CN106946532A - 一种彩色装饰保温防水砂浆 - Google Patents
一种彩色装饰保温防水砂浆 Download PDFInfo
- Publication number
- CN106946532A CN106946532A CN201710271513.XA CN201710271513A CN106946532A CN 106946532 A CN106946532 A CN 106946532A CN 201710271513 A CN201710271513 A CN 201710271513A CN 106946532 A CN106946532 A CN 106946532A
- Authority
- CN
- China
- Prior art keywords
- parts
- polychromy
- heat insulation
- component
- waterproof mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种彩色装饰保温防水砂浆，由以下重量份数的组份混合而成：组份A：2‑4份、组份B：8‑12份；所述组份A由以下重量份数的原料组成：硅丙乳液：30‑50份、苯丙乳液：10‑30份、纯丙乳液：30‑50份、杀菌剂：0.1‑0.3份、消泡剂：0.1‑0.3份、润湿剂：0.1‑0.2份、成膜助剂：1‑3份，分散剂：0.1‑0.3份、水：20‑30份；所述组份B由以下重量份数的原料组成：白水泥：30‑50份、彩砂：20‑40份、滑石粉：5‑15份、轻钙：5‑10份、重钙：5‑10份、颜料：1‑3份、纳米气凝胶：1‑5份。本发明得到的产品不反碱，制备得到的改性纳米气凝胶分散性好。
Description
技术领域：
本发明涉及一种彩色装饰保温防水砂浆。
背景技术：
防水砂浆是一种刚性防水材料，通过提高砂浆的密实性及改进抗裂性以达到防水抗渗的目的。防水砂浆具有良好的耐候性、抗渗性、密实性和极高的粘结力以及较强的防水防腐效果。它与普通水泥和特种水泥配置成的水泥砂浆，通过调和水泥砂浆浇铸或喷涂，手工涂抹的方法在混凝土及表面形成坚固的防水防腐砂浆层，属刚韧性防水防腐材料。但是现有的水泥基彩色防水砂浆存在这易反碱、纳米气凝胶团聚后难分散等问题，现有技术对此并没有解决之策。
发明内容：
本发明的目的就是针对现有技术存在的上述缺点，提供了一种彩色装饰保温防水砂浆，它不反碱，纳米气凝胶分散性好，解决了现有技术中存在的问题。
本发明为解决上述技术问题所采用的技术方案是：
一种彩色装饰保温防水砂浆，由以下重量份数的组份混合而成：组份A：2-4份、组份B：8-12份；所述组份A由以下重量份数的原料组成：硅丙乳液：30-50份、苯丙乳液：10-30份、纯丙乳液：30-50份、杀菌剂：0.1-0.3份、消泡剂：0.1-0.3份、润湿剂：0.1-0.2份、成膜助剂：1-3份，分散剂：0.1-0.3份、水：20-30份；所述组份B由以下重量份数的原料组成：白水泥：30-50份、彩砂：20-40份、滑石粉：5-15份、轻钙：5-10份、重钙：5-10份、颜料：1-3份、纳米气凝胶：1-5份。
优选的,所述杀菌剂为卡松；所述消泡剂为矿物油；所述润湿剂为P100；所述分散剂为5044分散剂。
优选的,所述彩砂为70-140目彩砂。
优选的,所述滑石粉为400目滑石粉。
优选的,所述轻钙为1250目轻钙。
优选的,所述重钙为800目重钙。
优选的,所述纳米气凝胶为改性纳米气凝胶。
所述改性纳米气凝胶的制备方法包括以下步骤：
S1、将润湿剂、分散剂、聚乙烯吡咯烷酮在搅拌下加入到无水醇溶液中；
S2、用有机碱将S1得到的溶液的pH值调节到9-11，然后搅拌2-6h；
S3、在S2得到的溶液中加入纳米气凝胶，超声分散至少30min，在此过程中加入硅烷偶联剂；
S4、将S3得到的溶液放入到高压釜内，在温度：180-240℃、压力：5-10MPa下反应1.5-3.5h，得到最终产品。
优选的，所述无水醇溶液为甲醇、乙醇、丙醇、异丙醇、正丁醇、异丁醇、仲丁醇、叔丁醇的一种或几种。
优选的，所述有机碱为甲醇钠或乙醇钾。
优选的，所述纳米气凝胶为二氧化硅气凝胶和二氧化钛气凝胶的混合物，二氧化硅气凝胶和二氧化钛气凝胶的质量比为3:1-1:1。
优选的，所述纳米气凝胶为30-50nm改性纳米气凝胶。
与现有技术相比，本发明的优点是：传统水泥基彩色装饰砂浆存在易返碱问题，本发明利用硅丙乳液、苯丙乳液、纯丙乳液复配技术及改性纳米气凝胶技术，通过吸附，密封包裹作用，从根本上解决彩色装饰砂浆返碱问题；纳米气凝胶在应用过程中存在团聚难分散问题，对其进行聚合物改性处理，使纳米气凝胶能够良好均匀的分散到料浆中，充分发挥作用；引入改性纳米气凝胶对游离的Na+,Ca2+,Mg2+等离子进行吸附，发生螯合反应，形成稳定的金属螯合物，从而从根源上杜绝砂浆返碱问题；改性纳米气凝胶解决了纳米气凝胶在应用过程中的团聚难分散问题，利用硅烷偶联剂，聚乙烯吡咯烷酮，润湿剂，5044分散剂，对其进行改性处理，使纳米气凝胶能够良好均匀的分散到料浆中，能够充分发挥其吸附面积大、重量轻、保温效果好的特性。
具体实施方式：
为能清楚说明本方案的技术特点，下面通过具体实施方式，对本发明进行详细阐述。
一种彩色装饰保温防水砂浆，由以下重量份数的组份混合而成：组份A：2-4份、组份B：8-12份；所述组份A由以下重量份数的原料组成：硅丙乳液：30-50份、苯丙乳液：10-30份、纯丙乳液：30-50份、杀菌剂：0.1-0.3份、消泡剂：0.1-0.3份、润湿剂：0.1-0.2份、成膜助剂：1-3份，分散剂：0.1-0.3份、水：20-30份；所述组份B由以下重量份数的原料组成：白水泥：30-50份、彩砂：20-40份、滑石粉：5-15份、轻钙：5-10份、重钙：5-10份、颜料：1-3份、纳米气凝胶：1-5份。
所述杀菌剂为卡松；所述消泡剂为矿物油；所述润湿剂为P100；所述分散剂为5044分散剂。所述彩砂为70-140目彩砂。所述滑石粉为400目滑石粉。所述轻钙为1250目轻钙。所述重钙为800目重钙。所述纳米气凝胶为30-50nm改性纳米气凝胶。
所述改性纳米气凝胶的制备方法包括以下步骤：
S1、将润湿剂、分散剂、聚乙烯吡咯烷酮在搅拌下加入到无水醇溶液中；
S2、用有机碱将S1得到的溶液的pH值调节到9-11，然后搅拌2-6h；
S3、在S2得到的溶液中加入纳米气凝胶，超声分散至少30min，在此过程中加入螯合剂；
S4、将S3得到的溶液放入到高压釜内，在温度：180-240℃、压力：5-10MPa下反应1.5-3.5h，得到最终产品。改性纳米气凝胶解决了纳米气凝胶在应用过程中的团聚难分散问题，利用硅烷偶联剂，聚乙烯吡咯烷酮，润湿剂，5044分散剂，对其进行改性处理，使纳米气凝胶能够良好均匀的分散到料浆中，能够充分发挥其吸附面积大、重量轻、保温效果好的特性。
所述无水醇溶液为甲醇、乙醇、丙醇、异丙醇、正丁醇、异丁醇、仲丁醇、叔丁醇的一种或几种。
所述有机碱为甲醇钠或乙醇钾。
所述纳米气凝胶为二氧化硅气凝胶和二氧化钛气凝胶的混合物，二氧化硅气凝胶和二氧化钛气凝胶的质量比为3:1-1:1。
组份A中的三种乳液可以形成连续的高分子薄膜，因此具有优良的防水性能，并且有效隔绝水汽，减少返碱；杀菌剂：杀菌、防霉；消泡剂：消除反应体系内部起泡；润湿剂：对粉料表面润湿，使粉料更容易与液相相容；分散剂：提高物料分散性；成膜助剂：降低乳液成膜温度；白水泥：胶凝材料；彩砂：骨料，增加强度，调节装饰性；滑石粉、轻钙、重钙：填料，并进行了一定的级配以提高产品性能；颜料：调节饰面效果；改性气凝胶：吸附游离的Na+,Ca2 +,Mg2+，减少返碱；降低导热系数，保温隔热，降低产品密度，从而减少自重。
对于改性纳米气凝胶的实施例如下：
实施例1：
S1、将P100润湿剂、5044分散剂、聚乙烯吡咯烷酮在搅拌下加入到无水甲醇溶液中；
S2、用甲醇钠将S1得到的溶液的pH值调节到9-11，然后搅拌2h；
S3、在S2得到的溶液中加入质量比为3:1二氧化硅气凝胶和二氧化钛气凝胶，超声分散30min，在此过程中加入硅烷偶联剂；
S4、将S3得到的溶液放入到高压釜内，在温度：180℃、压力：5MPa下反应1.5h，即可得到符合要求的产品。
实施例2：
S1、将P100润湿剂、5044分散剂、聚乙烯吡咯烷酮在搅拌下加入到无水甲醇溶液中；
S2、用甲醇钠将S1得到的溶液的pH值调节到9-11，然后搅拌4h；
S3、在S2得到的溶液中加入质量比为2:1二氧化硅气凝胶和二氧化钛气凝胶，超声分散30min，在此过程中加入硅烷偶联剂；
S4、将S3得到的溶液放入到高压釜内，在温度：210℃、压力：8MPa下反应2.5h，即可得到符合要求的产品。
实施例3：
S1、将P100润湿剂、5044分散剂、聚乙烯吡咯烷酮在搅拌下加入到无水甲醇溶液中；
S2、用甲醇钠将S1得到的溶液的pH值调节到9-11，然后搅拌6h；
S3、在S2得到的溶液中加入质量比为1:1二氧化硅气凝胶和二氧化钛气凝胶，超声分散30min，在此过程中加入硅烷偶联剂；
S4、将S3得到的溶液放入到高压釜内，在温度：240℃、压力：10MPa下反应3.5h，即可得到符合要求的产品。
对于防水砂浆的实施例如下：
实施例1：
S1、配备组份A：将如下质量的原料混合：硅丙乳液：30kg、苯丙乳液：10kg、纯丙乳液：30kg、杀菌剂：0.1kg、消泡剂：0.1kg、润湿剂：0.1kg、成膜助剂：1kg，分散剂：0.1kg、水：20kg；
S2、配备组份B：白水泥：30kg、彩砂：20kg、滑石粉：5kg、轻钙：5kg、重钙：5kg、颜料：1kg、改性纳米气凝胶：1kg；
S3、将组份A与组份B按照质量比2：8进行充分混合；
S4、施工：将S3得到的产品在一个平板上进行实验性施工，得到一个10cm见方、施工厚度5mm的砂浆块，作为1号产品。
实施例2：
S1、配备组份A：将如下质量的原料混合：硅丙乳液：50kg、苯丙乳液：30kg、纯丙乳液：50kg、杀菌剂：0.3kg、消泡剂：0.3kg、润湿剂：0.2kg、成膜助剂：3kg，分散剂：0.3kg、水：30kg；
S2、配备组份B：白水泥：50kg、彩砂：40kg、滑石粉：15kg、轻钙：10kg、重钙：10kg、颜料：3kg、改性纳米气凝胶：5kg；
S3、将组份A与组份B按照质量比4：12进行充分混合；
S4、施工：将S3得到的产品在一个平板上进行实验性施工，得到一个10cm见方、施工厚度5mm的砂浆块，作为2号产品。
实施例3：
S1、配备组份A：将如下质量的原料混合：硅丙乳液：40kg、苯丙乳液：20kg、纯丙乳液：40kg、杀菌剂：0.2kg、消泡剂：0.2kg、润湿剂：0.15kg、成膜助剂：2kg，分散剂：0.2kg、水：25kg；
S2、配备组份B：白水泥：40kg、彩砂：30kg、滑石粉：10kg、轻钙：7.5kg、重钙：7.5kg、颜料：2kg、改性纳米气凝胶：3kg；
S3、将组份A与组份B按照质量比3：10进行充分混合；
S4、施工：将S3得到的产品在一个平板上进行实验性施工，得到一个10cm见方、施工厚度5mm的砂浆块，作为3号产品。
实施例4：
S1、配备组份A：将如下质量的原料混合：硅丙乳液：40kg、苯丙乳液：20kg、纯丙乳液：40kg、杀菌剂：0.2kg、消泡剂：0.2kg、润湿剂：0.15kg、成膜助剂：2kg，分散剂：0.2kg、水：25kg；
S2、配备组份B：白水泥：40kg、彩砂：30kg、滑石粉：10kg、轻钙：7.5kg、重钙：7.5kg、颜料：2kg；
S3、将组份A与组份B按照质量比3：10进行充分混合；
S4、施工：将S3得到的产品在一个平板上进行实验性施工，得到一个10cm见方、施工厚度5mm的砂浆块，作为4号产品。
实施例5：
S1、配备组份A：将如下质量的原料混合：杀菌剂：0.2kg、消泡剂：0.2kg、润湿剂：0.15kg、成膜助剂：2kg，分散剂：0.2kg、水：25kg；
S2、配备组份B：白水泥：40kg、彩砂：30kg、滑石粉：10kg、轻钙：7.5kg、重钙：7.5kg、颜料：2kg、改性纳米气凝胶：3kg；
S3、将组份A与组份B按照质量比3：10进行充分混合；
S4、施工：将S3得到的产品在一个平板上进行实验性施工，得到一个10cm见方、施工厚度5mm的砂浆块，作为5号产品。
实施例6：
S1、配备组份A：将如下质量的原料混合杀菌剂：0.2kg、消泡剂：0.2kg、润湿剂：0.15kg、成膜助剂：2kg，分散剂：0.2kg、水：25kg；
S2、配备组份B：白水泥：40kg、彩砂：30kg、滑石粉：10kg、轻钙：7.5kg、重钙：7.5kg、颜料：2kg；
S3、将组份A与组份B按照质量比3：10进行充分混合；
S4、施工：将S3得到的产品在一个平板上进行实验性施工，得到一个10cm见方、施工厚度5mm的砂浆块，作为6号产品。
将1-6号产品放到同一环境下，经过一个月的时间之后观察，其中1号产品、2号产品、3号产品没有反碱现象，而4号产品、5号产品有轻微反碱，6号产品反碱现象非常严重。
由此可以看出：硅丙乳液、苯丙乳液、纯丙乳液复配技术及改性纳米气凝胶技术，通过吸附、密封包裹作用，从根本上解决彩色装饰砂浆返碱问题。
上述具体实施方式不能作为对本发明保护范围的限制，对于本技术领域的技术人员来说，对本发明实施方式所做出的任何替代改进或变换均落在本发明的保护范围内。
本发明未详述之处，均为本技术领域技术人员的公知技术。
Claims (10)
1.一种彩色装饰保温防水砂浆，其特征在于：由以下重量份数的组份混合而成：组份A：2-4份、组份B：8-12份；所述组份A由以下重量份数的原料组成：硅丙乳液：30-50份、苯丙乳液：10-30份、纯丙乳液：30-50份、杀菌剂：0.1-0.3份、消泡剂：0.1-0.3份、润湿剂：0.1-0.2份、成膜助剂：1-3份，分散剂：0.1-0.3份、水：20-30份；所述组份B由以下重量份数的原料组成：白水泥：30-50份、彩砂：20-40份、滑石粉：5-15份、轻钙：5-10份、重钙：5-10份、颜料：1-3份、纳米气凝胶：1-5份。
2.根据权利要求1所述的一种彩色装饰保温防水砂浆，其特征在于：所述杀菌剂为卡松；所述消泡剂为矿物油；所述润湿剂为P100；所述分散剂为5044分散剂。
3.根据权利要求1所述的一种彩色装饰保温防水砂浆，其特征在于：所述彩砂为70-140目彩砂。
4.根据权利要求1所述的一种彩色装饰保温防水砂浆，其特征在于：所述滑石粉为400目滑石粉；所述轻钙为1250目轻钙；所述重钙为800目重钙。
5.根据权利要求1所述的一种彩色装饰保温防水砂浆，其特征在于：所述纳米气凝胶为改性纳米气凝胶。
6.根据权利要求5所述的一种彩色装饰保温防水砂浆，其特征在于：所述改性纳米气凝胶的制备方法包括以下步骤：
S1、将润湿剂、分散剂、聚乙烯吡咯烷酮在搅拌下加入到无水醇溶液中；
S2、用有机碱将S1得到的溶液的pH值调节到9-11，然后搅拌2-6h；
S3、在S2得到的溶液中加入纳米气凝胶，超声分散至少30min，在此过程中加入硅烷偶联剂；
S4、将S3得到的溶液放入到高压釜内，在温度：180-240℃、压力：5-10MPa下反应1.5-3.5h，得到最终产品。
7.根据权利要求6所述的一种彩色装饰保温防水砂浆，其特征在于：所述无水醇溶液为甲醇、乙醇、丙醇、异丙醇、正丁醇、异丁醇、仲丁醇、叔丁醇的一种或几种。
8.根据权利要求6所述的一种彩色装饰保温防水砂浆，其特征在于：所述有机碱为甲醇钠或乙醇钾。
9.根据权利要求6所述的一种彩色装饰保温防水砂浆，其特征在于：所述纳米气凝胶为二氧化硅气凝胶和二氧化钛气凝胶的混合物，二氧化硅气凝胶和二氧化钛气凝胶的质量比为3:1-1:1。
10.根据权利要求5所述的一种彩色装饰保温防水砂浆，其特征在于：所述纳米气凝胶为30-50nm改性纳米气凝胶。