CN106928839A - The long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable - Google Patents
The long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable Download PDFInfo
- Publication number
- CN106928839A CN106928839A CN201710129752.1A CN201710129752A CN106928839A CN 106928839 A CN106928839 A CN 106928839A CN 201710129752 A CN201710129752 A CN 201710129752A CN 106928839 A CN106928839 A CN 106928839A
- Authority
- CN
- China
- Prior art keywords
- parts
- long
- metallic paint
- sand washing
- carriage shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable, including urethane acrylate, distilled water, organic siliconresin, light absorber, flatting silica, metal powder, nano pulp, antioxidant, light stabilizer, resorcinol, dispersant, defoamer, levelling agent.The present invention passes the luminous energy for absorbing by ultra-violet absorber and replaces to light stabilizer, and light stabilizer is converted by the luminous energy that molecular vibration will absorb；In addition, when even if extraneous sunlight is too strong, antioxidant can also participate in reaction, consumption degraded oxygen atom reaches the effect of duplicate protection；Flatting silica, fineness is good, and good dispersion is not thickened, good leveling property；Present invention introduces heat resistance, electrical insulating property, photostability that organosilicon can increase substantially coating.
Description
Technical field
The present invention relates to water paint field, and in particular to a kind of long-acting resistance to aqueous gold of sand washing high-iron carriage shell of high durable
Category coating.
Background technology
High ferro enters into the trip of people in recent years, carries the security of the lives and property of multifarious traveller, and introduce cost compared with
Height, therefore anti-corrosion, maintenance, the weather-proof, service life of high-iron carriage outer surface just become particularly important for a long time.High-iron carriage appearance
The supporting coating of coating paint vehicle requirement has good compatibility；Environmental protection, long-lasting protection, high glaze, high rigidity, high tenacity,
The excellent performances such as adhesive force；Resistance to marring, resistance to sand washing are good；Corrosion resistance；Uvioresistant, guarantor's light colour retention are all good.
The content of the invention
Regarding to the issue above, applied the invention provides a kind of long-acting resistance to sand washing high-iron carriage shell water-based metal of high durable
Material.
The present invention is adopted the technical scheme that：A kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of weathering high
Composition is included by mass fraction
65 parts of urethane acrylate
30 parts of distilled water
19 parts of organic siliconresin
15 parts of metal powder
6 parts of light absorber
6 parts of flatting silica
5 parts of nano pulp
2 parts of antioxidant
2 parts of light stabilizer
0.5 part of resorcinol
0.4 part of dispersant
0.4 part of defoamer
0.2 part of levelling agent.
As a kind of perferred technical scheme：Described organic siliconresin SN480 or SN600.
As a kind of perferred technical scheme：Described light absorber is aminodithioformic acid nickel salt.
As a kind of perferred technical scheme：Described metal powder is one or more in magnesium powder or iron powder.
As a kind of perferred technical scheme：Described nano pulp is nano titanium oxide or nano imvite.
As a kind of perferred technical scheme：Described antioxidant is tributyl phosphite or phosphorous acid benzene di-isooctyl.
As a kind of perferred technical scheme：Described light stabilizer is the one kind in UV-P, UV-327 or UV-326
Or it is several.
As a kind of perferred technical scheme：Described dispersant is SN5040；Described defoamer is A10：Described
Levelling agent is one or more in RM2020, A203.
The beneficial effects of the invention are as follows：（1）The luminous energy for absorbing is passed by ultra-violet absorber is replaced to light stabilizer, light is steady
Determine agent to be converted by the luminous energy that molecular vibration will absorb；（2）Even if external world's sunlight is too strong, antioxidant can also participate in reaction, disappear
Consumption degraded oxygen atom, reaches the effect of duplicate protection；（3）Flatting silica, fineness is good, and good dispersion is not thickened, good leveling property；（4）
Present invention introduces heat resistance, electrical insulating property, photostability that organosilicon can increase substantially coating；Environmental protection of the present invention, nothing
Pollution.
Specific embodiment
In order to further illustrate the present invention, the present invention is described in detail below by embodiment, but can not be by it
Be interpreted as limiting the scope of the present invention.
Embodiment 1
65 parts of urethane acrylate
30 parts of distilled water
19 parts of SN480
15 parts of magnesium powder
6 parts of aminodithioformic acid nickel salt
6 parts of flatting silica
5 parts of nano titanium oxide
2 parts of tributyl phosphite
2 parts of UV-P
0.5 part of resorcinol
0.4 part of SN5040
0.4 part of A10
0.2 part of RM2020.
Embodiment 2
65 parts of urethane acrylate
30 parts of distilled water
19 parts of SN600
15 parts of magnesium powder
6 parts of aminodithioformic acid nickel salt
6 parts of flatting silica
5 parts of nano imvite
2 parts of phosphorous acid benzene di-isooctyl
2 parts of UV-327
0.5 part of resorcinol
0.4 part of SN5040
0.4 part of A10
0.2 part of A203.
Embodiment 3
65 parts of urethane acrylate
30 parts of distilled water
19 parts of SN600
15 parts of iron powder
6 parts of aminodithioformic acid nickel salt
6 parts of flatting silica
5 parts of nano titanium oxide
2 parts of phosphorous acid benzene di-isooctyl
1 part of UV-327
1 part of UV-326
0.5 part of resorcinol
0.4 part of SN5040
0.4 part of A10
0.1 part of A203
0.1 part of RM2020.
It should be noted last that, above example is only used to supplement explaination technical scheme and unrestricted.To the greatest extent
Pipe has been described in detail with reference to embodiment to the present invention, this area it is vast it will be appreciated by the skilled person that to skill of the invention
Art scheme is modified or is replaced on an equal basis, and without departure from the spirit and scope of technical solution of the present invention, it all should cover at this
In the middle of the right of invention.
Claims (8)
1. the long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of a kind of weathering high, it is characterised in that：The long-acting resistance to punching of weathering high
The composition of sand high-iron carriage shell waterborne metallic paint is included by mass fraction
65 parts of urethane acrylate
30 parts of distilled water
19 parts of organic siliconresin
15 parts of metal powder
6 parts of light absorber
6 parts of flatting silica
5 parts of nano pulp
2 parts of antioxidant
2 parts of light stabilizer
0.5 part of resorcinol
0.4 part of dispersant
0.4 part of defoamer
0.2 part of levelling agent.
2. a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable according to claim 1, its feature
It is：Described organic siliconresin is SN480 or SN600.
3. a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable according to claim 1, its feature
It is：Described light absorber is aminodithioformic acid nickel salt.
4. a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable according to claim 1, its feature
It is：Described metal powder is one or more in magnesium powder or iron powder.
5. a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable according to claim 1, its feature
It is：Described nano pulp is nano titanium oxide or nano imvite.
6. a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable according to claim 1, its feature
It is：Described antioxidant is tributyl phosphite or phosphorous acid benzene di-isooctyl.
7. a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable according to claim 1, its feature
It is：Described light stabilizer is one or more in UV-P, UV-327 or UV-326.
8. a kind of long-acting resistance to sand washing high-iron carriage shell waterborne metallic paint of high durable according to claim 1, its feature
It is：Described dispersant is SN5040；Described defoamer is A10：Described levelling agent is in RM2020, A203
One or more.