CN106956474A - Fluosilicic fire proofing firbre felt - Google Patents
Fluosilicic fire proofing firbre felt Download PDFInfo
- Publication number
- CN106956474A CN106956474A CN201710127660.XA CN201710127660A CN106956474A CN 106956474 A CN106956474 A CN 106956474A CN 201710127660 A CN201710127660 A CN 201710127660A CN 106956474 A CN106956474 A CN 106956474A
- Authority
- CN
- China
- Prior art keywords
- fiber
- inorganic
- fire
- fiber layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of fluosilicic fire proofing firbre felt, described fluosilicic fire proofing firbre felt includes permeable fiber layer, fluororesin adherent layer and inorganic fireproof fiber layer, the permeable fiber layer uses bamboo fibre by warp, parallel is interwoven using Carbon fibe, the inorganic fireproof fiber layer is by horizontal inorganic fire fiber, longitudinal polyester fiber and the braiding of oblique carbon fiber are formed, described inorganic fire fiber accounts for 51% the 57% of the overall component of inorganic fireproof fiber layer, described polyester fiber accounts for 7% the 10% of the overall component of inorganic fireproof fiber layer, described carbon fiber accounts for 36% the 39% of the overall component of inorganic fireproof fiber layer.The present invention provides a kind of fluosilicic fire proofing firbre felt, has the advantages that intensity is high, fire resistance is good, pliability is good.
Description
Technical field
The present invention relates to a kind of fluosilicic fire proofing firbre felt.
Background technology
Glass fibre has extensive purposes in fields such as traffic, industry, building, environment, with glass field increasingly
Expand, in some fields, particularly with fields such as high alkali resistance, ageing resistances, common alkali-free glass fibre is due to its property
The defect of energy can not meet the market demand.Especially in building field, the reinforcing material of cement, common alkali-free glass are used as
Fiber does not have higher alkaline resistance properties, it is impossible to reach requirement.According to the market demand, it is necessary to seek with high alkali resistance, anti-ageing
The glass fibre for the property changed is used as reinforcing material.Once attempted to be coated with alkaline-resisting coating to improve alkali resistance on simple glass fiber,
But effect is not good.According to the market demand, it is necessary to seek with high alkali resistance, ageing resistance glass fibre as reinforcing material.
The alkali resistance of glass fibre is so improved, middle in glass grid structure resistance to alkaline constituents certainly will be added.For above feelings
Condition, many research institutions and glass fibre enterprise have carried out substantial amounts of experimental study, and the alkaline-resisting of glass fibre is improved by every means
Performance.By having determined effects of the ZrO2 in terms of alkali resistant, with the increase of ZrO2 contents, glass acid and alkali resistance
Improve, fiber weightlessness is reduced, and intensity level of the fiber in cement also increases.
Refractory fibre with high temperature resistant, vibration resistance, to the greatest extent heat, sound absorption and it is lightweight the advantages of, replaced brick structure and castable
And as fire resisting, insulation, heat-insulated, sound insulation, fireproof preferred material, obtained in industries such as metallurgy, oil, chemical industry, machinery, buildings
Extensive use.Refractory fibre is divided into noncrystalline and the major class of docrystalline two.Noncrystalline refractory fibre, including aluminosilicate property, HIGH-PURITY SILICON
Sour aluminum, aluminosilicate property containing chromium and high alumina fiber.Docrystalline refractory fibre, including mullite fiber, alumina fibre
And Zirconium oxide fibre.The temperature in use of general docrystalline refractory fibre is 1400 DEG C -1600 DEG C, right with industrial expansion
The requirement more and more higher of refractory fibre refractory temperature and its intensity.
The content of the invention
The present invention provides a kind of with intensity is high, fire resistance is good, the good advantage of pliability fluosilicic fire proofing firbre felt.
The technical scheme is that:A kind of fluosilicic fire proofing firbre felt, described fluosilicic fire proofing firbre felt includes ventilative fibre
Layer, fluororesin adherent layer and inorganic fireproof fiber layer are tieed up, the permeable fiber layer uses bamboo fibre by warp, and parallel uses Carbon fiber
Dimension is interwoven, and the inorganic fireproof fiber layer is woven by horizontal inorganic fire fiber, longitudinal polyester fiber and oblique carbon fiber
Form, described inorganic fire fiber accounts for the 51%-57% of the overall component of inorganic fireproof fiber layer, described polyester fiber accounts for inorganic
The 7%-10% of the overall component of fire proofing firbre layer, described carbon fiber accounts for the 36%-39% of the overall component of inorganic fireproof fiber layer.
In a preferred embodiment of the present invention, a diameter of 12.66 μm of the bamboo fibre, fiber number is 165dtex.
In a preferred embodiment of the present invention, described inorganic fire fiber accounts for the overall component of inorganic fireproof fiber layer
54%, described polyester fiber accounts for the 8% of the overall component of inorganic fireproof fiber layer, and it is total that described carbon fiber accounts for inorganic fireproof fiber layer
The 38% of body component.
A kind of fluosilicic fire proofing firbre felt of the present invention, has the advantages that intensity is high, fire resistance is good, pliability is good.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly being defined so as to be made to protection scope of the present invention.
Wherein, described fluosilicic fire proofing firbre felt includes permeable fiber layer, fluororesin adherent layer and inorganic fireproof fiber layer,
The permeable fiber layer uses bamboo fibre by warp, and parallel is interwoven using Carbon fibe, and the inorganic fireproof fiber layer is by horizontal stroke
Formed to inorganic fire fiber, longitudinal polyester fiber and the braiding of oblique carbon fiber, described inorganic fire fiber accounts for inorganic fire
The 51%-57% of fibrous layer totality component, described polyester fiber accounts for the 7%-10% of the overall component of inorganic fireproof fiber layer, described
Carbon fiber accounts for the 36%-39% of the overall component of inorganic fireproof fiber layer.
Further illustrate, a diameter of 12.66 μm of the bamboo fibre, fiber number is 165dtex, and described inorganic fire fiber is accounted for
The 54% of inorganic fireproof fiber layer totality component, described polyester fiber accounts for the 8% of the overall component of inorganic fireproof fiber layer, described
Carbon fiber accounts for the 38% of the overall component of inorganic fireproof fiber layer.
Further illustrating, inorganic fire fiber is all kinds of rock wools, mineral wool, mineral wool, aluminium silicate wool etc., with not
Fire, be stale-proof, not eating into, the characteristic such as not aging, but fibroid is crisp, frangibility.The country sprays formula inorganic fire using relatively broad
Fiber is HXPT alumina silicate thermal insulation sound absorption fiber, and its non-ignitable level fire protecting performance is tunnel, the preferred material of subway sqouynd absorption lowering noise,
The cost of its relative moderate, is also the ideal material of ultra-large type public building Acoustic treatment simultaneously.Inorganic fire fiber is to adopt
, can brokenly spray be on a surface of an with imported from America special equipment and glue special.Such as:Timber, metal, concrete and
Other construction materials, thickness unit weight can be designed by specific requirement.After spraying formed integral seamless every front cover, without cutting out every outward appearance
Succinctly.Spraying is tightly attached on each type objects, and long-term use will not be released.Main application 1, electric insulation:Silica gel cloth has higher
Electric insulation grade, can bear high-voltage loaded, can be made into the products such as empire cloth, sleeve pipe.2nd, non-metal compensator:Silica gel cloth can
Make the flexible connection device of pipeline, it can solve the destruction to pipeline of expanding with heat and contract with cold, silica gel cloth has higher temperature tolerance, prevents
Corruption, ageing resistace, elasticity and flexible good can be widely applied to oil, chemical industry, cement, the field such as energy.3rd, anti-corrosion side
Face:Silicone Rubber Coated glass fabric, can be as pipeline, and the inside and outside anticorrosive coating of savings, antiseptic property is excellent, and intensity is high, is one
Plant preferable anti-corrosion material.4th, other fields:Silicone Rubber Coated glass fibre membrane structure material can be applied to construction sealing materials,
High-temperature anticorrosion conveyer belt, the field such as packaging material.5th, it can be used as fire screen.
Further illustrating, fluororesin adherent layer has the characteristics that:1st, there is high adhesion between coating and metal:
External force can not be removed substantially, the attachment of metal and coating, as epidermis and the corium of people adhere to.Therefore solve convention liner tetrafluoro
Easily play drum between technique tetrafluoro layer and metal-based layer because adhesion is not enough, the defect come off, temperature change is frequently showed in environment
It is more obvious.2nd, the limitation of use scope of the convention liner tetrafluoro technique caused by shape is limited is overcome:Arbitrary shape is set
The sprayable processing of standby, parts;3rd, excellent shaping can cycling processability:Because fluoroplastics melt flow property is excellent,
After piece surface spraying, secondary operation can be also carried out, to meet the requirement controlled workpiece size precision.4th, it is excellent anti-
Sticky energy:Not only there is excellent anti-adhesion performance after spraying but also with excellent heat resistance, in -193 to 260 DEG C of height
Still possesses the anti-adhesion performance of uniqueness in warm use.5th, excellent vacuum-resistant performance:Be not in de- under any vacuum condition
Layer(In -0.01 to -0.1 MPa of vacuum).6th, excellent mechanical performance:Mechanical strength is big, resistance to have high rigidity and toughness. 7、
Excellent heat resistance:Can steadily in the long term it be used in the environment under -193 to 260 DEG C of high/low temperature.8th, excellent electric property:It is situated between
Electric constant and dielectric loss factor, all than relatively low, show high dielectric strength in very wide temperature and frequency range;9th, it is fire-retardant
Property:Fluororesin is all nonflammable under inflammable easily sudden and violent environment, is good fire proofing.10th, excellent wearability:By spy
Different processing can increase coating surface hardness, to improve wearability.11st, excellent corrosion resistance:Hardly by the corruption of any medium
Erosion.12nd, excellent high-purity cleanliness:Such as polysilicon industry, electroplating industry, special material reaction etc., not only reached anti-corrosion but also
Play high-purity clean effect present invention and a kind of fluosilicic fire proofing firbre felt is provided, with intensity is high, fire resistance is good, pliability is good
Advantage.
The embodiment of the present invention, but protection scope of the present invention is not limited thereto, it is any to be familiar with this area
Technical staff disclosed herein technical scope in, the change or replacement that can be expected without creative work should all be contained
Cover within protection scope of the present invention.Therefore, the protection model that protection scope of the present invention should be limited with claims
Enclose and be defined.
Claims (3)
1. a kind of fluosilicic fire proofing firbre felt, it is characterised in that:Described fluosilicic fire proofing firbre felt includes permeable fiber layer, fluororesin
Adherent layer and inorganic fireproof fiber layer, the permeable fiber layer use bamboo fibre by warp, and parallel is interwoven using Carbon fibe,
The inorganic fireproof fiber layer is formed by horizontal inorganic fire fiber, longitudinal polyester fiber and the braiding of oblique carbon fiber, described
Inorganic fire fiber accounts for the 51%-57% of the overall component of inorganic fireproof fiber layer, and described polyester fiber accounts for inorganic fireproof fiber layer
The 7%-10% of overall component, described carbon fiber accounts for the 36%-39% of the overall component of inorganic fireproof fiber layer.
2. fluosilicic fire proofing firbre felt according to claim 1, it is characterised in that:A diameter of 12.66 μm of the bamboo fibre, it is fine
Spend for 165dtex.
3. fluosilicic fire proofing firbre felt according to claim 1, it is characterised in that:Described inorganic fire fiber accounts for inorganic anti-
The 54% of the overall component of fiery fibrous layer, described polyester fiber accounts for the 8% of the overall component of inorganic fireproof fiber layer, described carbon fiber
Account for the 38% of the overall component of inorganic fireproof fiber layer.