CN106965499A - Porous compound film and preparation method thereof - Google Patents
Porous compound film and preparation method thereof Download PDFInfo
- Publication number
- CN106965499A CN106965499A CN201710085430.1A CN201710085430A CN106965499A CN 106965499 A CN106965499 A CN 106965499A CN 201710085430 A CN201710085430 A CN 201710085430A CN 106965499 A CN106965499 A CN 106965499A
- Authority
- CN
- China
- Prior art keywords
- membrane
- outer layer
- porous
- film
- compound film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to composite membrane field, more particularly to a kind of porous compound film and preparation method thereof, porous compound film, including basement membrane, the outer surface of the basement membrane, which is pasted with outer layer porous membrane, the outer layer porous membrane, is uniformly distributed hole, the average diameter of described hole is 1~10 μm, the preparation method of porous compound film, including step 1) in mass ratio, weigh outer layer copolymer:Acetylbutyrylcellulose is 6.5:3.5~9:1, as outer layer film raw material after being well mixed, outer layer film raw material and basement membrane polymer are put into double-deck cast film machine, the laminated film by basement membrane and outer membrane overlapping is obtained through double-deck cast film machine extrusion, simple tension and after being cooled and shaped process;2) laminated film is soaked in acetone soln, after acetylbutyrylcellulose in acetone extract outer membrane, outer membrane formation outer layer porous membrane obtains porous compound film after drying.The porous compound film has the characteristics of specific surface area is big.
Description
Technical field
The present invention relates to composite membrane field, more particularly to a kind of porous compound film and preparation method thereof.
Background technology
The high score that laminated film is composited by the film of two layers or multiple layers of different materials by modes such as gluing or hot pressing
Sub- material, laminated film can be made up of the film of multiple layers of different materials, therefore laminated film can be made to have multiple material concurrently
Partial properties, assign the more combining properties of laminated film.At present, laminated film is widely used in packaging field, due to THIN COMPOSITE
Film has pliability strong, and mechanical property is excellent, the low feature of production cost, researcher gradually by laminated film apply sensor,
The field such as ultracapacitor and functional fibre, still, traditional laminated film surface is all smooth, exists and compares surface
The small shortcoming of product, it is impossible to preferably realize sensing, conductive, the function such as absorption.
The content of the invention
To solve problem above, it is an object of the invention to provide a kind of porous compound film and preparation method thereof, this is porous
Laminated film has the characteristics of specific surface area is big.
To achieve the above object, the technical scheme designed by the present invention is:
Porous compound film, including basement membrane, the outer surface of the basement membrane are pasted with outer layer porous membrane, and the outer layer is porous
Hole is uniformly distributed on film, the average diameter of described hole is 1~10 μm;The basement membrane is polypropylene, polyethylene, polyester
With one kind in polyamide, the outer layer porous membrane is one kind in polypropylene, polyethylene, polyester and polyamide;The base
The thickness of film is 50~100 μm, and the thickness of the outer layer porous membrane is 50~100 μm.
Preferably, the outer layer porous membrane is same material with basement membrane.
The preparation method of porous compound film, comprises the following steps:
1) outer layer copolymer in mass ratio, is weighed:Acetylbutyrylcellulose is 6.5:3.5~9:1, conduct after being well mixed
Outer layer film raw material, double-deck cast film machine is put into by outer layer film raw material and basement membrane polymer, through double-deck cast film machine extrusion, is unidirectionally drawn
Stretch and be cooled and shaped the laminated film for obtaining being overlapped after process by basement membrane and outer membrane;The outer layer copolymer is polypropylene, gathered
One kind in ethene, polyester and polyamide;The basement membrane is one kind in polypropylene, polyethylene, polyester and polyamide;
2) laminated film is soaked in acetone soln, after acetylbutyrylcellulose in acetone extract outer membrane, outside
Tunic formation outer layer porous membrane, porous compound film is obtained after drying.
Preferably, the outer layer copolymer is same material with basement membrane polymer.Outer layer copolymer polymerize with basement membrane
Thing be porous compound film made from same material in two membranes composite effect more preferably, attaching it is tighter.
Preferably, outer layer porous membrane thickness is 50~100 μm, basement membrane thickness is 50~100 μm.
Preferably, the average diameter of the outer layer porous membrane Hole is 1~10 μm.
Preferably, the mass ratio of the outer layer film raw material and basement membrane polymer is 1:1~2.
The advantage of the invention is that:
1, compared with traditional composite membrane, outer membrane of the invention is outer layer porous membrane, and the specific surface area of outer layer is expanded
Big tens times, the porous compound film has micron-sized pore space structure, if being handled by functional materials, this is micron-sized
Pore space structure can adsorbed close functional materials so as to realizing special function, it is such as conductive, it is hydrophilic, it is hydrophobic, you can be spun special
Knitted fabric, is sensed, and the field such as ultracapacitor is applied.
2, after being combined by double-deck cast film machine, the composite effect of outer layer porous membrane and basement membrane is good, without viscous glutinous agent.
3, outer layer copolymer:Acetylbutyrylcellulose is 6.5:3.5~9:When 1, acetylbutyrylcellulose by and point
It is dispersed in outer layer copolymer, by blending extrusion one-way drawing, and continuous phase can not be formed, it is by acetone that acetate butyrate is fine
After dimension element extraction, outer membrane formation pore space structure, so as to form porous compound film.If mass ratio is more than 9:1, outer layer is porous thin
Hole diameter in film is too big more than 10 μm, influences the sensing or adsorption function of porous compound film;If mass ratio is less than 6.5:
3.5, blended extrusion one-way drawing can produce the acetylbutyrylcellulose of continuous phase, nanofiber is formed after acetone extract
Structure and pore space structure can not be formed.
Brief description of the drawings
Fig. 1 is the structural representation of porous compound film of the present invention;
Fig. 2 is the structural representation of outer layer porous membrane in Fig. 1;
Fig. 3 is step 1 in embodiment 1~4) the obtained structural representation of laminated film;
Each part numbers are as follows in figure:Outer layer porous membrane 1, basement membrane 2, outer membrane 3.
Embodiment
To more fully understand the present invention, invention is described in detail below with reference to accompanying drawing and instantiation.
Embodiment 1
The preparation method of porous compound film, comprises the following steps:
1) polypropylene 650g and acetylbutyrylcellulose 350g are weighed, as outer layer film raw material after being well mixed, then is weighed
Polypropylene 2000g is used as basement membrane polymer;Outer layer film raw material and basement membrane polymer are put into double-deck cast film machine, through bilayer curtain coating
The laminated film overlapped by basement membrane 2 and outer membrane 3 is obtained (such as Fig. 3 institutes after film machine extrusion, simple tension and cooling and shaping process
Show);
2) laminated film is soaked in acetone soln, after acetylbutyrylcellulose in acetone extract outer membrane 3, outside
The formation outer layer of tunic 3 porous membrane 1, porous compound film (as shown in Figure 1) is obtained after drying.
The thickness of outer layer porous membrane 1 is 50 μm in such as Fig. 1, porous compound film, and the thickness of basement membrane 2 is 100 μm, with reference to Fig. 2
Shown, the average diameter of the Hole of outer layer porous membrane 1 is 10 μm.
Embodiment 2
1) polyethylene 900g and acetylbutyrylcellulose 100g are weighed, as outer layer film raw material after being well mixed, then is weighed
Polyethylene 1000g is used as basement membrane polymer;Outer layer film raw material and basement membrane polymer are put into double-deck cast film machine, through bilayer curtain coating
The laminated film (as shown in Figure 3) overlapped by the outer membrane 3 of basement membrane 2 is obtained after film machine extrusion, simple tension and cooling and shaping process;
2) laminated film is soaked in acetone soln, after acetylbutyrylcellulose in acetone extract outer membrane, outside
The formation outer layer of tunic 3 porous membrane 1, porous compound film (as shown in Figure 1) is obtained after drying.
The thickness of outer layer porous membrane 1 is 100 μm in such as Fig. 1, porous compound film, and the thickness of basement membrane 2 is 50 μm, with reference to Fig. 2
Shown, the average diameter of the Hole of outer layer porous membrane 1 is 5 μm.
Embodiment 3
1) it is 300g to weigh polyester 700g with acetylbutyrylcellulose, as outer layer film raw material after being well mixed, then is weighed
Polyester 1500g is used as basement membrane polymer;Outer layer film raw material and basement membrane polymer are put into double-deck cast film machine, through double-deck casting films
The laminated film (as shown in Figure 3) overlapped by the outer membrane 3 of basement membrane 2 is obtained after machine extrusion, simple tension and cooling and shaping process;
2) laminated film is soaked in acetone soln, after acetylbutyrylcellulose in acetone extract outer membrane, outside
Tunic formation outer layer porous membrane, porous compound film (as shown in Figure 1) is obtained after drying.
The thickness of outer layer porous membrane 1 is 65 μm in such as Fig. 1, porous compound film, and the thickness of basement membrane 2 is 80 μm, with reference to Fig. 2 institutes
Show, the average diameter of the Hole of outer layer porous membrane 1 is 1 μm.
Embodiment 4
1) polyamide 800g and acetylbutyrylcellulose 200g are weighed, as outer layer film raw material after being well mixed, then is weighed
Polyamide 1000g is used as basement membrane polymer;Outer layer film raw material and basement membrane polymer are put into double-deck cast film machine, through bilayer curtain coating
The laminated film (as shown in Figure 3) overlapped by the outer membrane 3 of basement membrane 2 is obtained after film machine extrusion, simple tension and cooling and shaping process;
2) laminated film is soaked in acetone soln, after acetylbutyrylcellulose in acetone extract outer membrane, outside
Tunic formation outer layer porous membrane, porous compound film (as shown in Figure 1) is obtained after drying.
The thickness of outer layer porous membrane 1 is 70 μm in such as Fig. 1, porous compound film, and the thickness of basement membrane 2 is 75 μm, with reference to Fig. 2 institutes
Show, the average diameter of the Hole of outer layer porous membrane 1 is 6 μm.
Embodiment described above only expresses the several embodiments of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (7)
1. a kind of porous compound film, including basement membrane, it is characterised in that:It is porous thin that the outer surface of the basement membrane is pasted with outer layer
Hole is uniformly distributed on film, the outer layer porous membrane, the average diameter of described hole is 1~10 μm;The basement membrane is poly-
One kind in propylene, polyethylene, polyester and polyamide, the outer layer porous membrane is polypropylene, polyethylene, polyester and polyamide
In one kind;The thickness of the basement membrane is 50~100 μm, and the thickness of the outer layer porous membrane is 50~100 μm.
2. porous compound film according to claim 1, it is characterised in that:The outer layer porous membrane is same with basement membrane
Plant material.
3. a kind of preparation method of porous compound film, it is characterised in that:Comprise the following steps:
1) outer layer copolymer in mass ratio, is weighed:Acetylbutyrylcellulose is 6.5:3.5~9:1, it is used as outer layer after being well mixed
Film raw material, double-deck cast film machine is put into by outer layer film raw material and basement membrane polymer, through double-deck cast film machine extrusion, simple tension and
It is cooled and shaped the laminated film for obtaining being overlapped after process by basement membrane and outer membrane;The outer layer copolymer be polypropylene, polyethylene,
One kind in polyester and polyamide;The basement membrane is one kind in polypropylene, polyethylene, polyester and polyamide;
2) laminated film is soaked in acetone soln, after acetylbutyrylcellulose in acetone extract outer membrane, outer membrane
Outer layer porous membrane is formed, porous compound film is obtained after drying.
4. the preparation method of porous compound film according to claim 3, it is characterised in that:The outer layer copolymer and base
Membrane polymer is same material.
5. the preparation method of porous compound film according to claim 3, it is characterised in that:Outer layer porous membrane thickness is
50~100 μm, basement membrane thickness is 50~100 μm.
6. the preparation method of porous compound film according to claim 3, it is characterised in that:In the outer layer porous membrane
The average diameter of hole is 1~10 μm.
7. the preparation method of porous compound film according to claim 3, it is characterised in that:The outer layer film raw material and base
The mass ratio of membrane polymer is 1:1~2.