CN106947214A - A kind of elasticity concretion abrasive and preparation method applied to liquid injection glossing - Google Patents
A kind of elasticity concretion abrasive and preparation method applied to liquid injection glossing Download PDFInfo
- Publication number
- CN106947214A CN106947214A CN201710132084.8A CN201710132084A CN106947214A CN 106947214 A CN106947214 A CN 106947214A CN 201710132084 A CN201710132084 A CN 201710132084A CN 106947214 A CN106947214 A CN 106947214A
- Authority
- CN
- China
- Prior art keywords
- preparation
- elasticity
- concretion abrasive
- powder
- prestige
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of elasticity concretion abrasive applied to liquid injection glossing, making material is epoxy resin, organic siliconresin, the even film of organosilicon and alundum (Al2O3) or prestige silicon carbide micro-powder, and the even film of the epoxy resin, organic siliconresin, organosilicon and alundum (Al2O3) or prestige silicon carbide micro-powder adoption rate are 3:2:0.5:4.5 progress are mixed and modified, and then prepare concretion abrasive；Preparation method comprises the following steps：Step one, selection；Step 2, proportionality blending and modifying；Step 3, proportionality mixing and stirring；Step 4, stands and cools down；Step 5, crushes and sorts；It is of the invention effective to solve due to elastic force not enough and the problem of short life, effectively enhance the elasticity and service life of concretion abrasive, and the technique crushed by hot setting after blending and modifying obtains concretion abrasive, and then conveniently it is divided into the preparation that the particle feed flow state of various applicable models sprays grinding fluid.
Description
Technical field
It is especially a kind of to be applied to liquid injection buffer the present invention relates to concretion abrasive and its application and preparation technical field
The elasticity concretion abrasive and preparation method of skill.
Background technology
In the prior art, applied to liquid injection glossing there is the elastic pole of toughness in concretion abrasive and its extension application
The liquid injection of difference, metal material or other hard brittle materials, its concretion abrasive ratio is low, and service life is short, nonelastic, and existing
Preparation method inconvenience be divided into various applicable models particle feed flow state spray grinding fluid preparation.
Therefore a kind of new making formula and technique is needed to solve problems of the prior art.
The content of the invention
It is an object of the invention to provide a kind of elasticity concretion abrasive applied to liquid injection glossing and preparation
Method, it is with epoxy resin, organic siliconresin, the even film of organosilicon and alundum (Al2O3) or prestige silicon carbide micro-powder according to certain
The mixed and modified application and preparation of ratio is effectively solved due to elastic force not in the elasticity concretion abrasive of liquid injection glossing
The problem of enough and short life, the elasticity and service life of concretion abrasive are effectively enhanced, and it is solid by high temperature after blending and modifying
Change the technique crushed and obtain concretion abrasive, and then be conveniently divided into the preparation that the particle feed flow state of various applicable models sprays grinding fluid.
To achieve the above object, the present invention provides following technical scheme：A kind of bullet applied to liquid injection glossing
Property concretion abrasive, making material is polyester resin and polyurethane resin, and the epoxy resin, organic siliconresin, organosilicon are even
Film and alundum (Al2O3) or prestige silicon carbide micro-powder are according to 3:2:0.5:4.5 ratio mixing coordinates, blended modified high temperature
Solidification is crushed, and the particle feed flow state for being divided into various applicable models sprays the preparation of grinding fluid.
A kind of preparation method of elasticity concretion abrasive applied to liquid injection glossing, comprises the following steps：Step
Rapid one, selection；Step 2, proportionality blending and modifying；Step 3, proportionality mixing and stirring；Step 4, stands and cools down；Step
Rapid five, crush and sort.
In described step one, the even film of selection epoxy resin, organic siliconresin, organosilicon and alundum (Al2O3) or prestige
Silicon carbide micro-powder is the raw material of remarks polishing material；
In described step two, by step one first by epoxy resin, organic siliconresin and organo-silicon coupling agent with 3:2:
0.5 ratio is mixed 20 minutes, allows its abundant blending and modifying；
In described step three, blending and modifying resin obtained by step 2 is weighed, and by 5.5:4.5 ratio and three oxidations two
Aluminium or prestige silicon carbide micro-powder are sufficiently mixed stirring 30 minutes；
In described step four, blend obtained by step 3 is stood 10 minutes, is then placed in the baking box that temperature is 130 DEG C
Solidification takes out cooling after 60 minutes；
In described step five, the solidfied material after being cooled down in step 4 is crushed, must can be consolidated by the sorting of different factors is stand-by
Tie abrasive material.
As the further technical scheme of the present invention, the alundum (Al2O3) or prestige silicon carbide micro-powder can also be cerium oxide
Diamond boron oxide or ultrafine silica powder.
Compared with prior art, beneficial effect of the present invention：The present invention is with epoxy resin, organic siliconresin, the even film of organosilicon
Agent and alundum (Al2O3) or prestige silicon carbide micro-powder are according to certain mixed and modified application and preparation of ratio in liquid injection glossing
Elasticity concretion abrasive, effectively solve because elastic force is not enough and the problem of short life, effectively enhance concretion abrasive
Elasticity and service life, and the technique crushed by hot setting after blending and modifying obtains concretion abrasive, and then is conveniently divided into
The particle feed flow state of various applicable models sprays the preparation of grinding fluid.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
In the embodiment of the present invention, a kind of elasticity concretion abrasive applied to liquid injection glossing, making material is
Polyester resin and polyurethane resin, the even film of the epoxy resin, organic siliconresin, organosilicon and alundum (Al2O3) or prestige carbonization
Silicon powder is according to 3:2:0.5:4.5 ratio mixing coordinates, and blended modified hot setting is crushed, and is divided into various applicable models
Particle feed flow state spray grinding fluid preparation.
A kind of preparation method of elasticity concretion abrasive applied to liquid injection glossing, comprises the following steps：Step
Rapid one, selection；Step 2, proportionality blending and modifying；Step 3, proportionality mixing and stirring；Step 4, stands and cools down；Step
Rapid five, crush and sort.
In described step one, the even film of selection epoxy resin, organic siliconresin, organosilicon and alundum (Al2O3) or prestige
Silicon carbide micro-powder is the raw material of remarks polishing material；
In described step two, by step one first by epoxy resin, organic siliconresin and organo-silicon coupling agent with 3:2:
0.5 ratio is mixed 20 minutes, allows its abundant blending and modifying；
In described step three, blending and modifying resin obtained by step 2 is weighed, and by 5.5:4.5 ratio and three oxidations two
Aluminium or prestige silicon carbide micro-powder are sufficiently mixed stirring 30 minutes；
In described step four, blend obtained by step 3 is stood 10 minutes, is then placed in the baking box that temperature is 130 DEG C
Solidification takes out cooling after 60 minutes；
In described step five, the solidfied material after being cooled down in step 4 is crushed, must can be consolidated by the sorting of different factors is stand-by
Tie abrasive material.
As the further technical scheme of the present invention, the alundum (Al2O3) or prestige silicon carbide micro-powder can also be cerium oxide
Diamond boron oxide or ultrafine silica powder.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It may be appreciated other embodiment.
Claims (3)
1. a kind of elasticity concretion abrasive applied to liquid injection glossing, making material is polyester resin and polyurethane tree
Fat, it is characterised in that：The even film of the epoxy resin, organic siliconresin, organosilicon and alundum (Al2O3) or prestige silicon carbide micro-powder
According to 3:2:0.5:4.5 ratio mixing coordinates, and blended modified hot setting is crushed, and is divided into the particle of various applicable models
Feed flow state sprays the preparation of grinding fluid.
2. a kind of preparation method of elasticity concretion abrasive applied to liquid injection glossing, comprises the following steps：Step
One, selection；Step 2, proportionality blending and modifying；Step 3, proportionality mixing and stirring；Step 4, stands and cools down；Step
Five, crush and sort, it is characterised in that：
In described step one, the even film of selection epoxy resin, organic siliconresin, organosilicon and alundum (Al2O3) or prestige carbonization
Silicon powder is the raw material of remarks polishing material；
In described step two, by step one first by epoxy resin, organic siliconresin and organo-silicon coupling agent with 3:2:
0.5 ratio is mixed 20 minutes, allows its abundant blending and modifying；
In described step three, blending and modifying resin obtained by step 2 is weighed, and by 5.5:4.5 ratio and three oxidations two
Aluminium or prestige silicon carbide micro-powder are sufficiently mixed stirring 30 minutes；
In described step four, blend obtained by step 3 is stood 10 minutes, is then placed in the baking box that temperature is 130 DEG C
Solidification takes out cooling after 60 minutes；
In described step five, the solidfied material after being cooled down in step 4 is crushed, must can be consolidated by the sorting of different factors is stand-by
Tie abrasive material.
3. a kind of preparation of elasticity concretion abrasive applied to liquid injection glossing according to claim 1 or 2
Method, it is characterised in that：The alundum (Al2O3) or prestige silicon carbide micro-powder can also be cerium oxide diamond boron oxide or oxidation
Silicon powder.