CN106944938A - A kind of resin wheel - Google Patents
A kind of resin wheel Download PDFInfo
- Publication number
- CN106944938A CN106944938A CN201710328781.0A CN201710328781A CN106944938A CN 106944938 A CN106944938 A CN 106944938A CN 201710328781 A CN201710328781 A CN 201710328781A CN 106944938 A CN106944938 A CN 106944938A
- Authority
- CN
- China
- Prior art keywords
- emery wheel
- resin
- internal layer
- stirred
- wheel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of resin wheel, including emery wheel body, the emery wheel is made up of two outer layers and an internal layer, carbonized oil boron stone and diamond paste are added in the component of the outer layer described in two, aerobic aluminium hollow ball, resin-oatmeal and resin liquid are added in the component of described internal layer, ring network panel is fixed with the internal layer.The present invention in outer layer by adding boron carbide oilstone and diamond paste, so that the intensity of emery wheel is not only increased, while also increasing the polishing quality of emery wheel；Further, alumina hollow ball is added in the emery wheel internal layer, so as to improve emery wheel internal layer thermal diffusivity；Meanwhile, ring network panel is fixed with the emery wheel internal layer, so as to improve the integrally-built stability of emery wheel, the practicality of emery wheel is improved.
Description
Technical field
The invention mainly relates to the technical field of emery wheel, and in particular to a kind of resin wheel.
Technical background
Resin wheel, is the emery wheel made with resin, and intensity is high, applies in cutting sheet, Double End, heavy duty grinding wheel, throws
Halo etc..With certain elasticity, heat resistance is low, and self-sharpening is good, simple for production, the characteristics of process cycle is short；It is widely used in
Corase grind, snagging, cut-out and freely it is ground, such as mill steel ingot, casting is deburred.
In existing emery wheel in the market, it is utilized in structure more and improves the intensity of emery wheel and the radiating of emery wheel and polishing effect
Really, the method for changing wheel strength, radiating and polishing effect is realized using this pattern, limitation is very big, moreover, general feelings
Under condition, the effect of change is not it is obvious that moreover, maintaining the cycle of emery wheel beneficial effect very short, it is therefore desirable to develop one kind not
Only changed in structure, and the grinding wheel unit changed in production technology and emery wheel dispensing is important research class
Topic.
The content of the invention
Present invention generally provides a kind of resin wheel, to solve what is proposed in above-mentioned technical background, sent out only in structure
The raw method limitation for changing and changing wheel strength, radiating and polishing effect very big technical problem.
The present invention solve the technical scheme that uses of above-mentioned technical problem for:A kind of resin wheel, including emery wheel body, it is described
Emery wheel is made up of two outer layers and an internal layer, and carbonized oil boron stone and Buddha's warrior attendant are added in the component of the outer layer described in two
Stone abrasive pastes, add aerobic aluminium hollow ball, resin-oatmeal and resin liquid in the component of described internal layer, solid in the internal layer
Surely there is ring network panel.
It is preferred that, the emery wheel outer layer is by abrasive material, resin-oatmeal, resin liquid, wetting agent, coupling agent, iron sulfide, ice crystal
Mix and constitute with aerobic aluminium hollow ball hollow ball.
It is preferred that, the emery wheel internal layer is by abrasive material, resin-oatmeal, resin liquid, wetting agent, coupling agent, iron sulfide, ice crystal
Stone, colouring agent, carbonized oil boron stone and diamond paste mix composition.
It is preferred that, the emery wheel is mainly comprised the following steps：（1）First weigh quantitative abrasive material and wetting agent is added in agitated kettle
It is stirred, after stirring one end time, first adds appropriate coupling agent, iron sulfide, ice crystal and be stirred, is adding resin liquid
It is stirred, after a period of time, is stirred uniformly adding appropriate aerobic aluminium hollow ball, stirring a period of time with resin-oatmeal
Afterwards, shaped granule is selected by Vibration Screen, waits mixed material A；
（2）By above-mentioned steps（1）Afterwards, weighing quantitative abrasive material and wetting agent is added in agitated kettle and is stirred, stirring
After the time of one end, first add appropriate coupling agent, iron sulfide, ice crystal and be stirred, add resin liquid and resin-oatmeal progress
After stirring, a period of time, the appropriate carbonized oil boron stone of addition and diamond paste are sufficiently stirred for, after stirring, and are led to
Vibratory sieve screening shaped granule is crossed, mixed material B is obtained；
（3）The mixed material B of portion is selected, is thrown into mould, is tentatively suppressed by hydraulic press, when mixed material B quilts
When being expressed to definite shape, a mixed material A is being added, secondary compacting is being carried out by hydraulic press, when mixed material A is squeezed
When being pressed onto definite shape, in a mixed material B of addition, three compactings are carried out by hydraulic press, third time is suppressed material pressure
Shaping embryo material is made；
（4）After emery wheel embryo material is made, embryo material is taken out, embryo material is transported in heating furnace and carries out heat hardening；
（5）After emery wheel embryo material carries out heat hardening process, sharp processing is being carried out using car, grinding machine；
（6）After emery wheel completes sharp processing, test, pack.
It is preferred that, the ring network panel is fixed on the internal layer thickness centered position.
Compared with prior art, beneficial effects of the present invention are：
1. it is of the invention main by adding boron carbide oilstone in the emery wheel outer layer, add the hardness of emery wheel in itself so that
Emery wheel is difficult out scratch；Further, diamond paste is added in the emery wheel outer layer, improves the grinding matter of emery wheel
Amount；Meanwhile, combined using boron carbide oilstone with diamond paste, increase the amount of grinding of product in the unit interval, add
Grinding efficiency；
2. it is of the invention main by adding alumina hollow ball in the emery wheel internal layer, so as to improve the radiating inside emery wheel
Effect, adds the service life of emery wheel；
3. the present invention in the emery wheel internal layer by being fixed with ring network panel, so as to improve the structural strength of emery wheel, it is to avoid
Emery wheel because high speed rotation and caused by the phenomenon burst apart of emery wheel；
4. the main process by three compacting emery wheels of the invention, so as to further promote the structural strength of emery wheel, is prevented
The explosion of emery wheel.
Detailed explanation is carried out to the present invention below with reference to accompanying drawing and specific embodiment.
Brief description of the drawings
Fig. 1 is structural representation of the invention；
Fig. 2 is sectional view of the invention.
In figure：1- outer layers；2- internal layers；3- ring network panels.
Embodiment
For the ease of understanding the present invention, the present invention is described more fully below with reference to relevant drawings, accompanying drawing
In give the present invention some embodiments, but the present invention can be realized by different forms, however it is not limited to text institute
The embodiment of description, opposite is in order that more thorough comprehensive to present disclosure there is provided these embodiments.
Need explanation when, when element is referred to as " being fixedly arranged on " another element, it can be directly on another element
There can also be element placed in the middle, when an element is considered as " connection " another element, it can be directly to separately
One element may be simultaneously present centering elements, term as used herein " vertically ", " level ", "left", "right"
And similar statement is for illustrative purposes only.
Unless otherwise defined, all of technologies and scientific terms used here by the article is with belonging to technical field of the invention
The implication that technical staff generally connects is identical, herein in the description of the invention used term knowledge in order to describe tool
The purpose of the embodiment of body, it is not intended that of the invention in limitation, term as used herein " and/or " include one or more phases
The arbitrary and all combination of the Listed Items of pass.
Accompanying drawing 1-2, a kind of resin wheel, including emery wheel body are refer to, the emery wheel is by two outer layers 1 and one
Layer 2 is constituted, and carbonized oil boron stone and diamond paste is added in the component of the outer layer 1 described in two, in described internal layer 2
Component in add aerobic aluminium hollow ball, resin-oatmeal and resin liquid, ring network panel 3 is fixed with the internal layer 2, it is described
Ring network panel 3 is fixed on the thickness centered position of the internal layer 2.
The emery wheel outer layer 1 is empty by abrasive material, resin-oatmeal, resin liquid, wetting agent, coupling agent, iron sulfide, ice crystal and aerobic aluminium
Bulbus cordis hollow ball mixes composition.
The emery wheel internal layer 2 is by abrasive material, resin-oatmeal, resin liquid, wetting agent, coupling agent, iron sulfide, ice crystal, coloring
Agent, carbonized oil boron stone and diamond paste mix composition.
Embodiment 1, the emery wheel is mainly comprised the following steps：（1）First weigh quantitative abrasive material and wetting agent is added to agitated kettle
In be stirred, stirring one end time after, first add appropriate coupling agent, iron sulfide, ice crystal and be stirred, add resin
Liquid and resin-oatmeal are stirred, after a period of time, are stirred uniformly adding appropriate aerobic aluminium hollow ball, when stirring one section
Between after, shaped granule is selected by Vibration Screen, mixed material A is waited；（2）By above-mentioned steps（1）Afterwards, quantitative abrasive material is being weighed
It is added in agitated kettle and is stirred with wetting agent, after stirring one end time, first adds appropriate coupling agent, iron sulfide, ice crystal
Stone is stirred, and is stirred in addition resin liquid and resin-oatmeal, after a period of time, adds appropriate carbonized oil boron stone and Buddha's warrior attendant
Stone abrasive pastes are sufficiently stirred for, after stirring, and shaped granule is selected by Vibration Screen, obtain mixed material B；（3）Select one
The mixed material B of part, is thrown into mould, is tentatively suppressed by hydraulic press, when mixed material B is extruded to definite shape
When, a mixed material A is being added, secondary compacting is being carried out by hydraulic press, when mixed material A is extruded to definite shape
When, a mixed material B is being added, three compactings are carried out by hydraulic press, material is pressed into shaping embryo material by third time compacting；
（4）After emery wheel embryo material is made, embryo material is taken out, embryo material is transported in heating furnace and carries out heat hardening；（5）When emery wheel embryo material enters
After row heat hardening process, sharp processing is being carried out using car, grinding machine；（6）After emery wheel completes sharp processing, test,
Packaging.
Embodiment described above only expresses certain embodiment of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (5)
1. a kind of resin wheel, including emery wheel body, it is characterised in that：The emery wheel is by two outer layers（1）With an internal layer
（2）Composition, in the outer layer described in two（1）Component in add carbonized oil boron stone and diamond paste, in described
Layer（2）Component in add aerobic aluminium hollow ball, resin-oatmeal and resin liquid, in the internal layer（2）Inside it is fixed with annular grid
Plate（3）.
2. a kind of resin wheel according to claim 1, it is characterised in that：The emery wheel outer layer（1）It is by abrasive material, resin
Powder, resin liquid, wetting agent, coupling agent, iron sulfide, ice crystal and aerobic aluminium hollow ball hollow ball mix composition.
3. a kind of resin wheel according to claim 1, it is characterised in that：The emery wheel internal layer（2）It is by abrasive material, resin
Powder, resin liquid, wetting agent, coupling agent, iron sulfide, ice crystal, colouring agent, carbonized oil boron stone and diamond paste are mixed
Composition.
4. a kind of resin wheel according to claim 1-3, it is characterised in that：The emery wheel is mainly comprised the following steps：
（1）First weigh quantitative abrasive material and wetting agent is added in agitated kettle and is stirred, after stirring one end time, first add suitable
The coupling agent of amount, iron sulfide, ice crystal are stirred, and are stirred, after a period of time, are being added in addition resin liquid and resin-oatmeal
Enter appropriate aerobic aluminium hollow ball to be stirred uniformly, after stirring a period of time, shaped granule is selected by Vibration Screen, mixing is waited
Material A；
（2）By above-mentioned steps（1）Afterwards, weighing quantitative abrasive material and wetting agent is added in agitated kettle and is stirred, stirring
After the time of one end, first add appropriate coupling agent, iron sulfide, ice crystal and be stirred, add resin liquid and resin-oatmeal progress
After stirring, a period of time, the appropriate carbonized oil boron stone of addition and diamond paste are sufficiently stirred for, after stirring, and are led to
Vibratory sieve screening shaped granule is crossed, mixed material B is obtained；
（3）The mixed material B of portion is selected, is thrown into mould, is tentatively suppressed by hydraulic press, when mixed material B quilts
When being expressed to definite shape, a mixed material A is being added, secondary compacting is being carried out by hydraulic press, when mixed material A is squeezed
When being pressed onto definite shape, in a mixed material B of addition, three compactings are carried out by hydraulic press, third time is suppressed material pressure
Shaping embryo material is made；
（4）After emery wheel embryo material is made, embryo material is taken out, embryo material is transported in heating furnace and carries out heat hardening；
（5）After emery wheel embryo material carries out heat hardening process, sharp processing is being carried out using car, grinding machine；
（6）After emery wheel completes sharp processing, test, pack.
5. a kind of resin wheel according to claim 1, it is characterised in that：The ring network panel（1）It is fixed on described
Internal layer（2）Thickness centered position.