CN106955007A - It is a kind of sun-proof every light cloth - Google Patents
It is a kind of sun-proof every light cloth Download PDFInfo
- Publication number
- CN106955007A CN106955007A CN201710354401.0A CN201710354401A CN106955007A CN 106955007 A CN106955007 A CN 106955007A CN 201710354401 A CN201710354401 A CN 201710354401A CN 106955007 A CN106955007 A CN 106955007A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- sun
- proof
- film
- aluminium powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is a kind of sun-proof every light cloth, aluminium powder formation coat is coated at least on one one side of fabric body, the 0-0.35MM of aluminum powder particle size, the coat thickness is 0.3 2MM.The present invention's is sun-proof simple every light etamine making process, low cost, possess good sun-proof every optical property, according to the requirement of Shading intensity, in fabric body set single or double aluminium powder be that can reach effect, it is of the present invention it is sun-proof have every light cloth it is frivolous, every the good advantage of optical property, and it is environment friendly and pollution-free, it is adapted to various shading occasions and uses.
Description
Technical field
The present invention relates to sun-proof technical field, be especially for door and window it is sun-proof every light use it is a kind of sun-proof every light
Cloth.
Background technology
Prior art it is sun-proof every light mainly using the technology such as light insulation pad, in time using every light cloth, being obtained every light cloth
It is poor every photosensitiveness.
The content of the invention
For these problems of prior art, the present invention is provided every good a kind of sun-proof every light cloth of optical property.
In order to achieve the above object, the present invention provides following technical scheme：
It is a kind of sun-proof every light cloth, aluminium powder formation coat, the aluminium powder grain are coated at least on one one side of fabric body
0-0.35MM is spent, the coat thickness is 0.3-2MM.
Aluminium powder is the nano-scale aluminium flake prepared using PVD method, and PVD method is vaporize-condensation law, and PVD method prepares nanometer sheet
The technological process of shape aluminium powder is：Raw material prepares, forms organic release film, form nanometer aluminium film, elution, crush and collect, raw material
Set-up procedure includes just purity and deoiled for 99.99% aluminium wire or aluminium block cleaning, and the oxide layer on surface is removed in polishing；Formed
Organic release membrane process is included in the aluminium film surface that will be deposited and applies the smooth organic film of last layer；Formation forms nanometer aluminium film mistake
Journey includes purity being placed in high vacuum and low-pressure inert gas Ar for 99.99% aluminum strip, is made by the heating of evaporation source
With so that aluminium block evaporation gasification, low-pressure inert gas Ar purity is 99.99%, and operating pressure is 10KPa, and gas flow rate is
1.5m/s, the evaporating temperature of evaporation source is 1300-1800K；Elution process includes the substrate that deposited aluminium film being put into organic examination
Agent is eluted, and realizes the separation of nanometer aluminium film and substrate；Crushing process includes stirring the eluent progress machinery containing aluminium powder
Mix, nanometer aluminium film is crushed to required particle diameter.
In above-mentioned technical proposal, aluminium powder is set to be attached in fabric body by the way of vacuum evaporation and glue connection are strengthened.
In above-mentioned technical proposal, aluminium powder is coated on web surface in adhesive, drying and processing is then carried out again to complete.
Technology provided by the present invention is compared to the usefulness that traditional technical scheme has：
(1) sun-proof simple every light etamine making process, low cost of the invention, possesses good sun-proof every optical property, according to
The requirement of Shading intensity, the aluminium powder that single or double is set in fabric body is that can reach effect, of the present invention sun-proof
Have every light cloth frivolous, every the good advantage of optical property, and environment friendly and pollution-free, be adapted to various shading occasions and use.
(2) using grid cloth compared to traditional cloth, the performance with chemicals attacks such as excellent antiacid, alkali,
Meanwhile, overall structure is high through broadwise tensile strength so that heat-insulation layer has very high impact resistance ability, can in heat-insulation system
Play a part of " mild steel muscle ".
(3) the aluminium powder particle diameter distribution using vaporize-condensation law preparation is narrow, than greatly, aluminum flake surface is put down behind the footpath of aluminium powder
Whole smooth, the particle diameter of aluminium powder is easily controlled, while the evaporation rate of vaporize-condensation law is fast, efficiency high, easily realize it is extensive,
Continuous production.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
The accompanying drawing to be used needed for having technology description is briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, without having to pay creative labor, may be used also
To obtain other accompanying drawings according to these accompanying drawings.
Fig. 1 is structural representation of the invention.
Wherein:1st, fabric body；2nd, coat.
Embodiment
Below in conjunction with the accompanying drawing of the present invention, technical scheme is clearly and completely described, it is clear that institute
The embodiment of description is only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention,
The every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, belongs to this hair
The scope of bright protection.
According to Fig. 1, as a kind of sun-proof every light cloth shown in embodiment 1, coated on one one side of fabric body
Aluminium powder formation coat, aluminum powder particle size 0.2MM, coat thickness is 0.3MM, is made by the way of vacuum evaporation and glue connection are strengthened
Aluminium powder is attached in fabric body.
Aluminium powder is the nano-scale aluminium flake prepared using PVD method, and PVD method is vaporize-condensation law, and PVD method prepares nanometer sheet
The technological process of shape aluminium powder is：Raw material prepares, forms organic release film, form nanometer aluminium film, elution, crush and collect, raw material
Set-up procedure includes just purity and deoiled for 99.99% aluminium wire or aluminium block cleaning, and the oxide layer on surface is removed in polishing；Formed
Organic release membrane process is included in the aluminium film surface that will be deposited and applies the smooth organic film of last layer；Formation forms nanometer aluminium film mistake
Journey includes purity being placed in high vacuum and low-pressure inert gas Ar for 99.99% aluminum strip, is made by the heating of evaporation source
With so that aluminium block evaporation gasification, low-pressure inert gas Ar purity is 99.99%, and operating pressure is 10KPa, and gas flow rate is
1.5m/s, the evaporating temperature of evaporation source is 1300-1800K；Elution process includes the substrate that deposited aluminium film being put into organic examination
Agent is eluted, and realizes the separation of nanometer aluminium film and substrate；Crushing process includes stirring the eluent progress machinery containing aluminium powder
Mix, nanometer aluminium film is crushed to required particle diameter.
Embodiment 2 is a kind of sun-proof every light cloth, and aluminium powder formation coat, aluminium powder are coated on positive and negative two one sides of fabric body
Granularity 0.15MM, coat thickness is 0.4MM, and aluminium powder is coated on into web surface in adhesive, drying and processing is then carried out again
To complete.
The fabric body that the present invention is used uses grid cloth, screening area：0.3-1mm × 0.3-1mm, embodiment grid
The screening area of cloth：0.3mm×0.3mm.
The present invention use the distinctive covering power of aluminium powder, coat aluminium powder on the grid cloth of fabric body, can by grid it
Between pore separate external light and can not pass through,；Aluminium powder good reflection visible ray, ultraviolet light and infrared light are utilized simultaneously
Performance, therefore can possess good every photosensitiveness.
Although technical scheme know-why is simple, using aluminium powder is coated on grid cloth reach it is sun-proof every
The effect of light, rarely has technical inspiration in the prior art, according to the experiment of inventor, the product obtained using the technical program,
It is good every photosensitiveness, while the reflecting properties of aluminium powder, reflect heat so that the product obtained using the technical program has preferably anti-
Solarization property.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
Those familiar with the art the invention discloses technical scope in, change or replacement can be readily occurred in, should all be contained
Cover within protection scope of the present invention.
Claims (3)
1. it is a kind of sun-proof every light cloth, it is characterised in that：Aluminium powder formation coat, institute are coated at least on one one side of fabric body
0-0.35MM of aluminum powder particle size is stated, the coat thickness is 0.3-2MM.
2. one kind according to claim 1 is sun-proof every light cloth, it is characterised in that the aluminium powder is to be prepared using PVD method
Nano-scale aluminium flake, the PVD method is vaporize-condensation law, and the technological process that PVD method prepares nano-scale aluminium flake is：Raw material is accurate
It is standby, form organic release film, form nanometer aluminium film, elution, crush and collection, the raw material set-up procedure is including just purity
99.99% aluminium wire or aluminium block cleaning is deoiled, and the oxide layer on surface is removed in polishing；The organic release membrane process of formation includes
The smooth organic film of last layer is applied in the aluminium film surface that will be deposited；The nano aluminum membrane process that formed including being by purity
99.99% aluminum strip is placed in high vacuum and low-pressure inert gas Ar, passes through the heat effect of evaporation source so that aluminium block evaporates
Gasification, the low-pressure inert gas Ar purity is 99.99%, and operating pressure is 10KPa, and gas flow rate is 1.5m/s, the steaming
The evaporating temperature risen is 1300-1800K；The elution process includes the substrate that deposited aluminium film being put into organic reagent progress
Elution, realizes the separation of nanometer aluminium film and substrate；The crushing process includes the eluent containing aluminium powder carrying out mechanical agitation,
Nanometer aluminium film is crushed to required particle diameter.
3. one kind according to claim 1 is sun-proof every light cloth, it is characterised in that：Fabric body uses grid cloth, mesh face
Product：0.3—1mm×0.3—1mm.