed ball milling 10-30min, then forged at 820-880 DEG C
1-2h is burnt, grind into powder after room temperature is cooled to, then according to solid-to-liquid ratio 1:Powder after calcining is added to mole dense by 8-10
Spend in the sulfuric acid solution for 5mol/L, stir 1-2h, filtering is concentrated into the 1/3-1/2 of original volume, produces Ludox;
(2)Boehmite is crushed, 100-200 mesh sieves are crossed, matter is made in the boehmite powder stirring that adds water after then sieving
The suspension that amount fraction is 40-50%, ultrasonic disperse 15-20min, it is 20% that mass fraction is then slowly added under magnetic stirring
Salpeter solution, control H+Mol ratio with Al produces Alumina gel between 0.03-0.07;
(3)It is middle after stirring to add equivalent to mixed sols quality 0.8- by mass mixings such as Ludox and Alumina gels
1.6% sodium carbonate, 2-3% carbon black, 3-5% DBSA triethanolamine salt and 1.5-2.5% coconut oleoyl amine third
Base hydroxy sulfo lycine, stands 15-30min in 35-45 DEG C of water-bath after stirring, in 400-600r/min rotating speed
Lower stirring no longer increases to foam volume, and 24-48h is then stood in 30-40 DEG C of water-bath, then stands 7-10d at room temperature, then
5-8d is stood in 115-130 DEG C of oil bath, then 770-830 DEG C is warming up to 3-5 DEG C/min speed, 3-5h is incubated, then with
1-3 DEG C/min speed is cooled to 400-450 DEG C, is incubated 4-6h, then be warming up to 880-920 DEG C, guarantor with 2-4 DEG C/min speed
Warm 2-4h, then 1060-1120 DEG C is warming up to 1-2 DEG C/min speed, 1-3h is incubated, then cool with 3-5 DEG C/min speed
To 520-580 DEG C, 4-6h is incubated, room temperature is air-cooled to, crushed, produce porous silica-alumina composite ceramic;
(4)According to mass ratio 3-5:5-8:It is fine that 2-4 weighs portland cement, porous silica-alumina composite ceramic and carbon stone
Dimension, then by portland cement, porous silica-alumina composite ceramic and the dry-mixed 5-8min of carbon mineral wool, is then added
Appropriate water wet mixing 7-9min, control wet feed water content is in 10-15%;
(5)Wet feed obtained above is added to hydrostatic profile in mould, stands and is stripped after 3-4d, it is natural after steam curing
7-14d is conserved, required water-permeable brick is produced.
2. one kind according to claim 1 prepares sponge urban construction using aluminosilicate industrial residue and boehmite
With the method for water-permeable brick, it is characterised in that step(2)Described in aluminosilicate industrial residue for kaolin by processing extract
The remaining industrial residue of aluminum sulfate.
3. one kind according to claim 1 prepares sponge urban construction using aluminosilicate industrial residue and boehmite
With the method for water-permeable brick, it is characterised in that step(2)Described in ultrasonic power be 300-350W.
4. one kind according to claim 1 prepares sponge urban construction using aluminosilicate industrial residue and boehmite
With the method for water-permeable brick, it is characterised in that step(4)Described in portland cement be 52.5 grades of portland cements.
5. one kind according to claim 1 prepares sponge urban construction using aluminosilicate industrial residue and boehmite
With the method for water-permeable brick, it is characterised in that step(5)Described in briquetting pressure be 3-5MPa, the dwell time is 80-100s.
6. one kind according to claim 1 prepares sponge urban construction using aluminosilicate industrial residue and boehmite
With the method for water-permeable brick, it is characterised in that step(5)Described in steam curing system for heating 2-4h, constant temperature time is 8-
10h, cool 3-5h, and thermostat temperature is 70-90 DEG C.