CN106942073A - 一种茶香型猫砂及其制备工艺 - Google Patents
一种茶香型猫砂及其制备工艺 Download PDFInfo
- Publication number
- CN106942073A CN106942073A CN201710157674.6A CN201710157674A CN106942073A CN 106942073 A CN106942073 A CN 106942073A CN 201710157674 A CN201710157674 A CN 201710157674A CN 106942073 A CN106942073 A CN 106942073A
- Authority
- CN
- China
- Prior art keywords
- tea
- cat litter
- tea flavor
- mesh
- flavor cat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种卫生用品，具体涉及一种茶香型猫砂及其制备工艺，所述茶香型猫砂，以重量份计，其制备原料至少包括：淀粉5～10份；碳酸氢钠5～10份；抗菌剂1～3份；粘结剂3～6份；高吸水树脂1～3份；水5～10份；茶叶1～8份。
Description
技术领域
本发明涉及一种卫生用品，具体涉及一种茶香型猫砂及其制备工艺。
背景技术
宠物饲养在经济发达国家已经相当普及并受到广泛重视，即使在发展中国家和地区如中国，由于消费水平和经济能力的提高，饲养宠物也正在成为一种时尚并为越来越多的人所喜爱。随着宠物饲养的普及和人们对环境质量日益重视，对于如何能更好地解决饲养过程中宠物排泄物造成的环境污染问题，人们提出了更高的要求。
猫砂用于宠物排泄物处理的材料，尤其是用于处理猫的排泄物的材料，也可叫做宠物垫料。有较好的吸水性，一般会与猫砂盆(或称猫厕所)一并使用，将适量的猫砂倒于猫砂盆内，受过训练的猫当需要排泄时便会走进猫砂盆内排泄于其上面；使用猫砂是猫的本能、多数猫能轻易学会使用猫砂。随着人们饲养宠物类别的不断增加，猫砂还广泛用于其他宠物饲养中排泄物的处理。
经过几十年的研究和发展，市场上出现了很多新型的猫砂，猫砂的各项性能指标也得到了很大的提高。现在市场上销售的猫砂主要有以下几类：普通猫砂(粗砂)、膨润土猫砂、水晶猫砂、木屑猫砂、纸屑猫砂等。
(1)普通猫砂(粗砂)
经过简单程序处理的砂子，多由石块破碎制成，跟一般的砂子(例如建筑砂、路边的砂)比起来，比较清洁卫生，而且干燥无异味。不同的牌子，只是在砂石类别和颗粒粗细上有差别，高级点的则加上除臭功能，但效果一般不很明显，此类猫砂的价钱都很便宜。
虽然普通猫砂足以裹住宠物粪便，但其缺点在于无法吸收尿液，会直接流到盆底，好像在做堆肥一样。使用一两周后，整盆猫砂必须全换掉，否则屋内臭味十分明显，对人的健康和室内环境影响较大。
(2)膨润土猫砂
膨润土猫砂主要以天然膨润土为原料，外观为白色或灰白色的小颗粒，有的品牌是圆球形的颗粒或不规则形状的颗粒。它是目前使用最普遍的猫砂，吸水性很强，能将粪便里的水分很快吸收，结成一个大硬团。将所结成的硬块铲除，卫生方便。如遇到拉稀，也会成功的吸成一团，不再有普通猫砂裹不住粪便的烦恼。当凝结猫砂逐渐消耗时，主人可以随时往猫砂里添加新的猫砂，不需要全盆更换。
普通膨润土猫砂的缺点是：粉尘偏大，如果猫砂盆摆在房间里，家具表面会逐渐附着一层细细的白色粉末。猫身上也有一股土腥味儿，每次添加和清理的时候也有诸多不便；而且这种猫砂颗粒很细小，比较容易卡在猫的脚趾缝中，猫咪便后会将残留在脚趾缝里的小砂粒舔食掉。由于猫误食含膨润土的猫砂，会损害它的呼吸和消化系统；此外膨润土猫砂的除臭性能不佳，如果主人不及时清理掉结块的粪便和尿液，屋内很快会出现臭味。
(3)水晶猫砂
水晶猫砂的主要成分为硅胶，制成半透明的圆形颗粒或是一些不规则颗粒，它的最大特点是可冲洗，功效有防霉、抗菌、除臭等等。水晶猫砂的优点在于：重量轻，外表美观干净，味道较好，不需清理结块，不需天天补充猫砂，使用方便。其缺点在于：硅珠又轻又圆很容易被拨出来；很多猫对圆珠感兴趣，常会弄出来玩。有的猫还会把水晶砂吃掉，比较危险。而且水晶猫砂是由化工产品生产，长期使用也会对猫呼吸道产生不良的影响，并且这类猫砂在生产的时候也会严重污染空气环境。
(4)木屑猫砂
木屑猫砂产品是以回收松木、纸浆或小麦副产品为原料，辅以少量天然粘结剂造粒制成属于环保类型的猫砂产品。它的基本功效跟水晶猫砂差不多，没有粉尘或粉尘很小，不会造成空气的污染，而且防渗透的能力非常强，具有比较好的结团和除臭功能。直接吸收尿液、可直接丢弃到马桶中冲掉、平常不需过多清理。木屑猫砂在吸收尿液后会变成粉状，待整盆几乎变成粉状时，即可全部丢弃，使用寿命较长。基本上木屑猫砂臭味很小，但会有些许木头的味道,如果不喜欢松木或是其它木屑味道的主人应考虑是否购入。木屑猫砂一般多用于排泄量较少的宠物如蜥蜴、蛇等的垫料。
木屑猫砂的优点是：吸水效果佳；异味少，耗损率低，使用寿命长；使用方便，变成粉状后丢弃或冲入马桶即可。其缺点是：木屑易受潮、生跳蚤；有些猫不喜欢木头味道、不适应触感，甚至拒绝使用；价格比膨润土猫砂贵很多；木屑粉末很容易被带出盆外，污染居家。
(5)纸屑猫砂
纸屑猫砂的主要原料是废旧的新闻纸、报纸等经过处理制成的，有些纸屑猫砂中含有活性炭用以提高其吸附性能。
纸屑猫砂的优点在于：它属于软性砂，像米粒一样大小。在除臭方面，纸屑猫砂由于颗粒大小、硬度与一般矿砂差不多，所以不容易有臭味散出。纸屑猫砂由于颗粒比较小，因此用量较小，虽然没有结块，但尿湿后会呈灰色，很容易辨认，方便清除。而且可以倒入马桶冲掉，比较简便。其缺点是：纸屑猫砂的凝结力稍稍弱一些，有一些纸屑猫砂在使用的时候可以凝结，但会变成一团糊状。
(6)树脂猫砂
在猫砂中添加高分子树脂吸水材料以增加其吸水性，但是，高分子吸水树脂与其他成分相融合性较差，且高分子树脂类吸水材料普遍存在有抗盐能力差的缺点。吸蒸馏水可以达1-2千倍，但其吸收生理盐水只有几十倍。对于尿液的吸收能力并不是很好。
因而，非常有必要开发出一款多功能的猫砂。
发明内容
为了解决上述技术问题，本发明第一个方面提供了一种茶香型猫砂，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
在一种优选的实施方式中，所述茶香型猫砂，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
在一种优选的实施方式中，所述茶香型猫砂，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
在一种优选的实施方式中，所述抗菌剂选自：蛋白抑菌剂、高分子抑菌剂、胍盐抑菌剂、植物提取物抑菌剂中任意一种或几种的混合。
在一种优选的实施方式中，所述粘结剂为含壳聚糖的聚氨酯。
在一种优选的实施方式中，所述粘结剂中还包括磺化羧甲基壳聚糖。
在一种优选的实施方式中，所述高吸水树脂为丙烯酸-乙烯基吡啶-硅烷偶联剂改性纳米二氧化硅共聚物。
在一种优选的实施方式中，所述茶叶梗选自：绿茶、红茶、荷叶茶、玫瑰花茶的混合物。
本发明的第二个方面提供了一种茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
本发明的第三个方面提供了一种茶香型猫砂在粪便处理中的应用。
具体实施方式
参选以下本发明的优选实施方法的详述以及包括的实施例可更容易地理解本发明的内容。除非另有限定，本文使用的所有技术以及科学术语具有与本发明所属领域普通技术人员通常理解的相同的含义。当存在矛盾时，以本说明书中的定义为准。
如本文所用术语“由…制备”与“包含”同义。本文中所用的术语“包含”、“包括”、“具有”、“含有”或其任何其它变形，意在覆盖非排它性的包括。例如，包含所列要素的组合物、步骤、方法、制品或装置不必仅限于那些要素，而是可以包括未明确列出的其它要素或此种组合物、步骤、方法、制品或装置所固有的要素。
连接词“由…组成”排除任何未指出的要素、步骤或组分。如果用于权利要求中，此短语将使权利要求为封闭式，使其不包含除那些描述的材料以外的材料，但与其相关的常规杂质除外。当短语“由…组成”出现在权利要求主体的子句中而不是紧接在主题之后时，其仅限定在该子句中描述的要素；其它要素并不被排除在作为整体的所述权利要求之外。
当量、浓度、或者其它值或参数以范围、优选范围、或一系列上限优选值和下限优选值限定的范围表示时，这应当被理解为具体公开了由任何范围上限或优选值与任何范围下限或优选值的任一配对所形成的所有范围，而不论该范围是否单独公开了。例如，当公开了范围“1至5”时，所描述的范围应被解释为包括范围“1至4”、“1至3”、“1至2”、“1至2和4至5”、“1至3和5”等。当数值范围在本文中被描述时，除非另外说明，否则该范围意图包括其端值和在该范围内的所有整数和分数。
单数形式包括复数讨论对象，除非上下文中另外清楚地指明。“任选的”或者“任意一种”是指其后描述的事项或事件可以发生或不发生，而且该描述包括事件发生的情形和事件不发生的情形。
说明书和权利要求书中的近似用语用来修饰数量，表示本发明并不限定于该具体数量，还包括与该数量接近的可接受的而不会导致相关基本功能的改变的修正的部分。相应的，用“大约”、“约”等修饰一个数值，意为本发明不限于该精确数值。在某些例子中，近似用语可能对应于测量数值的仪器的精度。在本申请说明书和权利要求书中，范围限定可以组合和/或互换，如果没有另外说明这些范围包括其间所含有的所有子范围。
此外，本发明要素或组分前的不定冠词“一种”和“一个”对要素或组分的数量要求(即出现次数)无限制性。因此“一个”或“一种”应被解读为包括一个或至少一个，并且单数形式的要素或组分也包括复数形式，除非所述数量明显旨指单数形式。
为了解决上述技术问题，本发明第一个方面提供了一种茶香型猫砂，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
在一种优选的实施方式中，所述茶香型猫砂，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
在一种优选的实施方式中，所述茶香型猫砂，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
淀粉
本发明中，所述淀粉是葡萄糖分子聚合而成。
所述淀粉包括但不限于，玉米淀粉、菱角淀粉、莲藕淀粉、荸荠淀粉、马铃薯淀粉、木薯淀粉、红薯淀粉等。
本发明中，所述淀粉还可以包括氧化淀粉、交联淀粉、稳定淀粉、羟丙基化磷酸双淀粉酯等。
碳酸氢钠
本发明中，所述碳酸氢钠并没有特别的限制，主要为市售获得。
抗菌剂
本发明中，所述抗菌剂并没有特别的限制，可以列举的有：蛋白抑菌剂、高分子抑菌剂、胍盐抑菌剂、植物提取物抑菌剂等。
所述蛋白抑菌剂可以列举的有：天蚕素、大豆蛋白、血清白蛋白、胶原蛋白、丝素蛋白、乳清蛋白、麦清蛋白等。
所述高分子抑菌剂可以列举的有：聚季铵盐、壳聚糖及其衍生物等。
所述胍盐抑菌剂可以列举的有：聚六亚甲基(双)胍盐酸盐、聚六亚甲基(双)胍丙酸盐、聚六亚甲基(双)胍硝酸盐、聚六亚甲基(双)胍碳酸盐、聚六亚甲基(双)胍、聚六亚甲基(双)胍硬脂酸盐、聚六亚甲基(双)胍月桂酸盐、聚氧乙烯基胍盐酸盐等。
所述植物提取物抑菌剂可以列举的有：臭椿提取液、地榆提取液、黄芪提取液、红松球果提取液、厚朴提取液、板蓝根提取液、罗汉果提取液、茶叶提取液、甜茶提取液、番石榴叶提取液、竹叶提取液、白芍提取液、鱼腥草提取液、七叶胆提取液、藤茶提取液、金银花提取液、菊花提取液、虎杖提取液、九节茶提取液、甘草提取液、掌叶大黄根提取液、蛇床子果实提取液、黄芩根提取液、构树提取物等。
在一种优选的实施方式中，所述抗菌剂选自：羧甲基壳聚糖与羧甲基纤维素复合物。
术语“羧甲基壳聚糖与羧甲基纤维素复合物”是指羧甲基壳聚糖与羧甲基纤维素进行嵌段共聚得到的羧甲基壳聚糖与羧甲基纤维素复合物。
在一种优选的实施方式中，所述羧甲基壳聚糖与羧甲基纤维素复合物的制备方法为：
将10g羧甲基纤维素加入到200mL的蒸馏水中，在搅拌的条件下用30％的盐酸调pH值至3，然后按羧甲基壳聚糖与羧甲基纤维素的质量比为1：5，室温下混合搅拌5h。然后再用2mol/LNaOH将共混液调至中性，产生白色凝胶，过滤洗涤，在45℃下干燥，研磨，得到羧甲基壳聚糖与羧甲基纤维素复合物。
粘结剂
本发明中，所述粘结剂为主要是起到粘结作用的物质。
本发明中，所述粘结剂可以列举的有：糊精、瓜儿胶、黄原胶、阿拉伯树胶、羧甲基纤维素等。
在一种优选的实施方式中，所述粘结剂为含壳聚糖的聚氨酯。
术语“含壳聚糖的聚氨酯”是指以壳聚糖为原料合成得到的聚氨酯。
在一种优选的实施方式中，所述含壳聚糖的聚氨酯的制备方法为：将壳聚糖、甘油、环糊精的混合物作为多元醇，其中，壳聚糖、甘油、环糊精的重量比为1：1：1，将多元醇加入到丙酮溶剂中，搅拌，升温到60℃，然后加入异佛尔酮二异氰酸酯，其中，多元醇与异佛尔酮二异氰酸酯的重量比为1：2，然后再升温到80℃，反应5h，降温，搅拌均匀，出料，即得含壳聚糖的聚氨酯。
在一种优选的实施方式中，所述粘结剂中还包括磺化羧甲基壳聚糖。
术语“磺化羧甲基壳聚糖”是指将羧甲基壳聚糖进行磺化反应得到的磺化羧甲基壳聚糖。
在一种优选的实施方式中，所述磺化羧甲基壳聚糖的制备方法至少包括以下步骤：
将10g的羧甲基壳聚糖溶于30mLDMF中，室温下搅拌5～10h，得到羧甲基壳聚糖溶液。并将上述羧甲基壳聚糖溶液与4mL磺化试剂氯磺酸相接触，其中，反应温度80℃，反应时间2h，得到磺化羧甲基壳聚糖。
本发明人发现，本发明中使用粘结剂为含壳聚糖的聚氨酯可以具有较好的团结强度，本发明人猜测可能的原因在于，这种新型结构的聚氨酯可以与淀粉、高吸收水树脂、抗菌剂等形成非常好的交联网状结构，且碳酸氢钠、茶叶梗可以均匀分布在交联网状结构之中。当加入磺化羧甲基壳聚糖后，进一步增强其团结强度，可能的原因在于，磺化羧甲基壳聚糖不仅可以进步增强交联网状结构，还可以与碱性成分相互作用，进而达到本发明的有益效果。
高吸水树脂
本发明中，所述高吸水树脂并没有特别的限制，可以列举的有：淀粉系树脂、纤维素系树脂、高分子聚合物树脂等。
所述淀粉系树脂可以列举的有：玉米淀粉、马铃薯淀粉、木薯淀粉、小麦淀粉等。
所述纤维素系树脂可以列举的有：醋酸纤维素、乙酰丁酸纤维素、乙酰丙酸纤维素、甲基纤维素、乙基纤维素、羟丙基纤维素、羟乙基纤维素、羟丙基甲基纤维素、羟乙基甲基纤维素、羧甲基纤维素等。
所述高分子聚合物树脂可以列举的有：丙烯酸树脂等。
在一种优选的实施方式中，所述高吸水树脂为丙烯酸-乙烯基吡啶-硅烷偶联剂改性纳米二氧化硅共聚物。
术语“丙烯酸-乙烯基吡啶-硅烷偶联剂改性纳米二氧化硅共聚物”指的是丙烯酸、乙烯基吡啶、硅烷偶联剂改性纳米二氧化硅这三者的共聚物，其中，硅烷偶联剂改性纳米二氧化硅是指硅烷偶联剂与纳米二氧化硅相结合，得到的硅烷偶联剂改性纳米二氧化硅。
在一种优选的实施方式中，所述丙烯酸-乙烯基吡啶-硅烷偶联剂改性纳米二氧化硅共聚物的制备方法至少包括以下步骤：
(1)将1重量份的乙烯基苯基二甲氧基硅烷溶于乙醇后，再加入纳米二氧化硅，在40℃干燥2h除去乙醇。再在85℃真空加热3h除去吸附水、完成缩合反应，得到硅烷偶联剂改性纳米二氧化硅；
(2)将丙烯酸、乙烯基吡啶加入到200mL水中，并加入3g的十二烷基磺酸钠，搅拌均匀后，再加入硅烷偶联剂改性纳米二氧化硅，均匀搅拌混合后，加入2g引发剂过硫酸钾，升温至80℃下搅拌6小时，冷却出料。
所述丙烯酸不限于丙烯酸单体，还包括丙烯酸衍生物。所述丙烯酸衍生物可以列举的有：(甲基)丙烯酸甲酯、(甲基)丙烯酸乙酯、(甲基)丙烯酸正丙酯、(甲基)丙烯酸异丙酯、(甲基)丙烯酸正丁酯、(甲基)丙烯酸仲丁酯、(甲基)丙烯酸叔丁酯、(甲基)丙烯酸正戊酯、(甲基)丙烯酸异戊酯、(甲基)丙烯酸正己酯、(甲基)丙烯酸正庚酯、(甲基)丙烯酸正辛酯、(甲基)丙烯酸-2-乙基己酯、(甲基)丙烯酸壬酯、(甲基)丙烯酸癸酯、(甲基)丙烯酸十二烷基酯、(甲基)丙烯酸异冰片基酯、(甲基)丙烯酸环己酯等(甲基)丙烯酸的碳数1～15的直链、支链或环状烷基酯，(甲基)丙烯酸苄酯、(甲基)丙烯酸苯氧基乙酯、(甲基)丙烯酸苯酯等(甲基)丙烯酸芳基酯，(甲基)丙烯酸-2-甲氧基乙酯、(甲基)丙烯酸-2-乙氧基乙酯、(甲基)丙烯酸-2-甲氧基丙酯、(甲基)丙烯酸-3-甲氧基丙酯、(甲基)丙烯酸-2-甲氧基丁酯、(甲基)丙烯酸-4-甲氧基丁酯等(甲基)丙烯酸烷氧基酯，(甲基)丙烯酸乙二醇酯、(甲基)丙烯酸聚乙二醇酯、(甲基)丙烯酸丙二醇酯、(甲基)丙烯酸聚丙二醇酯等(甲基)丙烯酸烷二醇酯，(甲基)丙烯酸-2-羟基乙酯、(甲基)丙烯酸-2-羟基丙酯、(甲基)丙烯酸-3-羟基丙酯、(甲基)丙烯酸-4-羟基丁酯、(甲基)丙烯酸-2-羟基-3-氯丙酯、(甲基)丙烯酸-2-羟基-3-苯氧基丙酯等含羟基的单体，(甲基)丙烯酸、(甲基)丙烯酸-β-羧基乙酯、(甲基)丙烯酸-5-羧基戊酯、琥珀酸单(甲基)丙烯酰氧基乙酯、ω-羧基聚己内酯单(甲基)丙烯酸酯等含羧基的单体，(甲基)丙烯酸氨基乙酯、(甲基)丙烯酸二甲基氨基乙酯等含氨基的单体，(甲基)丙烯酰胺、N，N-二甲基(甲基)丙烯酰胺等含酰胺基的单体，(甲基)丙烯酸缩水甘油醚等含环氧基的单体等。
所述的硅烷偶联剂为含有双键的硅烷偶联剂，可以列举的有：乙烯基三甲氧基硅烷、甲基乙烯基二甲氧基硅烷、乙烯基苯基二甲氧基硅烷、乙烯基苯基二甲氧基硅烷、乙烯基三(2-甲氧基乙氧基)硅烷、乙烯基甲氧基二甲基硅烷、甲基乙烯基二甲氧基硅烷、(乙烯基二甲氧基硅烷基)-苯、甲基乙烯基二甲氧基硅烷、乙烯基甲氧基二甲基硅烷、苯乙烯乙基三甲氧基硅烷、乙烯基三(2-甲氧基乙氧基)硅烷等。
水
本发明中，所述水并没有特别的限制，可以为蒸馏水、自来水、纯净水、去离子水中的任意一种皆可。
茶叶梗
本发明中，所述茶叶梗可以为所有茶叶的梗。
在一种优选的实施方式中，所述茶叶梗选自：绿茶、红茶、荷叶茶、玫瑰花茶的混合物。
在一种优选的实施方式中，所述绿茶、红茶、荷叶茶、玫瑰花茶的重量比为：3：2：1：3。
在一种优选的实施方式中，所述茶叶梗的制备方法为：将绿茶、红茶、荷叶茶、玫瑰花茶按照重量比混合后，研磨至20目～500目，得到茶叶梗混合物，然后将茶叶梗混合物置于80％的酒精中浸泡1～3小时。
所述绿茶可以列举的有：碧螺春、西湖龙井、松峰绿茶等。
所述红茶可以列举的有：工夫红茶、小种红茶、红碎茶等。
本发明的第二个方面提供了一种茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
本发明的第三个方面提供了一种茶香型猫砂在粪便处理中的应用。
下面通过实施例对本发明进行具体描述。有必要在此指出的是，以下实施例只用于对本发明作进一步说明，不能理解为对本发明保护范围的限制，该领域的专业技术人员根据上述本发明的内容做出的一些非本质的改进和调整，仍属于本发明的保护范围。
另外，如果没有其它说明，所用原料都是市售的，且以下物料所用份数均为重量份。
实施例1
本发明的实施例1提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为天蚕素，购于郑州美力盾商贸有限公司；
所述粘结剂为瓜儿胶，购于任丘市广汇化工有限公司；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例2
本发明的实施例2提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为天蚕素，购于郑州美力盾商贸有限公司；
所述粘结剂为瓜儿胶，购于任丘市广汇化工有限公司；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例3
本发明的实施例3提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为天蚕素，购于郑州美力盾商贸有限公司；
所述粘结剂为瓜儿胶，购于任丘市广汇化工有限公司；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例4
本发明的实施例4提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为天蚕素，购于郑州美力盾商贸有限公司；
所述粘结剂为瓜儿胶，购于任丘市广汇化工有限公司；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例5
本发明的实施例5提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为天蚕素，购于郑州美力盾商贸有限公司；
所述粘结剂为瓜儿胶，购于任丘市广汇化工有限公司；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例6
本发明的实施例6提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为羧甲基壳聚糖与羧甲基纤维素复合物；
所述羧甲基壳聚糖与羧甲基纤维素复合物的制备方法为：将10g羧甲基纤维素加入到200mL的蒸馏水中，在搅拌的条件下用30％的盐酸调pH值至3，然后按羧甲基壳聚糖与羧甲基纤维素的质量比为1：5，室温下混合搅拌5h。然后再用2mol/LNaOH将共混液调至中性，产生白色凝胶，过滤洗涤，在45℃下干燥，研磨，得到羧甲基壳聚糖与羧甲基纤维素复合物。
所述粘结剂为瓜儿胶，购于任丘市广汇化工有限公司；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例7
本发明的实施例7提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为羧甲基壳聚糖与羧甲基纤维素复合物；
所述羧甲基壳聚糖与羧甲基纤维素复合物的制备方法为：将10g羧甲基纤维素加入到200mL的蒸馏水中，在搅拌的条件下用30％的盐酸调pH值至3，然后按羧甲基壳聚糖与羧甲基纤维素的质量比为1：5，室温下混合搅拌5h。然后再用2mol/LNaOH将共混液调至中性，产生白色凝胶，过滤洗涤，在45℃下干燥，研磨，得到羧甲基壳聚糖与羧甲基纤维素复合物。
所述粘结剂为含壳聚糖的聚氨酯；
所述含壳聚糖的聚氨酯的制备方法为：将壳聚糖、甘油、环糊精的混合物作为多元醇，其中，壳聚糖、甘油、环糊精的重量比为1：1：1，将多元醇加入到丙酮溶剂中，搅拌，升温到60℃，然后加入异佛尔酮二异氰酸酯，其中，多元醇与异佛尔酮二异氰酸酯的重量比为1：2，然后再升温到80℃，反应5h，降温，搅拌均匀，出料，即得含壳聚糖的聚氨酯。
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例8
本发明的实施例8提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为羧甲基壳聚糖与羧甲基纤维素复合物；
所述羧甲基壳聚糖与羧甲基纤维素复合物的制备方法为：将10g羧甲基纤维素加入到200mL的蒸馏水中，在搅拌的条件下用30％的盐酸调pH值至3，然后按羧甲基壳聚糖与羧甲基纤维素的质量比为1：5，室温下混合搅拌5h。然后再用2mol/LNaOH将共混液调至中性，产生白色凝胶，过滤洗涤，在45℃下干燥，研磨，得到羧甲基壳聚糖与羧甲基纤维素复合物。
所述粘结剂为含壳聚糖的聚氨酯和磺化羧甲基壳聚糖；
所述含壳聚糖的聚氨酯的制备方法为：将壳聚糖、甘油、环糊精的混合物作为多元醇，其中，壳聚糖、甘油、环糊精的重量比为1：1：1，将多元醇加入到丙酮溶剂中，搅拌，升温到60℃，然后加入异佛尔酮二异氰酸酯，其中，多元醇与异佛尔酮二异氰酸酯的重量比为1：2，然后再升温到80℃，反应5h，降温，搅拌均匀，出料，即得含壳聚糖的聚氨酯。
所述磺化羧甲基壳聚糖的制备方法包括以下步骤：
将10g的羧甲基壳聚糖溶于30mLDMF中，室温下搅拌10h，得到羧甲基壳聚糖溶液。并将上述羧甲基壳聚糖溶液与4mL磺化试剂氯磺酸相接触，其中，反应温度80℃，反应时间2h，得到磺化羧甲基壳聚糖。
其中，含壳聚糖的聚氨酯和磺化羧甲基壳聚糖的重量比为：1：1；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例9
本发明的实施例9提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为羧甲基壳聚糖与羧甲基纤维素复合物；
所述羧甲基壳聚糖与羧甲基纤维素复合物的制备方法为：将10g羧甲基纤维素加入到200mL的蒸馏水中，在搅拌的条件下用30％的盐酸调pH值至3，然后按羧甲基壳聚糖与羧甲基纤维素的质量比为1：5，室温下混合搅拌5h。然后再用2mol/LNaOH将共混液调至中性，产生白色凝胶，过滤洗涤，在45℃下干燥，研磨，得到羧甲基壳聚糖与羧甲基纤维素复合物。
所述粘结剂为含壳聚糖的聚氨酯和磺化羧甲基壳聚糖；
所述含壳聚糖的聚氨酯的制备方法为：将壳聚糖、甘油、环糊精的混合物作为多元醇，其中，壳聚糖、甘油、环糊精的重量比为1：1：1，将多元醇加入到丙酮溶剂中，搅拌，升温到60℃，然后加入异佛尔酮二异氰酸酯，其中，多元醇与异佛尔酮二异氰酸酯的重量比为1：2，然后再升温到80℃，反应5h，降温，搅拌均匀，出料，即得含壳聚糖的聚氨酯。
所述磺化羧甲基壳聚糖的制备方法包括以下步骤：
将10g的羧甲基壳聚糖溶于30mLDMF中，室温下搅拌10h，得到羧甲基壳聚糖溶液。并将上述羧甲基壳聚糖溶液与4mL磺化试剂氯磺酸相接触，其中，反应温度80℃，反应时间2h，得到磺化羧甲基壳聚糖。
其中，含壳聚糖的聚氨酯和磺化羧甲基壳聚糖的重量比为：10：1；
所述高吸水树脂为丙烯酸树脂，购于复纳新材料科技(上海)有限公司；
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例10
本发明的实施例10提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为羧甲基壳聚糖与羧甲基纤维素复合物；
所述羧甲基壳聚糖与羧甲基纤维素复合物的制备方法为：将10g羧甲基纤维素加入到200mL的蒸馏水中，在搅拌的条件下用30％的盐酸调pH值至3，然后按羧甲基壳聚糖与羧甲基纤维素的质量比为1：5，室温下混合搅拌5h。然后再用2mol/LNaOH将共混液调至中性，产生白色凝胶，过滤洗涤，在45℃下干燥，研磨，得到羧甲基壳聚糖与羧甲基纤维素复合物。
所述粘结剂为含壳聚糖的聚氨酯和磺化羧甲基壳聚糖；
所述含壳聚糖的聚氨酯的制备方法为：将壳聚糖、甘油、环糊精的混合物作为多元醇，其中，壳聚糖、甘油、环糊精的重量比为1：1：1，将多元醇加入到丙酮溶剂中，搅拌，升温到60℃，然后加入异佛尔酮二异氰酸酯，其中，多元醇与异佛尔酮二异氰酸酯的重量比为1：2，然后再升温到80℃，反应5h，降温，搅拌均匀，出料，即得含壳聚糖的聚氨酯。
所述磺化羧甲基壳聚糖的制备方法包括以下步骤：
将10g的羧甲基壳聚糖溶于30mLDMF中，室温下搅拌10h，得到羧甲基壳聚糖溶液。并将上述羧甲基壳聚糖溶液与4mL磺化试剂氯磺酸相接触，其中，反应温度80℃，反应时间2h，得到磺化羧甲基壳聚糖。
其中，含壳聚糖的聚氨酯和磺化羧甲基壳聚糖的重量比为：10：1；
所述高吸水树脂为丙烯酸-乙烯基吡啶-硅烷偶联剂改性纳米二氧化硅共聚物；
所述高吸水树脂的制备方法为：(1)将1重量份的乙烯基苯基二甲氧基硅烷溶于乙醇后，再加入纳米二氧化硅，在40℃干燥2h除去乙醇。再在85℃真空加热3h除去吸附水、完成缩合反应，得到硅烷偶联剂改性纳米二氧化硅；
(2)将丙烯酸、乙烯基吡啶加入到200mL水中，并加入3g的十二烷基磺酸钠，搅拌均匀后，再加入硅烷偶联剂改性纳米二氧化硅，均匀搅拌混合后，加入2g引发剂过硫酸钾，升温至80℃下搅拌6小时，冷却出料。
所述茶叶梗为绿茶，所述绿茶为西湖龙井茶叶梗。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
实施例11
本发明的实施例11提供了一种茶香型猫砂，以重量份计，其制备原料包括：
所述茶叶梗的目数为20目。
所述淀粉为玉米淀粉，购于河北祥龙玉米淀粉厂；
所述碳酸氢钠购于上海国药集团；
所述抗菌剂为羧甲基壳聚糖与羧甲基纤维素复合物；
所述羧甲基壳聚糖与羧甲基纤维素复合物的制备方法为：将10g羧甲基纤维素加入到200mL的蒸馏水中，在搅拌的条件下用30％的盐酸调pH值至3，然后按羧甲基壳聚糖与羧甲基纤维素的质量比为1：5，室温下混合搅拌5h。然后再用2mol/LNaOH将共混液调至中性，产生白色凝胶，过滤洗涤，在45℃下干燥，研磨，得到羧甲基壳聚糖与羧甲基纤维素复合物。
所述粘结剂为含壳聚糖的聚氨酯和磺化羧甲基壳聚糖；
所述含壳聚糖的聚氨酯的制备方法为：将壳聚糖、甘油、环糊精的混合物作为多元醇，其中，壳聚糖、甘油、环糊精的重量比为1：1：1，将多元醇加入到丙酮溶剂中，搅拌，升温到60℃，然后加入异佛尔酮二异氰酸酯，其中，多元醇与异佛尔酮二异氰酸酯的重量比为1：2，然后再升温到80℃，反应5h，降温，搅拌均匀，出料，即得含壳聚糖的聚氨酯。
所述磺化羧甲基壳聚糖的制备方法包括以下步骤：
将10g的羧甲基壳聚糖溶于30mLDMF中，室温下搅拌10h，得到羧甲基壳聚糖溶液。并将上述羧甲基壳聚糖溶液与4mL磺化试剂氯磺酸相接触，其中，反应温度80℃，反应时间2h，得到磺化羧甲基壳聚糖。
其中，含壳聚糖的聚氨酯和磺化羧甲基壳聚糖的重量比为：10：1；
所述高吸水树脂为丙烯酸-乙烯基吡啶-硅烷偶联剂改性纳米二氧化硅共聚物；
所述高吸水树脂的制备方法为：
(1)将1重量份的乙烯基苯基二甲氧基硅烷溶于乙醇后，再加入纳米二氧化硅，在40℃干燥2h除去乙醇。再在85℃真空加热3h除去吸附水、完成缩合反应，得到硅烷偶联剂改性纳米二氧化硅；
(2)将丙烯酸、乙烯基吡啶加入到200mL水中，并加入3g的十二烷基磺酸钠，搅拌均匀后，再加入硅烷偶联剂改性纳米二氧化硅，均匀搅拌混合后，加入2g引发剂过硫酸钾，升温至80℃下搅拌6小时，冷却出料。
所述茶叶梗选自：绿茶、红茶、荷叶茶、玫瑰花茶的混合物。
所述绿茶为西湖龙井茶叶梗；所述红茶为工夫红茶茶叶梗；
所述绿茶、红茶、荷叶茶、玫瑰花茶的重量比为：3：2：1：3。
所述茶叶梗的制备方法为：将绿茶、红茶、荷叶茶、玫瑰花茶按照重量比混合后，研磨至20目，得到茶叶梗混合物，然后将茶叶梗混合物置于80％的酒精中浸泡3小时。
所述茶香型猫砂的制备工艺，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
性能测试：
1、结团强度：结团后的猫砂分别距离地面5米和15米的高度自由下落，掉在地上不散开为合格，散开则为不合格。
2、吸水速度：将单个猫砂颗粒放在质量分数10％的氯化钠盐水中吸水后膨胀并剥离至体积不再变化所需的时间。
3、吸水速度：将单个猫砂颗粒放在中在质量分数10％的尿素中吸水后膨胀并剥离至体积不再变化所需的时间。
4、气味测试：将使用过的猫砂放置72h，选取100名嗅觉正常的成年人，测试是否有异味，有异味则不合格，无异味且能够闻到茶叶香味则合格。
表1为性能测试表
由上表可以看出，本发明中，得到的茶香型猫砂具有非常好的结团强度，较快的盐水吸水速度、尿素吸水速度，且长时间使用过的猫砂没有异味，且还带有茶叶香味，因而取得了意料不到的技术效果。
前述的实例仅是说明性的，用于解释本公开的特征的一些特征。所附的权利要求旨在要求可以设想的尽可能广的范围，且本文所呈现的实施例仅是根据所有可能的实施例的组合的选择的实施方式的说明。因此，申请人的用意是所附的权利要求不被说明本发明的特征的示例的选择限制。而且在科技上的进步将形成由于语言表达的不准确的原因而未被目前考虑的可能的等同物或子替换，且这些变化也应在可能的情况下被解释为被所附的权利要求覆盖。
Claims (10)
1.一种茶香型猫砂，其特征在于，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
2.如权利要求1所述的茶香型猫砂，其特征在于，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
3.如权利要求2所述的茶香型猫砂，其特征在于，以重量份计，其制备原料至少包括：
所述茶叶梗的目数为20目～500目。
4.如权利要求1～3所述的茶香型猫砂，其特征在于，所述抗菌剂选自：蛋白抑菌剂、高分子抑菌剂、胍盐抑菌剂、植物提取物抑菌剂中任意一种或几种的混合。
5.如权利要求1～3所述的茶香型猫砂，其特征在于，所述粘结剂为含壳聚糖的聚氨酯。
6.如权利要求1～5所述的茶香型猫砂，其特征在于，所述粘结剂中还包括磺化羧甲基壳聚糖。
7.如权利要求1～3所述的茶香型猫砂，其特征在于，所述高吸水树脂为丙烯酸-乙烯基吡啶-硅烷偶联剂改性纳米二氧化硅共聚物。
8.如权利要求1～3所述的茶香型猫砂，其特征在于，所述茶叶梗选自：绿茶、红茶、荷叶茶、玫瑰花茶的混合物。
9.如权利要求1～8所述的茶香型猫砂的制备方法，其特征在于，至少包括以下步骤：
(1)混料：将淀粉、碳酸氢钠、抗菌剂、粘结剂、高吸水树脂、水放入搅拌机中搅拌均匀后再加入茶叶梗，再次搅拌均匀；
(2)造粒：将步骤(1)中的混料放入造粒机中，得到成型的茶香型猫砂；
(3)干燥：将步骤(2)中茶香型猫砂进行烘干，得到茶香型猫砂。
10.如权利要求1～8所述的茶香型猫砂在粪便处理中的应用。