CN106939519A - A kind of self-cleaning fire-retardant decorative film production process of high-performance glass - Google Patents
A kind of self-cleaning fire-retardant decorative film production process of high-performance glass Download PDFInfo
- Publication number
- CN106939519A CN106939519A CN201710139279.5A CN201710139279A CN106939519A CN 106939519 A CN106939519 A CN 106939519A CN 201710139279 A CN201710139279 A CN 201710139279A CN 106939519 A CN106939519 A CN 106939519A
- Authority
- CN
- China
- Prior art keywords
- temperature
- baking oven
- production process
- self
- film production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of self-cleaning fire-retardant decorative film production process of high-performance glass.Specifically include following steps:(1) glass fibre base fabric is unreeled by unwinding device;(2) slurry is prepared, 200 revs/min are stirred 30 minutes;(3) a knife scraping coating forming processes are carried out;(4) setting temperature of knife scraping coating heat treatment:Pressing roll temperature is 130 DEG C 140 DEG C, and the temperature of baking oven 1 is 160 DEG C, and the temperature of baking oven 2 is 165 DEG C, and the temperature of baking oven 3 is 200 DEG C, the temperature of baking oven 4 is 200 DEG C, and the temperature of baking oven 5 is 200 DEG C, and the temperature of baking oven 6 is 200 DEG C, and the temperature of baking oven 7 is 200 DEG C, coating thickness is uniform, and surface effect is good, and plasticizing is good;(5) embossed is carried out again, the pressure of embossed wheel group and rubber wheel is set to 70kg, and embossed wheel is bright face roller;Embossing carries out cooling treatment after finishing;(6) finally wound again.Present invention process is simple, is made by knife scraping coating, sizing, embossing cooling, a winding process, has the advantages that intensity is high, prevents fires, mould proof, moistureproof.
Description
Technical field
The present invention relates to fire-retardant decorative film production process technical field, and in particular to a kind of high-performance glass is self-cleaning anti-
Fire decoration film production process.
Background technology
Common ceiling decoration film quality is light, about 220 ± 10 grams/m of grammes per square metre, and printing opacity is good, and centre, can without base fabric
Air brushing picture, but the insufficient strength during fabrication and installation, are easily drawn bad, bursting, deformation etc..
In summary, the present invention devises a kind of self-cleaning fire-retardant decorative film production process of high-performance glass.
The content of the invention
For deficiency present on prior art, the present invention seeks to be to provide a kind of high-performance glass self-cleaning fire prevention dress
Film production process is adornd, technique is simple, can air brushing picture, 230 ± 5 grams/m of final product quality, innovation use base fabric density
1000D(17*13)Glass-fiber-fabric, is made, product has by processes such as knife scraping coating, sizing, embossing cooling, a windings
Intensity is high, fire prevention, it is mould proof, moistureproof the advantages of.
To achieve these goals, the present invention is to realize by the following technical solutions:A kind of high-performance glass is self-cleaning
Fire-retardant decorative film production process, it comprises the following steps:(1) glass fibre base fabric is unreeled by unwinding device;
(2) slurry is prepared, 200 revs/min are stirred 30 minutes;
(3) a knife scraping coating forming processes are carried out;
(4) setting temperature of knife scraping coating heat treatment:Pressing roll temperature is 130 DEG C -140 DEG C, and the temperature of baking oven 1 is 160 DEG C, is dried
The temperature of case 2 is 165 DEG C, and the temperature of baking oven 3 is 200 DEG C, and the temperature of baking oven 4 is 200 DEG C, and the temperature of baking oven 5 is 200 DEG C, and the temperature of baking oven 6 is
200 DEG C, the temperature of baking oven 7 is 200 DEG C, and coating thickness is uniform, and surface effect is good, and plasticizing is good;
(5) embossed is carried out again, the pressure of embossed wheel group and rubber wheel is set to 70kg, and embossed wheel is bright face roller;Emboss
Cooling treatment is carried out after finishing;
(6) finally wound again.
Preferably, the glass fibre base fabric density in described step (1) is 1000D(17*13).
Preferably, the knife scraping coating in described step (3) is layer of silica gel, described layer of silica gel is 25 ± 5 grams/square
Rice.
Preferably, the knife scraping coating technical recipe in described step (3) is as follows:50 parts of silica gel A;50 parts of silica gel B;
6 parts of opacifier.
Preferably, the speed of the knife scraping coating heat treatment in described step (4) is controlled in 5 ± 1m/min.
Beneficial effects of the present invention:Technique is simple, can air brushing picture, 230 ± 5 grams/m of final product quality, innovation use
Base fabric density 1000D(17*13)Glass-fiber-fabric, is made by processes such as knife scraping coating, sizing, embossing cooling, a windings,
Product has the advantages that intensity high, fire prevention, mould proof, moistureproof.
Embodiment
To be easy to understand technological means, creation characteristic, reached purpose and effect of the invention realized, with reference to
Embodiment, is expanded on further the present invention.
Present embodiment uses following technical scheme:A kind of self-cleaning fire-retardant decorative film production process of high-performance glass,
Specifically include following steps:(1) glass fibre base fabric is unreeled by unwinding device;(2) slurry, 200 revs/min of stirrings 30 are prepared
Minute;(3) a knife scraping coating forming processes are carried out;(4) setting temperature of knife scraping coating heat treatment:Pressing roll temperature is
130 DEG C -140 DEG C, the temperature of baking oven 1 is 160 DEG C, and the temperature of baking oven 2 is 165 DEG C, and the temperature of baking oven 3 is 200 DEG C, and the temperature of baking oven 4 is 200
DEG C, the temperature of baking oven 5 is 200 DEG C, and the temperature of baking oven 6 is 200 DEG C, and the temperature of baking oven 7 is 200 DEG C, and coating thickness is uniform, surface effect
Good, plasticizing is good;(5) embossed is carried out again, the pressure of embossed wheel group and rubber wheel is set to 70kg, and embossed wheel is bright face
Roller;Embossing carries out cooling treatment after finishing;(6) finally wound again.
It is worth noting that, the glass fibre base fabric density in described step (1) is 1000D(17*13).
It is worth noting that, knife scraping coating in described step (3) is layer of silica gel, described layer of silica gel for 25 ± 5 grams/
Square metre.
It is worth noting that, the knife scraping coating technical recipe in described step (3) is as follows:50 parts of silica gel A;Silica gel B
50 parts;6 parts of opacifier.
In addition, the speed of the knife scraping coating heat treatment in described step (4) is controlled in 5 ± 1m/min.
Present embodiment simple production process, can air brushing picture, 230 ± 5 grams/m of final product quality, innovation is adopted
With base fabric density 1000D(17*13)Glass-fiber-fabric, by process making such as knife scraping coating, sizing, embossing cooling, a windings
There is high intensity into, product, it is fire prevention, mould proof, moistureproof.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (5)
1. a kind of self-cleaning fire-retardant decorative film production process of high-performance glass, it comprises the following steps:(1) by glass fibre base fabric by
Unwinding device is unreeled;
(2) slurry is prepared, 200 revs/min are stirred 30 minutes;
(3) a knife scraping coating forming processes are carried out;
(4) setting temperature of knife scraping coating heat treatment:Pressing roll temperature is 130 DEG C -140 DEG C, and the temperature of baking oven 1 is 160 DEG C, is dried
The temperature of case 2 is 165 DEG C, and the temperature of baking oven 3 is 200 DEG C, and the temperature of baking oven 4 is 200 DEG C, and the temperature of baking oven 5 is 200 DEG C, and the temperature of baking oven 6 is
200 DEG C, the temperature of baking oven 7 is 200 DEG C, and coating thickness is uniform, and surface effect is good, and plasticizing is good;
(5) embossed is carried out again, the pressure of embossed wheel group and rubber wheel is set to 70kg, and embossed wheel is bright face roller;Emboss
Cooling treatment is carried out after finishing;
(6) finally wound again.
2. the self-cleaning fire-retardant decorative film production process of a kind of high-performance glass according to claim 1, it is characterised in that described
The step of (1) in glass fibre base fabric density be 1000D.
3. the self-cleaning fire-retardant decorative film production process of a kind of high-performance glass according to claim 1, it is characterised in that described
The step of (3) in knife scraping coating be layer of silica gel, described layer of silica gel is 25 ± 5 grams/m.
4. the self-cleaning fire-retardant decorative film production process of a kind of high-performance glass according to claim 1, it is characterised in that described
The step of (3) in knife scraping coating technical recipe it is as follows:50 parts of silica gel A;50 parts of silica gel B;6 parts of opacifier.
5. the self-cleaning fire-retardant decorative film production process of a kind of high-performance glass according to claim 1, it is characterised in that described
The step of (4) in knife scraping coating heat treatment speed control in 5 ± 1m/min.