CN106965611A - The method for realizing transfer printing wood grain in metal material surface - Google Patents
The method for realizing transfer printing wood grain in metal material surface Download PDFInfo
- Publication number
- CN106965611A CN106965611A CN201710158491.6A CN201710158491A CN106965611A CN 106965611 A CN106965611 A CN 106965611A CN 201710158491 A CN201710158491 A CN 201710158491A CN 106965611 A CN106965611 A CN 106965611A
- Authority
- CN
- China
- Prior art keywords
- iron
- iron sheet
- iron pipe
- wood grain
- lathe work
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of method for realizing transfer printing wood grain in metal material surface, comprises the following steps：Clean processing is carried out to iron sheet/iron pipe surface；Wood grain powdery paints is mixed and made into using llowing group of materials；Material is by weight：Epoxy resin 60 65%, polyester resin 5 10%, levelling defoamer 1 1.5%, delustering agent 4 5%, filler 25 30%, colorant 0.5 1%；Mixed coating is shaken up into filtering；Above-mentioned coating is sprayed onto by iron sheet/iron pipe surface using electrostatic spraying transmitter, during spraying, powder is heated up to more than 230 °, constant temperature 20 minutes；Thickness is between 70 90 μm；The one side that transfer paper has lathe work is attached on the iron sheet/iron pipe sprayed；Iron sheet/the iron pipe for posting colour-line paper is subjected to high-temperature vacuum plastic uptake processing, plastic uptake temperature is 180 degree, and the time is 20 minutes；Lathe work on woodgrained paper is transferred on iron sheet/iron pipe.It is printed on iron sheet/iron pipe of lathe work client can be provided and more selects, the product that can just accomplish instead of former wood materials.Make the color on ironware surface more rich.
Description
Technical field
The present invention relates to transfer printing wood grain method, and in particular to a kind of method for realizing transfer printing wood grain in metal material surface.
Background technology
At present for the processing of metal surface, usually by the way of paint spraying, the appearance color of ironware is relatively single
One, without colour lines；Such as：Dining table and chair cabinet for TV, computer desk, coffee table, the surface of iron bed, color is all single.
The content of the invention
It is an object of the present invention to which the drawbacks described above for prior art can be realized there is provided one kind in metal material surface
The method of transfer printing wood grain, it is possible to resolve the problem of appearance face color of ironware is relatively single.
A kind of method for realizing transfer printing wood grain in metal material surface is provided, comprised the following steps：
A1, clean processing is carried out to iron sheet/iron pipe surface；
A2, wood grain powdery paints is mixed and made into using llowing group of materials；Material is by weight：
Epoxy resin 60-65%, polyester resin 5-10%, levelling defoamer 1-1.5%
Delustering agent 4-5%, filler 25-30%, colorant 0.5-1%；Mixed coating is shaken up into filtering；
Above-mentioned coating is sprayed onto by iron sheet/iron pipe surface using electrostatic spraying transmitter, during spraying, by powder be heated up to 230 ° with
On, constant temperature 20 minutes；Thickness is between 70-90 μm；
A3, the one side that transfer paper is had into lathe work are attached on the iron sheet/iron pipe surface sprayed；
A4, iron sheet/iron pipe progress high-temperature vacuum plastic uptake processing to posting colour-line paper, plastic uptake temperature is 180 degree, and the time is 20 points
Clock；Lathe work on woodgrained paper is transferred on iron sheet/iron pipe.
The present invention is by using the coating of proprietary formula to carrying out spray treatment on iron sheet/iron pipe surface so that woodgrained paper
On lathe work can more effectively adhere to the surface for being transferred to iron sheet/iron pipe.This iron sheet/the iron pipe for being printed on lathe work, can be provided
Client more selects, the product that can just accomplish instead of former wood materials.Woodgrained paper is not easy to come off and damaged；Make ironware table
The color variation in face, color is more rich.
Embodiment
1st, clean processing is carried out to iron sheet/iron pipe surface；
2nd, wood grain powdery paints is mixed and made into using llowing group of materials；Material is by weight：Epoxy resin 60-65%, polyester resin
5-10%, levelling defoamer 1-1.5%
Delustering agent 4-5%, filler 25-30%, colorant 0.5-1%；Mixed coating is shaken up into filtering；
3rd, above-mentioned coating is sprayed onto by iron sheet/iron pipe surface using electrostatic spraying transmitter, during spraying, by powder be heated up to 230 ° with
On, constant temperature 20 minutes；Thickness is between 70-90 μm；
4th, the one side that transfer paper has lathe work is attached on the iron sheet/iron pipe sprayed；
5th, the iron sheet/iron pipe for posting colour-line paper is subjected to high-temperature vacuum plastic uptake processing, plastic uptake temperature is 180 degree, and the time is 20 points
Clock；Lathe work on woodgrained paper can be transferred on the surface of iron sheet/iron pipe.
Using the coating of proprietary formula to carrying out spray treatment on iron sheet/iron pipe surface so that the lathe work energy on woodgrained paper
More effectively attachment is transferred to the surface of iron sheet/iron pipe.This iron sheet/the iron pipe for being printed on lathe work, can provide client more
Selection, the product that can just accomplish instead of former wood materials.Woodgrained paper is not easy to come off and damaged；Make the color on ironware surface many
Sample, color is more rich.
Claims (1)
1. the method for realizing transfer printing wood grain in metal material surface, it is characterised in that：Comprise the following steps：
A1, clean processing is carried out to iron sheet/iron pipe surface；
A2, wood grain powdery paints is mixed and made into using llowing group of materials；Material is by weight：
Epoxy resin 60-65%, polyester resin 5-10%, levelling defoamer 1-1.5%, delustering agent 4-5%, filler 25-30%, colorant
0.5-1%；Mixed coating is shaken up into filtering；Above-mentioned coating is sprayed onto by iron sheet/iron pipe surface shape using electrostatic spraying transmitter
Film forming layer, during spraying, more than 230 °, constant temperature 20 minutes are heated up to by powder；The thickness of film is sprayed between 70-90 μm；
A3, the one side that transfer paper is had into lathe work are attached on the iron sheet/iron pipe sprayed；
A4, the iron sheet/iron pipe progress high-temperature vacuum plastic uptake processing that will post colour-line paper, plastic uptake temperature is 180 degree, and the time is 20 points
Clock；Lathe work on woodgrained paper is transferred on iron sheet/iron pipe.